A kind of mask-making technology of optical curing plate
Technical field
The present invention relates to plate making technology, be specifically related to a kind of mask-making technology of optical curing plate.
Background technology
The substrate sheet material that prints usefulness in the prior art comprises flexible sheet and hard plate material, these sheet materials are because the restriction of material composition and processing technology PS (polystyrene) plate for example, behind the hectograph of making printing usefulness, generally also just can print 2~30,000 paper its serviceable life, after printing surpassed its limiting quantity, the quality of printing can sharply descend.Have in the plate-making running program again and cause the quality of printing to descend if various technological parameters are controlled improper meeting, or cause scrapping of galley, this will cause serious loss to printing enterprise.Therefore, be necessary that printing adds base version processing worker and improves to the sheet material of existing printing with substrate.
Summary of the invention
The objective of the invention is to overcome raw-material defective in the prior art, design a kind of mask-making technology of optical curing plate.The galley that adopts this processes to make should have, and is wear-resisting, durability is strong, and plate is difficult for exposure machine to be damaged.
For achieving the above object, technical scheme of the present invention is to adopt a kind of mask-making technology of optical curing plate, and described mask-making technology comprises following procedure of processing:
S1: plate-making, the polystyrene board that to handle admittedly through light and film film are packed into and are made optical curing plate in the platemaking machine, the time shutter of setting platemaking machine is 25 seconds~35 seconds, and setting the time that twice vacuumizes in the platemaking machine is 38 seconds~42 seconds for the first time, is 28 seconds~32 seconds for the second time;
S2: develop, development concentrate and water by dilution in 1: 6 and stir misciblely, are controlled at 24 ℃~26 ℃ with water temperature, the optical curing plate after exposing is put into developer solution, and back and forth shake, after pattern presented, taking-up also cleaned up with clear water;
S3: dry, utilize drying voluntarily or hot blast that the optical curing plate after developing is carried out air-dry processing, make its dry tack free, anhydrous mark and dirty point;
S4: baking, optical curing plate after will drying is heated to 200 ℃~240 ℃ with the temperature in the baking oven on the deflector roll platform, start the gear train of deflector roll, described optical curing plate is sent in the baking oven lentamente enters, described optical curing plate stoving time in described baking oven was controlled at 16 seconds~20 seconds;
S5: cleaning, with opaquing fluid, retouching paste and dilute sulfuric acid, the tawny sign at ink-receptive coating, blank position is removed clean under will leaving in development development cleaning step.
Wherein, in the described step of S1, the time shutter of setting described platemaking machine is 30 seconds, and setting the time that twice vacuumizes in the described platemaking machine is 40 seconds for the first time, is 30 seconds for the second time.
Wherein, in the described step of S2, water temperature is controlled at 25 ℃.
Wherein, in the described step of S4, the temperature in the described baking oven is heated to 220 ℃.
Wherein, in the described step of S4, the stoving time in the described baking oven was controlled at 18 seconds.
Wherein, in the described step of S4, described deflector roll travels at the uniform speed in described baking oven.
Wherein, in the described step of S3, the temperature of described hot blast is 15 ℃~20 ℃.
Wherein, the described polystyrene board of handling admittedly through light also need position processing, and the both sides of plate are flushed line.
Advantage of the present invention and beneficial effect are: because the present invention has adopted the polystyrene board of handling admittedly through light (UVPS) as substrate, and in processing technology, with this substrate and the film in platemaking machine compound after, make the forme of printing usefulness, this forme is the heating and temperature control of strictness in baking oven again, after control heat time heating time, can obtain a kind of have wear-resisting, the forme that durability is strong, this forme life-span of comparing with existing all kinds of galleys has improved about 10 times, being printing can bring up to 20~300,000 by original 2~30,000, and the quality of printing has obtained significant raising, when improving print quality, also can make the overall cost of printing obtain reduction.
Embodiment
Below in conjunction with drawings and Examples, the specific embodiment of the present invention is further described.Following examples only are used for technical scheme of the present invention more clearly is described, and can not limit protection scope of the present invention with this.
Embodiment 1
A kind of mask-making technology of optical curing plate, described mask-making technology comprises following procedure of processing:
The first step: plate-making, the polystyrene board that to handle admittedly through light and film film are packed into and are made optical curing plate in the platemaking machine, the time shutter of setting platemaking machine is 25 seconds~35 seconds, and setting the time that twice vacuumizes in the platemaking machine is 38 seconds~42 seconds for the first time, is 28 seconds~32 seconds for the second time;
Second step: develop, development concentrate and water by dilution in 1: 6 and stir misciblely, are controlled at 24 ℃~26 ℃ with water temperature, the optical curing plate after exposing is put into developer solution, and back and forth shake, after pattern presented, taking-up also cleaned up with clear water;
The 3rd step: dry, utilize drying voluntarily or hot blast that the optical curing plate after developing is carried out air-dry processing, make its dry tack free, anhydrous mark and dirty point;
The 4th step: baking, optical curing plate after will drying is heated to 200 ℃~240 ℃ with the temperature in the baking oven on the deflector roll platform, start the gear train of deflector roll, described optical curing plate is sent in the baking oven lentamente enters, described optical curing plate stoving time in described baking oven was controlled at 16 seconds~20 seconds;
The 5th step: cleaning, with opaquing fluid, retouching paste and dilute sulfuric acid, the tawny sign at ink-receptive coating, blank position is removed clean under will leaving in development development cleaning step.
Embodiment 2
On the basis of embodiment 1, preferred embodiment of the present invention comprises that in the described step of the first step, the time shutter of setting described platemaking machine is 30 seconds, and setting the time that twice vacuumizes in the described platemaking machine is 40 seconds for the first time, is 30 seconds for the second time.
Embodiment 3
On the basis of embodiment 2, preferred embodiment of the present invention also comprises, in described step of second step, water temperature is controlled at 25 ℃.
Embodiment 4
On the basis of embodiment 3, preferred embodiment of the present invention also comprises, in described step of the 4th step, the temperature in the described baking oven is heated to 220 ℃.
Embodiment 5
On the basis of embodiment 3, preferred embodiment of the present invention also comprises, in described step of the 4th step, the stoving time in the described baking oven is controlled at 18 seconds.
Embodiment 6
On the basis of embodiment 5, preferred embodiment of the present invention comprises that also in described step of the 4th step, described deflector roll travels at the uniform speed in described baking oven.
Embodiment 7
On the basis of embodiment 6, preferred embodiment of the present invention comprises that also in described step of the 3rd step, the temperature of described hot blast is 15 ℃~20 ℃.
Embodiment 8
On the basis of embodiment 1, preferred embodiment of the present invention comprises that also the described polystyrene board of handling admittedly through light also need position processing, and the both sides of plate are flushed line.
Because the foregoing description has adopted the polystyrene board of handling admittedly through light (UVPS) as substrate, and in processing technology, with this substrate and the film in platemaking machine compound after, make the forme of printing usefulness, this forme is the heating and temperature control of strictness in baking oven again, after control heat time heating time, can obtain a kind of have wear-resisting, the forme that durability is strong, this forme life-span of comparing with existing all kinds of galleys has improved about 10 times, being printing can bring up to 20~300,000 by original 2~30,000, and the quality of printing has obtained significant raising, when improving print quality, also can make the overall cost of printing obtain reduction.
The above only is a preferred implementation of the present invention; should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.