CN101736463A - Flame-retardant blended yarn and production method - Google Patents
Flame-retardant blended yarn and production method Download PDFInfo
- Publication number
- CN101736463A CN101736463A CN200910311316A CN200910311316A CN101736463A CN 101736463 A CN101736463 A CN 101736463A CN 200910311316 A CN200910311316 A CN 200910311316A CN 200910311316 A CN200910311316 A CN 200910311316A CN 101736463 A CN101736463 A CN 101736463A
- Authority
- CN
- China
- Prior art keywords
- flame
- retardant
- yawn
- blended yarn
- mins
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a flame-retardant blended yarn, which is formed by blending combed cotton, flame-retardant acrylic fibers and flame-retardant viscose glue, wherein the mass part ratio of the combed cotton to the flame-retardant acrylic fibers to the flame-retardant viscose glue is 20 to 20 to 60. The flame-retardant blended yarn uses the flame-retardant viscose glue and the flame-retardant acrylic fibers as main bodies and the combed cotton in a certain proportion is blended, so the wearing property of the flame-retardant blended yarn is improved and the application field of the flame-retardant blended yarn is enlarged based on fully considering the flame retardation of a final product. According to the ratio of the combed cotton to the flame-retardant acrylic fibers to the flame-retardant viscose glue of 20 to 20 to 60, the flame-retardant viscose glue and the flame-retardant acrylic fibers are used as the main bodies and the combed cotton in a certain proportion is blended, so the wearing property of the flame-retardant blended yarn is improved and the application field of the flame-retardant blended yarn is enlarged based on fully considering the flame retardation of the final product. Compared with the traditional flame-retardant viscose glue pure yarn, the blended yarn with 60 parts of flame-retardant viscose glue, 20 parts of flame-retardant acrylic fibers and 20 parts of combed cotton has the characteristics of good flame retardation, high strength, stable size, comfortable wearing property, rich color and the like.
Description
Technical field
The present invention relates to a kind of yarn and production method thereof, particularly a kind of flame-retardant blended yarn and production method thereof.
Background technology
Have now with combed cotton and make the lining that the yarn weaving gets, be smooth to the touch, comfortable and easy to wear, be fit to very much make high-grade clothing.But development along with the urban modernization construction, the difficult burning of people's textiles requires more and more higher, in many fire incidents, the consequence of introducing because of textile combustion is quite serious, a series of laws and regulations have also been formulated in countries in the world, and the fire resistance of the textiles that special population or occasion are used has proposed restricted specification requirement.And combed cotton belongs to cotton fiber, and the restriction of self material causes, and this is the yarn that raw material is made by combed cotton, and maximum shortcoming is inflammable, can't use as fire proofing.While, traditional flame retardant products was developed the wearability of having overemphasized the anti-flaming function of final products and having ignored product.
Summary of the invention
The objective of the invention is provides a kind of fire resistance good for the deficiency that solves above-mentioned technology, has the flame-retardant blended yarn and the production method thereof of wearability simultaneously again concurrently.
In order to achieve the above object, the flame-retardant blended yarn that the present invention is designed, it is formed by combed cotton, flame-retardant acrylic fibre and anti-flaming viscose blending, and wherein the ratio of quality and the number of copies of combed cotton, flame-retardant acrylic fibre and anti-flaming viscose is 20: 20: 60.This flame-retarding blended yarn that forms based on anti-flaming viscose and flame-retardant acrylic fibre, is sneaked into a certain proportion of combed cotton, on the basis that takes into full account the final products fire resistance, improves its wearability, enlarges the Application Areas of product.
The production method of the flame-retardant blended yarn that the present invention is designed is that 20: 20: 60 combed cotton of mass ratio, flame-retardant acrylic fibre and anti-flaming viscose are carried out following technology:
A002D → A035 → A036C → CJFA105 → A076E → comb and parallel cotton fibers prior to spinning FA201B → head and FA311 → two and FA311 → rove F458 → spun yarn FA503 → from winder.
Further scheme is, is easy to generate the shortcoming of static for fear of flame-retardant acrylic fibre, and described flame-retardant acrylic fibre adds before entering production technology and carried out oil in the antistatic finish vexed 24 hours.
Further scheme is, in order to control flame-retardant acrylic fibre and the combed cotton product quality in production process separately, the parameter of blowing frequency conversion autoleveller instrument is set in the production process: the comprehensive hired roughneck of the quantitative g/m:430g/m of blowing: 900 rev/mins of fixed length: 34.4m.
Further scheme is, in order to control drafting, rove, the quality of operations such as spun yarn, described comb and parallel cotton fibers prior to spinning FA201B does quantitatively: 19.5g/5m cylinder: 360 rev/mins of doffers: 19.1 rev/mins of licker-ins: 875 rev/mins of cylinder ~ cover plates space: 10 * 9 * 8 * 8 * 9 English silk cylinder ~ doffers: 5 English silks;
Described head and FA311 do quantitatively: 19.5g/5m always stretches oneself and yawn: stretch oneself and yawn after 8.1 times: 1.6 times of sliver exporting speeds: 350 meters/minute space: 11 * 6.5 * 14.5;
Described two and FA311 do quantitatively: 20.0g/5m always stretches oneself and yawn: stretch oneself and yawn after 7.85 times: 1.3 times of sliver exporting speeds: 350 meters/minute space: 11 * 6.5 * 14.5;
Described rove FA458 does quantitatively: 4.60g/100m always stretches oneself and yawn: stretch oneself and yawn after 8.67 times: carry coefficient for 1.27 times: 85 front rollers: 290 rev/mins space: 15 * 26 * 30
Described spun yarn FA503 does quantitatively: 1.338g/10m always stretches oneself and yawn: stretch oneself and yawn after 35.23 times: carry coefficient for 1.3 times: 365 twists: 95 sth. made by twisting/10cm front rollers: 170 rev/mins
Described from 1100 rev/mins of yarn defects of winder winding speed scope: N+300%, S+200%3cm, L+55%20cm, T-45%20cm
The flame-retardant blended yarn that the present invention is designed, it with combed cotton, flame-retardant acrylic fibre and anti-flaming viscose ratio 20: 20: 60 ratio, based on anti-flaming viscose and flame-retardant acrylic fibre, sneak into a certain proportion of combed cotton, on the basis that takes into full account the final products fire resistance, improve its wearability, enlarge the Application Areas of product.Compare with traditional anti-flaming viscose pure yarn, anti-flaming viscose 60/ flame-retardant acrylic fibre 20/ combed cotton 20 blended yarns have that fire resistance is good, intensity is high, dimensionally stable, take characteristics such as comfortable, rich color.Nap fabrics such as suitable manufacturing Fake Furs, as imitative fur, land otter fur, fox skin, raw weasel skin, grey squirrel etc., because of its fire resistance good, be fit to make products such as indoor shop decorations fabric, woolen toy, compare with natural animal skin, have strong, the imitative natural fur lifelike image of inexpensive, animal hair sense, light weight, warmth retention property good, take characteristics such as comfortable.Can be applied to also that family is spun, the clothing field, can be used for weaving bedding such as blanket, sheet, cover, women, children's clothes, sleeping suit for children, the old,weak,sick and disabled person's underwear and Work Clothes dress material, fine hair kind fabrics such as woman style animal hair overcoat, interlining, can also be applied to fields such as nonwoven such as senior towel, wallpaper, paper, belong to environmentally friendly flame-retardant acrylic fibre, great exploitation potential for its.
The production method of the combed cotton flame retardant acrylic blended yarns that the present invention is designed, be to get parameter in process sequence and each technology through repeatedly test, produce the flame-retardant blended yarn that obtains according to this production method, yarn strength and DIMENSIONAL STABILITY have been guaranteed, perfectly the characteristics of combed cotton and the characteristics of flame-retardant acrylic fibre and anti-flaming viscose are organically combined, avoid original fire-retardant pure yarn to be easy to generate the shortcoming of static simultaneously, had the favorable industrial application.
The specific embodiment
The present invention is further described by the following embodiment.
Embodiment 1:
The flame-retardant blended yarn that present embodiment is described, it is by flame-retardant blended yarn, and it is formed by combed cotton, flame-retardant acrylic fibre and anti-flaming viscose blending, and wherein the ratio of quality and the number of copies of combed cotton, flame-retardant acrylic fibre and anti-flaming viscose is 20: 20: 60.
Embodiment 2
The production method of the flame-retardant blended yarn that present embodiment is described is that 20: 20: 60 combed cotton of mass ratio, flame-retardant acrylic fibre and anti-flaming viscose are carried out following technology:
A002D → A035 → A036C → CJFA105 → A076E → comb and parallel cotton fibers prior to spinning FA201B → head and FA311 → two and FA311 → rove F458 → spun yarn FA503 → from winder.
Described flame-retardant acrylic fibre adds before entering production technology and carried out oil in the antistatic finish vexed 24 hours.
The parameter of blowing frequency conversion autoleveller instrument is set in the production process: the comprehensive hired roughneck of the quantitative g/m:430g/m of blowing: 900 rev/mins of fixed length: 34.4m.
Described comb and parallel cotton fibers prior to spinning FA201B does quantitatively: 19.5g/5m cylinder: 360 rev/mins of doffers: 19.1 rev/mins of licker-ins: 875 rev/mins of cylinder ~ cover plates space: 10 * 9 * 8 * 8 * 9 English silk cylinder ~ doffers: 5 English silks;
Described head and FA311 do quantitatively: 19.5g/5m always stretches oneself and yawn: stretch oneself and yawn after 8.1 times: 1.6 times of sliver exporting speeds: 350 meters/minute space: 11 * 6.5 * 14.5;
Described two and FA311 do quantitatively: 20.0g/5m always stretches oneself and yawn: stretch oneself and yawn after 7.85 times: 1.3 times of sliver exporting speeds: 350 meters/minute space: 11 * 6.5 * 14.5;
Described rove FA458 does quantitatively: 4.60g/100m always stretches oneself and yawn: stretch oneself and yawn after 8.67 times: carry coefficient for 1.27 times: 85 front rollers: 290 rev/mins space: 15 * 26 * 30;
Described spun yarn FA503 does quantitatively: 1.338g/10m always stretches oneself and yawn: stretch oneself and yawn after 35.23 times: carry coefficient for 1.3 times: 365 twists: 95 sth. made by twisting/10cm front rollers: 170 rev/mins;
Described from 1100 rev/mins of yarn defects of winder winding speed scope: N+300%, S+200%3cm, L+55%20cm, T-45% 20cm.
Claims (5)
1. a flame-retardant blended yarn is characterized in that it is formed by combed cotton, flame-retardant acrylic fibre and anti-flaming viscose blending, and wherein the ratio of quality and the number of copies of combed cotton, flame-retardant acrylic fibre and anti-flaming viscose is 20: 20: 60.
2. the production method of a flame-retardant blended yarn as claimed in claim 1 is characterized in that 20: 20: 60 combed cotton of mass ratio, flame-retardant acrylic fibre and anti-flaming viscose are carried out following technology:
A002D → A035 → A036C → CJFA105 → A076E → comb and parallel cotton fibers prior to spinning FA201B → head and FA311 → two and FA311 → rove F458 → spun yarn FA503 → from winder.
3. the production method of flame-retardant blended yarn according to claim 2, it is characterized in that described flame-retardant acrylic fibre adds before entering production technology carried out oil vexed 24 hours in the antistatic finish.
4. the production method of flame-retardant blended yarn according to claim 2 is characterized in that the parameter of blowing frequency conversion autoleveller instrument in the production process is set to: the comprehensive hired roughneck of the quantitative g/m:430g/m of blowing: 900 rev/mins of fixed length: 34.4m.
5. the production method of flame-retardant blended yarn according to claim 2, it is characterized in that described comb and parallel cotton fibers prior to spinning FA201B does quantitatively: 19.5g/5m cylinder: 360 rev/mins of doffers: 19.1 rev/mins of licker-ins: 875 rev/mins of cylinder ~ cover plates space: 10 * 9 * 8 * 8 * 9 English silk cylinder ~ doffers: 5 English silks;
Described head and FA311 do quantitatively: 19.5g/5m always stretches oneself and yawn: stretch oneself and yawn after 8.1 times: 1.6 times of sliver exporting speeds: 350 meters/minute space: 11 * 6.5 * 14.5;
Described two and FA311 do quantitatively: 20.0g/5m always stretches oneself and yawn: stretch oneself and yawn after 7.85 times: 1.3 times of sliver exporting speeds: 350 meters/minute space: 11 * 6.5 * 14.5;
Described rove FA458 does quantitatively: 4.60g/100m always stretches oneself and yawn: stretch oneself and yawn after 8.67 times: carry coefficient for 1.27 times: 85 front rollers: 290 rev/mins space: 15 * 26 * 30;
Described spun yarn FA503 does quantitatively: 1.338g/10m always stretches oneself and yawn: stretch oneself and yawn after 35.23 times: carry coefficient for 1.3 times: 365 twists: 95 sth. made by twisting/10cm front rollers: 170 rev/mins;
Described from 1100 rev/mins of yarn defects of winder winding speed scope: N+300%, S+200%3cm, L+55%20cm, T-45% 20cm.