CN107674437A - The processing method that a kind of textile fabric recycles - Google Patents
The processing method that a kind of textile fabric recycles Download PDFInfo
- Publication number
- CN107674437A CN107674437A CN201710805051.5A CN201710805051A CN107674437A CN 107674437 A CN107674437 A CN 107674437A CN 201710805051 A CN201710805051 A CN 201710805051A CN 107674437 A CN107674437 A CN 107674437A
- Authority
- CN
- China
- Prior art keywords
- textile fabric
- processing
- recycles
- processing method
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the processing method that a kind of textile fabric recycles, comprise the following steps:(1)Cleaning treatment,(2)Low-temperature grinding processing,(3)Stir process,(4)Recycling processing.The present invention has carried out special processing to textile fabric, effectively improve the use quality that its filling recycles, mechanical characteristic and the life-span of wood plastic composite are improved well, with good economic benefit and practical value, a kind of direction and technical support well are provided for the recycling of existing textile fabric, promotes the green and healthy development of textile industry.
Description
Technical field
The invention belongs to textile technology field, and in particular to the processing method that a kind of textile fabric recycles.
Background technology
Synthetic fibers are raw material types common in present weaving manufacturing field, and in textile operation, it can produce a large amount of
Synthetic fibers leftover pieces, handled more in a manner of landfill, burning, this measure not only causes the wave of raw material of substance
Take, cause the serious pollution of environment again, for the green and healthy development of textile industry, need badly and solved to this problem.
The content of the invention
The purpose of the present invention is to be directed to the problem of existing, there is provided the processing method that a kind of textile fabric recycles.
The present invention is achieved by the following technical solutions:
The processing method that a kind of textile fabric recycles, comprises the following steps:
(1)Cleaning treatment:
Drying for standby after handling one time is rinsed to textile fabric with clear water;
(2)Low-temperature grinding processing:
By step(1)Textile fabric after processing is put into pulverizer, and it is -140 ~ -150 DEG C to keep the temperature in pulverizer,
After the completion of take out it is standby;
(3)Stir process:
A. by step(2)Textile fabric after processing is put into mixer, adds the mixing of textile fabric gross mass 10 ~ 15%
Liquid, the temperature that then heating is kept stirring in machine is 115 ~ 125 DEG C, standby after 15 ~ 20min of stir process;In the mixed liquor
Each composition and its corresponding parts by weight are:12 ~ 15 parts of ethylene glycol, 6 ~ 8 parts of trichloroethanes, 3 ~ 5 parts of acetamides, 2 ~ 4 parts of O-phthalics
Acid, 4 ~ 7 parts of water;Acetamide and phthalic acid composition in mixed liquor can be modified to textile fabric, improve its surface-active,
Enhance the effect subsequently polymerizeing;
B. the temperature in mixer is down to 80 ~ 85 DEG C, continues to be stirred textile fabric, while apply it60Co- gamma-ray irradiations are handled, standby after 30 ~ 35min;
(4)Recycling processing:
A. by step(3)Textile fabric after processing naturally cools to standby after normal temperature;
B. will operate textile fabric and thermoplastic particle after a processing, wood powder, bentonite, calcium carbonate, wood moulding auxiliary agent according to
Mass ratio 20 ~ 25:18~22:30~35:8~10:10~14:1 ~ 2 is mixed, after finally hot-forming.
Further, step(1)Described in drying after textile fabric overall water content be 13 ~ 16%.In drying process
Ensure that textile fabric contains certain water content afterwards, the fragility of lifting fiber is crystallized using moisture, promotes follow-up low-temperature grinding
Efficiency and effect.
Further, step(2)Described in pulverization process after the granular size of textile fabric be 150 ~ 200 mesh.
Further, step(3)The rotating speed for operating the mixer stir process described in a is 1500 ~ 1700 revs/min.
Further, step(3)The rotating speed for operating the mixer stir process described in b is 800 ~ 1000 revs/min.
Further, step(3)Operate described in b60The accumulated dose of Co- gamma-ray irradiations processing is 12 ~ 14kGy.
Further, step(4)The thermoplastic particle operated described in b is polypropylene plastics particle, polyethylene modeling
Expect any one in particle, igelite particle.
Further, the textile fabric is any one in polypropylene fibre, acrylic fibers, terylene, polyamide fibre.
Textile fabric is used in the preparation of wood plastic composite by someone in the prior art, as fiber filling material
Used, the use characteristic of wood plastic composite can be lifted, achieve good effect, but generally to be added in the method big
The chemical solvent of amount, production cost is not only increased, while be also possible to that a large amount of waste liquids can be produced, secondary pollution is caused to environment.
Improvement is optimized to the reuse method of textile fabric to this present invention, textile fabric is carried out at crushing using low temperature
Reason, avoids solvent in the prior art(Organic solvent, resin etc.)Use, reduce cost, protect environment, then carry out
Special stir process, wherein first having carried out a stir process, in high temperature and mixed liquor under the treatment conditions of solvent, spin
Melting adhesion occurs between textured fiber particle, while again under conditions of high-speed stirred processing, textile fabric particle is constantly disperseed
Upset, ultimately form substantial amounts of small granule, and carried out secondary stirring treatment, reduce the environment temperature of stirring, now
The textile fabric particle of bulk is in half plastifying state, application60The processing of Co- gamma-ray irradiations can promote blended liquid modified
Polymerization between textile fabric, the relative molecular mass of the textile fabric particle of bulk is improved, enhances its mechanical strength characteristics,
Improve its filling using effect in wood plastic composite.
The present invention has advantages below compared with prior art:
The present invention has carried out special processing to textile fabric, effectively improves the use quality that its filling recycles, well
Mechanical characteristic and the life-span of wood plastic composite are improved, there is good economic benefit and practical value, it is fine for existing weaving
The recycling of dimension provides a kind of direction and technical support well, promotes the green and healthy development of textile industry.
Embodiment
Embodiment 1
The processing method that a kind of textile fabric recycles, comprises the following steps:
(1)Cleaning treatment:
Drying for standby after handling one time is rinsed to textile fabric with clear water;
(2)Low-temperature grinding processing:
By step(1)Textile fabric after processing is put into pulverizer, and it is -140 DEG C to keep the temperature in pulverizer, after the completion of
Take out standby;
(3)Stir process:
A. by step(2)Textile fabric after processing is put into mixer, adds the mixed liquor of textile fabric gross mass 10%,
Then the temperature that heating is kept stirring in machine is 115 DEG C, standby after stir process 15min;In the mixed liquor each composition and its
Corresponding to parts by weight is:12 parts of ethylene glycol, 6 parts of trichloroethanes, 3 parts of acetamides, 2 parts of phthalic acids, 4 parts of water;
B. the temperature in mixer is down to 80 DEG C, continues to be stirred textile fabric, while apply it60Co-γ
X ray irradiation x is handled, standby after 30min;
(4)Recycling processing:
A. by step(3)Textile fabric after processing naturally cools to standby after normal temperature;
B. will operate textile fabric and thermoplastic particle after a processing, wood powder, bentonite, calcium carbonate, wood moulding auxiliary agent according to
Mass ratio 20:18:30:8:10:1 is mixed, after finally hot-forming.
Further, step(1)Described in drying after textile fabric overall water content be 13%.
Further, step(2)Described in pulverization process after the granular size of textile fabric be 150 mesh.
Further, step(3)The rotating speed for operating the mixer stir process described in a is 1500 revs/min.
Further, step(3)The rotating speed for operating the mixer stir process described in b is 800 revs/min.
Further, step(3)Operate described in b60The accumulated dose of Co- gamma-ray irradiations processing is 12kGy.
Further, step(4)The thermoplastic particle operated described in b is polypropylene plastics particle.
Further, the textile fabric is polypropylene fibre.
Embodiment 2
The processing method that a kind of textile fabric recycles, comprises the following steps:
(1)Cleaning treatment:
Drying for standby after handling one time is rinsed to textile fabric with clear water;
(2)Low-temperature grinding processing:
By step(1)Textile fabric after processing is put into pulverizer, and it is -145 DEG C to keep the temperature in pulverizer, after the completion of
Take out standby;
(3)Stir process:
A. by step(2)Textile fabric after processing is put into mixer, adds the mixed liquor of textile fabric gross mass 13%,
Then the temperature that heating is kept stirring in machine is 120 DEG C, standby after stir process 18min;In the mixed liquor each composition and its
Corresponding to parts by weight is:14 parts of ethylene glycol, 7 parts of trichloroethanes, 4 parts of acetamides, 3 parts of phthalic acids, 6 parts of water;
B. the temperature in mixer is down to 83 DEG C, continues to be stirred textile fabric, while apply it60Co-γ
X ray irradiation x is handled, standby after 32min;
(4)Recycling processing:
A. by step(3)Textile fabric after processing naturally cools to standby after normal temperature;
B. will operate textile fabric and thermoplastic particle after a processing, wood powder, bentonite, calcium carbonate, wood moulding auxiliary agent according to
Mass ratio 22:20:33:9:12:1.5 are mixed, after finally hot-forming.
Further, step(1)Described in drying after textile fabric overall water content be 15%.
Further, step(2)Described in pulverization process after the granular size of textile fabric be 180 mesh.
Further, step(3)The rotating speed for operating the mixer stir process described in a is 1600 revs/min.
Further, step(3)The rotating speed for operating the mixer stir process described in b is 900 revs/min.
Further, step(3)Operate described in b60The accumulated dose of Co- gamma-ray irradiations processing is 13kGy.
Further, step(4)The thermoplastic particle operated described in b is vinyon particle.
Further, the textile fabric is terylene.
Embodiment 3
The processing method that a kind of textile fabric recycles, comprises the following steps:
(1)Cleaning treatment:
Drying for standby after handling one time is rinsed to textile fabric with clear water;
(2)Low-temperature grinding processing:
By step(1)Textile fabric after processing is put into pulverizer, and it is -150 DEG C to keep the temperature in pulverizer, after the completion of
Take out standby;
(3)Stir process:
A. by step(2)Textile fabric after processing is put into mixer, adds the mixed liquor of textile fabric gross mass 15%,
Then the temperature that heating is kept stirring in machine is 125 DEG C, standby after stir process 20min;In the mixed liquor each composition and its
Corresponding to parts by weight is:15 parts of ethylene glycol, 8 parts of trichloroethanes, 5 parts of acetamides, 4 parts of phthalic acids, 7 parts of water;
B. the temperature in mixer is down to 85 DEG C, continues to be stirred textile fabric, while apply it60Co-γ
X ray irradiation x is handled, standby after 35min;
(4)Recycling processing:
A. by step(3)Textile fabric after processing naturally cools to standby after normal temperature;
B. will operate textile fabric and thermoplastic particle after a processing, wood powder, bentonite, calcium carbonate, wood moulding auxiliary agent according to
Mass ratio 25:22:35:10:14:2 are mixed, after finally hot-forming.
Further, step(1)Described in drying after textile fabric overall water content be 16%.
Further, step(2)Described in pulverization process after the granular size of textile fabric be 200 mesh.
Further, step(3)The rotating speed for operating the mixer stir process described in a is 1700 revs/min.
Further, step(3)The rotating speed for operating the mixer stir process described in b is 1000 revs/min.
Further, step(3)Operate described in b60The accumulated dose of Co- gamma-ray irradiations processing is 14kGy.
Further, step(4)The thermoplastic particle operated described in b is igelite particle.
Further, the textile fabric is polyamide fibre.
Comparative example 1
This comparative example 1 compared with Example 2, saves step(3)Mixed liquor addition operation in stir process operation a, is removed
In addition method and step all same.
Comparative example 2
This comparative example 2 compared with Example 2, saves step(3)Operation b processing in stir process, method in addition
Step all same.
Control group
Existing textile fabric recycles the method in wood plastic composite(In addition to the processing of textile fabric is different, wood moulding is multiple
Remaining composition of condensation material is identical with preparation method).
In order to contrast effect of the present invention, to side described in above-described embodiment 2, comparative example 1, comparative example 2, control group
Wood plastic composite made from method carries out performance test, and specific correction data is as shown in table 1 below:
Table 1
Tensile strength(MPa) | Bending strength(MPa) | Nail-holding ability(N) | |
Embodiment 2 | 42.01 | 70.12 | 6250 |
Comparative example 1 | 35.18 | 64.26 | 5370 |
Comparative example 2 | 34.34 | 62.35 | 5180 |
Control group | 31.25 | 56.48 | 4810 |
The effect that processing method of the present invention recycles to textile fabric it can be seen from upper table 1 is more preferable, wood moulding made from correspondence
The integrated quality of composite more preferably, has more preferable promotional value and economic benefit.
Claims (8)
1. the processing method that a kind of textile fabric recycles, it is characterised in that comprise the following steps:
(1)Cleaning treatment:
Drying for standby after handling one time is rinsed to textile fabric with clear water;
(2)Low-temperature grinding processing:
By step(1)Textile fabric after processing is put into pulverizer, and it is -140 ~ -150 DEG C to keep the temperature in pulverizer,
After the completion of take out it is standby;
(3)Stir process:
A. by step(2)Textile fabric after processing is put into mixer, adds the mixing of textile fabric gross mass 10 ~ 15%
Liquid, the temperature that then heating is kept stirring in machine is 115 ~ 125 DEG C, standby after 15 ~ 20min of stir process;In the mixed liquor
Each composition and its corresponding parts by weight are:12 ~ 15 parts of ethylene glycol, 6 ~ 8 parts of trichloroethanes, 3 ~ 5 parts of acetamides, 2 ~ 4 parts of O-phthalics
Acid, 4 ~ 7 parts of water;
B. the temperature in mixer is down to 80 ~ 85 DEG C, continues to be stirred textile fabric, while apply it60Co-
Gamma-ray irradiation is handled, standby after 30 ~ 35min;
(4)Recycling processing:
A. by step(3)Textile fabric after processing naturally cools to standby after normal temperature;
B. will operate textile fabric and thermoplastic particle after a processing, wood powder, bentonite, calcium carbonate, wood moulding auxiliary agent according to
Mass ratio 20 ~ 25:18~22:30~35:8~10:10~14:1 ~ 2 is mixed, after finally hot-forming.
2. the processing method that a kind of textile fabric according to claim 1 recycles, it is characterised in that step(1)Middle institute
The overall water content of textile fabric is 13 ~ 16% after the drying stated.
3. the processing method that a kind of textile fabric according to claim 1 recycles, it is characterised in that step(2)Middle institute
The granular size of textile fabric is 150 ~ 200 mesh after the pulverization process stated.
4. the processing method that a kind of textile fabric according to claim 1 recycles, it is characterised in that step(3)Operate a
Described in mixer stir process rotating speed be 1500 ~ 1700 revs/min.
5. the processing method that a kind of textile fabric according to claim 1 recycles, it is characterised in that step(3)Operate b
Described in mixer stir process rotating speed be 800 ~ 1000 revs/min.
6. the processing method that a kind of textile fabric according to claim 1 recycles, it is characterised in that step(3)Operate b
Described in60The accumulated dose of Co- gamma-ray irradiations processing is 12 ~ 14kGy.
7. the processing method that a kind of textile fabric according to claim 1 recycles, it is characterised in that step(4)Operate b
Described in thermoplastic particle be polypropylene plastics particle, vinyon particle, appointing in igelite particle
Meaning is a kind of.
8. the processing method that a kind of textile fabric according to claim 1 recycles, it is characterised in that the textile fabric
For any one in polypropylene fibre, acrylic fibers, terylene, polyamide fibre.