CN101693771A - 闭孔泡孔聚氨酯弹性体卷材的制作工艺 - Google Patents

闭孔泡孔聚氨酯弹性体卷材的制作工艺 Download PDF

Info

Publication number
CN101693771A
CN101693771A CN200910210037A CN200910210037A CN101693771A CN 101693771 A CN101693771 A CN 101693771A CN 200910210037 A CN200910210037 A CN 200910210037A CN 200910210037 A CN200910210037 A CN 200910210037A CN 101693771 A CN101693771 A CN 101693771A
Authority
CN
China
Prior art keywords
polyphenyl
cell
foam
urethane
polyurethane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910210037A
Other languages
English (en)
Other versions
CN101693771B (zh
Inventor
欧阳鹰湘
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009102100376A priority Critical patent/CN101693771B/zh
Publication of CN101693771A publication Critical patent/CN101693771A/zh
Application granted granted Critical
Publication of CN101693771B publication Critical patent/CN101693771B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种制作运动地面的弹性体材料的制作工艺。本发明通过在聚氨酯弹性体粘稠液体中均匀混合聚苯泡沫颗粒，然后把粘稠液态的聚氨酯聚苯泡沫混合体刮涂在流动带基上，用带基将粘稠液态的聚氨酯聚苯泡沫混合体送入低温烘道内加温，使聚氨酯液体固化。接着带基将固化的聚氨酯送入高温烘道加温。聚苯泡沫颗粒玻璃化成膜附着在闭孔泡孔孔壁上，形成闭孔泡孔。最后即制成泡孔均匀，厚度一致弹性较好的运动地面卷材。本发明的优点是：不需模具发泡，材料不易老化变质，使用寿命较长；弹性较好，工艺简单，成本较低。

Description

闭孔泡孔聚氨酯弹性体卷材的制作工艺
技术领域
本发明涉及一种运动场所运动地面的材料的制作工艺，尤其涉及一种制作运动地面的弹性体材料的制作工艺。
背景技术
为增加聚氨酯弹性体运动地面的弹性，降低成本，一般制作时在聚氨酯材料中掺发泡剂。一般来讲，泡孔越大，弹性越好。但由于是开放性泡孔，泡孔若扩大，泡孔就容易塌陷，较难成形，影响地面的平整度。所以为保证厚度一致，制作该弹性体运动地面需借助模具成型，成本较高。并且泡孔中容易进水和存水，不但影响运动员水平的发挥，而且直接影响了运动地面的使用寿命。
发明内容
本发明的目的是制作一种闭孔泡孔聚氨酯弹性体卷材的工艺，它制作的弹性体卷材弥补了以往聚氨酯弹性体运动地面因有泡孔，容易塌陷变形的缺点，并且不需模具也可以保证厚度一致。
本发明的目的是通过下述技术方案实现的：
本发明通过在聚氨酯弹性体粘稠液体中均匀混合聚苯泡沫颗粒，搅拌均匀，呈粘稠液态的聚氨酯聚苯泡沫混合体，然后把粘稠液态的聚氨酯聚苯泡沫混合体刮涂在流动带基上。用带基将粘稠液态的聚氨酯聚苯泡沫混合体送入低温烘道，在烘道内加温，聚氨酯液体固化。接着带基将固化的聚氨酯送入高温烘道加温。聚苯泡沫颗粒消失，聚苯泡沫颗粒玻璃化成膜附着在闭孔泡孔孔壁上，形成闭孔泡孔。最后从高温烘道中送出，即制成泡孔均匀，厚度一致弹性较好的运动地面卷材。
因聚苯泡沫颗粒约含自身体积60倍的气体，在80～90℃时聚苯材料溶化，原泡沫颗粒形状存在，但聚苯材料液化成膜，附着在其颗粒消失形成的孔壁上成为闭孔泡孔。
本发明聚氨酯弹性体卷材的优点是：1、不需模具发泡；2、由于在使用中闭孔不吸水，材料不易老化，变质，使用寿命较长；3、闭孔泡孔均匀，成型容易，弹性较好；4、工艺简单，容易控制，成本较低。
附图说明
图1是本发明制作工艺示意图。
图中：1、聚氨酯聚苯泡沫混合体  2、70℃烘道  3、80℃-90℃烘道  4、卷材5、刮板、6、流动带基
具体实施方式
参见图1，本发明通过在60～70℃的聚氨酯弹性体粘稠液体中均匀混合其体积30％的聚苯泡沫颗粒，聚苯泡沫颗粒粒度Φ0.5mm。搅拌均匀，呈粘稠液态的聚氨酯聚苯泡沫混合体1。然后通过刮板5将呈粘稠液态的聚氨酯聚苯泡沫混合体1刮涂在流动带基6上，聚氨酯聚苯泡沫混合体1通过刮板5刮涂的厚度为3mm～25mm。聚氨酯聚苯泡沫混合体1由带基6送入70℃低温烘道2中，在烘道2内加温40分钟，聚氨酯液体固化。接着带基6将固化的聚氨酯聚苯泡沫混合体1送入80℃-90℃高温烘道3，在烘道3中加温10分钟。聚苯泡沫颗粒消失，聚苯泡沫颗粒玻璃化成膜附着在闭孔泡孔孔壁上。因聚苯泡沫颗粒约含自身体积60倍的气体，在80～90℃时聚苯材料溶化，原泡沫颗粒形状存在，但聚苯材料液化成膜，附着在其颗粒消失形成的孔壁上。最后，即制成泡孔均匀，厚度一致为3mm～25mm弹性较好的运动地面卷材4。

Claims (5)

1.一种闭孔泡孔聚氨酯弹性体卷材的制作工艺，其步骤是：
(1)在聚氨酯弹性体粘稠液体中均匀混合聚苯泡沫颗粒，搅拌均匀，呈粘稠液态的聚氨酯聚苯泡沫混合体；
(2)把粘稠液态的聚氨酯聚苯泡沫混合体刮涂在流动带基上；
(3)用带基将粘稠液态的聚氨酯聚苯泡沫混合体送入低温烘道，在烘道内加温，带有聚苯泡沫颗粒的聚氨酯液体固化；
(4)接着带基将固化的带有聚苯泡沫颗粒的聚氨酯送入高温烘道加温，经加温聚苯泡沫颗粒消失，聚苯泡沫颗粒玻璃化成膜附着在闭孔泡孔孔壁上，形成闭孔泡孔；最后从高温烘道中送出泡孔均匀、厚度一致弹性较好的闭孔泡孔聚氨酯弹性体卷材。
2.根据权利要求1所述的制作工艺，其特征在于：步骤(1)中，在60～70℃的聚氨酯弹性体粘稠液体中均匀混合其体积30％的聚苯泡沫颗粒，聚苯泡沫颗粒粒度Φ0.5mm。
3.根据权利要求1所述的制作工艺，其特征在于：步骤(2)中，聚氨酯聚苯泡沫混合体通过刮板刮涂在带基上的厚度为3mm～25mm。
4.根据权利要求1所述的制作工艺，其特征在于：步骤(3)中，聚氨酯聚苯泡沫混合体由带基送入70℃低温烘道中，在烘道内加温40分钟，聚氨酯液体固化。
5.根据权利要求1所述的制作工艺，其特征在于：步骤(4)中，带基将固化的聚氨酯聚苯泡沫混合体送入80℃-90℃高温烘道，在烘道中加温10分钟，最后从高温烘道中送出的闭孔泡孔聚氨酯弹性体卷材的厚度为3mm～25mm。
CN2009102100376A 2009-11-04 2009-11-04 闭孔泡孔聚氨酯弹性体卷材的制作工艺 Expired - Fee Related CN101693771B (zh)