CN101659821A - Aqueous wooden ware sprinkling paint - Google Patents
Aqueous wooden ware sprinkling paint Download PDFInfo
- Publication number
- CN101659821A CN101659821A CN200810142154A CN200810142154A CN101659821A CN 101659821 A CN101659821 A CN 101659821A CN 200810142154 A CN200810142154 A CN 200810142154A CN 200810142154 A CN200810142154 A CN 200810142154A CN 101659821 A CN101659821 A CN 101659821A
- Authority
- CN
- China
- Prior art keywords
- paint
- wooden ware
- aqueous wooden
- sprinkling
- thickening material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an aqueous wooden ware sprinkling paint. The paint mainly comprises the following components in portion by weight: 8 to 10 portions of water, 2 to 4 portions of film-forming assistant, 0.2 to 0.4 portion of wetting and dispersing agent, 0.4 to 0.8 portion of antifoaming agent, 50 to 60 portions of filler, 10 to 30 portions of acrylic emulsion, and 1 to 1.5 portions of thickening agent. The invention also discloses a preparation method for the aqueous wooden ware sprinkling paint. The aqueous wooden ware sprinkling paint has natural shape, strong texture, smoothness andhigh dryness; a finishing paint can be brushed for 60 minutes at the normal temperature of 25 DEG C; the finishing paint can adopt the double-component aqueous wooden ware paint; and after being dried for 12 hours, the finishing paint has ultrahigh hardness and excellent scratch resistance, is environment-friendly and safe, and is suitable for coating large-scale stage sound boxes and musical instruments.
Description
Technical field
The present invention relates to the wood lacquer field, relate in particular to a kind of water-based sprinkling paint of on woodenware audio amplifier, musical instrument, using.
Background technology
Be used for traditionally the application of wooden acoustic box, musical instrument many with the paint that contains a large amount of organic solvents such as benzene,toluene,xylene as coating, the drawback of using such coating clearly, that is: serious environment pollution, factory's operating environment is brought pollution, endangered the healthy of operator, therefore, such oil paint is limited to use just gradually.
So, the water-borne coatings that does not contain poisonous hazardous solvent is by a large amount of Application and Development, aqueous woodware paint in the market is many to be base-material with common emulsion, exist rate of drying slow, the shortcoming that hardness of paint film is low, as application number be: 200510136722.0, denomination of invention is: a kind of patent of invention of compound aqueous environment protection paint, disclose a kind of compound aqueous environment protection paint, it is characterized in that by seed emulsion, defoamer, wetting agent, dispersion agent, titanium dioxide, ferrotitanium is white, zinc phosphate, aluminium triphosphate, talcum powder, emulsion, film coalescence aid, neutralizing agent, anti-sudden strain of a muscle erosion agent and water are mixed with, and the weight percent of its component is: seed emulsion 50-60%, defoamer 0.2-0.5%, wetting agent 0.1-0.2%, dispersion agent 0.3-0.5%, titanium dioxide 5-8%, the white 10-15% of ferrotitanium, zinc phosphate 8-10%, aluminium triphosphate 8-10%, talcum powder 3-5%, film coalescence aid 2.5-3%, neutralizing agent 0.05-0.1%, the anti-erosion agent 0.1-0.2% that dodges, water 8-10%; Though the water-miscible paint of this invention has toxicological harmless, non-environmental-pollution, has no irritating odor, do not burn, and is easy to use, the characteristics of the level and smooth light of paint film, but still have the problem that rate of drying is slow, hardness is not enough, sticking power is not high enough.
Summary of the invention
Technical problem to be solved by this invention overcomes the deficiencies in the prior art exactly, provides that a kind of that use, moulding nature, texture are strong on woodenware audio amplifier, musical instrument, the water-based sprinkling paint of slyness and fast drying, hardness of paint film height, strong adhesion.
For solving the problems of the technologies described above, the technical measures that we take are:
The aqueous wooden ware sprinkling paint that the present invention relates to is characterized in that: this lacquer mainly is made of the component of following weight part: water 8-10 part, film coalescence aid 2-4 part, wetting dispersing agent 0.2-0.4 part, defoamer 0.4-0.8 part, filler 50-60 part, acrylic acid emulsion 10-30 part, thickening material 1-1.5 part.
The composition of described film coalescence aid and weight proportion are:
Alcohol ester-12 20%
Dipropylene glycol butyl ether 35%
Ethylene glycol monobutyl ether 45%.
Described wetting dispersing agent is the poly carboxylic acid amine salt, and the trade mark of selecting for use Rhom and Hass to produce is the product of OROTAN1124.
Described defoamer is a polysiloxane thick-slurry type product, and the trade mark of selecting for use Japanese Nuo Puke company to produce is the product of SN-345.
Described defoamer is a polysiloxane thick-slurry type product, and the trade mark that can adopt Japanese Nuo Puke company to produce is the product of SN-345.
The component of described filler and weight proportion are:
600 order silica powders 50%
1000 order lime carbonate 35%
1000 order talcum powder 15%.
The component of described thickening material and weight proportion are:
The low alkali swelling type thickening material 70% of shearing
The middle alkali swelling type thickening material 20% of shearing
Polyurethane associative thickener 10%.
The preparation method of the aqueous wooden ware sprinkling paint that the present invention relates to is characterized in that: this method comprises following processing step:
A. according to formula ratio, get the water of 3/5 amount, add in the ingredients pot, begin to stir with the rotating speed of 500-700rpm;
B. according to formula ratio, add film coalescence aid, wetting dispersing agent, defoamer, thickening material successively, after waiting to stir, add filler again: 600 order silica powders, 1000 order lime carbonate, 1000 order talcum powder, mixing speed is transferred to more than the 1200rpm, high speed dispersion formed even mill base more than 25 minutes;
C. the mill base that stirs is ground, until particle diameter≤35 μ m;
D. then ground mill base is changed in another ingredients pot, stirring at low speed is to even, add the acrylic acid emulsion of formula ratio and the water of remaining 2/5 formula ratio successively, stir more than at least 20 minutes, survey initial viscosity, according to measured initial viscosity, add the thickening material of formula ratio, 3500-4500mpas under viscosity to the 25 ℃ condition of adjusting slip.
Compared with prior art, water-based sprinkling paint of the present invention, have following superior technique effect: moulding nature, strong, slick and sly, the fast drying of texture, in normal temperature 25 degree down, can rinse overpainting in 60 minutes, finish paint can adopt aqueous wood lacquer with double components, behind dry 12 hours of the finish paint, hardness extra-high-speed, anti-scratch excellent performance, Environmental Safety is suitable for the application of large-scale stage audio amplifier, musical instrument.
Embodiment:
Below by describing technical solution of the present invention in conjunction with the embodiments in detail:
Raw material and the auxiliary agent that the present invention relates to specifically comprise:
The component of said film coalescence aid and weight proportion are:
Alcohol ester-12 (CS-12) 20%
Dipropylene glycol butyl ether (DPnB) 35%
Ethylene glycol monobutyl ether (BCS) 45%
Alcohol ester-12 (CS-12) is 2,2,4-trimethylammonium-1,3 pentanediol isobutyrate, and the trade mark that can adopt Yi Shi Man to produce is the product of TEXANOL.
The trade mark that the dipropylene glycol butyl ether can adopt DOW company to produce is the product of DPnB.
Ethylene glycol monobutyl ether can adopt local self-made products.
Said wetting dispersing agent is the poly carboxylic acid amine salt, and the trade mark that can adopt Rhom and Hass to produce is the product of OROTAN 1124.
Said defoamer is a polysiloxane thick-slurry type product, and the trade mark that can adopt Japanese Nuo Puke company to produce is the product of SN-345.
The component of said filler and weight proportion are:
600 order silica powders 50%
1000 order lime carbonate 35%
1000 order talcum powder 15%
Said 600 order silica powders, 1000 order lime carbonate, 1000 order talcum powder are the general industry product, and local bid in gets final product.
The trade mark that said ACRYLIC EMULSION can adopt U.S. Rhom and Hass to produce is the product of EP-6060.
The component of said thickening material and weight proportion are:
The low alkali swelling type thickening material 70% of shearing
The middle alkali swelling type thickening material 20% of shearing
Polyurethane associative thickener 10%
Low shearing alkali swelling type thickening material is an acrylate copolymer, and the trade mark that can adopt Rhom and Hass to produce is the product of ASE-60.
Middle shearing alkali swelling type thickening material is an acrylate copolymer, and the trade mark that can adopt Rhom and Hass to produce is the product of TT-935.
The trade mark that polyurethane associative thickener can adopt Rhom and Hass to produce is the product of SCT-275.
Embodiment 1:
Prescription: 10 parts in water, 3 parts of film coalescence aid, 0.4 part of wetting dispersing agent, 0.4 part of defoamer, 50 parts of fillers, 10 parts of acrylic acid emulsions, 1.5 parts of thickening materials.
Step of preparation process:
A. according to formula ratio, get the water of 3/5 amount, add in the ingredients pot, begin to stir with the rotating speed of 500-700rpm;
B. according to formula ratio, add film coalescence aid, wetting dispersing agent, defoamer, thickening material successively, after waiting to stir, add filler again: 600 order silica powders, 1000 order lime carbonate, 1000 order talcum powder, mixing speed is transferred to more than the 1200rpm, high speed dispersion formed even mill base more than 25 minutes;
C. the mill base that stirs is ground, until particle diameter≤35 μ m;
D. then ground mill base is changed in another ingredients pot, stirring at low speed is to even, add the acrylic acid emulsion of formula ratio and the water of remaining 2/5 formula ratio successively, stir more than at least 20 minutes, survey initial viscosity, according to measured initial viscosity, add the thickening material of formula ratio, 3500-4500mpas under viscosity to the 25 ℃ condition of adjusting slip.
Embodiment 2:
Prescription: 9 parts in water, 2 parts of film coalescence aid, 0.2 part of wetting dispersing agent, 0.8 part of defoamer, 60 parts of fillers, 30 parts of acrylic acid emulsions, 1 part of thickening material.
Preparation method: with embodiment 1.
Embodiment 3:
Prescription: 8 parts in water, 4 parts of film coalescence aid, 0.3 part of wetting dispersing agent, 0.6 part of defoamer, 56 parts of fillers, 20 parts of acrylic acid emulsions, 1.3 parts of thickening materials.
Preparation method: with embodiment 1.
Claims (8)
1, a kind of aqueous wooden ware sprinkling paint is characterized in that: this lacquer mainly is made of the component of following weight part: water 8-10 part, film coalescence aid 2-4 part, wetting dispersing agent 0.2-0.4 part, defoamer 0.4-0.8 part, filler 50-60 part, acrylic acid emulsion 10-30 part, thickening material 1-1.5 part.
2, aqueous wooden ware sprinkling paint as claimed in claim 1 is characterized in that: the composition of described film coalescence aid and weight proportion are:
Alcohol ester-12 20%
Dipropylene glycol butyl ether 35%
Ethylene glycol monobutyl ether 45%.
3, aqueous wooden ware sprinkling paint as claimed in claim 1 is characterized in that: described wetting dispersing agent is the poly carboxylic acid amine salt, and the trade mark of selecting for use Rhom and Hass to produce is the product of OROTAN 1124.
4, aqueous wooden ware sprinkling paint as claimed in claim 1 is characterized in that: described defoamer is a polysiloxane thick-slurry type product, and the trade mark of selecting for use Japanese Nuo Puke company to produce is the product of SN-345.
5, aqueous wooden ware sprinkling paint as claimed in claim 1 is characterized in that: described defoamer is a polysiloxane thick-slurry type product, and the trade mark that can adopt Japanese Nuo Puke company to produce is the product of SN-345.
6, aqueous wooden ware sprinkling paint as claimed in claim 1 is characterized in that: the component of described filler and weight proportion are:
600 order silica powders 50%
1000 order lime carbonate 35%
1000 order talcum powder 15%.
7, aqueous wooden ware sprinkling paint as claimed in claim 1 is characterized in that: the component of described thickening material and weight proportion are:
The low alkali swelling type thickening material 70% of shearing
The middle alkali swelling type thickening material 20% of shearing
Polyurethane associative thickener 10%.
8, a kind of preparation method of aqueous wooden ware sprinkling paint is characterized in that: this method comprises following processing step:
A. according to formula ratio, get the water of 3/5 amount, add in the ingredients pot, begin to stir with the rotating speed of 500-700rpm;
B. according to formula ratio, add film coalescence aid, wetting dispersing agent, defoamer, thickening material successively, after waiting to stir, add filler again: 600 order silica powders, 1000 order lime carbonate, 1000 order talcum powder, mixing speed is transferred to more than the 1200rpm, high speed dispersion formed even mill base more than 25 minutes;
C. the mill base that stirs is ground, until particle diameter≤35 μ m;
D. then ground mill base is changed in another ingredients pot, stirring at low speed is to even, add the acrylic acid emulsion of formula ratio and the water of remaining 2/5 formula ratio successively, stir more than at least 20 minutes, survey initial viscosity,, add the thickening material of formula ratio according to measured initial viscosity, the viscosity of regulating slip to 3500-4500mpas (25 ℃, 6#/60r).