CN101648806A - Ceramic solar plate - Google Patents
Ceramic solar plate Download PDFInfo
- Publication number
- CN101648806A CN101648806A CN200910163851A CN200910163851A CN101648806A CN 101648806 A CN101648806 A CN 101648806A CN 200910163851 A CN200910163851 A CN 200910163851A CN 200910163851 A CN200910163851 A CN 200910163851A CN 101648806 A CN101648806 A CN 101648806A
- Authority
- CN
- China
- Prior art keywords
- ceramic
- solar plate
- raw material
- ceramic solar
- base substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A dark ceramic solar plate is made of ordinary ceramic raw material, industrial waste with transition element compounds of which the total quantity is more than 5%, and metal mineral with transition elements of which the total quantity is more than 20%. The raw material is regularly processed into slurry material; a porous through hole plate is extruded and formed by an extrusion making method; through holes are processed to be communicated at both ends; end caps which are provided with inlets and outlets and made of the same material are bonded on both ends to form a blank body of the ceramicsolar plate, and the blank body of the ceramic solar plate is dried and sintered to obtain the ceramic solar plate or a ceramic solar plate covered with a dark or black ceramic layer on the surface.Compared with the prior solar heat collecting bodies such as vacuum glass tubes and copper-aluminum composite solar heat collecting bodies, the ceramic solar plate has the characteristics of low production cost, long service life, no attenuation of sun absorption ratio and higher average working efficiency in the whole service life. Compared with vanadium-titanium solar heat collecting plates of black ceramic based on vanadium extracting tailings and composite ceramic hollow solar heat collecting plates, the ceramic solar plate has the advantages of wide sources of raw materials, wide distribution places of the raw materials, short transmission distance of the raw materials and lower production cost.
Description
The present invention is dividing an application of " ceramic solar plate ", July 5 2006 applying date of original application, application number 200610045289.4, invention and created name " ceramic solar plate ".The specification sheets of dividing an application, Figure of description, summary, Figure of abstract are the same with the original application content.
(1) technical field
The present invention relates to the method that sun power utilizes, be manufacture method specifically, say so in more detail about with conventional ceramic raw material, the trade waste that is rich in transition element, metalliferous mineral being the method that raw material is made the ceramic solar energy heat-collection body about the solar energy heating body.
(2) background technology
Sun power is renewable, inexhaustible, not environmentally hazardous green energy resource, be again unstable, thin, the low density energy, solar water heater is mainly adopted in the solar energy thermal utilization, the solar water heater key part is the solar energy heating body, mainly be glass tube with vacuum and the compound heat collection body of copper aluminium at present, both all have the following disadvantages: 1. price height---every square metre of hundreds of units of price; 2. the life-span is short---and metal is perishable, and especially weld seam is perishable, and there are problems such as vacuum life and the easy fragmentation of body in glass tube with vacuum, causes both mean lifetime to be difficult to reach 10 years; 3. average efficiency is not high---and both all adopt the low temperature coating, and 1. the low temperature coating began to wear out in several years, and sunlight absorption rate progressively descends, and whole life period average efficiency is not high; 2. copper material costliness, tube spacing be from greatly, and aluminium sheet absorbs lateral transport behind the sun power and gives medium in the copper pipe, average heat transfer distance 30 millimeter.Because structural limitations, the space is big between the glass tube with vacuum pipe, and the black absorption layer only accounts for structural area about 50%, and noon, sunlight was strong, but a large amount of sunlight pass the space between pipe during noon sunlight direct projection, have influenced collecting efficiency.
Solar paint is difficult to thoroughly solve the sunlight absorption rate attenuation problem, and is therefore cheap, and long service life, the solar energy heating body with certain sunlight absorption rate should be the products that more has practical value.
(3) summary of the invention
The objective of the invention is to utilize cheap raw material, simple production technology manufacturing low cost, long lifetime, have higher sunlight absorption rate, and the ceramic hollow solar energy heating body that sunlight absorption rate can not decay in time, be called ceramic hollow solar heat-collection plate, be called for short ceramic solar plate.
The present invention is achieved in that
The core component of solar energy thermal utilization is the solar energy heating body of hollow, is main heat-conducting medium and heating purposes thing with water, and topmost technico-economical comparison is production cost, work-ing life, working efficiency.
Production cost:
Mainly constitute by the factors such as energy consumption in the prices of raw and semifnished materials, complex manufacturing degree, the manufacturing processed, the conventional ceramic raw material is clay, quartz, feldspar, the price of this class raw material is relevant with foreign matter contents such as the Fe that influences the goods whiteness, Ti, make ceramic solar plate and do not require whiteness, cheap ceramic raw material be can adopt, various trade wastes, mining mine tailing, metalliferous mineral etc. also can be adopted.Ceramic solar plate of the present invention is to adopt vacuum pugging extrusion molding production porous ventilating hole plate, and this is a kind of serialization, forming method in large-scale, high-efficiency, and production technique is simple.Ceramic has higher intensity, about 100 ℃ of ceramic solar plate use temperatures, intensity there is not excessive demand, can adopt more low melting point raw material, firing temperature is reduced, firing temperature can be controlled between 1000~1250 ℃, and adopts the kiln of large-scale continuous production, further reduces and burns till energy consumption.
Goods price reflection production cost, the roughly market price of at present various relevant goods: 500~600 yuan/T of conventional ceramic flat board, 20~30 yuan/m
2, the about 3000 yuan/T of the pig iron, 4500 yuan/T of steel plate, 24000 yuan/T of aluminium, 70000 yuan/T of copper material, ceramic proportion is about 1/3 of iron and steel, and the ceramic solar plate of scale operation might be realized the production cost of every square metre of tens of units.
Work-ing life:
Water temperature in the solar energy heating body can reach 100 ℃, hot water is than the easier corroding metal material of cold water, temperature can be near 200 ℃ in the solar energy heating body during empty the solarization, stupalith can accomplish that fully burn into does not wear out, do not fade under said temperature, the thermal treatment of advanced ceramics industry can make ceramic have less internal stress, the inwall scale can be with scale remover or acids solution removal, to realize many decades even to go up century-old work-ing life.
Working efficiency:
The surface is that reflective surface or pure white 's object sunlight absorption rate is lower, in general, high more for the dark more sunlight absorption rate of the object surface color of the non-reflective surface in surface, ceramic solar plate adopts cheap ceramic raw material, trade waste, the mining mine tailing, metalliferous mineral etc., can make ceramic solar plate have light gray, grey, Dark grey, brown, red, purple, beige, the grey black look, chocolate, the matrix of black or upper layer, make it have higher sunlight absorption rate, the ceramic solar plate firing temperature is above 1000 ℃, structure is very stable, can not fade even be in for a long time under 200 ℃ of left and right sides temperature yet, sunlight absorption rate is decay in time not, thereby makes it in decades, last century-old life period has higher working efficiency all the time.
Be described in further detail the raw material of ceramic solar plate, conventional ceramic can be divided into domestic ceramics, snitaryware, architectural pottery, electroceramics etc., usually ceramic comes from the requirement of whiteness and electrical insulating property, the transition element often repelling colour generation or reduce electrical insulating property is as Fe, Mn, Ti, V, Cr, Ni, Cu, Co, Zn, Zr, Nb, Mo, W etc., these elements are counted as the impurity in the ceramic raw material, they can reduce the whiteness of goods and destroy electrical insulating property, so the raw material of conventional ceramic base substrate mainly is Si, Al, Mg, Ca, K, the oxide compound of Na, purity is high more, quality is high more, and price is expensive more.Indivedual exceptions are also arranged, and as the raw material of dark-red enameled pottery, red flooring tile, black pottery art product etc., dark-red enameled pottery is raw material with the purple clay, and red flooring tile is raw material with the red clay, wherein rhombohedral iron ore (Fe
2O
3) content near 10%, burned product is red, black pottery art product are with strong reducing flame calcined clay goods, make the wherein Fe of redness
2O
3Be reduced to the FeO of black, make goods present band glossy black surface.For reducing cost, ceramics also uses some trade waste such as coal gangue etc. as ceramic raw material.
Yet, because the business reason pottery is not all to be white, except that white glaze, other glaze have various colors, the base substrate of the polished brick in porcelain character of no frush glazing also has shades of colour, for making pottery present shades of colour, people add various ceramic colorants in ceramic raw material, overwhelming majority tinting material all is the transition element by easy colour generation, mainly the oxide compound or the compound of the period 4 transition element that is easy to get greatly of the amount of being are used commercially pure metal oxide for obtaining these tinting materials people, compound is through preparation meticulously, strict control firing temperature, firing atmosphere makes it present various chromatic colours.These oxide compounds, compound generally are to extract from metalliferous mineral through the complicated a large amount of energy of enrichment, smelting process for production, consumption with metalliferous mineral, and recombination, purification just obtain these ceramic colorants, and cost is very expensive.
Transition element generally is meant the only partially filled element of d track in the electron structure, the d track divides easily, cause electronics generation transition and colour generation, the d electronics can all or part of participate in into key, cause different valence state, be in different valence state with a kind of element and can manifest different colours, can present Huang as the v element different valence state, blue, green, purple, ferric iron is red, ferrous iron is black or the like, the reaction that multiple transition element wherein takes place when ceramic firing temperature burns till after mixing is very complicated, the color that is presented is difficult to infer with theory, generally need to determine by a large amount of experiments, adopting cobalt as black ceramic pigment is tinting material, can adopt CoO 20%, CuO 10%, Cr
2O
310%, Fe
2O
320%, MuO40% mixes promptly becomes a kind of ceramic black colorant after 1200 ℃ of sintering are pulverized again.
Ceramic solar plate is the ceramic hollow sheeting with fluid inlet and outlet, can the courverte layer in the hollow sheeting, outside surface can the covering surfaces layer, for absorbing sunlight as much as possible, its outside surface or sunny slope are not reflective, non-white, the surface can have darker color, as light gray, grey, Dark grey, brown, red, purple, blue look, beige, the grey black look, chocolate, shades of colours such as black, color is dark more, sunlight absorption rate is high more, and the raw material of ceramic solar plate is that the conventional ceramic raw material comprises that iron oxide content surpasses 3% ceramic raw material, red clay, be rich in the trade waste of transition element, metalliferous mineral.
Above-mentioned conventional ceramic raw material is meant a large amount of clays that use of ceramic industry, quartzy, the feldspar raw material, iron oxide content is meant that above 3% ceramic raw material to common ceramics be inferior, the clay of the low grade that price is low, quartzy, ceramic raw materials such as feldspar, red clay is meant that appearance is red, iron oxide content>5% can be used to make the red clay of red flooring tile, the trade waste that is rich in transition element is meant the Fe based on the period 4 transition element, Mn, Ti, V, Cr, Ni, Cu, Co, Zn, Zr, Nb, Mo, the oxide compound of W or total amount of compound surpass 5% or contain a large amount of SiC, the trade waste of elemental silicon, these wastes or to be called waste residue normally dark and black comprise the ferroalloy industry waste residue, the iron and steel industry waste residue, nonferrous metallurgy industry waste residue, the chemical industry waste residue.Various ferromanganese slags contain MnO 5-50%, FeO 0.2-2.5% in the ferroalloy industry waste residue, and the silicochrome slag contains Cr
2O
30.1-5%, Cr 2-10.5%, SiC 4-22%, Si 7-8%, in, low, extra low carbon ferrochromium slag contains Cr
2O
32-7%, FeO 1-3%, ferro-silicon slag contain FeO 3-7%, SiC 20-29%, Si 7-10%, and the ferrotungsten slag contains MnO 20-25%, FeO 3-9%, and molybdenum iron slag contains FeO 13-15%, and the chromium metal leached mud contains Cr
2O
32-7%, Fe
2O
38-13%, the chromium metal metallurgical slag contains Cr
2O
311-14%, electrolytic manganese residues contains MnSO
4About 15%, Fe (OH)
3About 30%, silicon manganese slag contains MnO 8-18%, FeO 0.2-2%, and the silicomanganese flue dust contains MnO
220-24%, the ferronickel slag contains FeO 40%, Cr
2O
340%.Bessemer furnace slag contains Fe in the iron and steel industry waste residue
2O
31.4-11%, FeO 7-21%, MnO 0.9-4.5%, the open hearth slag contains Fe
2O
31.7-7.4%, FeO 7-36%, MnO 0.6-3.9%, the steel rolling iron scale contains Fe
2O
3Near 100%, vanadium titano-magnetite ironmaking slag contains TiO
210-17%, Fe
2O
3About 4%, vanadium titano-magnetite steel-making slag contains ferric oxide 11-13%, MnO 1-1.2%, V
2O
52.3-2.9%, TiO
22-2.9%.The electric furnace copper ashes contains FeO26-34% in the nonferrous metallurgy industry waste residue, and copper blast-furnace Water Quenching Slag (being commonly called as black sand) contains FeO+Fe
2O
340-50%, wet type copper smelting leached mud contain Fe 50%, Cu 1.13%, Pb 1.05%, Zn 0.2%, Bi 0.15%, Mn 0.04%, plumbous fuming furnace Water Quenching Slag be with the blast-furnace cinder of the plumbous output of refining again the waste after fuming furnace reclaims plumbous, zinc include Fe
2O
338.6-38.7%, Pb 0.06-0.37%, Zn 0.8-1.3%, aluminium metallurgy factory makes Al
2O
3In time, discharges the waste red mud and contains Fe
2O
38-10%, TiO
22.5%, the pyrite cinder of output contains Fe when making sulfuric acid with sulfurous iron ore in the chemical industry waste residue
2O
341-49%, FeO 10-10.4%, TiO0.4-0.5%, MnO 0.1-0.5%, CuO 2-4%.Metalliferous mineral is meant mineral such as the common iron ore that contains the period 4 transition element, and maroon contains Fe
2O
330-70%, chromite, garnet contains Cr
2O
330-54%, FeO 12-17%, ilmenite, black purple contains TiO 50-60%, FeO 22-35%, Fe
2O
37-15%, MnO 0.5-4%, manganese ore, chocolate, MnO
240-78%, Mn
3O
44-32%, Fe 1-18%, nickel-containing limonite, brown contains Ni 1.2-1.4%, Co 0.1-0.2%, Cr
2O
33%, Fe 35-50%, vanadium titano-magnetite, black contains V 0.4-1.8%, TiO
29-34%, Fe
2O
315-50%, FeO 9-34%, MnO 0.2-6%, Cr
2O
30.1-0.7%, niobite, black contains Nb
2O
59-68%, Ta
2O
51-15%, TiO 1-3%, MnO 1-3%, SnO 2-5%, FeO 12-20%, wolframite, chocolate contain WO
365-67%, FeO 12-15%, MnO 8-12%, Sn 0.17-0.8%.The purpose of selecting these trade wastes that are rich in transition element and metalliferous mineral for use is to provide painted composition for ceramic solar plate base substrate or upper layer, makes base substrate or upper layer present dark color or black, makes it absorb more sunlight.
Ceramic solar plate is that shadow area is greater than 0.2 square metre, non-white with import and export, dark colour, the opaque hollow ceramic plate in surface, or the plate outside surface covers the hollow ceramic plate of dark color or black ceramic layer, or plate internal surface courverte layer, the plate outside surface covers the hollow ceramic plate of dark color or black ceramic layer, with the conventional ceramic raw material, transition element total amount of compound except that tailings in vanadium extraction surpasses the trade waste of 5% (weight), the transition element total amount of compound surpasses one or more manufacturing dark colour ceramics of the metalliferous mineral of 20% (weight), especially ceramic solar plate, be processed into pug with above-mentioned raw materials through routine, with the method extrusion moulding porous ventilating hole plate that extrudes, through processing through hole is communicated with at the place, two ends, the bonding material of the same race in two ends is brought the plug of outlet into, form the ceramic solar plate base substrate, perhaps with the conventional ceramic raw material with aforesaid method make the ceramic solar plate base substrate with conventional ceramic raw material and above-mentioned trade waste or (with) metalliferous mineral mixes and wears into the ceramic solar plate base substrate that formation on the outside surface that mud covers the ceramic solar plate base substrate has top coat, with above-mentioned ceramic solar plate base substrate drying, burn till the ceramic solar plate that promptly obtains ceramic solar plate or surface coverage dark color or black ceramic layer, perhaps make the ceramic solar plate base substrate with aforesaid method with the conventional ceramic raw material, cover common glaze in the plate, with conventional ceramic raw material and above-mentioned trade waste or (with) metalliferous mineral mixes to wear on the outside surface that mud covers the ceramic solar plate base substrate and forms the ceramic solar plate base substrate with top coat, the base substrate drying, burn till and promptly obtain internal surface and have glaze and outside surface that the ceramic solar plate of dark color or black ceramic layer is arranged.
The raw material sources of ceramic solar plate are very extensive, supply quantity is very sufficient, can make the ceramic solar plate of enormous quantity, but for concrete certain producer, may not have various raw materials near the grown place, under situation about significantly promoting with the petroleum price rise trucking costs at present, the raw material freight charges have great effect to production cost, so the present invention selects for the producer provides the multi-scheme of raw material type, and each producer can be produced by alap raw materials cost.
The production technique of ceramic solar plate is subjected near the influence of the raw material supply in grown place, different production technique is adopted in different raw material supplies, as cheap porcelain ceramic raw material and the industrial residue that is rich in transition element are arranged near the grown place, can adopt production technique one: after ceramic raw material and waste residue difference or common the pulverizing, be mixed and made into pug, through vacuum pugging and the old plasticity pug preferably that becomes, is porous ventilating hole plate base substrate with extrusion shaping machine with mud material forming, pug between two holes of two ends is removed, the plug that has import and export that other does material of the same race sticks on two termination faces of porous ventilating hole plate, the two ends mouth of pipe is all communicated with each hole in the ventilating hole plate, form the blanket of ceramic solar plate, the blanket drying, burn till and promptly become the ceramic solar plate of surface for dark color or black.
Lack industrial residue or the metalliferous mineral that is rich in transition element if near the grown place ceramic raw material is arranged, can adopt production technique two: the hollow blanket of ceramic raw material being made ceramic solar plate with the method for production technique one, ceramic raw material is mixed with above-mentioned waste residue or the mineral buied, levigate becoming on the outside surface of sunny slope that ceramic mud covers blanket, drying again, burn till and promptly become the ceramic solar plate that the surface has dark color or black ceramic layer, note the prescription and the firing temperature of adjustment sheet surface layer, make upper layer sinter porcelain into, and do not make it become vitreous glaze, glaze can cause reflective, reduces the absorption to sunlight.
If have certain perviousness after the ceramic raw material that adopt the grown place burns till, can adopt production technique three: ceramic raw material is pulverized made pug through vacuum pugging, old, extrusion forming is a porous ventilating hole plate base substrate, pug between two holes of two ends is removed, other does having on two end faces that the plug of importing and exporting the mouth of pipe sticks on the porous hollow sheeting of material of the same race, make the two ends mouth of pipe identical with each hole in the hollow sheeting, form the ceramic solar plate base substrate, on base substrate inwall or outside surface, cover the conventional ceramic glaze, again ceramic raw material is mixed on the outside surface that the mud that grinds covers the blanket sunny slope drying with above-mentioned waste residue or mineral, burn till and promptly become the ceramic solar plate that there are glaze and dark color or black ceramic layer in the surface.
(4) description of drawings
Describe the method for ceramic solar sheet metal forming of the present invention in detail below in conjunction with accompanying drawing:
The ventilating hole plate 3-that 1-porous ventilating hole plate 2-two ends through hole links to each other has the plug 4-ceramic solar plate base substrate of import and export
(5) specific embodiments
Embodiment
1. the iron oxide content that is commonly referred to be inferior raw material with ceramics is 5%, titanium oxide content is that 3.2% ceramic raw material is made pug with common ceramic device and technology, through vacuum pugging and old after extrude with vacuum-extruder and to become porous ventilating hole plate base substrate, pug between two holes of two ends is removed, other does having on two termination faces that the plug that passes in and out the mouth of pipe sticks on the porous ventilating hole plate of material of the same race, make that each hole all communicates in the two ends mouth of pipe and the ventilating hole plate, form the ceramic solar plate blanket, the blanket drying, burn till and promptly become the surperficial gray ceramic solar plate that is.
2. as embodiment 1 described method, the employing iron oxide content is 9% red clay, and the ceramic solar plate of manufacturing is red.
3. as method as described in the embodiment 1, adopting conventional ceramic raw material and ferromanganese slag is raw material, and wherein the ferromanganese slag accounts for 35%, contains MnO 15%, FeO 2% in the ferromanganese slag, and the ceramic solar plate of manufacturing is a Dark grey.
4. adopting conventional ceramic raw material and ferrotungsten slag as method as described in the embodiment 1 is raw material, and wherein the ferrotungsten slag accounts for 40%, contains MnO 21%, FeO7% in the ferrotungsten slag, and the ceramic solar plate of manufacturing is the grey black look.
5. adopting conventional ceramic raw material and slag as method as described in the embodiment 1 is raw material, and wherein slag accounts for 35%, contains Fe in the slag
2O
38%, FeO 11%, and the ceramic solar plate of MnO 3%, manufacturing is a Dark grey.
6. adopting conventional ceramic raw material and wet type copper smelting leached mud as method as described in the embodiment 1 is raw material, and wherein leached mud accounts for 30%, contains Fe40%, Cu 1%, Pb 0.8%, Zn 0.1%, Bi 0.1% in the leached mud, and the ceramic solar plate of manufacturing is a Dark grey.
7. adopting conventional ceramic raw material and pyrite cinder as method as described in the embodiment 1 is raw material, and wherein pyrite cinder accounts for 50%, contains Fe in the pyrite cinder
2O
328%, FeO 8%, Ti 0.4%, MnO 0.3%, CuO 3%, the ceramic solar plate of manufacturing is a Dark grey.
8. as method as described in the embodiment 1, add chromium metal metallurgical slag 20% in the conventional ceramic raw material, molybdenum iron slag 25% contains Cr in the chromium metal metallurgical slag
2O
313%, contain FeO 14% in the molybdenum iron slag, the ceramic solar plate of manufacturing is the grey black look.
9. as method as described in the embodiment 1, make the ceramic solar plate base substrate with the conventional ceramic raw material, add 60% ferrotungsten sizing and become mud in the conventional ceramic raw material, be sprayed on the outside surface of ceramic solar plate base substrate, the ceramic solar plate of manufacturing is a black.
10. as method as described in the embodiment 1, make the ceramic solar plate base substrate with the conventional ceramic raw material, add 70% niobite and wear into mud in the conventional ceramic raw material, be sprayed on the outside surface of ceramic solar plate base substrate, the ceramic solar plate of manufacturing is a black.
11. as method as described in the embodiment 1, ceramic solar plate with certain ceramic raw material manufacturing inferior has phenomenon of osmosis, base substrate is through biscuiting, at solar panel biscuit internal surface dip-coating one deck conventional ceramic glaze slip, on the sunny slope of solar panel, spray one deck such as embodiment 9 described mud again, the sunny slope of the ceramic solar plate of manufacturing is a black, and ceramic solar plate does not seep water.
Claims (6)
1. ceramic solar plate, it is characterized in that surpassing the dark colour hollow ceramic plate of one or more manufacturings of the trade waste of 5% (weight), metalliferous mineral that the transition element total amount of compound surpasses 20% (weight) with conventional ceramic raw material, transition element total amount of compound except that tailings in vanadium extraction, or the plate outside surface covers the hollow ceramic plate of dark ceramic layer, or plate internal surface courverte layer, the plate outside surface covers the hollow ceramic plate of dark ceramic layer.
2. the manufacture method of a ceramic solar plate, it is characterized in that with the conventional ceramic raw material, transition element total amount of compound except that tailings in vanadium extraction surpasses the trade waste of 5% (weight), the transition element total amount of compound surpasses one or more of metalliferous mineral of 20% (weight), be processed into the ceramic solar plate base substrate through routine, perhaps making the ceramic solar plate base substrate with the conventional ceramic raw material with ordinary method mixes the conventional ceramic raw material and wears into the ceramic solar plate base substrate that formation on the outside surface that mud covers the ceramic solar plate base substrate has top coat with above-mentioned trade waste or/and metalliferous mineral, with above-mentioned ceramic solar plate base substrate drying, burn till the ceramic solar plate that promptly obtains ceramic solar plate or surface coverage dark color or black ceramic layer, perhaps make the ceramic solar plate base substrate with aforesaid method with the conventional ceramic raw material, cover common glaze in the plate, the conventional ceramic raw material mixed with above-mentioned trade waste or/and metalliferous mineral to wear into form the ceramic solar plate base substrate with top coat, base substrate drying on the outside surface that mud covers the ceramic solar plate base substrate, burn till and promptly obtain internal surface and have glaze and outside surface that the ceramic solar plate of dark color or black ceramic layer is arranged.
3. according to the manufacture method of the described ceramic solar plate of claim 2, it is characterized in that with the conventional ceramic raw material, transition element total amount of compound except that tailings in vanadium extraction surpasses the trade waste of 5% (weight), one or more of metalliferous mineral that the transition element total amount of compound surpasses 20% (weight) are processed into pug through routine, with the method extrusion moulding porous ventilating hole plate that extrudes, through processing through hole is communicated with at the place, two ends, the bonding material of the same race in two ends is brought the plug of outlet into, form the ceramic solar plate base substrate, perhaps making the ceramic solar plate base substrate with the conventional ceramic raw material with aforesaid method mixes the conventional ceramic raw material and wears into the ceramic solar plate base substrate that formation on the outside surface that mud covers the ceramic solar plate base substrate has top coat with above-mentioned trade waste or/and metalliferous mineral, with above-mentioned ceramic solar plate base substrate drying, burn till the ceramic solar plate that promptly obtains ceramic solar plate or surface coverage dark color or black ceramic layer, perhaps make the ceramic solar plate base substrate with aforesaid method with the conventional ceramic raw material, cover common glaze in the plate, the conventional ceramic raw material mixed with above-mentioned trade waste or/and metalliferous mineral to wear into form the ceramic solar plate base substrate with top coat, base substrate drying on the outside surface that mud covers the ceramic solar plate base substrate, burn till and promptly obtain internal surface and have glaze and outside surface that the ceramic solar plate of dark color or black ceramic layer is arranged.
4. according to the described ceramic solar plate of claim 1, it is characterized in that described conventional ceramic raw material is meant clay, feldspar, quartz, comprise that iron oxide content surpasses 3% ceramic raw material and red clay.
5. according to the described ceramic solar plate of claim 1, it is characterized in that described trade waste is meant various ferromanganese slags in the ferroalloy industry waste residue, silicochrome slag, in, low, the extra low carbon ferrochromium slag, ferro-silicon slag, ferrotungsten slag, molybdenum iron slag, chromium metal leached mud, chromium metal metallurgical slag, electrolytic manganese residues, silicon manganese slag, silicomanganese flue dust, the ferronickel slag, bessemer furnace slag in the iron and steel industry waste residue, open hearth slag, steel rolling iron scale, vanadium titano-magnetite ironmaking slag, vanadium titano-magnetite steel-making slag, electric furnace copper ashes in the nonferrous metallurgy industry waste residue, copper blast-furnace Water Quenching Slag, the wet type copper smelting leached mud, plumbous fuming furnace Water Quenching Slag, red mud, pyrite cinder in the chemical industry waste residue.
6. according to the described ceramic solar plate of claim 1, it is characterized in that described metalliferous mineral is meant common iron ore, chromite, ilmenite, manganese ore, nickel-containing limonite, vanadium titano-magnetite, niobite, wolframite.