CN101634128A - Method for manufacturing carborundum sparkling cameo wear-resistance floor - Google Patents
Method for manufacturing carborundum sparkling cameo wear-resistance floor Download PDFInfo
- Publication number
- CN101634128A CN101634128A CN200810053920A CN200810053920A CN101634128A CN 101634128 A CN101634128 A CN 101634128A CN 200810053920 A CN200810053920 A CN 200810053920A CN 200810053920 A CN200810053920 A CN 200810053920A CN 101634128 A CN101634128 A CN 101634128A
- Authority
- CN
- China
- Prior art keywords
- floor
- cement
- wear
- varnish
- terrace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing a carborundum sparkling cameo wear-resistance floor. The carborundum sparkling cameo wear-resistance floor pressed by the method can be pressed with various cameos producing rock sheet, pebble, human being and animal effects. The color and luster of the prior color floor which has no wear-resistance material is worn off after being walked on by tourists for 2 to 3 years. The carborundum sparkling cameo wear-resistance floor manufactured by the method beatifies the variety of color floors, has improved wear resistance and can be used for more than then years without fading and losing luster due to the use of wear-resistance silicon carborundum.
Description
Technical field:
The invention belongs to the building ground floor material, specially refer to a kind of preparation method of carborundum sparkling cameo wear-resistance floor.
Background technology:
The abrasion-proof terrace of China mostly is to adopt not saturated polyester ground at present, or the abrasion-proof terrace of epoxy resin village material, the main high-abrasive material of this abrasion-proof terrace is a quartz sand, also there is part to adopt diamond dust, this terrace mostly is used between special-purpose vehicle, what the earliest diamond dust is used for floor material is plastics floor in the Beijing Metro compartment, be filled with green carbide diamond dust fragmentarily on this celadon plastic cement, this makes this place of walking mill for a long time, Beijing Metro compartment is wear-resisting wear-resistant very attractive in appearance again.A kind of diamond dust abrasion-proof terrace of the present invention mainly is to adopt common cement material, be on common portland cement terrace, suppress the terrace of various anaglyphs, this terrace is on the surface of pressing process, spill the sparkling diamond dust of one deck, then with the color floor compacting tool set that various anaglyphs are arranged, also can select for use " a kind of cement cameo floor pressing composite die " of Lian Xu invention to carry out the terrace compacting, carborundum sparkling cameo wear-resistance floor with the present invention's compacting, can suppress various embossments, the rock sheet is arranged, the cobble effect is arranged, also have various personages, the animal effect, anaglyph terrace in the past, when not managing high-abrasive material, in about 2~3 years, can walk because of the visitor, grind off the color and the gloss of color floor, and the carborundum sparkling abrasion-proof terrace that the present invention makes, promptly beautified the kind of color floor, make terrace increase rub proofness again, because having adopted wear-resisting diamond dust, the life-span of color floor to be the more than ten years does not fade, do not tarnish.
Technology contents:
The present invention adopts 46 orders~five kinds of green silicon carbide silicon carbides of 100 purposes, also having black silicon carbide diamond dust is main wear-resisting and glittering material, this granular material is sprinkled upon on the compacting coloured cement terrace, the secure bond of process and lustrous surface resin, form superhard wearing layer, and as green silicon carbide particle and black carbon silicon grain, because be the polyhedron of flash of light, can sparking flash of light under the light of any angle.Because the terrace on square and the terrace in various paths, all be in the open down, irradiation through sunlight, can make road glittering, daytime is as the golden road, and the moonlight at night makes the path become real Avenue of Stars, and such color floor will make any one tourist attractions make something perfect even more perfect.
Specific embodiments:
Make the random type stone of 1 square meter moulding color floor:
1. on the square ground of floating cement, after the cement floor initial set does not have the surface and swims, available hand sprinkles the cement material for color floor pressing die for preparing uniformly, the thickness of material is 2~4 millimeters, with the color that do not expose ordinary Portland cement on the former cement floor that spreads punishment in advance is standard, spread the back with plasterer's trowel the floating troweling of material, if do not spread uniformly can benefit spread one time floating again, this is to be the first pass of terrace color motif with the salmon pink.
Because be orange band black texture scrape shape stone, this just need use trowel floating with the grey black coloured cement for preparing sprinkling fragmentarily on the basis of first pass then, deep mixed full of stains or spots natural effect of refuting can occur like this behind pressing mold.
3. the surfacing of cement floor press...withed one's finger after initial set, can be in the time of lines of the hand seal can occurring sprinkling the calcareous separating powder of one deck on the terrace, and separating powder adopts dark series, with rich colors.Then with the compacting of terrace relief die, pressing process is that the workman steps down on the mould and rams to the mould pressurization with beetle or iron plate, comes with the deep mixed rough effect that extrudes random shape stone, by that analogy.
4. the anaglyph terrace that suppresses, can solidify intensity is arranged after spraying last layer surface gloss oil, gloss oil adopts nitro-resin varnish, also can adopt alkyd varnish, when varnish does not have drying, will be with 60 order black silicon carbides or green silicon carbide particle, be sprinkled upon the surface of having brushed varnish equably, because the thickness of 60 order silicon-carbide particles is substantially near the thickness of varnish, the particle of carborundum is trickled down on varnish, exposes 1/3rd gloss, promptly can sparkle, in the time of can reducing people again and walk to the friction of varnish, as the green of highly abrasion-resistant material and black silicon carbide particle, can make the colour cement terrace that very strong abrasion resistance is arranged, than tens times of present ordinary Portland cement material and quartz sand material wear-resistants, and the sparking flash of light that always do not stop of the green silicon carbide particle that exposes, very shape is seen.
Claims (1)
1. the preparation method of a corundum sparkling cameo wear-resistance floor is characterized in that:
Make the random type stone of 1 square meter moulding color floor:
(1) on the square ground of floating cement, after the cement floor initial set does not have the surface and swims, available hand sprinkles the cement material for color floor pressing die for preparing uniformly, the thickness of material is 2~4 millimeters, with the color that do not expose ordinary Portland cement on the former cement floor that spreads punishment in advance is standard, spread the back with plasterer's trowel the floating troweling of material, if do not spread uniformly can benefit spread one time floating again, this is to be the first pass of terrace color motif with the salmon pink.
(2) because be orange band black texture scrape shape stone, this just need use trowel floating with the grey black coloured cement for preparing sprinkling fragmentarily on the basis of first pass then, deep mixed full of stains or spots natural effect of refuting can occur like this behind pressing mold.
(3) surfacing of cement floor press...withed one's finger after initial set, can be in the time of lines of the hand seal can occurring sprinkling the calcareous separating powder of one deck on the terrace, and separating powder adopts dark series, with rich colors.Then with the compacting of terrace relief die, pressing process is that the workman steps down on the mould and rams to the mould pressurization with beetle or iron plate, comes with the deep mixed rough effect that extrudes random shape stone, by that analogy.
(4) the anaglyph terrace that suppresses, can solidify intensity is arranged after spraying last layer surface gloss oil, gloss oil adopts nitro-resin varnish, also can adopt alkyd varnish, when varnish does not have drying, will be with 60 order black silicon carbides or green silicon carbide particle, be sprinkled upon the surface of having brushed varnish equably, because the thickness of 60 order silicon-carbide particles is substantially near the thickness of varnish, the particle of carborundum is trickled down on varnish, exposes 1/3rd gloss, promptly can sparkle, in the time of can reducing people again and walk to the friction of varnish, as the green of highly abrasion-resistant material and black silicon carbide particle, can make the colour cement terrace that very strong abrasion resistance is arranged, than tens times of present ordinary Portland cement material and quartz sand material wear-resistants, and the sparking flash of light that always do not stop of the green silicon carbide particle that exposes, very shape is seen.