CN101684541B - 用在泵阀产品上的双相不锈钢 - Google Patents
用在泵阀产品上的双相不锈钢 Download PDFInfo
- Publication number
- CN101684541B CN101684541B CN2008101966023A CN200810196602A CN101684541B CN 101684541 B CN101684541 B CN 101684541B CN 2008101966023 A CN2008101966023 A CN 2008101966023A CN 200810196602 A CN200810196602 A CN 200810196602A CN 101684541 B CN101684541 B CN 101684541B
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- pump valve
- duplex stainless
- valve products
- equal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种耐腐蚀性强的用在泵阀产品上的双相不锈钢,其组成成分及各成分重量百分比如下:C:≤0.03%、Mn:≤1.5%、Si:≤1%、P:≤0.04%、S:≤0.02%、Cr:21~23.5%、Ni:4.5~6.5%、Mo:2.5~3.5%、Cu:≤1%、N:0.1~0.3%、余量为Fe。其优点是:这种用在泵阀产品上的双相不锈钢与Ni-Cr型奥氏体不锈钢相比具有很高的耐腐蚀性、屈服强度和耐磨性。
Description
技术领域
本发明涉及一种双相不锈钢,尤其涉及一种用在泵阀产品上的双相不锈钢。
背景技术
随着我国化学工业的迅猛发展,各种带有颗粒状的强酸介质对泵阀产品的制造材料要求越来越高,国内现有的泵阀产品的制造材料一般采用Ni-Cr型奥氏体不锈钢,由这种材料制造出来的泵阀产品很容易被各种带有颗粒状的强酸介质腐蚀,使用寿命多则1-2两个月,少则几天,需要经常对其进行维护和更换,严重影响了化工企业的正常生产。
发明内容
本发明所要解决的技术问题是:提供一种耐腐蚀性强的用在泵阀产品上的双相不锈钢。
为了解决上述技术问题,本发明的技术方案为:用在泵阀产品上的双相不锈钢,其组成成分及各成分重量百分比如下:C:≤0.03%、Mn:≤1.5%、Si:≤1%、P:≤0.04%、S:≤0.02%、Cr:21~23.5%、Ni:4.5~6.5%、Mo:2.5~3.5%、Cu:≤1%、N:0.1~0.3%、余量为Fe。
本发明的优点是:这种用在泵阀产品上的双相不锈钢与Ni-Cr型奥氏体不锈钢相比具有很高的耐腐蚀性、屈服强度和耐磨性。
具体实施方式
下面结合具体实施例详细描述一下本发明。
实施例1:
用在泵阀产品上的双相不锈钢,其组成成分及各成分重量百分比如下:C:0.03%、Mn:1.5%、Si:1%、P:0.04%、S:0.02%、Cr:23.5%、Ni:6.5%、Mo:3.5%、Cu:1%、N:0.3%、余量为Fe。
实施例2:
用在泵阀产品上的双相不锈钢,其组成成分及各成分重量百分比如下:C:0.02%、Mn:1%、Si:0.5%、P:0.02%、S:0.01%、Cr:22%、Ni:5%、Mo:3%、Cu:0.5%、N:0.2%、余量为Fe。
实施例3:
用在泵阀产品上的双相不锈钢,其组成成分及各成分重量百分比如下:C:0.03%、Mn:1.5%、Si:1%、P:0.04%、S:0.02%、Cr:21%、Ni:4.5%、Mo:2.5%、Cu:1%、N:0.1%、余量为Fe。
上述三个实施例中的用在泵阀产品上的双相不锈钢冶炼过程都是一样的,首先向冶炼炉中加入炉料,待炉料在冶炼炉中形成溶液后,向冶炼炉中加入铬、钼、镍,形成溶液后,马上加入覆盖剂造渣,渣形成之后充分搅拌,然后对钢液进行取样分析,分析结果如果发现渣太稀或太稠,则将渣扒去,重新造渣。分析结果如果发现渣符合要求,就对渣进行脱氧,使用Si-Ca粉扩散脱氧,其重量百分比为钢液的0.3~0.4%,分批加入,每5~10分钟加入一次,加入时要将其散在渣面上,钢液的温度要保持在1550℃~1580℃。对钢液取样进行成分分析,根据成分分析结果加入适量的Si-Fe、Mn-Fe,加大功率升温,同时加入Si-Ca粉扩散脱氧,当温度到达1600℃~1620℃时,渣呈灰白色或咖啡色取样,浇收缩杯,如浇收缩杯试棒收缩良好,温度大于1600℃,立即加入氮元素准备出钢,将已经准备好的Si-Ca放在包底,沉淀终脱氧,进行浇注,得到所需的坯料。
这种用在泵阀产品上的双相不锈钢是一种碳的含量较低、铬的含量较高、镍的含量不高的合金材料,经固溶处理后,其基体组织为铁素体和奥氏体共存的复相钢,与Ni-Cr型奥氏体不锈钢相比具有很高的耐腐蚀性、屈服强度和耐磨性。
Claims (1)
1.用在泵阀产品上的双相不锈钢,其特征在于:其组成成分及各成分重量百分比如下:C:≤0.03%、Mn:≤1.5%、Si:≤1%、P:≤0.04%、S:≤0.02%、Cr:21~22 %、Ni:4.5~6.5%、Mo:2.5~3.5%、Cu:≤1%、N:0.1~0.3%、余量为Fe。