CN101654866A - Method for improving odor of dry or wet fibrilia - Google Patents
Method for improving odor of dry or wet fibrilia Download PDFInfo
- Publication number
- CN101654866A CN101654866A CN200910182959A CN200910182959A CN101654866A CN 101654866 A CN101654866 A CN 101654866A CN 200910182959 A CN200910182959 A CN 200910182959A CN 200910182959 A CN200910182959 A CN 200910182959A CN 101654866 A CN101654866 A CN 101654866A
- Authority
- CN
- China
- Prior art keywords
- fibrilia
- odor
- wet
- dry
- test
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method for improving the odor of dry or wet fibrilia, in particular for increasing the odor property and the anti-mildew property of a raw material of dry or wet fibrilia for an interior decoration part of a motorcar. The method is characterized by adopting the following process sequences: taking fibrilia and mandarin oil as raw materials; uniformly spraying the mandarinoil on the fibrilia; after the fibrilia on which the mandarin oil is sprayed is placed at the temperature ranging from 21 to 25 DEG C and the humidity ranging from 60 to 70 percent, carrying out an odor test; and putting the fibrilia on which the odor test is carried out in opened glass ware, and assessing the odor of the fibrilia again 15 days later. The method is simple and needs low cost, however, the improved effect is considerably obvious; the method not only can increase the favorable odor of the dry fibrilia, but also can completely improve the annoying odor of the wet fibrilia and also enhance the anti-mildew property of the wet fibrilia; and the improved effect can be maintained for a long time.
Description
Technical field
The present invention relates to a kind of method of improving odor of dry or wet fibrilia, is exactly to improve odor property and the anti-mildew sex change energy of automotive upholstery raw material flax fibre under dried hygrometric state specifically.
Background technology
Development along with auto manufacturing technology, automobile industry is more and more higher to the requirement of automotive upholstery,, the environmental protection attractive in appearance except requiring, also require low cost, light weight, intensity height, recyclable utilization and biodegradable, have an acoustical behavior preferably simultaneously, to improve automobile making economy and user's comfort, so increasing natural fabric reinforced composite is used in the automotive upholstery.
The automotive upholstery that flax fibre is made can satisfy biodegradability can satisfy lightweight requirements again, helps the sustainable development of environment.But find that in actual use the inside gadget of being made by flax fibre is too heavy with the smell of sheet material, test result can not satisfy customer requirement, and the source of its smell mainly is a flax fibre, and especially after flax fibre made moist, smell was just more pungent.
At present also do not specialize in the method for improving the flax fibre smell, under the situation that smell is had strict demand, mainly meet the demands, but its cost also increases much thereupon by the processing technology of adjusting flax fibre.
Summary of the invention
The objective of the invention is to overcome above-mentioned weak point, thereby provide a kind of method of improving the flax fibre odor properties by tangerine oil, it can not only improve the smelling good of dry state fibrilia smell, and can improve the wet fibrilia odour nuisance fully, can strengthen the method for improving odor of dry or wet fibrilia of anti-mildew sex change under the flax fibre hygrometric state simultaneously again.
According to technical scheme provided by the invention, a kind of method of improving odor of dry or wet fibrilia, adopt following processing step: its component proportioning is counted by weight:
Get 100 parts of flax fibres, 3～7 parts of tangerine oils; Be sprayed at tangerine oil on the flax fibre uniformly; Spraying distance is 5～10cm, is 21～25 ℃ with the flax fibre that is sprayed with tangerine oil in temperature, and humidity is to place the test of the laggard promoting the circulation of qi flavor of 12～24h under 60～70% conditions; The flax fibre of testing is placed in the unlimited glassware, estimates its smell once more after 15 days.
Described flax fibre refers to natural unprocessed linen fibre, tossa or hemp.
Compared with the prior art the present invention has the following advantages:
The inventive method is simple and with low cost, but it improves the effect highly significant, can not only improve the smelling good of dry state fibrilia smell, and can improve the wet fibrilia odour nuisance fully, can strengthen simultaneously the anti-mildew sex change under the flax fibre hygrometric state again, improving effect can keep for a long time.
The specific embodiment
The Henan, the flax fibre place of production of using in the test, the sincere fiber crops industry in effluent south provides, and flax fibre is the natural fiber crops semi-finished product through degreasing combing two procedures.
Following the present invention will be further described in conjunction with the embodiments:
Embodiment one: a kind of method of improving dry state and wet fibrilia smell of the present invention, and adopt following processing step: its component proportioning is counted by weight:
The present invention is sprayed at the tangerine oil of 3 parts of weight with sprayer on the linen fibre of 100 parts of weight (preparing 2 parts) uniformly; Spraying distance is 5cm, then the flax fibre that is sprayed with tangerine oil is kept in the open glass vessel, is placed under the standard environment condition of 21 ℃ of temperature, humidity 60% and places 12h.
The test of dry state smell:
A copy of it of above pretreated sample is placed in the ground glass stoppered bottle of band ground lid, the volume ratio of sample and vial is 1: 20, sample hangs in the vial by U.S.'s AE line, at the bottom of not contacting bottle, the lid lid is tightly prevented gas leakage, again the vial that sample is housed is placed on temperature control precision in ± 2 ℃ the ventilation baking oven, oven temperature is set to (+70 ± 2) ℃, keeps 24
+ 0 -2From baking oven, take out vial after hour, wait be cooled to indoor temperature after, lid is opened a part passes judgment on experts by 5 smells and pass judgment on according to the grade of subordinate list 1, test result is 5 grades.Test the back and evaluate smell according to the preceding preservation condition preservation of test once more after 15 days, the result is 6 grades.
The test of hygrometric state smell:
Wherein another part of above pretreated sample is placed in the ground glass stoppered bottle of band ground lid, the volume ratio of sample and vial is 1: 20, place the distilled water of 1/5 volume in the bottle, sample hangs in the vial by U.S.'s AE line, at the bottom of not contacting bottle and distilled water, the lid lid is tightly prevented gas leakage, again the vial that sample is housed is placed on temperature control precision in ± 2 ℃ the ventilation baking oven, oven temperature is set to (+70 ± 2) ℃, keeps 24
+ 0 -2From baking oven, take out vial after hour, wait be cooled to indoor temperature after, lid is opened a part passes judgment on experts by 5 smells and pass judgment on according to the grade of subordinate list 1, test result is 5 grades.Test the back and evaluate smell according to the preceding preservation condition preservation of test once more after 15 days, the result is 5 grades and does not go mouldy.
Embodiment 2: a kind of method of improving dry state and wet fibrilia smell of the present invention, and adopt following processing step: its component proportioning is counted by weight:
The present invention is sprayed at the tangerine oil of 5 parts of weight with sprayer on the flax fibre of 100 parts of weight (preparing 2 parts) uniformly, spraying distance is 7.5cm, the flax fibre that is sprayed with tangerine oil is kept at is placed on 23 ℃ of temperature in the open glass vessel, place 18h under the standard state humidity 65% standard environment condition.
The test of dry state smell:
A copy of it of above pretreated sample is placed in the ground glass stoppered bottle of band ground lid, the volume ratio of sample and vial is 1: 20, sample hangs in the vial by U.S.'s AE line, at the bottom of not contacting bottle, the lid lid is tightly prevented gas leakage, again the vial that sample is housed is placed on temperature control precision in ± 2 ℃ the ventilation baking oven, oven temperature is set to (+70 ± 2) ℃, keeps 24
+ 0 -2From baking oven, take out vial after hour, wait be cooled to indoor temperature after, lid is opened a part passes judgment on experts by 5 smells and pass judgment on according to the grade of subordinate list 1, test result is 6 grades.Test the back and evaluate smell according to the preceding preservation condition preservation of test once more after 15 days, the result is 7 grades.
The test of hygrometric state smell:
Wherein another part of above pretreated sample is placed in the ground glass stoppered bottle of band ground lid, the volume ratio of sample and vial is 1: 20, place the distilled water of 1/5 volume in the bottle, sample hangs in the vial by U.S.'s AE line, at the bottom of not contacting bottle and distilled water, the lid lid is tightly prevented gas leakage, again the vial that sample is housed is placed on temperature control precision in ± 2 ℃ the ventilation baking oven, oven temperature is set to (+70 ± 2) ℃, keeps 24
+ 0 -2From baking oven, take out vial after hour, wait be cooled to indoor temperature after, lid is opened a part passes judgment on experts by 5 smells and pass judgment on according to the grade of subordinate list 1, test result is 7 grades.Test the back and evaluate smell according to the preceding preservation condition preservation of test once more after 15 days, the result is 8 grades and does not go mouldy.
Embodiment 3: a kind of method of improving dry state and wet fibrilia smell of the present invention, and adopt following processing step: its component proportioning is counted by weight:
The present invention is sprayed at the tangerine oil of 7 parts of weight with sprayer on the flax fibre of 100 parts of weight (preparing 2 parts) uniformly, spraying distance is 10cm, the flax fibre that is sprayed with tangerine oil is kept at is placed on 25 ℃ of temperature in the open glass vessel, place 24h under the humidity 70% standard environment condition.
The test of dry state smell:
A copy of it of above pretreated sample is placed in the ground glass stoppered bottle of band ground lid, the volume ratio of sample and vial is 1: 20, sample hangs in the vial by U.S.'s AE line, at the bottom of not contacting bottle, the lid lid is tightly prevented gas leakage, again the vial that sample is housed is placed on temperature control precision in ± 2 ℃ the ventilation baking oven, oven temperature is set to (+70 ± 2) ℃, keeps 24
+ 0 -2From baking oven, take out vial after hour, wait be cooled to indoor temperature after, lid is opened a part passes judgment on experts by 5 smells and pass judgment on according to the grade of subordinate list 1, test result is 5 grades.Test and evaluate smell once more after 15d is preserved according to the preceding preservation condition of test in the back, the result is 6 grades.
The test of hygrometric state smell:
Wherein another part of above pretreated sample is placed in the ground glass stoppered bottle of band ground lid, the volume ratio of sample and vial is 1: 20, place the distilled water of 1/5 volume in the bottle, sample hangs in the vial by U.S.'s AE line, at the bottom of not contacting bottle and distilled water, the lid lid is tightly prevented gas leakage, again the vial that sample is housed is placed on temperature control precision in ± 2 ℃ the ventilation baking oven, oven temperature is set to (+70 ± 2) ℃, keeps 24
+ 0 -2From baking oven, take out vial after hour, wait be cooled to indoor temperature after, lid is opened a part passes judgment on experts by 5 smells and pass judgment on according to the grade of subordinate list 1, test result is 6 grades.Test the back and evaluate smell according to the preceding preservation condition preservation of test once more after 15 days, the result is 7 grades and does not go mouldy.
Comparative Examples 1: the present invention is kept at the flax fibre of 100 parts of weight and is placed on 23 ℃ of temperature in the open glass bottle, and 18h under the standard environment condition of humidity 65% carries out the smell test according to above-mentioned dry state smell method of testing afterwards, and test result is 5 grades.Test the back and evaluate smell according to the preceding preservation condition preservation of test once more after 15 days, the result is 5 grades.
Comparative Examples 2: the present invention is kept at the flax fibre of 100 parts of weight and is placed on 23 ℃ of temperature in the open glass bottle, and 18h under the standard environment condition of humidity 65% carries out the smell test according to above-mentioned hygrometric state smell method of testing afterwards, and test result is 2 grades.Test the back and evaluate smell according to the preceding preservation condition preservation of test once more after 15 days, the result is 2 grades, and overgrows with black points.
Remarks: estimate rank and see attached list 1.
Subordinate list 1
| ??10 | Odorlessness |
| ??9 | |
| ??8 | Can feel smell a little |
| ??7 | |
| ??6 | Can stand |
| ??5 | |
| ??4 | Horrible |
| ??3 | |
| ??2 | Acutely |
| ??1 | Can not stand |
Claims (2)
1, a kind of method of improving odor of dry or wet fibrilia is characterized in that: adopt following processing step: its component proportioning is counted by weight:
Get 100 parts of flax fibres, 3～7 parts of tangerine oils; Be sprayed at tangerine oil on the flax fibre uniformly; Spraying distance is 5～10cm, is 21～25 ℃ with the flax fibre that is sprayed with tangerine oil in temperature, and humidity is to place the test of the laggard promoting the circulation of qi flavor of 12～24h under 60～70% conditions; The flax fibre that smell was tested is placed in the unlimited glassware then, estimates its smell once more after 15 days.
2, a kind of method of improving odor of dry or wet fibrilia according to claim 1 is characterized in that described flax fibre refers to natural unprocessed linen fibre, tossa or hemp.