CN101701119A - 一种抗油污自洁水性氟碳漆 - Google Patents
一种抗油污自洁水性氟碳漆 Download PDFInfo
- Publication number
- CN101701119A CN101701119A CN200910309995A CN200910309995A CN101701119A CN 101701119 A CN101701119 A CN 101701119A CN 200910309995 A CN200910309995 A CN 200910309995A CN 200910309995 A CN200910309995 A CN 200910309995A CN 101701119 A CN101701119 A CN 101701119A
- Authority
- CN
- China
- Prior art keywords
- rub resistance
- cleaning aqueous
- resistance self
- oil rub
- aqueous fluorocarbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗油污自洁水性氟碳漆。由下述重量百分含量的物料组成:聚羧酸胺盐0.5-1.3%、表面活性剂0.1-0.4%、pH调节剂0.1-0.3%、消泡剂0.4-0.8%、乙二醇2.0-4.0%、成膜助剂2.0-5.5%、钛白粉7.5-30%、氟碳乳液50-80%、增稠剂0.3-0.8%、防霉剂0.1-0.8%、防腐剂0.1-0.2%、余量为水。本发明产品,环保、施工简单、耐水抗碱、防霉防藻、附着力强、耐候性好、超强耐溶剂性、超低表面能;本发明采用的原料易得,制备方便。
Description
技术领域
本发明涉及一种漆,特别涉及一种抗油污自洁水性氟碳漆。
背景技术
普通墙面抗污性不好、容易产生雨流痕迹、墙体易开裂、发花、粉化、起皮、长霉,很多墙面存在乱张贴、乱涂乱画等问题,影响人们的家居生活和城市的美观。
通过涂刷墙面漆可以改善上述问题,但是目前许多墙面漆抗污性、耐溶剂性不强、耐水耐碱性耐老化性不好,防霉防藻力差,漆膜表面张力高、散发挥发性气体,不够安全环保,不能解决或不能完全解决这些问题,特别是墙面乱张贴、乱涂乱画后污渍难以去除问题。
发明内容
为了克服上述问题,本发明提供一种抗油污自洁水性氟碳漆。
本发明所采取的技术方案是:
一种抗油污自洁水性氟碳漆,由下述重量百分含量的物料组成:聚羧酸胺盐0.5-1.3%、表面活性剂0.1-0.4%、pH调节剂0.1-0.3%、消泡剂0.2-0.5%、乙二醇2.-4.0%、成膜助剂2.0-5.5%、钛白粉7.5-30%、氟碳乳液50-80%、增稠剂0.3-0.8%、防霉剂0.1-0.8%、防腐剂0.1-0.2%、余量为水。
本发明有益效果是:本发明产品,环保、施工简单、耐水抗碱、防霉防藻、附着力强、耐候性好、超强耐溶剂性、超低表面能;本发明采用的原料易得,制备方便。
具体实施方式
下面结合实例,进一步说明本发明。
以下各实施例中,聚羧酸均聚胺盐为英国布莱克本公司的165。
表面活性剂为美国3M公司的全氟代脂肪族聚合物脂,型号为F4430。
pH调节剂为美国DOW公司的AMP-95。
消泡剂为深圳明佳公司的有机硅和矿物油混合物产品,型号为7120。
成膜助剂为美国DOW公司三丙二醇丁醚,型号为TPnB。
钛白粉为金红石型。
氟碳乳液为大金氟化学公司的氟碳乳液,型号为S800。
增稠剂为BASF公司的聚氨脂增稠剂,型号为NLS300。
防霉剂为法国先创公司的的胺基甲酸-1-氯-苯并咪唑-2-甲基酸和N-(3,4二氯苯基)-N.N-二甲基脲的混合物产品,型号为AF2130。
防腐剂为法国先创公司的异噻唑啉酮,型号为GT2060。
实施例1
聚羧酸胺盐1.1%、表面活性剂0.3%、pH调节剂0.2%、消泡剂0.5%、乙二醇3.0%、成膜助剂3.3%、钛白粉21%、氟碳乳液63%、增稠剂0.5%、防霉剂0.8%、防腐剂0.2%、余量为水,混合均匀得到产品。
实施例2
聚羧酸胺盐1.3%、表面活性剂0.4%、pH调节剂0.2%、消泡剂0.35%、乙二醇2.0%、成膜助剂2.0%、钛白粉30%、氟碳乳液50%、增稠剂0.8%、防霉剂0.3%、防腐剂0.1%、余量为水,混合均匀得到产品。
实施例3
聚羧酸胺盐0.85%、表面活性剂0.25%、pH调节剂0.15%、消泡剂0.3%、乙二醇3.5%、成膜助剂3.6%、钛白粉18%、氟碳乳液67%、增稠剂0.55%、防霉剂0.5%、防腐剂0.13%、余量为水,混合均匀得到产品。
实施例4
聚羧酸胺盐0.6%、表面活性剂0.2%、pH调节剂0.3%、消泡剂0.25%、乙二醇4.0%、成膜助剂4.0%、钛白粉15%、氟碳乳液70%、增稠剂0.45%、防霉剂0.8%、防腐剂0.15%、余量为水,混合均匀得到产品。
实施例5
聚羧酸胺盐0.5%、表面活性剂0.1%、pH调节剂0.1%、消泡剂0.2%、乙二醇4.0%、成膜助剂5.5%、钛白粉7.5%、氟碳乳液80%、增稠剂0.3%、防霉剂0.3%、防腐剂0.18%、余量为水,混合均匀得到产品。
实验结果表明,在此基础上生产的产品耐候性可达1500小时以上,漆膜表面张力比普通氟碳漆降低60%、吸水性降低50%,抗污性大大提高。
本发明产品,环保、施工简单、耐水抗碱、防霉防藻、附着力强、耐候性好、超强耐溶剂性、超低表面能;本发明采用的原料易得,制备方便。
Claims (8)
1.一种抗油污自洁水性氟碳漆,由下述重量百分含量的物料组成:聚羧酸胺盐0.5-1.3%、表面活性剂0.1-0.4%、pH调节剂0.1-0.3%、消泡剂0.2-0.5%、乙二醇2.0-4.0%、成膜助剂2.0-5.5%、钛白粉7.5-30%、氟碳乳液50-80%、增稠剂0.3-0.8%、防霉剂0.1-0.8%、防腐剂0.1-0.2%、余量为水。
2.根据权利要求1所述的一种抗油污自洁水性氟碳漆,其特征在于:表面活性剂为全氟代脂肪族聚合物。
3.根据权利要求1所述的一种抗油污自洁水性氟碳漆,其特征在于:pH调节剂为DOW公司的AMP-95。
4.根据权利要求1所述的一种抗油污自洁水性氟碳漆,其特征在于:消泡剂为有机硅和矿物油混合物。
5.根据权利要求1所述的一种抗油污自洁水性氟碳漆,其特征在于:成膜助剂为三丙二醇丁醚。
6.根据权利要求1所述的一种抗油污自洁水性氟碳漆,其特征在于:钛白粉为金红石型。
7.根据权利要求1所述的一种抗油污自洁水性氟碳漆,其特征在于:增稠剂为聚氨脂。
8.根据权利要求1所述的一种抗油污自洁水性氟碳漆,其特征在于:防霉剂为异噻唑啉酮。