CN101602489A - The method for preparing chlorinated lime and Calcium Chloride Powder Anhydrous with hydrated lime to treat chlorine water - Google Patents
The method for preparing chlorinated lime and Calcium Chloride Powder Anhydrous with hydrated lime to treat chlorine water Download PDFInfo
- Publication number
- CN101602489A CN101602489A CNA2009100375603A CN200910037560A CN101602489A CN 101602489 A CN101602489 A CN 101602489A CN A2009100375603 A CNA2009100375603 A CN A2009100375603A CN 200910037560 A CN200910037560 A CN 200910037560A CN 101602489 A CN101602489 A CN 101602489A
- Authority
- CN
- China
- Prior art keywords
- lime
- calcium chloride
- chloride powder
- chlorine water
- chlorine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the method for preparing chlorinated lime and Calcium Chloride Powder Anhydrous with hydrated lime to treat chlorine water, its main technical schemes is to utilize the chlorine water of white lime and chlorine industry to carry out chemical reaction slowly, suction filtration obtains filter cake and is fooling dry grinding to obtain the chlorinated lime finished product, and filtrate obtains the Calcium Chloride Powder Anhydrous finished product through underpressure distillation.When the present invention has thoroughly eliminated the useless chlorine water of chlorine industry and pollutes, can also create certain economic benefits for enterprise.
Description
Technical field:
The invention belongs to the technical field that three industrial wastes are handled, particularly prepare the method for chlorinated lime and Calcium Chloride Powder Anhydrous with hydrated lime to treat chlorine water.
Technical background:
At present, the chlorine water disposal of three wastes of chlor-alkali plant mainly neutralizes by alkaline matter, generally is to adopt carbide slag or white lime to neutralize to become Losantin and calcium chloride is directly drained.Administer completely, alleviated pollution though removed chlorine and chlorine root and hypochlorous acid and hypochlorite,, pollution substance still exists.The present invention can solve all objectionable impuritiess in chlorine water the inside completely, and makes it to turn waste into wealth and become Chemicals, has not only thoroughly eliminated source of pollution but also created economic worth.
Summary of the invention:
The purpose of this invention is to provide and a kind ofly prepared the method for chlorinated lime and Calcium Chloride Powder Anhydrous, thoroughly effectively administered the pollution of the chlorine water of chlor-alkali plant, can also create economic worth for enterprise with hydrated lime to treat chlorine water.
In order to realize above-mentioned purpose, two portions were about technical scheme of the present invention was divided:
The top technical scheme is:
With content is that 85-95% white lime (8) calcium hydroxide and unglazed chlorine water (9) are mixed in the treater (1) according to mass ratio 1: 10-20, carries out long-time 2-3 hour slow stirring reaction, till reaction liquid no chlorine root of check and hypochlorite.Add white lime until complete reaction if will continue in addition.
The lower section technical scheme is:
Carry out suction filtration to above-mentioned reaction solution this moment, the filter cake that suction filtration (2) obtains is a Losantin, drying (4) is pulverized (6) becomes the Losantin finished product, filtrate is that calcium chloride dihydrate obtains the Calcium Chloride Powder Anhydrous finished product through the dark distillation of decompression (3) through condensation (5), and it is for sale to enter finishing room (7) more respectively.
The chemical principle of its technical scheme is:
Ca(OH)
2+HClO＝＝CaClO+H
2O
Ca(OH)
2+Cl
2＝＝CaCl
2+H
2O
Description of drawings:
Accompanying drawing is a process flow diagram of the present invention, wherein
1---treater, 2---suction filter pump, 3---the underpressure distillation device, 4---moisture eliminator, 5---condenser, 6---pulverizer, 7---finishing room, 8---white lime drops into line, and 9---chlorine water drops into line.
Concrete embodiment:
Embodiment one: (unglazed chlorine water contains hypochlorous acid 1.2%; Contain chlorine 0.3%)
With 500 kilograms of content is that 90% white lime (8) calcium hydroxide and unglazed chlorine water (9) are mixed in the treater (1) according to mass ratio at 1: 15, carries out long-time 2-3 hour slow stirring reaction, till reaction liquid no chlorine root of check and hypochlorite.Add white lime until complete reaction if will continue in addition.
Carry out suction filtration to above-mentioned reaction solution this moment, the filter cake that suction filtration (2) obtains is a Losantin, drying (4) is pulverized (6) and is obtained 110.34 kilograms Losantin finished product, filtrate is that calcium chloride dihydrate obtains 31.66 kilograms Calcium Chloride Powder Anhydrous finished product through the dark distillation of decompression (3) through condensation (5), and it is for sale to enter finishing room (7) more respectively.
Claims (5)
1 one kinds of methods that prepare chlorinated lime and Calcium Chloride Powder Anhydrous with hydrated lime to treat chlorine water, obtain filter cake and filtrate and form through deep processing again by white lime and chlorine water reaction suction filtration, it is characterized in that white lime respectively with the hypochlorous acid and the chlorine reaction of chlorine water the inside, when obtaining chlorinated lime, go back the by-product Calcium Chloride Powder Anhydrous.
2 claims 1 are described a kind ofly to prepare the method for chlorinated lime and Calcium Chloride Powder Anhydrous with hydrated lime to treat chlorine water, it is characterized in that white lime respectively with the hypochlorous acid and the chlorine reaction of chlorine water the inside, when obtaining chlorinated lime, go back the by-product Calcium Chloride Powder Anhydrous.Its concrete technical scheme is divided two portions composition up and down: wherein the concrete technical matters process in top is:
With content is that 85-95% white lime (8) calcium hydroxide and unglazed chlorine water (9) are mixed in the treater (1) according to mass ratio 1: 10-20, carries out long-time 2-3 hour slow stirring reaction, till reaction liquid no chlorine root of check and hypochlorite.Add white lime until complete reaction if will continue in addition.
3 claims 1 and 2 describedly a kind ofly prepare the method for chlorinated lime and Calcium Chloride Powder Anhydrous with hydrated lime to treat chlorine water, it is characterized in that white lime respectively with the hypochlorous acid and the chlorine reaction of chlorine water the inside, when obtaining chlorinated lime, go back the by-product Calcium Chloride Powder Anhydrous.Its concrete technical scheme is divided two portions composition up and down: the concrete technical matters process of its lower middle portion is:
Carry out suction filtration to above-mentioned reaction solution this moment, the filter cake that suction filtration (2) obtains is a Losantin, drying (4) is pulverized (6) becomes the Losantin finished product, filtrate is that calcium chloride dihydrate obtains the Calcium Chloride Powder Anhydrous finished product through the dark distillation of decompression (3) through condensation (5), and it is for sale to enter finishing room (7) more respectively.
The described a kind of method for preparing chlorinated lime and Calcium Chloride Powder Anhydrous with hydrated lime to treat chlorine water of 4 claims 2, it is characterized in that with content being that 85-95% white lime (8) calcium hydroxide and unglazed chlorine water (9) are mixed in the treater (1) according to mass ratio 1: 10-20, carry out long-time 2-3 hour slow stirring reaction, till reaction liquid no chlorine root of check and hypochlorite.Add white lime until complete reaction if will continue in addition.
5 claims 2 and 3 described a kind of methods that prepare chlorinated lime and Calcium Chloride Powder Anhydrous with hydrated lime to treat chlorine water, it is characterized in that this moment above-mentioned reaction solution being carried out suction filtration, the filter cake that suction filtration (2) obtains is a Losantin, drying (4) is pulverized (6) becomes the Losantin finished product, filtrate is that calcium chloride dihydrate obtains the Calcium Chloride Powder Anhydrous finished product through the dark distillation of decompression (3) through condensation (5), and it is for sale to enter finishing room (7) more respectively.