CN101650542B - Developing magnetic roller recycling method - Google Patents
Developing magnetic roller recycling method Download PDFInfo
- Publication number
- CN101650542B CN101650542B CN2009100188202A CN200910018820A CN101650542B CN 101650542 B CN101650542 B CN 101650542B CN 2009100188202 A CN2009100188202 A CN 2009100188202A CN 200910018820 A CN200910018820 A CN 200910018820A CN 101650542 B CN101650542 B CN 101650542B
- Authority
- CN
- China
- Prior art keywords
- magnetic roller
- coating
- recoat
- surface coating
- blasting treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a regeneration method of waste magnetic roller of laser consumable jump type developing. The method comprises the following steps: removing the aging on the surface coating; carrying out sandblasted treatment on the appearance of the coating by an automatic sandblasting machine; completely removing the coating to expose the aluminium base of the magnetic roller; and then coating a coating of graphite-material coating liquid; finally carrying out sandblasted treatment on the coating of the surface of the magnetic roller. The method has the advantages of simple structure and good effect, and saves resources and reduces cost.
Description
Technical field
The present invention relates to a kind of method that makes the regeneration of waste and old laser consumable jump type magnetic roller.
Background technology
Magnetic roller in the toner cartridge is after the life-span of prining through one or several cycle, its surperficial coating can attenuation, roughness diminishes or because of causing magnetic roller surface coating to wear out with the carbon dust Long contact time, not only pollute the environment and directly the magnetic roller is done to discard, and cause the waste of resource, thereby need carry out regeneration to this waste magnetic roller.Existing way is that magnetic roller surface is carried out being used for producing after the blasting treatment, but the coating on magnetic roller surface can diminish at thickness after sandblast, can't guarantee print quality.
Summary of the invention
Because the aluminium base part of magnetic roller inside in use is can not be affected, principle according to jump type developing, with changing the thickness and the roughness on magnetic roller surface, make surface thickness consistent with finished product magnetic roller with roughness, so just can recover the original function of magnetic roller.
Further specify this method below with reference to the accompanying drawings:
Description of drawings:
Accompanying drawing is the technological process of developing magnetic roll regeneration method:
As shown in drawings, laser consumable jump type developing magnetic roller regeneration method step is as follows:
The first step: the cleaning of magnetic roller surface coating.Removal to magnetic roller surface coating, its method is to carry out the sandblast of outward appearance coating with automatic sand-blasting machine (the employed model of present technique is the YDX-09A type) (parameter is air pressure 0.4kap, the sand grains net is 180 orders, and sand grains is the diamond material) handle, expose the aluminium base of magnetic roller;
Second step: magnetic roller surface recoat.Aluminium base being placed on the automatic recoat machine of filling the graphite material masking liquid of magnetic roller carried out recoat to the magnetic roller, it is 25-40 μ m that machine is adjusted the thickness that the position makes coating, divide and be sprayed into for 3 times, it is that 50 ℃, humidity are to toast in 0% the environmental test chamber that every spray once is placed on the magnetic roller temperature, spray after the baking of surperficial masking liquid done next time, require the surface coating uniformity;
The 3rd step: magnetic roller blasting treatment.Magnetic roller surface coating behind the recoat is carried out blasting treatment, and the automatic sand-blasting machine device parameter is air pressure 0.14kap, and the sand grains net is 240 orders, and sand grains is the diamond material, and the magnetic roller surface coating parameter after its sandblast is between the Rz1.2-1.8;
The 4th step: packing.Leave the magnetic roller of institute's recoat blasting treatment the poly-bag of sealing in.
During concrete enforcement, according to the above-mentioned steps operation, the contrast of the magnetic roller of acquisition and finished product magnetic roller is as follows:
This shows, approaching on the quality of prining by magnetic roller and normal magnetic flux roller that this technology is handled, present technique with the HP1010 printer corresponding laser consumable model be HP2612 the magnetic roller is that example compares, the result is close with the normal magnetic flux roller on the quality of prining by the magnetic roller of this technical finesse, can satisfy the quality demand of prining.
Claims (3)
1. jump type developing magnetic roller regeneration method in the laser printer: it is characterized in that implementation step is:
The cleaning of magnetic roller surface coating: carry out the sandblast of outward appearance coating with automatic sand-blasting machine, and expose the aluminium base of magnetic roller,
Magnetic roller surface coating carries out recoat: aluminium base being placed on the automatic recoat machine of filling the graphite material masking liquid of magnetic roller carried out recoat to the magnetic roller, and it is 25-40 μ m that machine is adjusted the thickness that the position makes coating, the surface coating uniformity,
The blasting treatment of magnetic roller: the magnetic roller surface coating behind the recoat carries out blasting treatment, makes the surface coating parameter between Rz1.2-1.8,
Packing: leave the magnetic roller of institute's recoat blasting treatment the poly-bag of sealing in.
2. jump type developing magnetic roller regeneration method in the laser printer according to claim 1, it is characterized in that: magnetic roller surface is carried out dividing in the recoat process be sprayed into for 3 times, it is that 50 ℃, humidity are to toast in 0% the environmental test chamber that every spray once is placed on the magnetic roller temperature, sprays after surperficial masking liquid baking is done next time.
3. jump type developing magnetic roller regeneration method in the laser printer according to claim 1, it is characterized in that: in the magnetic roller blasting treatment process, the automatic sand-blasting machine device parameter is air pressure 0.14kap, and the sand grains net is 240 orders, and sand grains is the diamond material.