CN101747062A - 一种炼钢用钢包上水口砖 - Google Patents

一种炼钢用钢包上水口砖 Download PDF

Info

Publication number
CN101747062A
CN101747062A CN200810231106A CN200810231106A CN101747062A CN 101747062 A CN101747062 A CN 101747062A CN 200810231106 A CN200810231106 A CN 200810231106A CN 200810231106 A CN200810231106 A CN 200810231106A CN 101747062 A CN101747062 A CN 101747062A
Authority
CN
China
Prior art keywords
upper nozzle
nozzle brick
steelmaking
fused
weight parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200810231106A
Other languages
English (en)
Inventor
张富强
管军红
陈建强
周威辛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHENGZHOU DONGFANG SANLI REFRACTORY MATERIALS CO Ltd
Original Assignee
ZHENGZHOU DONGFANG SANLI REFRACTORY MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHENGZHOU DONGFANG SANLI REFRACTORY MATERIALS CO Ltd filed Critical ZHENGZHOU DONGFANG SANLI REFRACTORY MATERIALS CO Ltd
Priority to CN200810231106A priority Critical patent/CN101747062A/zh
Publication of CN101747062A publication Critical patent/CN101747062A/zh
Pending legal-status Critical Current

Abstract

一种炼钢用钢包上水口砖，以电熔白刚玉为主要原料，在原料中添加原料总重量8～14％的电熔锆莫来石。本发明将电熔锆莫来石引入到上水口砖中，可以起到以下两种主要作用：①生成主晶相或次晶相，使材料具有特殊的性能；②对原有材料起改性作用。本发明的炼钢用上水口砖能承受高温钢水的冲刷，有良好的耐浸蚀性，抗震性能好，透气性好等优点。

Description

一种炼钢用钢包上水口砖
技术领域
本发明属于炼钢技术领域，具体涉及一种炼钢用上水口砖。
背景技术
水口砖是炼钢必不可少的重要功能性耐火材料，传统水口砖主要有高铝质、刚玉质、镁碳质等。现有的上水口砖在使用的过程中，在钢包预热及浇筑过程中容易产生微裂纹，使用后冷态裂纹增多，另外现有的上水口砖大多为单一组分，抗钢水侵蚀及耐剥落性较差，从而影响其使用稳定性及安全性。
发明内容
本发明要解决的技术问题是现有的刚玉质钢包上水口砖存在的抗钢水侵蚀及耐剥落性差，使用寿命短的技术问题，提供一种使用寿命长的炼钢用上水口砖。
为解决上述技术问题，本发明采用的技术方案如下：
本发明的炼钢用钢包上水口砖，以电熔白刚玉为主要原料，其中在原料中添加原料总重量8～14％的电熔锆莫来石。
炼钢用钢包上水口砖的原料配方如下：
3～1mm电熔白刚玉30～45重量份
1～0.088mm电熔白刚玉10～20重量份
≤0.088mm电熔白刚玉35～45重量份
2.5～1mm电熔锆莫来石8～14重量份。
本发明将电熔锆莫来石引入到上水口砖中，可以起到以下两种主要作用：①生成主晶相或次晶相，使材料具有特殊的性能；②对原有材料起改性作用。本发明的炼钢用上水口砖能承受高温钢水的冲刷，有良好的耐浸蚀性，抗震性能好，透气性好等优点。
具体实施方式
下面结合实施例对本发明作详细说明，但并不以任何方式限制本发明。
实施例1
炼钢用钢包上水口砖的原料配方如下：
3～1mm电熔白刚玉30重量份
1～0.088mm电熔白刚玉15重量份
≤0.088mm电熔白刚玉40重量份
2.5～1mm电熔锆莫来石8重量份。
实施例2
炼钢用钢包上水口砖的原料配方如下：
3～1mm电熔白刚玉35重量份
1～0.088mm电熔白刚玉20重量份
≤0.088mm电熔白刚玉35重量份
2.5～1mm电熔锆莫来石10重量份。
实施例3
炼钢用钢包上水口砖的原料配方如下：
3～1mm电熔白刚玉40重量份
1～0.088mm电熔白刚玉18重量份
≤0.088mm电熔白刚玉45重量份
2.5～1mm电熔锆莫来石12重量份。
实施例4
炼钢用钢包上水口砖的原料配方如下：
3～1mm电熔白刚玉45重量份
1～0.088mm电熔白刚玉10重量份
≤0.088mm电熔白刚玉42重量份
2.5～1mm电熔锆莫来石14重量份。
本发明的炼钢用钢包上水口砖的制备方法为：原料→配比→混碾→成型→干燥→烧成→拣选→预热→浸渍→干馏→检测→包装→出厂。
本发明的钢包上水口砖与现有的钢玉质钢包上水口砖的理化性能及平均使用寿命参数对比如表1。
表1本发明的上水口砖与现有的上水口砖的理化性能及平均使用寿命对比
Figure G2008102311067D0000031

Claims (2)

1.一种炼钢用钢包上水口砖，以电熔白刚玉为主要原料，其特征在于：在原料中添加原料总重量8～14％的电熔锆莫来石。
2.根据权利要求1所述的炼钢用钢包上水口砖，其特征在于：其原料配方如下：
3～1mm电熔白刚玉30～45重量份
1～0.088mm电熔白刚玉10～20重量份
≤0.088mm电熔白刚玉35～45重量份
2.5～1mm电熔锆莫来石8～14重量份。
CN200810231106A 2008-11-27 2008-11-27 一种炼钢用钢包上水口砖 Pending CN101747062A (zh)