CN101734882A - High-strength and wear-resisting bricks for construction and decoration - Google Patents
High-strength and wear-resisting bricks for construction and decoration Download PDFInfo
- Publication number
- CN101734882A CN101734882A CN200810228579A CN200810228579A CN101734882A CN 101734882 A CN101734882 A CN 101734882A CN 200810228579 A CN200810228579 A CN 200810228579A CN 200810228579 A CN200810228579 A CN 200810228579A CN 101734882 A CN101734882 A CN 101734882A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- strength
- decoration
- bricks
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-strength and wear-resisting bricks for construction and decoration, which are prepared from the following raw materials in part by weight: 70 to 100 parts of unsaturated polyester resin, 1 to 10 parts of parting agent, 15 to 25 parts of titanium dioxide, 20 to 25 parts of dibutyl phthalate, 1 to 10 parts of benzoyl peroxide paste, 1 to 10 parts of calcium stearate, 5 to 15 parts of fine sand, 0.1 to 1 part of triphenyl phosphate, 2 to 8 parts of coking gallic acid, 35 to 45 parts of expanded perlite, 5 to 25 parts of zircon sand and 0.5 to 5 parts of sandstone. The bricks are wide in resources of raw materials and tests prove that the bricks can be quickly hardened and are stable in product performance, innoxious, pollution-free to environment, short in production period and low in cost. The bricks have high strength, wear resistance, frost resistance, flame resistance, heat preservation, sound insulation and heat insulation, insulation, high rigidity, acid-base resistance and long service life, and are ideal high-strength and wear-resisting bricks for the decoration of inside and outside wall surfaces and ground in architectural decoration industry.
Description
Technical field
The present invention relates to a kind of a kind of high-strength, wear-resisting building and decoration brick of architectural decoration.
Background technology
Since the nineties in last century, world developed country has forbidden the decoration of glass curtain wall at high-rise, mainly is because it exists light pollution and glass to come off and hurts sb.'s feelings.The decoration of exterior wall of the building of brick post, brick wall structure and ceramic tile, mosaic, because of a large amount of earth resources of need, be subjected to the influence of the environment and the eubiosis, having limited it is using, replacing is the high buildings and large mansions of Lightweight Steel Construction and with novel chemical building material assembly type building, various high-performance, environment-friendly type paint should and produce.The synthetic resins novel material, safety, environmental protection, color and luster are abundant because it has, anti-fouling and self-cleaning is strong, lasting, decorative effect that economy can reach aluminium sheet curtain, stone material curtain again, are widely used in the construction renovation of novel building and old building thing.
Summary of the invention
The present invention is proposed by the problems referred to above, and a kind of interior wall face and ground decoration brick that is used for buildings is provided, and has building and the decoration brick that wear-resisting, anti-combustion, insulation effect are arranged.
In order to realize above purpose, technical scheme of the present invention is: a kind of high-strength, wear-resisting building and decoration are used brick, it is characterized in that counting ratio by following raw materials in parts by weight is prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: thin wind sand: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=70～100: 1～10: 15～25: 20～25: 1～10: 1～10: 5～15: 0.1～1: 2～8: 35～45: 5～25: 0.5～5.
A kind of high-strength, wear-resisting building and decoration are used brick, it is characterized in that counting ratio by following raw materials in parts by weight is prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: thin wind sand: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=80～90: 2～8: 17～22: 21～24: 2～8: 2～8: 7～12: 0.6～0.9: 3～7: 38～42: 10～20: 1～3.
A kind of high-strength, wear-resisting building and decoration are used brick, it is characterized in that counting ratio by following raw materials in parts by weight is prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: thin wind sand: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=85: 5: 20: 22: 5: 5: 10: 0.5: 5: 40: 15: 1.
A kind of high-strength, wear-resisting building and the decoration manufacture method of brick has the following steps:
(1), choose raw material by above mass parts and in resin, add earlier an amount of staining agent, the 3rd and gather materials, add breeze and other pulvis again, stir then, be poured on the chromium plating black iron plate after evenly, be placed on plane bumper shake and put down, be paved with standby.
(2), zircon sand, sandstone put into be ground into powder in the pulverizer, and stir.Add above-mentioned pulvis again in the 3rd gathers materials, continue then to stir, evenly the back is injected framed, keep flat the slightly iron plate strickling of the surface layer of hardness in framed earlier, topped another piece iron plate is carried out punching press again, below 40 ℃, solidify 5-20MIN, the demoulding, throw off iron plate up and down, natural curing 48h, edging finishing, soaking 10-30min with the 20%-35% sodium hydroxide solution then is alkali cleaning, flushing is dried, and just obtains surfacing, is finished product.
A kind of high-strength, wear-resisting building of the present invention and decoration are used brick, and raw material resources is wide, and is fast set time through evidence, and end properties is stable, nontoxic, nonpollution environment.With short production cycle, cost is low.It is good to have high-strength, wear-resisting, freeze proof, anti-combustion, insulation, sound insulation, heat-proof quality, insulation, hardness height, and acid and alkali-resistance, long service life are wall face and comparatively ideal high-strength, the abrasive bricks of ground decoration in the architectural decoration.
Embodiment
Embodiment one
A kind of high-strength, wear-resisting building and decoration are used brick, it is characterized in that counting ratio by following raw materials in parts by weight is prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: thin wind sand: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=85: 5: 20: 22: 5: 5: 10: 0.5: 5: 40: 15: 1.
A kind of high-strength, wear-resisting building and the decoration manufacture method of brick has the following steps:
(1), choose raw material by above mass parts and in resin, add earlier an amount of staining agent, the 3rd and gather materials, add breeze and other pulvis again, stir then, be poured on the chromium plating black iron plate after evenly, be placed on plane bumper shake and put down, be paved with standby.
(2), zircon sand, sandstone put into be ground into powder in the pulverizer, and stir.Add above-mentioned pulvis again in the 3rd gathers materials, continue then to stir, evenly the back is injected framed, keep flat the slightly iron plate strickling of the surface layer of hardness in framed earlier, topped another piece iron plate is carried out punching press again, below 40 ℃, solidify 5-20MIN, the demoulding, throw off iron plate up and down, natural curing 48h, edging finishing, soaking 10-30min with the 20%-35% sodium hydroxide solution then is alkali cleaning, flushing is dried, and just obtains surfacing, is finished product.
Embodiment two
A kind of high-strength, wear-resisting building and decoration are used brick, count ratio by following raw materials in parts by weight and are prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: thin wind sand: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=70: 10: 25: 25: 10: 1: 5: 0.1: 2: 45: 25: 5.Manufacture method is with embodiment one.
Embodiment three
A kind of high-strength, wear-resisting building and decoration are used brick, it is characterized in that counting ratio by following raw materials in parts by weight is prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: thin wind sand: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=100: 1: 15: 20: 1: 10: 15: 1: 8: 35: 5: 0.5.Manufacture method is with embodiment one.
Embodiment four
A kind of high-strength, wear-resisting building and decoration are used brick, it is characterized in that counting ratio by following raw materials in parts by weight is prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: thin wind sand: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=80: 2: 17: 24: 2: 8: 7: 0.9: 3: 42: 10: 3.
Embodiment five
A kind of high-strength, wear-resisting building and decoration are used brick, it is characterized in that counting ratio by following raw materials in parts by weight is prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: thin wind sand: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=90: 2: 22: 21: 8: 2: 12: 0.6: 7: 38: 20: 1.
Claims (4)
1. high-strength, a wear-resisting building and decorate and use brick, it is characterized in that counting ratio by following raw materials in parts by weight is prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: wind sand carefully: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=70～100: 1～10: 15～25: 20～25: 1～10: 1～10: 5～15: 0.1～1: 2～8: 35～45: 5～25: 0.5～5.
2. a kind of high-strength, wear-resisting building according to claim 1 and decoration are used brick, it is characterized in that counting ratio by following raw materials in parts by weight is prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: thin wind sand: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=80～90: 2～8: 17～22: 21～24: 2～8: 2～8: 7～12: 0.6～0.9: 3～7: 38～42: 10～20: 1～3.
3. a kind of high-strength, wear-resisting building according to claim 1 and decoration are used brick, it is characterized in that counting ratio by following raw materials in parts by weight is prepared from: unsaturated polyester resin: separant: titanium dioxide: dibutyl phthalate: benzoyl peroxide is stuck with paste: calcium stearate: thin wind sand: triphenylphosphate: pyrogallol: swelling perlite powder: zircon sand: sandstone=85: 5: 20: 22: 5: 5: 10: 0.5: 5: 40: 15: 1.
4. high-strength, a wear-resisting building and decorate manufacture method with brick has the following steps:
(1), choose raw material by above mass parts and in resin, add earlier an amount of staining agent, the 3rd and gather materials, add breeze and other pulvis again, stir then, be poured on the chromium plating black iron plate after evenly, be placed on plane bumper shake and put down, be paved with standby.
(2), zircon sand, sandstone put into be ground into powder in the pulverizer, and stir.Add above-mentioned pulvis again in the 3rd gathers materials, continue then to stir, evenly the back is injected framed, keep flat the slightly iron plate strickling of the surface layer of hardness in framed earlier, topped another piece iron plate is carried out punching press again, below 40 ℃, solidify 5-20MIN, the demoulding, throw off iron plate up and down, natural curing 48h, edging finishing, soaking 10-30min with the 20%-35% sodium hydroxide solution then is alkali cleaning, flushing is dried, and just obtains surfacing, is finished product.