CN101768795A - Processing method and application of color polyester staple fibre - Google Patents
Processing method and application of color polyester staple fibre Download PDFInfo
- Publication number
- CN101768795A CN101768795A CN200810243243A CN200810243243A CN101768795A CN 101768795 A CN101768795 A CN 101768795A CN 200810243243 A CN200810243243 A CN 200810243243A CN 200810243243 A CN200810243243 A CN 200810243243A CN 101768795 A CN101768795 A CN 101768795A
- Authority
- CN
- China
- Prior art keywords
- color
- staple fibre
- polyester staple
- processing method
- waste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A processing method and application of color polyester staple fibre relate to a processing method and application of polyester staple fibre, wherein small chemical fibre pulp lumps and waste color polyester beverage bottles are used as main raw materials. The processing method comprises the following steps: selecting waste polyester beverage bottles with the same color or different colors according to different goals and requests, cleaning, drying, grinding to 1-8mm of particles; using 15-30 parts of particles by weight to heat to 250-298 DEG C in a container, after completely melting the particles, adding 70-95 parts of grinded small chemical fibre pulp lumps by weight, mixing evenly; and spinning to obtain the color polyester staple fibre. The waste color beverage bottles and small chemical fibre pulp lumps are used as main raw materials so as to fully utilize the waste. As viewed from resource utilization, the potentialities of resources are effectively developed; as viewed from environmental protection, the processing period of the waste is reduced; and as viewed from economy, the waste has utilization value and a certain additional value. Meanwhile, the produced color yarn can be directly used in fabric, thus canceling dyeing and finishing processes, namely a factor of environmental pollution.
Description
Technical field
The present invention relates to a kind of processing method and application thereof of terylene short fiber, the manufacture method and the application thereof of a kind of color polyester short fiber of more specifically saying so.
Background technology
Textiles all needs dyeing and finishing, and on cotton, hairs fabric, dyeing and finishing technology is ripe relatively, but can pollute environment.On the chemical fibre kind fabric, carry out the dyeing and finishing technology complexity, the cost height, uniformity is poor, and stability is bad.At present, there is a large amount of lumps to produce, belongs to the secondary pollutant of production, do not make full use of in little chemical fibre industry.Simultaneously, in the life, there is a large amount of colored plastic beverage bottles to go out of use now, is used as garbage disposal mostly, also be not fully utilized.
Summary of the invention
The present invention is directed to above problem, providing a kind of is raw material with discarded colour drinks bottle and little chemical fibre lumps, directly is processed into the color polyester short fiber, saves road, back dyeing and finishing process, thus the processing method of environmentally friendly color polyester staple fibre.The present invention provides this processing method to make the application of color polyester staple fibre simultaneously.
The technical scheme of processing method of the present invention is: it is a main raw material with little chemical fibre lumps, useless variegated polyester beverage bottle, processing according to the following steps:
1), the color matching of selecting materials, according to target require to select the useless polyester beverage bottle of identical or different color, clean, drying, pulverizing is 1～8mm particle;
2), batching, get 15～30 weight portion particulate material, in container, heat to 250～298 ℃, after melting fully, add the little chemical fibre lumps of 70～95 parts by weight of crushed, evenly mix;
3), spray silk, make color polyester staple fibre.
In batching step, add an amount of delustring masterbatch.
Application scheme of the present invention is: the described color polyester staple fibre that makes spins, and makes the color polyester yarn, with the cotton yarn blending, makes coloured yarn again.
The present invention is a main raw material with discarded colour drinks bottle and little chemical fibre lumps, has made full use of discarded object.From utilization of resources angle, effectively excavated the potential of resource; From environmental angle, reduced the processing cycle of discarded object; From economic angle, make discarded object that value arranged, give its certain added value.Simultaneously, the multicolored yarn of producing can be directly used in fabric, reduces dyeing and finishing process, has reduced by a factor of environmental pollution.
The specific embodiment
Embodiment one
It is a main raw material with little chemical fibre lumps, useless variegated polyester beverage bottle for processing method of the present invention, processing according to the following steps:
1), select the useless polyester beverage bottle of white, clean, drying is pulverized the particle into 3mm;
2), batching, get 20 weight portion particulate material, in container, heat to 260 ℃, after melting fully, add the little chemical fibre lumps of 80 parts by weight of crushed, evenly mix;
3), spray silk, make the white polyester staple fibre.
In batching step, add an amount of delustring masterbatch.
Application scheme of the present invention is: the described white polyester short staple spinning that makes, make the white polyester yarn, and with the cotton yarn blending, make white yarn again.
Embodiment two
Processing method of the present invention is to be main raw material with little chemical fibre lumps, useless variegated polyester beverage bottle, processing according to the following steps:
1), the green useless polyester beverage bottle of choosing, clean, drying is pulverized the particle into 1mm;
2), 15 weight portion particulate material, in container, heat to 250 ℃, after melting fully, add the little chemical fibre lumps of 95 parts by weight of crushed, evenly mix;
3), spray silk, make green polyester staple fiber.
In batching step, add an amount of delustring masterbatch.
During application of the present invention, will make green color polyester staple fibre spinning, make green spun polyester thread, with the cotton yarn blending, make green yarn again.
Embodiment three:
Processing method of the present invention is to be main raw material with little chemical fibre lumps, useless variegated polyester beverage bottle, processing according to the following steps:
1), the useless polyester beverage bottle of, black red by the choosing of 2: 1 weight ratios, clean, drying mixes that to pulverize be 1～8mm particle;
2), get 30 weight portion particulate material, in container, heat to 250 ℃, after melting fully, add the little chemical fibre lumps of 70 parts by weight of crushed, evenly mix;
3), spray silk, make the purple polyester staple fiber.
In batching step, add an amount of delustring masterbatch.
Application scheme of the present invention is with the spinning of purple polyester staple fiber, makes the purple spun polyester thread, with the cotton yarn blending, makes the purple yarn again.
Claims (3)
1. the processing method of a color polyester staple fibre, it is a main raw material with little chemical fibre lumps, useless variegated polyester beverage bottle, it is characterized in that, according to the following steps processing:
1), the color matching of selecting materials, according to target require to select the useless polyester beverage bottle of identical or different color, clean, drying, pulverizing is 1～8mm particle;
2), batching, get 15～30 weight portion particulate material, in container, heat to 250～298 ℃, after melting fully, add the little chemical fibre lumps of 70～95 parts by weight of crushed, evenly mix;
3), spray silk, make color polyester staple fibre.
2. the processing method of a kind of color polyester staple fibre according to claim 1 is characterized in that, in batching step, adds an amount of delustring masterbatch.
3. a kind of application of color polyester staple fibre according to claim 1 is characterized in that, the described color polyester staple fibre that makes spins, and makes the color polyester yarn, with the cotton yarn blending, makes coloured yarn again.