CN101618951A - Manufacturing method of ceramic glaze art toughened glass for furniture and product thereof - Google Patents
Manufacturing method of ceramic glaze art toughened glass for furniture and product thereof Download PDFInfo
- Publication number
- CN101618951A CN101618951A CN200910181655A CN200910181655A CN101618951A CN 101618951 A CN101618951 A CN 101618951A CN 200910181655 A CN200910181655 A CN 200910181655A CN 200910181655 A CN200910181655 A CN 200910181655A CN 101618951 A CN101618951 A CN 101618951A
- Authority
- CN
- China
- Prior art keywords
- toughened glass
- ceramic glaze
- glass
- furniture
- art toughened
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of ceramic glaze art toughened glass for furniture and a product thereof, comprising the steps of screen painting, drying and high-temperature sintering in a toughening furnace. The invention also discloses the ceramic glaze art toughened glass manufactured by the manufacturing method. The invention has the advantages that the method utilizes inorganic high-temperature lead-free ceramic glaze inks; the ceramic glaze art toughened glass can be sintered in the toughening furnace at the high temperature of 700 DEG C; glaze and oxide film molecules are interconnected and deeply combined; a layer of color glaze with high hardness is formed on the surface of the glass, does not fall off, can not aging and never fades and has higher intensity; the impact resistance is 20 times of that of common glass, and the ceramic glaze art toughened glass is radiation-free, environment-protective and economic.
Description
Technical field
The present invention relates to manufacture method of a kind of toughened glass and products thereof, particularly manufacture method of a kind of ceramic glaze art toughened glass for furniture and products thereof.
Background technology
Often use toughened glass as finishing material in industries such as furniture, decorations, the toughened glass of using at present adopts low temperature spraying lacquer to make various patterns mostly, and baking forms then, and its surface often comes off, fades, ageing-resistant ability, not acid and alkali-resistance.In addition, the printing ink that low temperature spraying baking finish is used is organic printing ink, can not enter the annealing furnace sintering after the spraying.Moreover the thinner that the low temperature spraying is used contains benzene, is unfavorable for environment protection.
Summary of the invention
Technical problem to be solved by this invention provides the manufacture method of a kind of practicality, colour-fast, shock-resistant, ceramic glaze art toughened glass for furniture that security is higher, and the toughened glass that adopts this method to make.
For solving the problems of the technologies described above, technical scheme of the present invention is: a kind of manufacture method of ceramic glaze art toughened glass for furniture, and it comprises following step:
A, silk screen printing: it comprises following steps: (1) makes film substrate; (2) film substrate is placed on the sensitization table top; (3) will after spreading sensitive materials, the silk screen that stretches tight on the net machine that stretches tight after sensitization in 30 minutes, be made into screen printing forme on the sensitization platform; (4) screen printing forme is placed on the screen process press, puts into inorganic high-temp lead-free ceramics muffle painting ink printing;
B, oven dry: the glass that prints is put into stoving oven, and oven dry is 5 minutes under 180 ℃ of high temperature;
C, annealing furnace high temperature sintering: the glass of oven dry is put into glass tempering furnace, and sintering is 20 minutes under 700 ℃ of high temperature.
For the effect that helps drying, the stoving oven in the described baking step is the continous way stoving oven.
Because the technology of usability optical cement is simple, economic, practical, and film speed is fast, half tone is durable in use, and striping is easy, and anti-dissolubility is good, and described sensitive materials is photoresists.
The ceramic glaze art toughened glass for furniture that the manufacture method of above-mentioned ceramic glaze art toughened glass for furniture is made.
The invention has the beneficial effects as follows: method of the present invention is used inorganic high-temp lead-free ceramics muffle painting printing ink, can be in the annealing furnace of 700 ℃ of high temperature sintering, after the oxidation film layer molecule commissure of muffle painting and glass, the degree of depth combination, make the surface of glass form the very high colored glaze of one deck hardness, do not come off, do not have aging, will never fade, its intensity is higher, impact resistance is about 20 times of simple glass, and does not have radiation, environmental protection and economy.
Description of drawings
Accompanying drawing is a steps flow chart synoptic diagram of the present invention.
Embodiment
The present invention will be further described in detail below in conjunction with specific embodiment.
As shown in drawings, the present invention is made up of silk screen printing 1, oven dry 2 and annealing furnace high temperature sintering 3 steps.
Wherein, silk screen printing 1 comprises following steps:
(1) make film substrate, press the good original copy of composition, image and Color Scheme of decoration painting, the film substrate of making forms comparatively complicated patterns after making product print.
(2) film substrate is placed on the sensitization table top, film substrate face is attached to the printing surface (convex surface) of silk screen, be placed on exposure in the vacuum exposure machine then.Time shutter decides according to the thickness of photoresists and the energy of exposure lamp and the requirement of made half tone, generally will measure the time shutter by the phototimer slide rule before use, and then the time shutter of fixing made half tone.
(3) silk screen is stretched tight, the net that stretches tight is silk screen to be tightened and is fixed on the screen frame with the support as the silk screen printing pattern, after the silk screen that stretches tight on the net machine that stretches tight is spread sensitive materials, is being made into screen printing forme on the sensitization platform after sensitization in 30 minutes.
Silk screen kind on the market is a lot of at present,, considers from cost and suitability aspect generally that nylon mesh is for using the most general silk screen kind as silk silk screen, nylon mesh, terylene silk net, wire cloth etc.
The more sensitive materials of usefulness has two kinds on the market at present, and a kind of is photoresists, and a kind of then is sensitive film.Because usability optical cement technology is simple, economic, practical, and film speed is fast, half tone is durable in use, and striping is easy, and anti-dissolubility is good; And consider the different sorts printing ink that version film that sensitive materials forms should be fitted performance requriements, pressrun, bear the suitable number of times of sdueegee scrape pressures, with the bonding force of silk screen, do not produce the demoulding fault when printing, easily peel off, be beneficial to the factors such as regeneration of silk screen plate, the present invention selects for use photoresists as sensitive materials.
(4) screen printing forme is placed on the screen process press, puts into inorganic high-temp lead-free ceramics muffle painting ink printing; The selection that printing ink uses should be considered the characteristic of four aspects of printing ink: 1, optical index: as wavelength, L*a*b* and Yxy color value, spectrum induction curve, whiteness, gloss and the density of main color; 2, rheology index: such as plasticity, relative viscosity, thixotropy index, yield value, China ink silk weak point degree, pseudo-plasticity/thixotropy description, levels of adhesion and thermal viscosity stability; 3, solidify index: comprise curing speed and energy scale (concerning UV printing ink, comprise and recommend consumption, wattage, high-absorbable energy and the characteristics of luminescence); 4, physical attribute: the abrasive property under the particular viscosity, specific gravity, tackiness, wear resistance, flexible, surface tension, curing critical surface tension, critical amount of pigment.Organic printing ink is used in general low temperature spraying baking finish, for example paint, oil colour etc., because the characteristic of organic printing ink, it cannot enter and carry out sintering in the annealing furnace, makes that the glass properties of making is relatively poor.
Oven dry 2 is put into stoving oven with the glass that prints exactly, and oven dry is 5 minutes under 180 ℃ of high temperature; In order to reach the effect of oven dry better, stoving oven is the continous way stoving oven.
Annealing furnace high temperature sintering 3 is that the glass of oven dry is put into glass tempering furnace, and sintering is 20 minutes under 700 ℃ of high temperature.Use inorganic high-temp lead-free ceramics muffle painting printing ink, can be in the annealing furnace of 700 ℃ of high temperature sintering, after the oxidation film layer molecule commissure of muffle painting and glass, the degree of depth combination, make the surface of glass form the very high colored glaze of one deck hardness, do not come off, do not have aging, will never fade, its intensity is higher, impact resistance is about 20 times of simple glass, and does not have radiation, environmental protection and economy.
The color of the toughened glass that making method of the present invention is made can freely design, and can be colors such as blue and white, ancient bronze modelled after an antique, grouan, and its art and stereoscopic sensation are stronger.The toughened glass that making method of the present invention is made is ageing-resistant, do not have radiation, can be used as Jia Furniture, finishing material, has characteristics such as practical and attractive, bright and clean.
The foregoing description does not limit the present invention in any way, and every employing is equal to replaces or technical scheme that the mode of equivalent transformation obtains all drops in protection scope of the present invention.
Claims (4)
1, a kind of manufacture method of ceramic glaze art toughened glass for furniture is characterized in that comprising following step:
A, silk screen printing (1), it comprises following steps: (1) makes film substrate; (2) film substrate is placed on the sensitization table top; (3) will after spreading sensitive materials, the silk screen that stretches tight on the net machine that stretches tight after sensitization in 30 minutes, be made into screen printing forme on the sensitization platform; (4) screen printing forme is placed on the screen process press, puts into inorganic high-temp lead-free ceramics muffle painting ink printing;
B, oven dry (2): the glass that prints is put into stoving oven, and oven dry is 5 minutes under 180 ℃ of high temperature;
C, annealing furnace high temperature sintering (3): the glass of oven dry is put into glass tempering furnace, and sintering is 20 minutes under 700 ℃ of high temperature.
2, the manufacture method of ceramic glaze art toughened glass for furniture according to claim 1 is characterized in that: the stoving oven in described oven dry (2) step is the continous way stoving oven.
3, the manufacture method of ceramic glaze art toughened glass for furniture according to claim 1 is characterized in that: described sensitive materials is photoresists.
4, a kind of ceramic glaze art toughened glass for furniture of making according to the manufacture method of claim 1,2 or 3 described ceramic glaze art toughened glass for furniture.