CN101735628A - Waste tire rubber powder modified asphalt and preparation method thereof - Google Patents
Waste tire rubber powder modified asphalt and preparation method thereof Download PDFInfo
- Publication number
- CN101735628A CN101735628A CN201010013604A CN201010013604A CN101735628A CN 101735628 A CN101735628 A CN 101735628A CN 201010013604 A CN201010013604 A CN 201010013604A CN 201010013604 A CN201010013604 A CN 201010013604A CN 101735628 A CN101735628 A CN 101735628A
- Authority
- CN
- China
- Prior art keywords
- rubber powder
- waste tire
- tire rubber
- asphalt
- modified asphalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses waste tire rubber powder modified asphalt and a preparation method thereof. The waste tire rubber powder modified asphalt contains the following components in part by weight: 70 to 90 parts of matrix asphalt and 10 to 30 parts of waste tire rubber powder. The preparation method for the waste tire rubber powder modified asphalt comprises the following steps: according to the weight ratio, heating the matrix asphalt to the temperature of between 160 and 200 DEG C to ensure that the matrix asphalt is melted into liquid asphalt; adding the waste tire rubber powder, stirring uniformly, guaranteeing that the waste tire rubber powder swells for 10 to 30 minutes in the temperature region; then, adopting a shearing machine to shear the waste tire rubber powder for 10 to 30 minutes; pumping the waste tire rubber powder into a development can and developing for 30 to 60 minutes so as to prepare the waste tire rubber powder modified asphalt with high performance. The waste tire rubber powder modified asphalt has the advantages of excellent comprehensive performance, simple technology, low production cost, low device requirement, short time, energy conservation, no environmental pollution, comprehensive utilization of wastes, and the like, and is applied to paving and maintaining asphalt roads, and constructing the municipal road engineering.
Description
Technical field
The present invention relates to a kind of novel road-making material, specifically, is a kind of waste tire rubber powder modified asphalt and preparation method thereof.
Background technology
Since the reform and opening-up, the communications and transportation cause of China has obtained great achievement highly visible.Country has proposed the great strategic task of development Modern Traffic transport trade---and put forth effort to advance resource-conserving, environmentally friendly communications and transportation development, implement " material economy and recycle special campaigns plan ", advocate the cyclic utilization of waste energetically.
As everyone knows, petroleum pitch has many good performances as a kind of mineral rubber ramming material, has become the main paver of construction fields such as highway, airport at present.But because the asphaltene molecule amount is less, wider distribution, so its mechanical property is big to the susceptibility of temperature, low temperature easily becomes fragile, and high temperature easily dissolves, and its elasticity, ageing-resistant performance and fatigue performance are also very poor.
Definition according to China's " asphalt highway construction technique normalizing " (JTG F40-2004), modifying asphalt is meant additives (properties-correcting agent) such as admixture rubber, resin, high molecular polymer, rock asphalt, levigated rubber powder or other materials, and the performance that makes pitch or asphalt is improved and the asphaltic binder made.
Rubber asphalt is that the rubber powder of content more than 15% (more than 180 ℃) under the condition of high temperature reacts the modifying asphalt agglutinate that obtains with molten the expanding of pitch.Rubber powder with asphalt high-temperature thorough mixing state under absorb molten the expanding of lightweight oil content face in the pitch, form the very high gel-film of asphalt content at the rubber powder particle surface simultaneously, the rubber powder particle links together by gel-film, forms a compatible body of solid-liquid that viscosity is very big.Adopt waste tire rubber powder, can improve bituminous crack resistance at low-temperature, high temperature stability performance, ageing resistance, anti-fatigue performance, elasticity, viscosity etc. effectively, strengthen the cling property of asphalt, and reduced the driving noise on road surface effectively, increased traveling security and comfortableness.
Publication number is the patent application of CN1528823, discloses a kind of preparation method of waste rubber powder modified asphalt.This method adopts two step process to prepare rubber powder modified asphalt masterbatch and rubber powder/polymer composite modified asphalt.This method is the extending oil of the rubber powder of 10-60% and 0-20% to be added to carry out shear agitation in the pitch, mix and be prepared into masterbatch in 1-6 hour under temperature 140-250 ℃, then masterbatch is dissolved with the pitch dilution and adds polymkeric substance (SBS) etc.This method causes the viscosity of masterbatch quite big because having added high-load rubber powder when the preparation masterbatch, equipment requirements is very high, added extending oil the quality of pitch own has been produced influence, finally having added polymkeric substance (SBS) etc. is worth very high, the finished product of producing can't obtain the acceptance in market, the most fatal a bit is, employed pitch when employed pitch has limited and blent when making masterbatch, if two kinds of pitches are the pitch of different varieties, mix asphalt itself is exactly to reduce the bituminous quality so, so require narrow to bituminous.Its production time is longer, and from beginning to need 5 hours at least to final finished, production efficiency is low.
Publication number is the patent application of CN1609165, discloses a kind of waste Crumb rubber modified asphalt and preparation method thereof.This method be temperature 150-200 ℃ down will be by 60 eye mesh screens mixing waste Crumb rubber, SBS, SBR, the stablizer of different-grain diameter join in the pitch according to a certain percentage, processing through specific equipments such as shears or colloidal mills is prepared into the rubber modified asphalt with satisfactory stability.Though this composite modified bituminous performance that makes has obtained good raising, but also come with some shortcomings: the one, owing to SBS, SBR polymkeric substance can improve the bituminous viscosity effectively, add rubber powder, the bituminous viscosity is too big, to having caused very big difficulty in production, pumping, transportation, the construction process; The 2nd, because the modifying process viscosity is too big,, only be 1%-6% so the volume of waste Crumb rubber is very limited, do not obtain useful effect to reducing cost, alleviate environmental pressure, according to the ASTM standard, can not be referred to as rubber modified asphalt; The 3rd, polymkeric substance (SBS, SBR) cost is very high, and polymkeric substance is high to the modification temperature requirement, time requirement is long, has not only quickened bituminous and has worn out, and performance can not get guaranteeing effective control that the cost aspect does not have yet.
Publication number is the patent application of CN1733843, discloses a kind of rubber powder modified asphalt production technique.This technology is under temperature 160-210 ℃, with 20 orders-80 purpose rubber powder particle and matrix pitch in 1-3: 8 parts by weight ratio joins in the pitch, No. 200, the aromatic solvent that adds 1%-5%, become rubber powder modified asphalt through 40 minutes-5 hours prepared in reaction.This method is the method that the U.S. adopts the earliest, its stability in storage extreme difference, and rubber powder precipitates easily, emanates, and has added aromatic solvent and has changed asphalt component especially No. 200.So rubber modified asphalt quality instability of producing.
Publication number is that the patent application of CN1765998 discloses a kind of waste Crumb rubber modified asphalt composition and method of making the same.This method is at first coupling agent (0.1%-5.0%) and thinner (0%-10%) to be joined in the 60 purpose rubber powders according to a certain percentage to mix, the rubber powder that to handle (1%-29.5%) joins in the pitch (70%-98.5%) and goes then, grinds through specific equipments such as high-shear or colloidal mills and is prepared into rubber powder modified asphalt in 30-180 minute.Its preparation process complexity, it is can't branch in rubber powder even that the first step joins in the rubber powder back to coupling agent, thinner, makes the rubber powder viscosity change, easily caking.The 60 purpose rubber powders that use are difficult to suitability for industrialized production, cost an arm and a leg.The bituminous component that the adding of coupling agent (monoalkoxy type titanic acid ester etc.), thinner (solvent wet goods) changes, and it costs an arm and a leg, laboratory test can be used, and the suitability for industrialized production difficulty is very big.
Publication number is the patent application of CN101104739, discloses a kind of rubber powder modified asphalt and working method thereof.This method is proportionally mixed matrix pitch, rubber powder, first linking agent, thinner, second linking agent etc. and is prepared modifying asphalt.This method has been added multiple auxiliary agent, the production process more complicated, and first linking agent of employing (sulphur, rock asphalt) has reduced asphalt viscosity, but its value is very high; The adding of thinner (solvent oil, furfural extract oil, vacuum distillate) has changed the component of matrix pitch, the bituminous high-temperature behavior of damage, and generation has a strong impact on to asphalt quality; The use of second linking agent (SBS) makes the price of the finished product to reduce, and also just can not embody the value of comprehensive utilization of waste materials.
Publication number is the patent application of CN 101265363, discloses a kind of waste old powder-modified asphalt and preparation method.This method is heated to 150-160 ℃ with matrix pitch, slowly add rubber powder (30-60 order) then, solubilizing agent (used oil, coal tar, thermal oil, solvent oil) and dispersion agent (nano-metal-oxide), stir then, continue to be warming up to 170-220 ℃, at 170-220 ℃ of following high speed shear 30-40 minute, store then and grew 45-90 minute, promptly obtain rubber modified asphalt.Though this method can be produced high performance rubber modified asphalt, but weak point is arranged also: after one, rubber powder being joined in 150-160 ℃ the matrix pitch,, cause mixed viscosity very big because temperature is too low, if make it even, very high to the requirement of equipment; Two, the solubilizing agent of Jia Ruing (used oil, coal tar, thermal oil) has certain injury to human body, and the thermal oil price is 20000 yuan/ton, and industrial production can not realize; Three, the use of dispersion agent (nano-metal-oxide) makes production process complicated; Four, it is more difficult mixed 150-160 ℃ rubber asphalt being warming up to 70-220 ℃ in the short period of time, the requirement height of equipment, and production efficiency is low; Five, according to its claim 12, the equipment rotating speed is 5000-7000 rev/min, can't realize in actual production process.
Publication number is the patent application of CN101348350, discloses a kind of waste rubber powder composite modified asphalt and preparation method thereof.This method is that liquid bitumen is joined in the shears, and Sha Suobide (1-5 part) stirs, add rubber powder again, be warming up to 180-220 ℃, molten expanding 5-30 minute, shear and put into hold-up vessel growth 30-60 minute after 10-30 minute, be prepared into waste rubber powder composite modified asphalt.The preparation of composite modified asphalt is current relatively more popular research direction, but the value ratio of composite modified asphalt is expensive, and production process is more complicated also, and is very high to the requirement of production unit.
Publication number is the patent application of CN101538409, discloses a kind of waste old powder-modified asphalt and preparation method thereof, and its method and patent publication No. are that the method side of patent disclosure of CN101348350 is similar, all are a kind of methods of compounded rubber modified asphalt.Its compound remodeling that uses and be carboxylic styrene-butadiene rubber, carboxy nitrile rubber, epoxy natural rubber or the like, the price of this different materials is all very expensive, our discussion of the essential attributes of suitability for industrialized production.
In the above-mentioned patent application among the preparation method of disclosed rubber powder modified asphalt, additive is more, composite modified cost is too high, the adding of additive, solubilizing agent, linking agent etc., not only make the bituminous component change, have a strong impact on asphalt quality, the program of more feasible production is complicated, and efficient is low.
Summary of the invention
Along with Chinese economic development, road Traffic Volume is increasing, and vehicle load is more and more higher, and the phenomenon that causes occurring on the road surface diseases such as rut, crack, hole groove is day more outstanding, has had a strong impact on use properties and the traveling security and the comfortableness of road.Obviously, the solution of these problems all be unable to do without high performance pitch.Purpose of the present invention, be to overcome the shortcoming that existing waste tire rubber powder modified asphalt exists, a kind of good combination property is provided, produce convenient, be easy to control, production cost is low, save energy, environmental pollution are little waste tire rubber powder modified asphalt and preparation method thereof.
The present invention is achieved in that by two kinds of components of following Different Weight part formulated:
Matrix pitch 70-90 part
Waste tire rubber powder 10-30 part
Preferred weight part proportioning of component of the present invention is:
Matrix pitch 75-80 part
Waste tire rubber powder 20-25 part
Optimum weight part proportioning of component of the present invention is:
78 parts of matrix pitches
22 parts of waste tire rubber powders
Above-mentioned matrix pitch, a kind of in vacuum residuum, straight-run pitch, oxidized bitumen, mediation pitch, the rock asphalt, matrix pitch is 60-120 25 ℃ penetration degree, 0.1mm; Above-mentioned waste tire rubber powder is the rubber powder that heavy duty tire is made, and fineness is the 20-40 order;
Waste tire rubber powder in the proportioning of the present invention, its principle of work and power is: by the lightweight oil content in the molten absorption base pitch that expands of high temperature, the waste tire rubber powder particle volume expands, in pitch, form the successive elastomerics, help pitch opposing low temperature and shrink, increase pitch elasticity and improve anti-aging, the anti-fatigue performance of bituminous.
The preparation method of the present invention's waste tire rubber powder modified asphalt is as follows:
1. the matrix pitch temperature is heated to 130-160 ℃, makes it that good flowability be arranged;
2. continue to be warming up to 180-200 ℃, add waste tire rubber powder;
3. insulation is molten expanded 10-30 minute, and stirred, and sheared then 10-30 minute;
4. grew 30-60 minute, preparation becomes high-performance scrap tire rubber modifying asphalt of the present invention.
Contain waste tire rubber powder in the proportioning raw materials of the present invention, the main raw material of waste tire rubber powder is a damaged tire, and the comprehensive utilization of damaged tire makes that serious day by day " black pollution " obtained alleviation.Contain natural rubber, synthetic rubber, vulcanizing agent, carbon black and minor amounts of additives in the waste tire rubber powder, the composition of waste tire rubber powder is very tangible to the bituminous modified effect.Road surface, the bridge floor of waste tire rubber powder modified asphalt making of the present invention have been used, improved between the road surface layer with layer bonding, anti-low temperature, the high temperature resistant property on road surface have effectively been improved, elasticity, the cling property on road surface have been improved effectively, the ageing resistance and the anti-fatigue performance on road surface have been improved effectively, reduce road surface driving noise effectively, improved traveling security and comfortableness.High-performance scrap tire rubber modifying asphalt of the present invention, have good combination property, produce convenient, be easy to that control, production cost are low, advantage such as save energy, environmental pollution are little, be widely used in the making and maintenance and municipal engineering construction of asphalt roads.
Embodiment
Below in conjunction with nine embodiment, the present invention is described in more detail, but the invention is not restricted to these embodiment.
Embodiment 1 produces waste tire rubber powder modified asphalt 500kg
Raw-material weight proportion is as follows:
Matrix pitch 450kg
Waste tire rubber powder 50kg
Matrix pitch is a vacuum residuum, is 60-120 25 ℃ penetration degrees, 0.1mm; Waste tire rubber powder is the rubber powder that heavy duty tire is made, and fineness is for being 30 orders, and waste tire rubber powder is provided by the Shaanxi magnificent plinth engineering materials Science and Technology Co., Ltd. of growing up.
Its preparation method is as follows:
1. the matrix pitch temperature is heated to 130 ℃, makes it that good flowability be arranged;
2. continue to be warming up to 180 ℃, add waste tire rubber powder at mixing device by well heater;
3. insulation is molten expanded 30 minutes, and stirred, and sheared then 30 minutes;
4. put into hold-up vessel and grew 30 minutes, be prepared into this product.
Embodiment 2 produces waste tire rubber powder modified asphalt 500kg
Raw-material weight proportion is as follows:
Matrix pitch 425kg
Waste tire rubber powder 75kg
Matrix pitch is perfectly straight pitch, is 60-120 25 ℃ penetration degrees, 0.1mm; Waste tire rubber powder is the rubber powder that heavy duty tire is made, and fineness is 40 orders, and waste tire rubber powder is provided by the Shaanxi magnificent plinth engineering materials Science and Technology Co., Ltd. of growing up.
Its preparation method is as follows:
1. the matrix pitch temperature is heated to 160 ℃, makes it that good flowability be arranged;
2. continue to be warming up to 200 ℃, in mixing device, add waste tire rubber powder by well heater;
3. insulation is molten expanded 30 minutes, and stirred, and sheared 20 minutes by shears then;
4. put into hold-up vessel and grew 30 minutes, preparation becomes this product.
Embodiment 3 produces waste tire rubber powder modified asphalt 500kg
Raw-material weight proportion is as follows:
Matrix pitch 400kg
Waste tire rubber powder 100kg
Matrix pitch is a rock asphalt, is 60-120 25 ℃ penetration degrees, 0.1mm; Waste tire rubber powder is the rubber powder that heavy duty tire is made, and fineness is 30 orders, and waste tire rubber powder is provided by the Shaanxi magnificent plinth engineering materials Science and Technology Co., Ltd. of growing up.
Its preparation method is as follows:
1. the matrix pitch temperature is heated to 150 ℃, makes it that good flowability be arranged;
2. continue to be warming up to 200 ℃, in mixing device, add waste tire rubber powder;
3. insulation is molten expanded 20 minutes, and stirred, and entered shears then and sheared 30 minutes;
4. put into hold-up vessel and grew 30 minutes, make this product.
Embodiment 4 produces waste tire rubber powder modified asphalt 500kg
The raw-material weight proportioning is as follows:
Matrix pitch 375kg
Waste tire rubber powder 125kg
Matrix pitch is 60-120 for being in harmonious proportion pitch 25 ℃ penetration degrees, 0.1mm; Waste tire rubber powder is the rubber powder that heavy duty tire is made, and fineness is 20 orders, and waste tire rubber powder is provided by the Shaanxi magnificent plinth engineering materials Science and Technology Co., Ltd. of growing up.
Its preparation method is as follows:
1. the matrix pitch temperature is heated to 150 ℃, makes it that good flowability be arranged;
2. continue to be warming up to 190 ℃ by well heater, in mixing device, add waste tire rubber powder;
3. insulation is molten expanded 30 minutes, and stirred, and entered shears subsequently and sheared 30 minutes;
4. put into hold-up vessel and grew 30 minutes, make this product.
Embodiment 5 produces waste tire rubber powder modified asphalt 500kg
The raw-material weight proportioning is as follows:
Matrix pitch 350kg
Waste tire rubber powder 150kg
Matrix pitch is a rock asphalt, is 60-120 25 ℃ penetration degrees, 0.1mm; Waste tire rubber powder is the rubber powder that heavy duty tire is made, and fineness is 40 orders, and waste tire rubber powder is provided by the Shaanxi magnificent plinth engineering materials Science and Technology Co., Ltd. of growing up.
Its preparation method is as follows:
1. the matrix pitch temperature is heated to 150 ℃, makes it that good flowability be arranged;
2. continue to be warming up to 180 ℃, in mixing device, add waste tire rubber powder;
3. insulation is molten expanded 30 minutes, and stirred,, enter shears subsequently and sheared 30 minutes;
4. put into hold-up vessel and grew 30 minutes, make this product.
Embodiment 6 produces waste tire rubber powder modified asphalt 500kg
The proportioning of raw-material weight is as follows:
Matrix pitch 350kg
Waste tire rubber powder 150kg
Matrix pitch is 60-120 for being in harmonious proportion pitch 25 ℃ penetration degrees, 0.1mm; Waste tire rubber powder is the rubber powder that heavy duty tire is made, and fineness is 30 orders.
Its preparation method is as follows:
1. the matrix pitch temperature is heated to 140 ℃, makes it that good flowability be arranged;
2. continue to be warming up to 190 ℃, in mixing device, add waste tire rubber powder;
3. insulation is molten expanded 30 minutes, and stirred, and entered shears subsequently and sheared 30 minutes;
4. put into hold-up vessel and grew 30 minutes, make this product.
Embodiment 7 produces waste tire rubber powder modified asphalt 500kg
Raw-material weight proportion is as follows:
Matrix pitch 350kg
Waste tire rubber powder 150kg
Matrix pitch is an oxidized bitumen, is 60-120 25 ℃ penetration degrees, 0.1mm: waste tire rubber powder is the rubber powder that heavy duty tire is made, and fineness is 20 orders.
Its preparation method is as follows:
1. the matrix pitch temperature is heated to 160 ℃, makes it that good flowability be arranged;
2. continue to be warming up to 200 ℃ by well heater, in mixing device, add waste tire rubber powder;
3. insulation is molten expanded 20 minutes, and stirred, and entered shears subsequently and sheared 20 minutes;
4. grew 45 minutes in the hold-up vessel, make this product.
Embodiment 8 produces waste tire rubber powder modified asphalt 500kg
Raw-material weight proportion is as follows:
Matrix pitch 400kg
Waste tire rubber powder 100kg
Matrix pitch is a vacuum residuum, is 60-120 25 ℃ penetration degrees, 0.1mm; Waste tire rubber powder is the rubber powder that heavy duty tire is made, and fineness is 20 orders.
Its preparation method is as follows:
1. the matrix pitch temperature is heated to 155 ℃, makes it that good flowability be arranged;
2. continue to be warming up to 190 ℃, in mixing device, add waste tire rubber powder;
3. insulation is molten expanded 30 minutes, and stirred, and entered shears subsequently and sheared 30 minutes;
4. put into hold-up vessel and grew 300 minutes, make this product.
Embodiment 9 produces waste tire rubber powder modified asphalt 500kg
Raw-material weight proportion is as follows:
Matrix pitch 385kg
Waste tire rubber powder 115kg
Matrix pitch is a straight-run pitch, is 60-120 25 ℃ penetration degrees, 0.1mm; Waste tire rubber powder is the rubber powder that heavy duty tire is made, and fineness is 30 orders.
Its preparation method is as follows:
1. the matrix pitch temperature is heated to 150 ℃, makes it that good flowability be arranged;
2. continue to be warming up to 195 ℃, in mixing device, add waste tire rubber powder;
3. insulation is molten expanded 30 minutes, and stirred, and entered shears subsequently and sheared 30 minutes;
4. put into hold-up vessel and grew 45 minutes, make this product.
Claims (6)
1. a waste tire rubber powder modified asphalt is characterized in that, contains following component and weight part proportioning:
Matrix pitch 70-90 part
Waste tire rubber powder 10-30 part
2. according to claim 1 described waste tire rubber powder modified asphalt, it is characterized in that preferred weight part proportioning of component is:
Matrix pitch 75-80 part
Waste tire rubber powder 20-25 part
Optimum weight part proportioning of component is:
78 parts of matrix pitches
22 parts of waste tire rubber powders
3. according to claim 1 or 2 described waste tire rubber powder modified asphalts, it is characterized in that described waste tire rubber powder is the rubber powder that heavy duty tire is made, fineness is 20-40 day; Described matrix pitch, a kind of in vacuum residuum or perfectly straight pitch, rock asphalt, the mediation pitch.
4. according to the preparation method of claim 1 or 2 described waste tire rubber powder modified asphalts, it is characterized in that, carry out according to following step:
(1) matrix pitch is heated to 160-200 ℃;
(2) waste tire rubber powder is joined in the above-mentioned pitch, after stirring, insulation swelling 10-30 minute:
(3) sheared 10-30 minute at 180-190 ℃;
(4) grew 30-60 minute, promptly make waste tire rubber powder modified asphalt.
5. according to the preparation method of claim 4 described waste tire rubber powder modified asphalts, it is characterized in that the stirring of said (2) adopts agitator to carry out, agitator speed is 500-1000 rev/min.
6. according to the preparation method of claim 4 described waste tire rubber powder modified asphalts, it is characterized in that the shearing of said (3) adopts triode line formula high speed shear mulser to carry out, its rotating speed is 1440 to change minute, and the gap between the blade is 0.5 μ m.