CN101724377B - High-strength condensed type double-component organosilicon acid-resisting sealant and preparation method thereof - Google Patents
High-strength condensed type double-component organosilicon acid-resisting sealant and preparation method thereof Download PDFInfo
- Publication number
- CN101724377B CN101724377B CN 200810201877 CN200810201877A CN101724377B CN 101724377 B CN101724377 B CN 101724377B CN 200810201877 CN200810201877 CN 200810201877 CN 200810201877 A CN200810201877 A CN 200810201877A CN 101724377 B CN101724377 B CN 101724377B
- Authority
- CN
- China
- Prior art keywords
- component
- strength
- type double
- resisting
- condensed type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a high-strength condensed type double-component organosilicon acid-resisting sealant and a preparation method thereof. In the invention, a component A is prepared by mixing 107 silastic, fillings, paints, a plasticiser and a deep solidifying accelerator and a component B is prepared from a multifunctional group organosilicon crosslinker, a coupling agent and a catalyst. The component A and the component B are mixed according to a certain proportion to prepare the high-strength condensed type double-component organosilicon acid-resisting sealant in using process. Even immersed in a sulfuric acid solution with a concentration of 5% for 15 days, the strength variation of the sealant is no more than 20%, the tensile-strength is above 2.0MPa and the shear strength is above 1.8MPa. The invention has the advantages of adjustable operation time, fast deep solidification at room temperature, higher-strength adhesion force, sound acid-resisting and weather-resisting performances and long service life and is mainly applied to the acid-resisting field of flues of the power plant and the field of high-strength adhesion.
Description
Technical field
The present invention relates to a kind of high-strength condensed type double-component organosilicon acid-resisting sealant and preparation method thereof, belong to the seal gum technical field.
Background technology
Room temperature vulcanized silicone rubber is take hydroxy-end capped polydimethylsiloxane as basic glue, forms through cooperating with linking agent, catalyzer, filler etc., can be divided into one-pack type (RTV1 type) and two-component type (RTV2 type) by packaged form.
The shortcoming of single-component RTV1 type silicon rubber sealant is that deep layer is solidified slowly.It is strong that but the advantage of two component RTV2 type silicon rubber sealants is deep curing, quick solidifying, resistance to hydrolysis.Rubber composition has resistant of high or low temperature, weather resisteant, and the premium propertiess such as chemical resistance, and form class rubber performance such as hardness and the ductile solidifying product with excellence, thereby the value that has a wide range of applications.
In power plant flue building or acidproof field, used material of construction sealing agent must have certain intensity, hardness and good adhesive property, and can bear the long-term corrosion of acidic medium in using and performance does not have greatly changed.The loss that has the document statistics whole world to cause because of acid corrosion in 1 year surpasses 10,000,000,000 dollars, and people more and more pay close attention to the problem of acid corrosion buildings and metal, especially the corrosion of flue.
The development of at present existing acid-resisting sealant.A kind of acidproof RTV silicon rubber sealant (Xu Yu etc., the development of acidproof RTV silicon rubber sealant, organosilicon material are disclosed such as document, 2001,15 (4): 20-21), the performance in the pH6 weak acidic medium is more stable, but only is suitable for water purifier acid resistance dielectric seal.And for example denomination of invention is that " anticorrosive high temperature sealing glue " (publication number is CN1214356, open day is on April 21st, 1999) a kind of single-component anticorrosive high temperature sealing glue disclosed, its use temperature is wide, strong alkali-acid resistance, but because sealing glue need be heated to more than 100 ℃ and be cured, difficulty is solidified in the deep.Therefore acid resistance or the use properties aspect of acid-resisting sealant of the prior art are still undesirable.
Summary of the invention
The object of the invention is to overcome the defective of prior art acid-resisting sealant aspect acid resistance and performance easy to use, a kind of high-strength condensed type double-component organosilicon acid-resisting sealant is provided.The present invention is applicable to acidproof field and high strength bonding field.
Another object of the present invention provides a kind of preparation method of high-strength condensed type double-component organosilicon acid-resisting sealant.
For achieving the above object, the present invention can be achieved through the following technical solutions:
A kind of high-strength condensed type double-component organosilicon acid-resisting sealant comprises component A and component B, it is characterized in that, and with the two components of A, B, be that catalyzer carries out crosslinking reaction acquisition high-strength condensed type double-component organosilicon acid-resisting sealant through dibutyl tin laurate.
Sealing glue will have very high viscosity, in order to better processing property is arranged, miniflow drops down or the thixotroping lotion so the viscosity of A component should be, and generally selects 107 silicon rubber of 5000-80000cps range of viscosities.In parts by weight, component A comprises following material:
107 silicon rubber 10
Pigment 0-10
Softening agent 5-15
Filler 60-150
Deep layer curing catalyst 0.1-1.5.
Described pigment is one or more the mixture in U carbon black, iron oxide black, the titanium dioxide.
Described softening agent is silicone oil with low viscosity, comprises a kind of in 100cps silicone oil, the hydroxy silicon oil or both mixing.
Described filler is one or more the mixture in white carbon black, silica powder, diatomite, silicon powder, calcium carbonate, the kaolin.
Described deep layer curing catalyst is the phosphatic aqueous solution, and wherein the weight percent concentration of the phosphatic aqueous solution is 0.1-0.4%.
In parts by weight, component B comprises following material:
Linking agent 30-50
Coupling agent 5-15
Dibutyl tin laurate 0.4-1.0.
Described linking agent is the polyfunctional group organosilicon cross-linking agent, such as wherein one or more mixing of methyltrimethoxy silane, Union carbide A-162, tetraethoxysilane, dimethyldiethoxysilane, vinyltriethoxysilane, vinyltrimethoxy silane.
Described coupling agent is organo-silicon coupling agent, such as wherein one or more mixing of β-aminoethyl-γ-aminopropyl-triethoxyl silane or its dipolymer, γ-glycidoxypropyltrime,hoxysilane, γ-(methacryloxy) propyl trimethoxy silicane.
High-strength condensed type double-component organosilicon acid-resisting sealant of the present invention is realized by following steps:
Step 1: count by weight, with 100 part of 107 silicon rubber, 0-10 parts of pigment and 5-15 parts of softening agent mixing and stirring, add 60-150 parts of fillers under the normal temperature, mix at 60 ℃-80 ℃, add 0.1-1.5 parts of deep layer curing catalysts after the cooling, obtain the A component;
Step 2: count by weight, with 30-50 parts of linking agents, 5-15 parts of coupling agents and 0.4-1.0 parts of dibutyl tin laurates are mixed to get the B component;
Step 3: during use, the B component that the A component that step 1 is prepared and step 2 prepare by weight proportion 100:5-10 mixes rear deaeration, solidifies to obtain high-strength condensed type double-component organosilicon acid-resisting sealant.
In above-mentioned preparation method's the first step, when adding 107 silicon rubber, softening agent, count by weight, add 0-10 parts pigment, can make the high-strength condensed type double-component organosilicon acid-resisting sealant of different colours.As add the U carbon black and be prepared into black high-strength degree acid-resisting sealant; Add iron oxide black and be prepared into blue mass colour high strength acid resistant seal gum; Add titanium dioxide and be prepared into white high strength acid resistant seal gum etc.
Owing to adopted technique scheme, the present invention has the following advantages:
1. high-strength condensed type double-component organosilicon acid-resisting sealant is neutral organic silica gel, not corroding metal.
2. operable time is short, but the room temperature rapid deep zone solidifies.
3. has higher intensity, good acid resistance, resistant of high or low temperature and weathering resistance, long service life.
4. described seal gum soaked in 5% sulfuric acid after 15 days, and its tensile strength and shearing resistance can reach respectively 2.0MPa and more than the 1.8MPa.
Embodiment
In order to make technique means of the present invention, creation characteristic, to reach purpose and effect is easy to understand, below in conjunction with embodiment, further set forth the present invention, but embodiments of the present invention are not limited to this.
Embodiment 1
In parts by weight, under the normal temperature, be 107 silicon rubber of 20000cps with 100 parts of viscosity, 5 parts of U carbon blacks join in 15 parts of 100cps silicone oil and the 10 parts of hydroxy silicon oils, stir, and add 90 parts of silicon powders and 4 parts of thermal silicas, mix at 60 ℃, adding 1.4 parts of weight percent concentration after the cooling is 0.1% aqueous phosphatic, and sulfuration makes component A.With 50 parts of tetraethyl silicate, 10 parts of vinyltriethoxysilanes, 10 parts of β-aminoethyl-γ-aminopropyl-triethoxyl silanes, 5 parts of γ-glycidoxypropyltrime,hoxysilane, 0.8 part of dibutyl tin laurate mixing makes component B.During use, in parts by weight, component A and component B mix rear deaeration in the ratio of 100:5, solidify to get high-strength condensed type double-component organosilicon acid-resisting sealant sheet A.After testing, performance perameter such as the table 1 of high-strength condensed type double-component organosilicon acid-resisting sealant sheet A.
The fundamental property of table 1 high-strength condensed type double-component organosilicon acid-resisting sealant sheet A
Sealing film cohesive force, strong adhesion have good mechanical property and acid resistance.
Embodiment 2
In parts by weight, under the normal temperature, be 107 silicon rubber of 50000cps with 100 parts of viscosity, 5 parts of U carbon blacks join in 15 parts of 100cps silicone oil and the 10 parts of hydroxy silicon oils, stir, and add 70 parts of silicon powders and 10 parts of precipitated silicas, mix at 70 ℃, adding 1.4 parts of weight percent concentration after the cooling is 0.3% aqueous phosphatic, and sulfuration makes component A.With 30 parts of methyl silicates, 20 parts of dimethyldiethoxysilanes, 10 parts of vinyltrimethoxy silanes, 8 parts of γ-(methacryloxy) propyl trimethoxy silicanes, 10 parts of γ-glycidoxypropyltrime,hoxysilane, 0.9 part of dibutyl tin laurate mixing makes component B.During use, in weight ratio, component A and component B mix rear deaeration in the ratio of 100:7, solidify to get high-strength condensed type double-component organosilicon acid-resisting sealant sheet B.After testing, performance perameter such as the table 2 of high-strength condensed type double-component organosilicon acid-resisting sealant sheet B.
The fundamental property of table 2 high-strength condensed type double-component organosilicon acid-resisting sealant sheet B
Embodiment 3
In parts by weight, under the normal temperature, be 107 silicon rubber of 50000cps with 100 parts of viscosity, 5 parts of U carbon blacks join in 15 parts of 100cps silicone oil and the 10 parts of hydroxy silicon oils, stir, and add 100 parts of calcium carbonate and 10 parts of thermal silicas, mix at 80 ℃, adding 1.4 parts of weight percent concentration after the cooling is 0.4% aqueous phosphatic, and sulfuration makes component A.With 30 parts of methyl silicates, 20 parts of dimethyldiethoxysilanes, 10 parts of vinyltrimethoxy silanes, 5 parts of γ-(methacryloxy) propyl trimethoxy silicanes, 10 parts of β-aminoethyl-γ-aminopropyl-triethoxyl silanes, 1 part of dibutyl tin laurate mixing makes component B.During use, in weight ratio, component A and component B mix rear deaeration in the ratio of 100:10, solidify to get high-strength condensed type double-component organosilicon acid-resisting sealant sheet C.After testing, performance perameter such as the table 3 of high-strength condensed type double-component organosilicon acid-resisting sealant sheet C.
The fundamental property of table 3 high-strength condensed type double-component organosilicon acid-resisting sealant sheet C
More than show and described ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that describes in above-described embodiment and the specification sheets just illustrates principle of the present invention; the present invention also has various changes and modifications without departing from the spirit and scope of the present invention, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (6)
1. a high-strength condensed type double-component organosilicon acid-resisting sealant comprises component A and component B, it is characterized in that, in parts by weight, component A comprises following material:
In parts by weight, component B comprises following material:
Linking agent 30-50
Coupling agent 5-15
Dibutyl tin laurate 0.4-1.0
In part by weight, the ratio of component A and component B is 100:5-10;
The wherein said deep layer curing catalyst concentration that is weight percentage is the aqueous phosphatic of 0.1-0.4%, and described linking agent is the polyfunctional group organosilicon cross-linking agent, and described coupling agent is organo-silicon coupling agent, and
Described polyfunctional group organosilicon cross-linking agent is wherein one or more the mixing of methyltrimethoxy silane, Union carbide A-162, tetraethoxysilane, dimethyldiethoxysilane, vinyltriethoxysilane, vinyltrimethoxy silane
Described organo-silicon coupling agent is wherein one or more the mixture of β-aminoethyl-γ-aminopropyl-triethoxyl silane or its dipolymer, γ-glycidoxypropyltrime,hoxysilane, γ-(methacryloxy) propyl trimethoxy silicane.
2. high-strength condensed type double-component organosilicon acid-resisting sealant according to claim 1 is characterized in that, described pigment is one or more the mixture in U carbon black, iron oxide black, the titanium dioxide.
3. high-strength condensed type double-component organosilicon acid-resisting sealant according to claim 1 is characterized in that, described softening agent is silicone oil with low viscosity.
4. high-strength condensed type double-component organosilicon acid-resisting sealant according to claim 3 is characterized in that, described silicone oil with low viscosity is a kind of in 100cps silicone oil, the hydroxy silicon oil or both mixing.
5. high-strength condensed type double-component organosilicon acid-resisting sealant according to claim 1 is characterized in that, described filler is one or more the mixture in white carbon black, silica powder, diatomite, silicon powder, the kaolin.
6. a method for preparing high-strength condensed type double-component organosilicon acid-resisting sealant claimed in claim 1 is characterized in that, may further comprise the steps:
Step 1: count by weight, with 100 part of 107 silicon rubber, 0-10 part pigment and 5-15 part softening agent mixing and stirring, add 60-150 part filler under the normal temperature, mix at 60 ℃-80 ℃, add 0.1-1.5 part deep layer curing catalyst after the cooling, obtain the A component;
Step 2: count by weight, with 30-50 part linking agent, 5-15 part coupling agent and 0.4-1.0 part dibutyl tin laurate are mixed to get the B component;
Step 3: during use, the B component that the A component that step 1 is prepared and step 2 prepare by weight proportion 100:5-10 mixes rear deaeration, solidifies to obtain high-strength condensed type double-component organosilicon acid-resisting sealant.