CN101759402A - Concrete fireproof hollow lath - Google Patents
Concrete fireproof hollow lath Download PDFInfo
- Publication number
- CN101759402A CN101759402A CN200810158924A CN200810158924A CN101759402A CN 101759402 A CN101759402 A CN 101759402A CN 200810158924 A CN200810158924 A CN 200810158924A CN 200810158924 A CN200810158924 A CN 200810158924A CN 101759402 A CN101759402 A CN 101759402A
- Authority
- CN
- China
- Prior art keywords
- percent
- fireproof
- concrete
- hollow lath
- fly ash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a concrete fireproof hollow lath, which is characterized in that fireproof filling materials are filled in a hollow lath. The concrete fireproof hollow lath is prepared from the following ingredients: sepiolite, low calcium fly ash, fireproof cement, fireproof filling materials, fly ash, expanded perlite and porcelain granules and polypropylene fiber. The invention has the concrete recipe consisting of, by weight percent: 15 to 25 percent of sepiolite, 12 to 25 percent of low calcium fly ash, 10 to 25 percent of diamond stones, 15 to 30 percent of fireproof cement, 20 to 35 percent of cement filling materials, 12 to 22 percent of fly ash, 16 to 22 percent of expanded perlite and porcelain granules and 0.05 to 1 percent of polypropylene fiber. The concrete fireproof hollow lath manufactured by the invention has the advantages that the specific gravity conforms to the requirements of light wall plates, the compactness is high, the contraction value is low, and the fireproof coefficient is large.
Description
Technical field
The present invention relates to a kind of building and ornament materials and manufacture method thereof, particularly a kind of concrete fireproof hollow lath.
Technical background
Partition plate is a kind of building and ornament materials commonly used, partition plate commonly used generally is divided into combined type wallboard and light lath, the combined type wallboard is composited by the material of two or more unlike materials, light lath is to be made of commaterial, make hollow shape to reduce weight more, the GRc wallboard that purposes is wider is the type, present fire-retardant wall plate generally adopts composite structure, its complex manufacturing, the cost height, and light lath often mostly is Portland cement or other colloidal material owing to its composition material, and fire resistance is relatively poor relatively.
Summary of the invention
Fireproof concrete hollow partition lath, it is characterized in that concrete prescription is (weight percent): sepiolite 15-25%, low calcium fly ash 12-25%, diamond stone 10-25%, refractory cements 15-30%, fire resistant infilling 20-5%, flyash 12-22%, pearlstone and haydite 16-22%, polypropylene fiber 0.05-1%.Described fireproof concrete hollow partition lath is characterized in that: described refractory cements adopts luminite cement or aluminate cement; Frog stone, pearlstone, blast-furnace slag or vitrified brick powder are adopted in fire resistant infilling.
The present invention compared with prior art, adopt refractory cements and fire resistant infilling in the partition plate, can improve the fire resistance of partition plate, and has better economy, the polypropylene fibre that adds can improve the folding strength of partition plate, and foam is evenly distributed in the slip, and the sealing spilehole that solidifies back formation not only reduces partition plate weight, can also play heat-blocking action, make the partition plate fire resistance better.
Claims (2)
1. concrete fireproof hollow lath, it is characterized in that concrete prescription is (weight percent): sepiolite 15-25%, low calcium fly ash 12-25%, diamond stone 10-25%, refractory cements 15-30%, fire resistant infilling 20-35%, flyash 12-22%, pearlstone and haydite 16-22%, polypropylene fiber 0.05-1%.
2. a kind of concrete fireproof hollow lath according to claim 1 is characterized in that: described refractory cements adopts luminite cement or aluminate cement; Frog stone, pearlstone, blast-furnace slag or vitrified brick powder are adopted in fire resistant infilling.