CN101701349A - Band steel oxidized surface processing device and surface processing method - Google Patents
Band steel oxidized surface processing device and surface processing method Download PDFInfo
- Publication number
- CN101701349A CN101701349A CN200910232285A CN200910232285A CN101701349A CN 101701349 A CN101701349 A CN 101701349A CN 200910232285 A CN200910232285 A CN 200910232285A CN 200910232285 A CN200910232285 A CN 200910232285A CN 101701349 A CN101701349 A CN 101701349A
- Authority
- CN
- China
- Prior art keywords
- band steel
- stainless steel
- steel
- pulse
- surface processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of steel plate surface processing, in particular to a band steel oxidized surface-processing method comprising the following steps of: (1) providing a band steel and a stainless steel sheet to be processed; (2) putting the band steel and the stainless steel sheet to be processed in an electrolyte containing 5-25g/L of sodium chlorate and 2-28g/L of alkali metal hydroxide; (3) connecting the band steel to be processed with an anode of a direct current (DC) power supply and connecting the stainless steel sheet with a cathode; and (4) galvanizing a pulse DC with the pulse current density of 10-25A/dm2, the peak voltage of 330-500V, the pulse time of 0.1-5.0 ms equal to pulse interval time and the whole treatment time of 10-60 minutes. The method has novel conception, reasonable structure, low cost and simple procedures, greatly improves the working efficiency, eliminates the waste pollution, protects the environment and decreases the cost.
Description
Technical field
The present invention relates to the surface of steel plate processing technology field, especially a kind of band steel oxidation surface preparation.
Background technology
Steel plate must keep the pure iron active surface of the cleaning of an oxide-free and the existence of other fouls before pot galvanize.This method is by the method for pickling the iron scale on surface to be removed earlier, is coated with last layer then and protects by zinc chloride or by the solvent that ammonium chloride and zinc chloride mixing are formed, thereby prevent that steel plate is oxidized again.The operation on existing processing band steel oxidation surface is loaded down with trivial details, long processing time, and efficient is low, the cost height particularly can produce a large amount of sewage, contaminate environment in treating processes, administer sewage and will spend necessary cost again, improved the tooling cost of whole operation so greatly.
Summary of the invention
For the operation that overcomes existing processing band steel oxidation surface is loaded down with trivial details, long processing time, efficient is low, the cost height, the deficiency of high pollution the invention provides a kind of band steel oxidation surface preparation.
The technical solution adopted for the present invention to solve the technical problems is: a kind of band steel oxidation surface preparation may further comprise the steps:
(1) provides pending band steel and stainless steel substrates;
(2) pending band steel and stainless steel substrates are put into the electrolytic solution that contains 5-25g/L sodium chlorate and 2-28g/L alkali metal hydroxide;
(3) pending band steel is linked to each other with the anode of direct supply, stainless steel substrates links to each other with negative electrode;
(4) passing to pulse current density is 10-25A/dm
2, crest voltage is the pulse direct current of 330-500V, and the burst length is 0.1-5.0ms, equals the burst length interpulse period, and its overall treatment time is 10-60 minute.
According to another embodiment of the invention, comprise that further electrolytic solution contains the trisodium phosphate of 10-35g/L.
According to another embodiment of the invention, comprise that further belt steel surface imposes the pre-plated film of polymer earlier, to increase the initial disruptive voltage of reaction.
According to another embodiment of the invention, comprise that further alkali metal hydroxide is to be sodium hydroxide or potassium hydroxide.
A kind of band steel oxidation surface processing device comprises fluid storage tank, direct supply and lead, seasoning electrolytic solution in the fluid storage tank, and the anode of direct supply connects belt steel surface, and stainless steel is connected with negative electrode.
The invention has the beneficial effects as follows that this method is novel, and is rational in infrastructure, cost is low, and operation is simple, has improved working efficiency greatly.Simultaneously, eliminate the pollution of refuse, protected environment, reduced cost.
Description of drawings
The present invention is further described below in conjunction with drawings and Examples.
Fig. 1 is a structural representation of the present invention.
1. fluid storage tanks among the figure, 2. direct supply, 3. lead, 4. electrolytic solution, 5. band steel, 6. stainless steel.
Embodiment
The present invention is further detailed explanation with preferred embodiment in conjunction with the accompanying drawings now.These accompanying drawings are the synoptic diagram of simplification, basic structure of the present invention only is described in a schematic way, so it only show the formation relevant with the present invention.
As Fig. 1 is structural representation of the present invention, and a kind of band steel oxidation surface preparation may further comprise the steps:
(1) provides pending band steel 5 and stainless steel substrates 6;
(2) pending band steel 5 and stainless steel substrates 6 are put into the electrolytic solution 4 that contains 5-25g/L sodium chlorate and 2-28g/L alkali metal hydroxide;
(3) pending band steel 5 is linked to each other with the anode of direct supply 2, stainless steel substrates 6 links to each other with negative electrode;
(4) passing to pulse current density is 10-25A/dm
2, crest voltage is the pulse direct current of 330-500V, and the burst length is 0.1-5.0ms, equals the burst length interpulse period, and its overall treatment time is 10-60 minute.Electrolytic solution 4 contains the trisodium phosphate of 10-35g/L.Band steel 5 surfaces impose the pre-plated film of polymer earlier, to increase the initial disruptive voltage of reaction.Alkali metal hydroxide is to be sodium hydroxide or potassium hydroxide.
A kind of band steel oxidation surface processing device, comprise fluid storage tank 1, direct supply 2 and lead 3, seasoning electrolytic solution 4 in the fluid storage tank 1, electrolytic solution 4 is for containing 5-25g/L sodium chlorate and 2-28g/L alkali metal hydroxide, and wherein alkali metal hydroxide is to be sodium hydroxide or potassium hydroxide; Electrolytic solution 4 also contains the trisodium phosphate of 10-35g/L.Anode connecting band steel 5 surfaces of direct supply 2, stainless steel 6 is connected with negative electrode.Passing to pulse current density is 10-25A/dm
2, crest voltage is the pulse direct current of 330-500V, and the burst length is 0.1-5.0ms, equals the burst length interpulse period, and its overall treatment time is 10-60 minute.This method is novel, and is rational in infrastructure, and cost is low, and operation is simple, improved working efficiency greatly.Simultaneously, eliminate the pollution of refuse, protected environment, reduced cost.
With above-mentioned foundation desirable embodiment of the present invention is enlightenment, and by above-mentioned description, the related work personnel can carry out various change and modification fully in the scope that does not depart from this invention technological thought.The technical scope of this invention is not limited to the content on the specification sheets, must determine its technical scope according to the claim scope.
Claims (5)
1. be with the steel oxidation surface preparation for one kind, it is characterized in that: may further comprise the steps:
(1) provides pending band steel (5) and stainless steel substrates (6);
(2) pending band steel (5) and stainless steel substrates (6) are put into the electrolytic solution (4) that contains 5-25g/L sodium chlorate and 2-28g/L alkali metal hydroxide;
(3) pending band steel (5) is linked to each other with the anode of direct supply (2), stainless steel substrates (6) links to each other with negative electrode;
(4) passing to pulse current density is 10-25A/dm
2, crest voltage is the pulse direct current of 330-500V, and the burst length is 0.1-5.0ms, equals the burst length interpulse period, and its overall treatment time is 10-60 minute.
2. band steel oxidation surface preparation according to claim 1 is characterized in that: electrolytic solution (4) contains the trisodium phosphate of 10-35g/L.
3. band steel oxidation surface preparation according to claim 1 is characterized in that: band steel (5) surface imposes the pre-plated film of polymer earlier, to increase the initial disruptive voltage of reaction.
4. band steel oxidation surface preparation according to claim 1 is characterized in that: alkali metal hydroxide is to be sodium hydroxide or potassium hydroxide.
5. be with the steel oxidation surface processing device for one kind, it is characterized in that: comprise fluid storage tank (1), direct supply (2) and lead (3), the interior seasoning electrolytic solution of fluid storage tank (1) (4), anode connecting band steel (5) surface of direct supply (2), stainless steel (6) is connected with negative electrode.