CN101760274A - 复合型煤及其制备方法 - Google Patents

复合型煤及其制备方法 Download PDF

Info

Publication number
CN101760274A
CN101760274A CN200910263965A CN200910263965A CN101760274A CN 101760274 A CN101760274 A CN 101760274A CN 200910263965 A CN200910263965 A CN 200910263965A CN 200910263965 A CN200910263965 A CN 200910263965A CN 101760274 A CN101760274 A CN 101760274A
Authority
CN
China
Prior art keywords
parts
coal
composite
preparation
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910263965A
Other languages
English (en)
Inventor
庄利斌
庄宇静
张霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN200910263965A priority Critical patent/CN101760274A/zh
Publication of CN101760274A publication Critical patent/CN101760274A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种复合型煤及其制备方法，它由以下重量的原料制成：洗中煤30-45％，煤泥30-45％，矸石10-20％，复合助剂4-8％，水10-14％；所述的复合助剂是由下列重量份的原料制成：木质素磺酸钙5-15份，磷酸二氢钠1-6份，电石灰0-7份，氯化镁5-15份，腐植酸铵0.5-5份，氢氧化钙5-15份，硝酸钾2-6份，高锰酸钾0.5-3份，硝酸钠0.2-2份，氯化钠0-3份，高岭土6-12份，蓖麻籽油渣3-7份，聚乙烯醇0.2-1份，水8-12份。其制备方法的步骤如下：将洗中煤，矸石，用粉碎机粉碎后，与煤泥，复合助剂加入搅拌机进行混合，搅拌均匀后经型煤压制机压制而成。本发明制备工艺简单，不需要烘干，二氧化硫和烟尘排放少，适用于工业、民用、石灰窑锻烧及电厂等各种锅炉中应用。

Description

复合型煤及其制备方法
技术领域
本发明属于锅炉燃料及其制备方法，具体涉及一种复合型煤及其制备方法。
背景技术
型煤是我国重要的燃料之一，它是以粉煤为主要原料，按具体用途所要求的配比，机械强度，和形状大小经机械加工压制成型的，具有一定强度和尺寸及形状各异的煤成品。传统的型煤大多采用原煤加入适当比例的黄泥，粘土或石灰制成，原煤使用量大，不仅造成很大的资源浪费，而且原煤中含有比较高的硫化物，在燃烧过程中有大量的二氧化硫、烟尘等污染物排出，对周围环境造成了很大污染，其制备工艺也较复杂，型煤制成后需要烘干或风干。
发明内容
本发明所要解决的技术问题是提供一种制备工艺简单，不需要烘干，二氧化硫和烟尘排放少，能达到环保要求的复合型煤及其制备方法。
本发明的技术方案：一种复合型煤，它由以下重量的原料制成：洗中煤30-45％，煤泥30-45％，矸石10-20％，复合助剂4-8％，水10-14％；所述的复合助剂是由下列重量份的原料制成：木质素磺酸钙5-15份，磷酸二氢钠1-6份，电石灰0-7份，氯化镁5-15份，腐植酸铵0.5-5份，氢氧化钙5-15份，硝酸钾2-6份，高锰酸钾0.5-3份，硝酸钠0.2-2份，氯化钠0-3份，高岭土6-12份，蓖麻籽油渣3-7份，聚乙烯醇0.2-1份，水8-12份。
上述复合型煤的制备方法，它的步骤如下：将洗中煤30-45％，矸石10-20％，用粉碎机粉碎后，与煤泥30-45％，复合助剂4-8％，水10-14％加入搅拌机进行混合，搅拌均匀后经型煤压制机压制而成。
本发明与现有技术相比具有以下有益效果：设备投资低，较型煤烘干工艺的设备投资低50-60％，在-20摄氏度气温下也可正常生产，制成的型煤无需烘干，冷强度大于500N/个，热强度大于300N/个，该型煤易燃烧，灰融点大于等于1250℃，运输破碎率小于5％，消烟效果可达70-90％。该型煤适用于工业、民用、石灰窑锻烧及电厂等各种锅炉中应用。该型煤经中国科学院山西煤炭化学研究所煤质分析测试报告如下表：
Figure G2009102639659D00021
经太原市环境检测结果如下：
样品MS-06-001：煤中全硫(％)0.30；煤的灰分43.13；
样品MS-06-002：煤中全硫(％)1.06；煤的灰分26.02。
具体实施方式
实施例1
一种复合型煤，它由以下重量的原料制成：一种复合型煤，洗中煤30％，煤泥45％，矸石10％，复合助剂5％，水10％；其中复合助剂的组分与重量含量为：木质素磺酸钙10份，磷酸二氢钠2份，电石灰3份，氯化镁10份，腐植酸铵3份，氢氧化钙10份，硝酸钾4份，高锰酸钾1份，硝酸钠1份，氯化钠2份，高岭土8份，蓖麻籽油渣5份，聚乙烯醇0.8份，水10份。
上述复合型煤的制备方法，它的步骤如下：将洗中煤30％，矸石10％，用粉碎机粉碎后，与煤泥45％，复合助剂5％，水10％加入搅拌机进行混合，搅拌均匀后经型煤压制机压制而成。
实施例2
一种复合型煤，它由以下重量的原料制成：洗中煤32％，煤泥30％，矸石20％，复合助剂4％，水14％；其中复合助剂的组分与重量含量为：木质素磺酸钙10份，磷酸二氢钠2份，电石灰3份，氯化镁10份，腐植酸铵3份，氢氧化钙10份，硝酸钾4份，高锰酸钾1份，硝酸钠1份，氯化钠2份，高岭土8份，蓖麻籽油渣5份，聚乙烯醇0.8份，水10份。
上述复合型煤的制备方法，它的步骤如下：将洗中煤32％，矸石20％，用粉碎机粉碎后，与煤泥30％，复合助剂4％，水14％加入搅拌机进行混合，搅拌均匀后经型煤压制机压制而成。
实施例3
一种复合型煤，它由以下重量的原料制成：洗中煤35％，煤泥35％，矸石15％，复合助剂5％，水10％；其中复合助剂的组分与重量含量为：木质素磺酸钙10份，磷酸二氢钠2份，电石灰3份，氯化镁10份，腐植酸铵3份，氢氧化钙10份，硝酸钾4份，高锰酸钾1份，硝酸钠1份，氯化钠2份，高岭土8份，蓖麻籽油渣5份，聚乙烯醇0.8份，水10份。
上述复合型煤的制备方法，它的步骤如下：将洗中煤35％，矸石15％，用粉碎机粉碎后，与煤泥35％，复合助剂5％，水10％加入搅拌机进行混合，搅拌均匀后经型煤压制机压制而成。

Claims (2)

1.一种复合型煤，其特征是它由以下重量的原料制成：洗中煤30-45％，煤泥30-45％，矸石10-20％，复合助剂4-8％，水10-14％；所述的复合助剂是由下列重量份的原料制成：木质素磺酸钙5-15份，磷酸二氢钠1-6份，电石灰0-7份，氯化镁5-15份，腐植酸铵0.5-5份，氢氧化钙5-15份，硝酸钾2-6份，高锰酸钾0.5-3份，硝酸钠0.2-2份，氯化钠0-3份，高岭土6-12份，蓖麻籽油渣3-7份，聚乙烯醇0.2-1份，水8-12份。
2.权利要求1所述的复合型煤的制备方法，其特征是它的步骤如下：将洗中煤30-45％，矸石10-20％，用粉碎机粉碎后，与煤泥30-45％，复合助剂4-8％，水10-14％加入搅拌机进行混合，搅拌均匀后经型煤压制机压制而成。
CN200910263965A 2009-12-31 2009-12-31 复合型煤及其制备方法 Pending CN101760274A (zh)