CN101629889B - 轻骨料混凝土压力吸水率测定方法 - Google Patents
轻骨料混凝土压力吸水率测定方法 Download PDFInfo
- Publication number
- CN101629889B CN101629889B CN2009100566047A CN200910056604A CN101629889B CN 101629889 B CN101629889 B CN 101629889B CN 2009100566047 A CN2009100566047 A CN 2009100566047A CN 200910056604 A CN200910056604 A CN 200910056604A CN 101629889 B CN101629889 B CN 101629889B
- Authority
- CN
- China
- Prior art keywords
- lightweight aggregate
- concrete
- aggregate concrete
- water absorption
- absorption rate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种轻骨料混凝土压力吸水率测定方法,其包括步骤:将混凝土和轻骨料拌合均匀;称取CW克的混合均匀的轻骨料混凝土,并置于4.75mm方孔筛中,筛除水泥砂浆,之后称量筛除的水泥砂浆的重量为MW1克;将拌合均匀的轻骨料混凝土装入含气量测定仪的容器中,并插捣密实,之后通过该含气量测定仪向轻骨料混凝土中注气加压至压力不下降为止;重新称取一定量的经过加压的轻骨料混凝土CW克,并置于4.75mm方孔筛中,筛除水泥砂浆,之后称量筛除的水泥砂浆的重量为MW2克;利用公式
Description
技术领域
本发明涉及一种轻骨料混凝土的压力吸水率测定方法。
背景技术
轻骨料混凝土以粉煤灰陶粒、页岩陶粒、粘土陶粒等多孔材料为骨料,用硅酸盐水泥、水和外加剂(或不掺外加剂)按配合比要求配制而成的混凝土。轻骨料混凝土具有轻质、保温的效果,在工业与民用建筑中用量越来越大;但是,轻骨料混凝土以粉煤灰陶粒、页岩陶粒、粘土陶粒等多孔材料为骨料,该些骨料吸水率较大,而且随着压力的增大轻骨料的吸水率会增加,因此采用泵送的方法灌注轻骨料混凝土时,在泵送压力作用下,多孔的轻骨料会在泵压的作用下,吸水导致混凝土变稠、变干,失去流动性而堵塞泵管;因此在一般的轻骨料混凝土的施工中通常是采用将轻骨料混凝土吊到建筑物顶,这也是轻骨料混凝土不能广泛应用的主要原因之一。
发明内容
本发明要解决的技术问题在于提供一种轻骨料混凝土压力吸水率测定方法,在泵送之前测定轻骨料混凝土在一定压力下的吸水率,并根据该吸水率测得所要泵送的轻骨料混凝土的吸水量,并将和吸水量等量的水在泵送之前添加到轻骨料混凝土中,从而使轻骨料在泵送前就已经达到吸水饱和的状态,在泵送的状态下不会出现轻骨料混凝土变稠、变干失去流动性而堵塞泵管。
为解决以上技术问题,本发明提供一种轻骨料混凝土压力吸水率测定方法,其包括步骤:
将混凝土和轻骨料拌合均匀;
称取CW克的混合均匀的轻骨料混凝土,并置于方孔筛中,利用该方孔筛过筛其中的轻骨料混凝土筛除水泥砂浆,之后称量筛除的水泥砂浆的重量为MW1克;
将拌合均匀的轻骨料混凝土装入加压的容器中,并插捣密实,之后通过该加压容器向轻骨料混凝土中注气加压至压力不下降为止;
将轻骨料混凝土倒出,拌合均匀后重新称取一定量的经过加压的轻骨料混凝土CW克,并置于方孔筛中,利用该方孔筛过筛其中的轻骨料混凝土筛除水泥砂浆,之后称量筛除的水泥砂浆的重量为MW2克;
本发明的进一步改进在于还包括步骤:将轻骨料和混凝土拌和均匀后,测定该轻骨料混凝土的塌落度,如果该塌落度达不到设定的标准,则重新调配轻骨料混凝土的比例,直至塌落度达到设定的标准。
本发明的进一步改进在于:所用的加压容器为直读式混凝土含气量测定仪。
本发明的进一步改进在于:所述的方孔筛为4.75mm方孔筛。
通过以上所述的技术方案,本发明所提供的轻骨料混凝土压力吸水率测定方法,利用含气量测定仪对需要泵送的轻骨料混凝土在泵送之前进行加压吸水,通过质量差的原理测定轻骨料混凝土在一定压力下的吸水率,并根据该吸水率测得所要泵送的轻骨料混凝土的吸水量,并将和吸水量等量的水在泵送之前添加到轻骨料混凝土中,从而使轻骨料在泵送前就已经达到吸水饱和的状态,在泵送的状态下不会出现轻骨料混凝土变稠、变干失去流动性而堵塞泵管。
附图说明
无
具体实施方式
通常,轻骨料在正式用于拌合混凝土之前,需要先预先用水浸泡或预湿,由于是在常压状态下浸泡或预湿,即使轻骨料吸水饱和或吸水基本稳定,在泵送压力状态下,轻骨料还会继续吸水,直到在压力状态下,吸水饱和为止。因此如何测定出轻骨料混凝土在泵压状态下的压力吸水率,是能否实现顺利泵送的关键。
为了解决轻骨料混凝土在泵送时出现的堵塞、变干的现象,本发明提供的轻骨料混凝土压力吸水率测定方法,可以测定轻骨料混凝土在泵压状 态下的吸水率,从而计算出吸水量,可在泵送混凝土前将该额外的吸水量注入混凝土中,从而避免在泵送时出现的堵塞、变干等现象。其具体的方法如下:
首先将将轻骨料和混凝土拌合均匀,并测定塌落度是否满足需要的塌落度,如果测定的塌落度不符合标准,需要重新对轻骨料和混凝土进行配比,之后再测定塌落度直至达到需要的标准,混凝土拌合物的塌落度应不小于180mm;
称取CW克(在该实施例中取5000.0g)符合塌落度要求的轻骨料混凝土,置于方孔筛中(该实施例使用4.75mm方孔筛,在选择方孔筛时方孔筛的孔径要保证轻骨料混凝土不会被筛除)过筛其中的轻骨料混凝土筛除水泥砂浆,称量其筛除的水泥砂浆重量MW1,精确至1g;
将符合塌落度要求拌合均匀的混凝土装入加压容器中,本实施例中使用直读式含气量测定仪(无水式)中的容器,将轻骨料混凝土插捣密实后,注气加压,在加压的情况下,轻骨料混凝土将继续吸水,直至压力不下降为止,轻骨料混凝土吸水饱和;
将混凝土倒出,拌合均匀后重新测定塌落度,此时的混凝土塌落度应是能够满足泵送要求的下限值即大于等于120mm,若塌落度小于此值,应重新调整配合比到符合要求为止;
重新称取CW克在该实施例中取5000.0g经过加压的拌和均匀的轻骨料混凝土置于方孔筛中(该实施例使用4.75mm方孔筛)进行筛分其中的轻骨料混凝土筛除水泥砂浆,称量其筛除的水泥砂浆重量MW2,精确至1g。重量之差:MW1-MW2即为5000.0g混凝土的压力吸水重;
计算出轻骨料混凝土的压力吸水率R: 计算结果精确至0.1%。
在配制、生产混凝土时,对于质量为M的轻骨料混凝土,其吸水量为M×R,在对该质量为M的轻骨料混凝土进行泵送时将该M×R重量的部分额外的水量增加在混凝土拌合中,就能满足混凝土泵送要求,不会导致由于压力吸水、混凝土变稠而堵塞泵管现象发生。
在该具体实施例中使用的直读式含气量测定仪(无水式),具有读数速度快的特点。由于不再单独注入水,从而具有维持混凝土拌合物一致的特点。
Claims (4)
2.如权利要求1所述的轻骨料混凝土压力吸水率测定方法,其特征在于还包括步骤:在加压前将轻骨料和混凝土拌和均匀后,测定该轻骨料混凝土的塌落度,如果该塌落度达不到设定的标准,则重新调配轻骨料混凝土的比例,直至塌落度达到设定的标准;
在加压后将轻骨料和混凝土拌和均匀后,测定该轻骨料混凝土的塌落度,如果该塌落度达不到设定的标准,则重新调配轻骨料混凝土的比例,直至塌落度达到设定的标准。
3.如权利要求1~2任一所述的轻骨料混凝土压力吸水率测定方法,其特征在于:所用的加压容器为直读式混凝土含气量测定仪。
4.如权利要求3所述的轻骨料混凝土压力吸水率测定方法,其特征在于:所述的方孔筛为4.75mm方孔筛。