CN101698206B - Technique for producing titanium-copper compound wire - Google Patents
Technique for producing titanium-copper compound wire Download PDFInfo
- Publication number
- CN101698206B CN101698206B CN2009102185618A CN200910218561A CN101698206B CN 101698206 B CN101698206 B CN 101698206B CN 2009102185618 A CN2009102185618 A CN 2009102185618A CN 200910218561 A CN200910218561 A CN 200910218561A CN 101698206 B CN101698206 B CN 101698206B
- Authority
- CN
- China
- Prior art keywords
- titanium
- bar
- copper composite
- copper
- sleeve pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to the field of a technique for producing a titanium-copper compound wire. The invention has the technical proposal that the technique comprises the following steps: selecting a titanium or titanium alloy pipe in proper dimensions meeting the national standard as a sleeve pipe (1); selecting a copper rod matching the dimensions of the titanium pipe as a rod material (2); penetrating the rod material (2) into the sleeve pipe (1), and attaching the rod material (2) to the sleeve pipe (1) by using an explosion compounding method to make a titanium-copper compound rod and form a titanium-base compound layer (3); and swaging the titanium-copper compound rod, and drawing to make the titanium-copper compound wire. The titanium-copper compound wire has the advantages of high bond strength, high surface smoothness and high quality of finished products. The invention changes the current unfavorable situation that the high-quality titanium-copper compound wire in China still highly depends on import, and enjoys favorable economic benefits.
Description
Technical field
The present invention relates to a kind of titanium-copper composite wires method field of manufacturing.
Background technology
It is blast composite algorithm, hot extrusion method or manufacture method such as rolling that the manufacture method that is used for the titanium-copper composite wires of industries such as chlor-alkali, electric power, plating, electrolysis, hydrometallurgy, electronics, military project at present mainly adopts, but there are production technology difficult problems such as bond strength is low, processing cost height, the titanium-copper composite wires bond quality that produces is poor, easy to crack, can't satisfy the development need of high-precision technical industries such as electronics, military project, cause the domestic unfavorable situation that still highly depends on import for high-quality titanium-copper composite wires at present.
Summary of the invention
The manufacturing process that provides a kind of titanium-copper composite wires to be solved by this invention, make layer of titanium metal and metal copper layer fit closely, the titanium copper bond strength is high and not easy to crack, can utilize existing equipment to realize the production domesticization that high-quality titanium-copper composite wires is produced, develop and expand the application market of titanium-copper composite wires rapidly, reach foreign exchange earning, obtain the effect of the stronger market competitiveness and good economic benefit.
The present invention is for solving the problems of the technologies described above, and the technical scheme of employing is:
The implementation process of manufacture method mainly is divided into the following step:
A) blank is prepared: select for use the certain size titanium alloy tube that meets national standard or titanium pipe as sleeve pipe (1); Select for use with the corresponding copper rod of casing inner diameter size as bar (2);
B) poling carries out sleeve pipe (1) inner surface and bar outer surface (2) the oil removing cleaning, cleans and refresh, then with in bar (2) threading (1);
C) blast is compound, and it is compound to adopt the blast composite algorithm that the sleeve pipe (1) that penetrates bar (2) is exploded, and makes sleeve pipe (1) and bar (2) fit together, and makes to form titanium copper composite bed (3) between sleeve pipe (1) and the bar (2), makes titanium and copper composite bar;
D) processing of swaging is heated to the processing of swaging after the uniform temperature with titanium and copper composite bar, is processed into the titanium and copper composite bar of certain diameter;
E) drawing will be heated to the titanium-copper composite wires that is drawn into required size after the uniform temperature through the titanium and copper composite bar after the processing of swaging;
F) finishing is removed burr to the titanium-copper composite wires outer surface that drawing is made, and reconditioning scratches, and excises two terminations, makes the titanium-copper composite wires finished product.
Wherein, step d) can adopt rolling, titanium and copper composite bar is heated to the titanium and copper composite bar that is rolled into certain diameter after the uniform temperature.
Be 600--720 ℃ for sleeve pipe (1) for the processing temperature of swaging of titanium alloy tube in the step d).
Be 600--650 ℃ for sleeve pipe (1) for the processing temperature of swaging of titanium pipe in the step d).
Step d) is 400-500 ℃ for sleeve pipe (1) for the rolling heating-up temperature of titanium alloy tube.
Step d) is 350-450 ℃ for sleeve pipe (1) for the rolling heating-up temperature of titanium pipe.
The invention has the beneficial effects as follows, the titanium-copper composite wires that adopts the present invention to make, the titanium copper metal level is fitted firmly, the yield rate height, the surface smoothness height, the titanium copper section is even, can utilize existing equipment to realize the production domesticization of titanium-copper composite wires as early as possible, both satisfy domestic market demand, and can export goods and earn foreign currency again, created good economic benefit.
Description of drawings
Figure titanium-copper composite wires structural representation
1. sleeve pipes among the figure; 2. bar; 3. titanium base composite bed;
The specific embodiment
Below in conjunction with accompanying drawing be to external diameter
The specific embodiment of the manufacture process of the titanium-copper composite wires of 4mm is described in further detail, and the concrete manufacturing step of titanium-copper composite wires is:
A) blank is prepared, and selects for use to meet the GB/T3624-1995 standard, and the trade mark is TA1, and specification is
19 * 1.2mm titanium pipe is as sleeve pipe (1); Select for use to meet GB/T4423-1992, specification is
16 red copper bar is as bar (2);
B) poling carries out sleeve pipe (1) inner surface and bar outer surface (2) the oil removing cleaning, cleans and refresh, and removes burr and dirt, and it is even to reach circularity, then with in bar (2) threading (1);
C) blast is compound, the sleeve pipe (1) that will penetrate bar (2) is inserted in the blast composite algorithm tradition frock sleeve pipe, explosive and draw lead-in wire on cloth between frock sleeve pipe and the sleeve pipe (1), instantaneous explosion behind the some combustion wire, powerful explosive force fits tightly sleeve pipe (1) and bar (2) together, form titanium copper composite bed (3), make the titanium and copper composite bar shown in the accompanying drawing, this moment, the external diameter of titanium and copper composite bar was about
18.4mm;
D) processing of swaging is inserted titanium and copper composite bar after the heating furnace heating and titanium and copper composite bar to be put into the swager processing of repeatedly swaging, and the temperature of swaging remains on 600--650 ℃, until titanium and copper composite bar is machined to
The titanium and copper composite bar of 10mm;
E) drawing, to insert in the heating furnace through the titanium and copper composite bar after the processing of swaging and put into drawbench after the heating, supporting suitable mould carries out drawing, the drawing temperature is at 350--400 ℃, drawing speed 1.5-2.5 rice/minute, control drawing passes sizing reduction 0.8-1.2mm after drawing repeatedly, is drawn into titanium and copper composite bar
The titanium-copper composite wires of 4mm;
F) finishing is removed burr to the titanium-copper composite wires outer surface that drawing is made, and reconditioning scratches, and excises two terminations, makes the finished product titanium-copper composite wires;
Claims (2)
1. the manufacturing process of a titanium-copper composite wires is characterized in that, the concrete manufacture process of titanium-copper composite wires follows these steps to carry out:
A) blank is prepared: select for use the certain size titanium alloy tube that meets national standard or titanium pipe as sleeve pipe (1); Select for use with the corresponding copper rod of casing inner diameter size as bar (2);
B) poling carries out sleeve pipe (1) inner surface and bar outer surface (2) the oil removing cleaning, cleans and refresh, then with in bar (2) threading (1);
C) blast is compound, and it is compound to adopt the blast composite algorithm that the sleeve pipe (1) that penetrates bar (2) is exploded, and makes sleeve pipe (1) and bar (2) fit together, and makes to form titanium copper composite bed (3) between sleeve pipe (1) and the bar (2), makes titanium and copper composite bar;
D) processing of swaging, titanium and copper composite bar is heated to the processing of swaging after the uniform temperature, be processed into the titanium and copper composite bar of certain diameter, its middle sleeve (1) is 600--720 ℃ for the processing temperature of swaging of titanium alloy tube, and the processing temperature of swaging of titanium pipe is 600--650 ℃;
E) drawing will be heated to the titanium-copper composite wires that is drawn into required size after 350--400 ℃ through the titanium and copper composite bar after the processing of swaging;
F) finishing is removed burr to the titanium-copper composite wires outer surface that drawing is made, and reconditioning scratches, and excises two terminations, makes the titanium-copper composite wires finished product.
2. according to the described technique for producing titanium-copper compound wire of claim 1, it is characterized in that, employing is heated to the titanium and copper composite bar that is rolled into certain diameter after the uniform temperature with titanium and copper composite bar and comes replacement step d), wherein the rolling heating-up temperature of titanium alloy tube is 400-500 ℃, and the rolling heating-up temperature of titanium pipe is 350-450 ℃.