CN101659558A - 500kg-class energy-saving heat insulation lining material and preparation method thereof - Google Patents
500kg-class energy-saving heat insulation lining material and preparation method thereof Download PDFInfo
- Publication number
- CN101659558A CN101659558A CN200910090389A CN200910090389A CN101659558A CN 101659558 A CN101659558 A CN 101659558A CN 200910090389 A CN200910090389 A CN 200910090389A CN 200910090389 A CN200910090389 A CN 200910090389A CN 101659558 A CN101659558 A CN 101659558A
- Authority
- CN
- China
- Prior art keywords
- energy
- lining material
- preparation
- heat insulation
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the field of refractory material, and relates to a 500kg-class energy-saving heat insulation lining material and a preparation method thereof which are widely applied to various heat engineering kiln industries. The lining material is prepared by adding water reducing agent and dispersing agent into the mixture of expanded perlite with different grain size distribution, diatomite, Hongshan soil and pure calcium aluminate cement. Compared with the common light heat insulation lining material, the energy-saving lining material prepared by the invention has the characteristics of high strength, low heat conduction rate, good heat insulation effect and long service cycle; furthermore, the energy-saving heat insulation lining material has the volume density of 500 plusor minus 30kg/m<3> at the normal temperature, and has important significance for energy conservation and emission reduction as well as reducing the running cost of heat engineering kilns.
Description
Technical field
The invention belongs to fire resisting material field, relate to a kind of energy-saving heat-insulating lining material and preparation method thereof, be widely used in each thermal kiln furnace industry.
Background technology
Energy shortage is the reality of the world today, and save energy is the important tasks in various countries, and under this form, energy-saving lining is mathematical to the importance of modern industry kiln.Traditional Industrial Stoves are the purpose that reaches heat preservation energy-saving, usually in heavy refractory brick is built body or heavy unshape refractory construction body by laying bricks or stones or outside increase thermal insulation layer, but the heavy layer has strengthened bulky kiln to bear a heavy burden, and for batch furnace, the accumulation of heat loss is big especially.
Summary of the invention
The objective of the invention is concrete working condition, provide a kind of volume density at 500 ± 30kg/m at various thermal kiln furnaces
3In the scope, thermal conductivity is low, intensity is high, the insulated lining material of high insulating effect.
Energy-conservation lining is meant and does not readily conduct heat, hot-fluid is had the single-material or the matrix material of remarkable impedance behavior.The characteristics that energy-conservation lining possesses are: volume density is little; Thermal conductivity is low; Furnace lining intensity height increases than ceramic fiber material on resistance to compression and anti-airflow scouring ability; Constructional method can adopt and smear, pouring type, and is convenient and swift and pollution-free.Applicable Thermal Equipment of energy-conservation lining and occasion are:
*The various Fuel Furnace furnace linings (furnace wall and furnace roof) of working temperature≤1250 ℃;
*The backing thermal insulation layer (furnace wall and furnace roof) of various High-temp. kiln interface temperatures≤1050 ℃;
*Industrial Boiler furnace roof lining;
*The resistance furnace lining of working temperature≤1200 ℃;
A kind of 500kg class energy-saving heat insulation lining material and preparation method thereof, it is characterized in that at first carrying out the starting material apolegamy, adopting perlite is aggregate, with big vast mountain soil, diatomite and pure calcium aluminate cement is that matrix is formed, and adds tripoly phosphate sodium STPP, Sodium hexametaphosphate 99 in addition as water reducer and dispersion agent on the matrix material basis.
Its matrix material is pressed the preparation of column weight amount per-cent:
Perlite (0.3-0.6mm) 45-55%
Flood mountain soil 5-15%
Diatomite 3-10%
Pure calcium aluminate cement 30-37%
The add-on weight percent of tripoly phosphate sodium STPP, Sodium hexametaphosphate 99 is
Tripoly phosphate sodium STPP 0.1-0.2%
Sodium hexametaphosphate 99 0.02-0.06%
After raw material was selected, its preparation technology was: earlier pure calcium aluminate cement and tripoly phosphate sodium STPP, Sodium hexametaphosphate 99 are put into the twin-shaft mixer pre-mixing and evenly make premix, be packaged into pouch afterwards; After in mixer, perlite, big vast mountain soil, diatomite being mixed then, the sack of packing into; At last pouch is put into and promptly finished after sack seals.In the job location, will put in order bag material, comprise the premix in the pouch, all put into forced stirrer, pre-mixing once more adds water and stirred 3～5 minutes after mixing, and to pour mould into be position to be cast to the material that will stir afterwards, or directly smear construction.After the natural curing 48 hours, can carry out baking processing.
Energy-conservation lining by the inventive method preparation is compared with traditional lightweight heat-proof lining material, and its excellent performance mainly shows on the thermal conductivity.
The thermal conductivity of energy-conservation lining is lower, according to refractory materials thermal conductivity test method (discharge flat band method) YB/4130-2005, recording energy-conservation lining is 0.10W/ (mK) 350 ℃ thermal conductivity, and common lightweight heat-proof lining 350 ℃ thermal conductivity more than 0.15W/ (mK).Energy-conservation like this lining just has better heat insulating effect, and more effective cutting down the consumption of energy saved a large amount of energy.
Embodiment:
Realize that concrete mode of the present invention is:
Prescription one:
Perlite (0.3-0.6mm) 45%
Flood mountain soil 15%
Diatomite 3%
Pure calcium aluminate cement 37%
Tripoly phosphate sodium STPP 0.2%
Sodium hexametaphosphate 99 0.06%
Prescription two:
Perlite (0.3-0.6mm) 50%
Flood mountain soil 10%
Diatomite 5%
Pure calcium aluminate cement 35%
Tripoly phosphate sodium STPP 0.15%
Sodium hexametaphosphate 99 0.04%
Prescription three:
Perlite (0.3-0.6mm) 55%
Flood mountain soil 5%
Diatomite 10%
Pure calcium aluminate cement 30%
Tripoly phosphate sodium STPP 0.1%
Sodium hexametaphosphate 99 0.02%
Earlier pure calcium aluminate cement and tripoly phosphate sodium STPP, Sodium hexametaphosphate 99 are put into the twin-shaft mixer pre-mixing and evenly make premix, be packaged into pouch afterwards; After in mixer, diatomite, perlite, big vast mountain soil being mixed then, the sack of packing into; At last pouch is put into and promptly finished after sack seals.
Performance index according to the energy-conservation lining of the present invention preparation see the following form 1:
Table 1
Claims (1)
1, a kind of 500kg class energy-saving heat insulation lining material and preparation method thereof, it is characterized in that: the perlite that adopts the different grain size grating is formed as matrix, and is added tripoly phosphate sodium STPP, Sodium hexametaphosphate 99 in addition as water reducer and dispersion agent on the matrix material basis as aggregate and diatomite, big vast mountain soil, pure calcium aluminate cement;
Its matrix material is pressed the preparation of column weight amount per-cent:
Perlite, granularity are 0.3-0.6mm 45-55%
Flood mountain soil 5-15%
Diatomite 3-10%
Pure calcium aluminate cement 30-37%
The add-on weight percent of tripoly phosphate sodium STPP, Sodium hexametaphosphate 99 is:
Tripoly phosphate sodium STPP 0.1-0.2%
Sodium hexametaphosphate 99 0.02-0.06%
Preparation process is: be packaged into pouch after earlier premix A evenly being made in pure calcium aluminate cement and tripoly phosphate sodium STPP, Sodium hexametaphosphate 99 pre-mixing; After in mixer, perlite, diatomite, big vast mountain soil and Preblend A being mixed then, the sack of packing into; At last pouch is put into and promptly finished after sack seals; In the job location, will put in order bag material, comprise the premix in the pouch, all put into forced stirrer, pre-mixing once more adds water and stirred 3～5 minutes after mixing, and to pour mould into be position to be cast to the material that will stir afterwards; Or directly smear construction, natural curing is carried out the preparation that baking processing is finished energy-conservation lining after 48 hours again.