CN101596593A - Petroleum bit matrix powder - Google Patents
Petroleum bit matrix powder Download PDFInfo
- Publication number
- CN101596593A CN101596593A CNA2009100596818A CN200910059681A CN101596593A CN 101596593 A CN101596593 A CN 101596593A CN A2009100596818 A CNA2009100596818 A CN A2009100596818A CN 200910059681 A CN200910059681 A CN 200910059681A CN 101596593 A CN101596593 A CN 101596593A
- Authority
- CN
- China
- Prior art keywords
- powder
- content
- nickel
- bit matrix
- particle size
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of petroleum bit matrix powder, it is characterized in that, mainly be made up of the material of following percentage by weight: cast tungsten carbide powder, granularity are 65～400 orders, 25～75%; Alloy tungsten-carbide powder, granularity are 65～400 orders, 10～60%; Nickel-base alloy powder, granularity are 100～325 orders 10～40%; Nickel powder, granularity are 5～15 microns, 2%～8%.Mechanical property detection by the prepared carcass powder of the present invention shows that not only its bending strength performance has improved 30～40% than traditional carcass powder, and the impact flexibility of carcass has improved 3～4 times than traditional carcass powder.Simultaneously, the wearability of prepared carcass powder and erosive wear resistance have improved 5～10% than traditional carcass powder.
Description
Technical field
The present invention relates to a kind of drill bit metallurgical material, specifically be meant a kind of petroleum bit matrix powder that is used to make oil bit.
Background technology
In the oil drilling in modern times, the oil diamond bit has been used as the main recommended products of drilling bit with the high advantage of its drilling efficiency.Along with further developing of petroleum drilling technology, petroleum drilling engineering also proposes higher performance requirement to diamond bit at present, as when requiring drilling well its rate of penetration faster, under the prerequisite of the wearability of guarantee fund's diamond bit own, also further require the cutting wing of diamond bit darker, thinner.Also require simultaneously can effectively cool off at the cutting teeth of high-speed cutting work, and the landwaste of cutting energy rapid drainage etc.But, the carcass powder of present diamond bit is just formed by conventional cast tungsten carbide and the nickel powder system of mixing, the surface quality of its carcass and smooth degree are not high, and also have pore and defective such as loose, therefore make these diamond bits can not well satisfy present actual demand.Therefore, develop a kind of new petroleum bit matrix powder, making its drill bit that is made into can satisfy present various high performance requirements fully is problems that those skilled in the art very urgently solve.
Summary of the invention
The preparation that the objective of the invention is to overcome the carcass powder of present diamond bit is can not the existing drill bit rate of penetration of fine solution fast, the cutting wing is dark, thin, and cutting teeth can not effectively cool off can not rapid drainage with landwaste defective, provide a kind of not only constituent simple, and can be fine satisfy above-mentioned requirements petroleum bit matrix powder.
Purpose of the present invention is achieved through the following technical solutions: petroleum bit matrix powder, mainly form by the material of following percentage by weight,
Cast tungsten carbide powder granularity is 65～400 orders 25～75%,
Alloy tungsten-carbide powder granularity is 65～400 orders 10～60%,
The nickel-base alloy powder granularity is 100～325 orders 10～40%,
The nickel powder granularity is 5～15 micron 2%～8%.
In order better to realize the present invention, the content of described cast tungsten carbide powder is 30～55%, and the content of alloy tungsten-carbide powder is 25～40%, and the content of nickel-base alloy powder is 15～35%, and the content of nickel powder is 3～6%.
The content of described cast tungsten carbide powder is 35～40%, and the content of alloy tungsten-carbide powder is 30～35%, and the content of nickel-base alloy powder is 25～30%, and the content of nickel powder is 3～4%.
The content of described cast tungsten carbide powder is 40～45%, and the content of alloy tungsten-carbide powder is 35～40%, and the content of nickel-base alloy powder is 15～20%, and the content of nickel powder is 4～5.5%.
The content of described cast tungsten carbide powder is 35%, and the content of alloy tungsten-carbide powder is 32%, and the content of nickel-base alloy powder is 29.5%, and the content of nickel powder is 3.5%; Or the content of described cast tungsten carbide powder is 43%, and the content of alloy tungsten-carbide powder is 37%, and the content of nickel-base alloy powder is 15%, and the content of nickel powder is 5%.
The present invention compared with prior art has following advantage and beneficial effect:
(1) bending strength according to the diamond bit matrix powder that makes after traditional component and the percentage by weight mixing only is 550～600MPa, impact flexibility is 2.0～2.5J, and the bending strength of the bit matrix powder that makes after mixing according to component of the present invention and percentage by weight can reach 780～880MPa, impact flexibility even up to 9～11J.Therefore the more traditional diamond bit matrix powder of the present invention is compared, its mechanical property improves a lot, its bending strength performance has improved 30～40% than traditional diamond bit matrix powder, and impact flexibility has improved 3～4 times than traditional diamond bit matrix powder.
(2) with equal pressure with under with equidistant condition, the carcass that traditional diamond drill bit matrix and the present invention are made carries out comparing behind the sandblast 3min, traditional diamond drill bit matrix sheet erosion depth ratio carcass of the present invention surface is dark 6%, and it is wide by 10% that the erosion area is received on traditional diamond drill bit matrix surface ratio carcass of the present invention surface.Therefore, wearability and the abrasion-resistance according to the more traditional diamond drill bit matrix of the carcass that makes after component of the present invention and the percentage by weight mixing improved 5～10%.
(3) according to the carcass that makes after said components of the present invention and the percentage by weight mixing, all more traditional carcass of its surface quality and smooth degree improves a lot, and does not exist pore to reach defectives such as loose, therefore is well positioned to meet present various high performance requirements.
The specific embodiment
The present invention is described in further detail below in conjunction with embodiment, but embodiments of the present invention are not limited thereto.
Embodiment 1
With this petroleum bit matrix powder of preparation 100g is example, and next the present invention will be described.During preparation, taking by weighing particle size range is 65～400 purpose cast tungsten carbide powder 25g, and particle size range is 65～400 purpose alloy tungsten carbide 53g, and particle size range is 100～325 purpose nickel-base alloy powder 20g, and particle size range is 5～15 microns nickel powder 2g.
Embodiment 2
During this petroleum bit matrix powder of preparation 100g, taking by weighing particle size range is 65～400 purpose cast tungsten carbide powder 75g, particle size range is 65～400 purpose alloy tungsten carbide 10g, and particle size range is 100～325 purpose nickel-base alloy powder 10g, and particle size range is 5～15 microns nickel powder 5g.
Embodiment 3
During this petroleum bit matrix powder of preparation 100g, taking by weighing particle size range is 65～400 purpose cast tungsten carbide powder 30g, particle size range is 65～400 purpose alloy tungsten carbide 30g, and particle size range is 100～325 purpose nickel-base alloy powder 35g, and particle size range is 5～15 microns nickel powder 5g.
Embodiment 4
During this petroleum bit matrix powder of preparation 100g, taking by weighing particle size range is 65～400 purpose cast tungsten carbide powder 55g, particle size range is 65～400 purpose alloy tungsten carbide 25g, and particle size range is 100～325 purpose nickel-base alloy powder 15g, and particle size range is 5～15 microns nickel powder 5g.
Embodiment 5
During this petroleum bit matrix powder of preparation 100g, taking by weighing particle size range is 65～400 purpose cast tungsten carbide powder 35g, particle size range is 65～400 purpose alloy tungsten carbide 35g, and particle size range is 100～325 purpose nickel-base alloy powder 27g, and particle size range is 5～15 microns nickel powder 3g.
Embodiment 6
During this petroleum bit matrix powder of preparation 100g, taking by weighing particle size range is 65～400 purpose cast tungsten carbide powder 40g, particle size range is 65～400 purpose alloy tungsten carbide 30g, and particle size range is 100～325 purpose nickel-base alloy powder 26g, and particle size range is 5～15 microns nickel powder 4g.
Embodiment 7
During this petroleum bit matrix powder of preparation 100g, taking by weighing particle size range is 65～400 purpose cast tungsten carbide powder 40g, particle size range is 65～400 purpose alloy tungsten carbide 40g, and particle size range is 100～325 purpose nickel-base alloy powder 15g, and particle size range is 5～15 microns nickel powder 5g.
Embodiment 8
During this petroleum bit matrix powder of preparation 100g, taking by weighing particle size range is 65～400 purpose cast tungsten carbide powder 45g, particle size range is 65～400 purpose alloy tungsten carbide 35g, and particle size range is 100～325 purpose nickel-base alloy powder 15g, and particle size range is 5～15 microns nickel powder 5g.
Embodiment 9
During this petroleum bit matrix powder of preparation 100g, taking by weighing particle size range is 65～400 purpose cast tungsten carbide powder 35g, particle size range is 65～400 purpose alloy tungsten carbide 32g, and particle size range is 100～325 purpose nickel-base alloy powder 29.5g, and particle size range is 5～15 microns nickel powder 3.5g.
Embodiment 10
During this petroleum bit matrix powder of preparation 100g, taking by weighing particle size range is 65～400 purpose cast tungsten carbide powder 43g, particle size range is 65～400 purpose alloy tungsten carbide 37g, and particle size range is 100～325 purpose nickel-base alloy powder 15g, and particle size range is 5～15 microns nickel powder 5g.
As mentioned above, just can well realize the present invention.
Claims (6)
1, petroleum bit matrix powder is characterized in that, mainly forms by the material of following percentage by weight,
Cast tungsten carbide powder granularity is 65～400 orders 25～75%,
Alloy tungsten-carbide powder granularity is 65～400 orders 10～60%,
The nickel-base alloy powder granularity is 100～325 orders 10～40%,
The nickel powder granularity is 5～15 micron 2%～8%.
2, petroleum bit matrix powder according to claim 1, it is characterized in that the content of described cast tungsten carbide powder is 30～55%, the content of alloy tungsten-carbide powder is 25～40%, the content of nickel-base alloy powder is 15～35%, and the content of nickel powder is 3～6%.
3, petroleum bit matrix powder according to claim 1, it is characterized in that the content of described cast tungsten carbide powder is 35～40%, the content of alloy tungsten-carbide powder is 30～35%, the content of nickel-base alloy powder is 25～30%, and the content of nickel powder is 3～4%.
4, petroleum bit matrix powder according to claim 1, it is characterized in that the content of described cast tungsten carbide powder is 40～45%, the content of alloy tungsten-carbide powder is 35～40%, the content of nickel-base alloy powder is 15～20%, and the content of nickel powder is 4～5.5%.
5, petroleum bit matrix powder according to claim 1 is characterized in that, the content of described cast tungsten carbide powder is 35%, and the content of alloy tungsten-carbide powder is 32%, and the content of nickel-base alloy powder is 29.5%, and the content of nickel powder is 3.5%.
6, petroleum bit matrix powder according to claim 1 is characterized in that, the content of described cast tungsten carbide powder is 43%, and the content of alloy tungsten-carbide powder is 37%, and the content of nickel-base alloy powder is 15%, and the content of nickel powder is 5%.