CN101774814A - Ceramic and carbon nano-fiber composite material and preparation method thereof - Google Patents
Ceramic and carbon nano-fiber composite material and preparation method thereof Download PDFInfo
- Publication number
- CN101774814A CN101774814A CN201010031349A CN201010031349A CN101774814A CN 101774814 A CN101774814 A CN 101774814A CN 201010031349 A CN201010031349 A CN 201010031349A CN 201010031349 A CN201010031349 A CN 201010031349A CN 101774814 A CN101774814 A CN 101774814A
- Authority
- CN
- China
- Prior art keywords
- carbon
- pottery
- ceramic
- composite material
- carbon nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a ceramic and carbon nano-fiber composite material and a preparation method thereof. The preparation method has a principle of directly growing carbon nano-fiber in a ceramic hole which is formed in a ceramic body in the ceramic forming process to prepare the ceramic and composite material. The specific process comprises the following steps: mixing a metallic catalyst and ceramics; inputting carbonous gas to a system in an intermediate stage of preparing the ceramics by sintering or pyrogenation; directly growing the carbon nano-fiber in the hole by utilizing the metallic catalyst formed in the ceramic hole; and further rising the temperature and sintering or pyrolyzing the ceramics which grows the carbon nano-fiber to prepare the carbon nano-fiber and ceramic composite material. Through the in-situ preparation method, the ceramic composite material with the uniformly-distributed carbon nano-fiber can be prepared. As the growing of the carbon nano-fiber is completed by one step in the process of sintering or pyrolyzing the ceramics, the flow process is simple and controllable, and has the characteristics of low preparation temperature; the composite materials with different shapes and sizes can be prepared; and the flow process can be applied to the preparation of the high-performance fiber reinforced ceramic composite material and in an application field thereof.
Description
Technical field
The present invention relates to a kind of pottery and carbon nano-fiber composite material and preparation method, specifically is that the growth in situ single stage method prepares carbon nanofiber and ceramic composite, belongs to technical field of material.
Background technology
Pottery has advantages such as low density, high rigidity, excellent high-temperature performance, is the important materials of hi-techs such as aerospace, the energy and building and civil area.The high performance fiber of fiber composite ceramics material use can be toughness reinforcing and intensified ceramic, be stoped crackle, improves the mechanical property of pottery, can obtain to conduct electricity simultaneously and the material of functional performance.Traditional fiber and ceramic composite are normally based on the carbon fiber of micron order diameter and pottery preparation, the method of preparation is that fiber production is become precast body, by mode and Ceramic Composite such as liquid phase or gas-phase permeations, through oversintering or pyrogenically prepared fiber and ceramic composite.The carbon fiber diameter is big, the surface is that inertia and toughness are lower, and problems such as it and ceramic matrix exist that the interface does not match, heat or structural stress have influenced performances such as the mechanics of matrix material, high temperature resistant, anti-oxidant and heat shock resistance.
Carbon nanofiber is that diameter is nano level carbon fibre material, comprise solid carbon nanofiber and hollow carbon nano-tube material, it has the vertical ratio of high length, high-specific surface area, high strength, high-modulus, high tenacity and excellent physics, mechanics and functional performance such as high conductivity, high thermal conductivity, be ideal material (the W.A.Curtin and B.W.Sheldon that strengthens stupalith, " CNT-Reinforced Ceramics and Metals; " Materials Today, 7,44-49 (2004)).At present, adopting carbon nanofiber to strengthen pottery mainly is that the carbon nanofiber that will prepare joins in the pottery, mixes or dispersion by machinery or liquid phase etc., and then carries out sintering or pyrolysis preparation.Another composite pathway is to grow carbon nanotube on ceramic powder particle earlier, and then the composite powder sintering prepared carbon nanotube and ceramic composite (E.Flahaut, A.Peigney, Ch.Laurent, Ch.Marliere, F.Chastel F and A.Rousset, " Carbon Nanotube-Metal-OxideNanocomposites:Microstructure; Electrical Conductivity and Mechanical Properties; " ActaMater, 48,3803-12 (2000)).But these methods exist the problem of general character, and promptly carbon nanofiber is reunited in pottery easily, is difficult to reach evenly compound; Simultaneously, carbon nanofiber is stochastic distribution in matrix, and non-orientation because agglomeration traits is difficult to reach the dispersion of higher volumes.These difficulties are subject matter (X.T.Wang that the restriction composite property improves, N.P.Padture and H.Tanaka, " Contact-Damage-Resistant Ceramic/Single-Wall carbonNanotubes and Ceramic/Graphite Composites; " Nat.Mater.3,539-544 (2004)).On the other hand, adopt these methods because carbon nanofiber is distributed in ceramic grain surface, it stops intergranular sintering in the ceramic post sintering process, make material be difficult to densification, and the high temperature sintering that adopts or fast plasma sintering because high sintering temperature, the structure of the compound intravital carbon nanofiber of easy damaged, thereby influence performance of composites (C.Balazsi, Z.Konya, F.Weber, L.P.Biro and P.Arato, " Preparation and Characterization of Carbon NanotubeReinforced Silicon Nitride Composites; " Materials Science and Engineering, 23,1133-37 (2003)).
At above problem, the invention provides the carbon nanofiber of growth in situ in ceramic matrix and ceramic composite and preparation method thereof.Direct growth goes out carbon nanofiber to principle in the hole that forms in ceramic body in order to utilize in the process of sintering or pyrolysis preparation pottery.The principle of growth carbon nanofiber is can form (A.C.Dupuis by the catalytic pyrolysis carbon-containing atmosphere on metal catalysts such as iron, cobalt, nickel at a certain temperature according to carbon nanofiber, " The Catalyst in the CCVD of CarbonNanotubes:a Review; " Progress in Materials Science, 50,929-61 (2005)).
Concrete grammar is for introducing granules of catalyst in ceramic hole, preparing in sintering or pyrolysis provides carbon source in the ceramic process, under suitable temperature, grow carbon nanofiber in the hole of pottery.Adopt this method in ceramic matrix, direct growth to go out carbon nanofiber, the carbon nanofiber that grows forms homodisperse in pottery, growth back further elevated temperature makes ceramic densifying, and the contraction of pottery is combined closely the carbon nanofiber and the pottery of growth in it.Can solve carbon nanofiber with this method and in ceramic matrix, disperse uneven problem, prepare that a step composite growth goes out carbon nanofiber in the ceramic process, prepare the ceramic composite of fine and close carbon nanofiber.Adopt this method, can under lower temperature, just prepare the matrix material of carbon nanofiber and pottery.
Summary of the invention
The object of the present invention is to provide a kind of pottery and carbon nano-fiber composite material and preparation method, described material is to prepare one step of carbon nanofiber that original position grows in pottery, the preparation method grows carbon nanofiber in the nanoporous that forms in ceramic body in the process of sintering and pyrolysis pottery, thereafter sintering and pyrolysis make ceramic densifying under the elevated temperature, therefore adopt present method a step to obtain closely knit shaped ceramic bodies.This growth in situ method goes out owing to carbon nanofiber direct growth in pottery; do not need blending in of fibers; process such as functionalization and dispersion; a preparation fiber and matrix material step in sintering or pyrolysis finishes; therefore; it is simple that the present invention has preparation process, and the advantage that the material formation temperature is lower is fit to scale preparation.Adopt the carbon nano-fiber composite material of this growth in situ method preparation to have homodisperse characteristics, can be used for preparing high performance carbon nano-fiber composite material.Therefore, the present invention is a kind of ideal method of preparation carbon nanofiber and ceramic composite.
Pottery provided by the invention and carbon nano-fiber composite material are to be matrix with the pottery, grow carbon nanofiber in the nanoporous that forms in the preparation pottery within it, form matrix material through sintering or pyrolysis.
The principle of the technology of the present invention is that foundation prepares in the pottery at sintering or pyrolysis, and the development and the densification process of material experience micron and nanoporous utilize the micron, the nanoporous that produce in the ceramic forming process, direct growth carbon nanofiber in these holes.Being implemented in the approach that grows carbon nanofiber in the ceramic hole is to sneak into a certain amount of metal catalyst or metallic precursor in pottery in advance; in the process of sintering or pyrolysis pottery; carbonaceous gas is provided in protective atmosphere, is implemented in the space in the pottery and grows carbon nanofiber.
In preparation pottery or ceramic forerunner, add metallic catalyzer, in pottery forms, in system, import carbonaceous gas or liquid, the granules of catalyst that in ceramic hole, forms, the catalytic pyrolysis carbonaceous gas grows carbon nanofiber in the hole.
Described carbon nanofiber refers to that carbon has the carbon material of 1-dimention nano diameter, comprises solid carbon fiber and hollow tubulose carbon fiber etc., and the diameter of carbon nanofiber is 1-500nm.
Described pottery is siliceous pottery, comprises potteries such as SiOC, SiCN, SiC, SiBCN, or contain Fe, Ni simultaneously in the middle of them, Co, Al, metallic elements such as Zr, Cu.
Described pottery is the compound of oxide ceramics such as silicon carbide, silicon nitride, carbonitride of silicium, silicon oxide carbide pottery and alumina-ceramic, zirconia ceramics.
Can add sintering aid in described pottery, sintered ceramic is used MgO and Y usually
2O
3Deng and composition thereof.
Described ceramic forerunner is siliceous polymkeric substance, includes but not limited to one or more mixing of polysiloxane, Polycarbosilane, polysilazane, poly-silicon borine.
Described catalyzer is metal, metal oxide, metal-salt or their mixing, comprises Fe, Co, Ni, Ru, Rh, Pd, Ir, Pt and oxide compound thereof, metal-salt or their mixing.
The step that the preparation method of a kind of pottery provided by the invention and carbon nano-fiber composite material comprises:
To contain in the silicon precursor that to add the carbon nanofibers grow catalyst mix even, pour the mould cross moulding into, under atmosphere protection, be heated to certain temperature, and feed carbon source for growth and go out carbon nanofiber, make pottery and carbon nano-fiber composite material.
Described carbon source is one or more mixing of hydrocarbon polymer, hydrocarbon, hydrocarbon oxygen compound.
Described atmosphere is non-oxidizing atmosphere, comprises inert atmospheres such as reducing atmospheres such as hydrogen, ammonia and argon gas, helium, nitrogen.
Described catalyzer is metal, metal oxide, metal-salt or their mixing, comprises Fe, Co, Ni, Ru, Rh, Pd, Ir, Pt and oxide compound thereof, metal-salt or their mixing.The content of described catalyzer in raw material can be 0.1-10wt.%.
Described feeding carbon source temperature is 500-1400 ℃.
A kind of pottery provided by the invention and carbon nano-fiber composite material are to be raw material with siliceous ceramic forerunner and carbon source; contain and add the carbon nanofibers grow catalyzer in the silicon precursor; cross moulding in mould; under argon gas, hydrogen, nitrogen or the protection of their mixed atmosphere, be heated to 600-1200 ℃ then; feed carbon source; grow carbon nanofiber, make pottery and carbon nano-fiber composite material.Siliceous ceramic forerunner: the mixing of one or more of polysiloxane, Polycarbosilane, poly-nitrogen silane, poly-Si-B-C-N, poly-silicon boron oxygen carbon (for example: the mixing of hydrogen-containing siloxane, vinyl cyclotetrasiloxane and polydimethylsiloxane).Carbon source: the mixing of one or more of hydrocarbon polymer, hydrocarbon, hydrocarbon oxygen compound can be selected from one or more mixing of ethanol, ethylene glycol, acetone, dimethylbenzene, normal hexane, methane, acetylene or ethene.The growth carbon nano-fiber catalyst: metal, metal oxide, metal-salt or several mixing comprise for example Fe, Co, Ni, Ru, Rh, Pd, Ir, Pt and oxide compound thereof, metal-salt or several mixing.Preferred iron(ic) chloride or ferrocene.
The present invention grows carbon nanofiber in a step in the process of preparation pottery in pottery, to the pottery of the carbon nanofiber of growth further under the elevated temperature sintering and pyrolysis make its densification, therefore obtain fine and close shaped ceramic bodies.This growth in situ method is owing to direct growth in pottery goes out fiber; do not need fiber dispersion; process such as functionalization and mixing; since the preparation be in sintering or pyrolysis one the step finish; can prepare carbon nanofiber and ceramic composite under lower temperature, therefore, it is simple that the technology of the present invention has a preparation process; advantages such as preparation cost is low are fit to scale preparation.Simultaneously, adopt the carbon nano-fiber composite material of this growth in situ method preparation to have homodisperse characteristics, and can prepare three-dimensional block matrix material, can develop into and have high performance carbon nano-fiber composite material, can be applicable to prepare high-performance fiber and strengthen ceramic composite and Application Areas thereof.
Description of drawings
SiOC pottery and carbon nano-fiber composite material profile scanning Electronic Speculum figure that Fig. 1 makes for the embodiment of the invention 1.
SiOC pottery and carbon nano-fiber composite material sem photograph that Fig. 2 makes for the embodiment of the invention 1.
SiOC pottery and carbon nano-fiber composite material transmission electron microscope picture that Fig. 3 makes for the embodiment of the invention 1.
SiOC pottery and carbon nano-fiber composite material transmission electron microscope picture that Fig. 4 makes for the embodiment of the invention 1.
SiOC pottery and carbon nano-fiber composite material profile scanning Electronic Speculum figure that Fig. 5 makes for the embodiment of the invention 4.
SiOC pottery and carbon nano-fiber composite material profile scanning Electronic Speculum figure that Fig. 6 makes for the embodiment of the invention 7.
SiOC pottery and carbon nano-fiber composite material profile scanning Electronic Speculum figure that Fig. 7 makes for the embodiment of the invention 8.
SiCN pottery and carbon nano-fiber composite material profile scanning Electronic Speculum figure that Fig. 8 makes for the embodiment of the invention 14.
Embodiment
Embodiment 1: 2g hydrogen-containing siloxane, 1g vinyl cyclotetrasiloxane and 1.5g polydimethylsiloxane are mixed, add 45mg FeCl
3, add the 45mg platinum catalyst, pour mould into, 80 ℃ of heating 4h obtain formed body, and formed body is put into stove, be warming up to 850 ℃ in the argon gas, feed 15ml/h ethanol growth carbon pipe 30min, temperature is risen to 1000 ℃ of pyrolysis 1h prepare silicon-oxygen-carbon ceramic and carbon nano-fiber composite material body.Pound disconnected matrix material with blunt, vertical many carbon nanofibers (accompanying drawing 1) that detaches are arranged from ceramic matrix with the fresh section of scanning electron microscopic observation.The carbon nanofiber (accompanying drawing 2) of vertical many bridgings is arranged in the new crack that forms, another zone of scanning electron microscopic observation composite bodies, further specify and in ceramic body, grow carbon nanofiber.Observed carbon nanofiber diameter 5-100nm.With the broken sample of transmission electron microscope observing, to observe carbon nanofiber and have hollow structure, two sidewalls are the graphite linings that number equates, prove that the carbon nanofiber that forms is carbon nanotube structure (accompanying drawing 3).Observe carbon nanofiber (accompanying drawing 4) simultaneously, diameter 100-500nm with solid construction.
Embodiment 2: adopt the identical method of example 1, with the FeCl that adds in the ceramic forerunner
3The amount of catalyzer is reduced to 4.5mg, and pyrolysis obtains SiOC pottery and carbon nano-fiber composite material.
Embodiment 3: adopt the identical method of example 1, with the FeCl that adds in the ceramic forerunner
3The amount of catalyzer is reduced to 450mg, and pyrolysis obtains SiOC pottery and carbon nano-fiber composite material.
Embodiment 4: adopt the identical method of example 1, will feed the carbon source temperature and be upgraded to 1000 ℃, obtain SiOC pottery and carbon nano-fiber composite material after grow carbon nanofiber and the pyrolysis.Scanning electron microscopic observation matrix material section has the carbon nanofiber of extracting from matrix, and as accompanying drawing 5, Fibre diameter is 20-50nm.
Embodiment 5: adopts the identical method of example 1, changes the amount of silicon-oxygen-carbon ceramic presoma, and 1.5g hydrogen-containing siloxane/1.5g vinyl cyclotetrasiloxane/1.5g polydimethylsiloxane, pyrolysis obtains SiOC pottery and carbon nano-fiber composite material.
Embodiment 6: adopts the identical method of example 1, changes the amount of silicon-oxygen-carbon ceramic presoma, and 2g hydrogen-containing siloxane/1g vinyl cyclotetrasiloxane, pyrolysis obtains SiOC pottery and carbon nano-fiber composite material.
Embodiment 7: adopt the identical method of example 1, protective atmosphere is a nitrogen, and pyrolysis obtains SiOC silicon-oxygen-carbon ceramic and carbon nano-fiber composite material.Scanning electron microscopic observation matrix material section has carbon nanofiber, as accompanying drawing 6.
Embodiment 8: adopt the identical method of example 6, carbon source kind is an ethene, and pyrolysis obtains SiOC silicon-oxygen-carbon ceramic and carbon nano-fiber composite material.Scanning electron microscopic observation matrix material section has carbon nanofiber, as accompanying drawing 7.
Embodiment 9: adopt the identical method of example 7, change the feeding amount and the feeding time of carbon source, ethene feeds with the speed of 30ml/h, and 15min stops, and pyrolysis obtains SiOC pottery and carbon nano-fiber composite material.
Embodiment 10: adopt the identical method of example 1, protective atmosphere is a hydrogen, and pyrolysis obtains SiOC pottery and carbon nano-fiber composite material.
Embodiment 11: adopt the identical method of example 1, protective atmosphere is argon gas and hydrogen, and pyrolysis obtains SiOC pottery and carbon nano-fiber composite material.
Embodiment 12: adopt the identical method of example 1, it is 600 ℃ that carbon source feeds temperature, and pyrolysis obtains SiOC pottery and carbon nano-fiber composite material.
Embodiment 13: adopt the identical method of example 1, change the ceramic forerunner kind, the 10g Polycarbosilane is replaced the polysiloxane presoma, pyrolysis obtains SiC pottery and carbon nano-fiber composite material.
Embodiment 14: adopt the identical method of example 1, change the ceramic forerunner kind, the 5g polysilazane is replaced the polysiloxane presoma, pyrolysis obtains SiCN pottery and carbon nano-fiber composite material.Scanning electron microscopic observation matrix material section has carbon nanofiber, and fiber is evenly distributed in matrix, as accompanying drawing 8.
Embodiment 15: adopt the identical method of example 1, change catalyzer into the 0.045g ferrocene, pyrolysis obtains pottery and carbon nano-fiber composite material.
Embodiment 16: ferrocene sneaked into in silicon carbide, silicon nitride and the alumina powder, and dry-pressing formed, put into stove and heat, to 850 ℃, feed the ethanol carbon source, prepare carbon nanofiber and ceramic composite.
Claims (10)
1. pottery and carbon nano-fiber composite material, it is characterized in that it is to be prepared from for the matrix compound carbon nanofiber with the pottery, in the process of preparation pottery, utilize pottery to form the hole that the intermediate stage forms in ceramic body, through oversintering or pyrolysis, direct growth goes out carbon nanofiber in the hole, forms matrix material.
2. according to the described matrix material of claim 1, it is characterized in that in preparation pottery or ceramic forerunner, adding metallic catalyzer, in forming, pottery in system, imports carbonaceous gas, the granules of catalyst that in ceramic hole, forms, the catalytic pyrolysis carbonaceous gas grows carbon nanofiber in the hole.
3. according to claim 1 or 2 described matrix materials, it is characterized in that described carbon nanofiber is meant the carbon nanofiber material with nanometer grade diameter with one-dimentional structure of carbon, comprise solid carbon nanofiber and hollow tubulose carbon nanofiber, the diameter of carbon nanofiber is 1-500nm.
4. according to claim 1 or 2 described matrix materials, it is characterized in that described pottery is siliceous pottery, comprise potteries such as SiOC, SiCN, SiC, SiBCN, or contain Fe, Ni simultaneously in the middle of them, Co, Al, metallic elements such as Zr, Cu.
5. according to claim 1 or 2 described matrix materials, it is characterized in that described pottery is the compound of oxide ceramics such as silicon carbide, silicon nitride, carbonitride of silicium, silicon oxide carbide pottery and alumina-ceramic, zirconia ceramics.
6. according to the described matrix material of claim 2, it is characterized in that described ceramic forerunner is siliceous polymkeric substance, include but not limited to one or more mixing of polysiloxane, Polycarbosilane, polysilazane, poly-silicon borine.
7. according to the described matrix material of claim 2, it is characterized in that described catalyzer is metal, metal oxide, metal-salt or their mixing, comprises Fe, Co, Ni, Ru, Rh, Pd, Ir, Pt and oxide compound thereof, metal-salt or their mixing.
8. the preparation method of pottery and carbon nano-fiber composite material is characterized in that the step that comprises:
To contain in the silicon precursor that to add the carbon nanofibers grow catalyst mix even, pour the mould cross moulding into, under atmosphere protection, heat, and feed carbon source for growth and go out carbon nanofiber, make pottery and carbon nano-fiber composite material;
Described carbon source is one or more mixing of hydrocarbon polymer, hydrocarbon, hydrocarbon oxygen compound;
Described atmosphere is non-oxidizing atmosphere, comprises inert atmospheres such as reducing atmospheres such as hydrogen, ammonia and argon gas, helium, nitrogen;
Described catalyzer is metal, metal oxide, metal-salt or their mixing, comprises Fe, Co, Ni, Ru, Rh, Pd, Ir, Pt and oxide compound thereof, metal-salt or their mixing; The content of described catalyzer in raw material is 0.1-10wt.%;
Described feeding carbon source temperature is 500-1400 ℃.
9. the preparation method of pottery and carbon nano-fiber composite material; it is characterized in that being is raw material with siliceous ceramic forerunner and carbon source; contain and add the carbon nanofibers grow catalyzer in the silicon precursor; cross moulding in mould; under argon gas, hydrogen, nitrogen or the protection of their mixed atmosphere, be heated to 600-1200 ℃ then; feed carbon source, grow carbon nanofiber, make pottery and carbon nano-fiber composite material.
10. in accordance with the method for claim 9, it is characterized in that described siliceous ceramic forerunner is: the mixing of one or more of polysiloxane, Polycarbosilane, poly-nitrogen silane, poly-Si-B-C-N, poly-silicon boron oxygen carbon; Carbon source is selected from: the mixing of one or more of ethanol, ethylene glycol, acetone, dimethylbenzene, normal hexane, methane, acetylene or ethene; Described carbon nanofibers grow carbon nano-fiber catalyst is: iron(ic) chloride or ferrocene.