CN101590571A - 基于自愈合机制的激光金属直接成形实验方法 - Google Patents

基于自愈合机制的激光金属直接成形实验方法 Download PDF

Info

Publication number
CN101590571A
CN101590571A CN 200910022659 CN200910022659A CN101590571A CN 101590571 A CN101590571 A CN 101590571A CN 200910022659 CN200910022659 CN 200910022659 CN 200910022659 A CN200910022659 A CN 200910022659A CN 101590571 A CN101590571 A CN 101590571A
Authority
CN
China
Prior art keywords
powder
forming
defocusing amount
self
focus
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200910022659
Other languages
English (en)
Other versions
CN101590571B (zh
Inventor
张安峰
李涤尘
皮刚
张利锋
朱刚贤
卢秉恒
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xian Jiaotong University
Original Assignee
Xian Jiaotong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xian Jiaotong University filed Critical Xian Jiaotong University
Priority to CN 200910022659 priority Critical patent/CN101590571B/zh
Publication of CN101590571A publication Critical patent/CN101590571A/zh
Application granted granted Critical
Publication of CN101590571B publication Critical patent/CN101590571B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种基于自愈合机制的激光金属直接成形实验方法，采用相同基本工艺参数，分别在不同粉末离焦量情况下进行激光单道金属成形实验，得到不同粉末离焦量情况下单道金属成形截面厚度的变化规律。分析该规律得到粉末负离焦情况下存在一种自愈合机制，随着成形的进行能自动消除成形过程中因工艺不稳定而产生的成形面凹凸不平现象，保证成形过程的稳定进行。运用粉末负离焦所产生的自愈合效应，能够在开环控制系统下实现复杂薄壁零件的高质量堆积成形。

Description

基于自愈合机制的激光金属直接成形实验方法
技术领域
本发明涉及一种适用于激光金属直接成形制造、激光表面熔覆和易损零部件的激光修复等方法，特别涉及一种基于自愈合机制的激光金属直接成形实验方法。
背景技术
激光金属直接成形技术融合了快速成形技术和激光熔覆技术，以“离散-堆积”成形原理为基础。首先在计算机中生成最终功能零件的三维模型；然后将零件的三维数据信息转换为一系列的二维轮廓几何信息，层面几何信息融合成形参数生成扫描路径数控代码，控制成形系统采用同步送料激光熔覆的方法按照轮廓轨迹逐层扫描堆积材料；最终形成三维实体零件或仅需进行少量加工的近形件。激光金属直接成形除了具有与快速原型技术相同的特点之外，还具有一些独特的优点：(1)制造速度快，节省材料，降低成本；(2)不需采用模具，使得制造成本降低15％～30％，生产周期节省40％～70％；(3)可以生产用传统方法难于生产甚至不能生产的形状复杂的零件；(4)可在零件不同部位形成不同成分和组织的梯度功能材料结构；(5)金属零件完全致密、组织细小，力学性能超过锻件，近成形件可直接使用或者仅需少量的后续机加工便可使用。由于具有以上优点，激光金属直接成形技术逐渐成为先进制造技术研究的热点，并在航空航天、汽车船舶和武器装备等领域得到广泛应用。然而，由于成形工艺条件复杂，熔池形状受基材与粉末合金物理化学性能、激光成形工艺参数等诸多因素的影响，随着激光成形高度的逐层增加，成形表面会产生凹凸不平现象，并具有累积效应。在开环控制系统下，多层堆积后会因为凹凸累积出现严重锯齿状而无法继续堆积。调节工艺参数(改变Z轴增量)能解决该问题，但同时又引入了成形零件高度不可预测等新的问题；引入闭环控制能有效解决该问题，但却增加了系统复杂程度，同时增大成本，操作也不方便。
发明内容
本发明的目的是提供一种基于自愈合机制的激光金属直接成形实验方法，该方法可以消除激光金属直接制造零件时，产生的成形表面凹凸不平现象，使成形过程能平稳进行。
为了达到以上目的，本发明是采取如下技术方案予以实现的：
一种基于自愈合机制的激光金属直接成形实验方法，包括以下步骤：
(1)设定基本工艺参数为：激光光斑直径为0.5mm，扫描速度为6mm/s，送粉量为8.8g/min，载气量为8L/min；
(2)采用相同的基本工艺参数，分别在不同粉末离焦量情况下进行激光金属成形实验，测量不同粉末离焦量情况下激光金属成形熔覆层厚度，得到粉末离焦量对熔覆层厚度影响规律为：粉末汇聚时，熔覆层厚度最大；粉末负离焦时，单层熔覆层厚度h随负离焦量增大而减小；粉末正离焦时，单层熔覆层厚度h随正离焦量增大而减小；
(3)分析粉末离焦量对熔覆层厚度影响规律，得到粉末在负离焦情况下，多层堆积存在自愈合效应，即成形面出现凸凹时，凹陷处负离焦量减小，下一层熔覆时熔覆层厚度会增大，凹陷被填平；凸起处负离焦量较大，下一层熔覆时，熔覆层厚度会减小，凸起处变平缓；
(4)根据步骤(3)粉末在负离焦情况下，多层堆积成形存在自愈合效应，选用粉末离焦量为负的工艺条件进行激光金属直接成形，从而实现自动愈合或消除成形过程中因工艺参数不稳定而出现的工件表面凹凸不平现象。
上述方案中，所述粉末离焦量参数定义如下：粉末汇聚点O距喷粉头出口为4mm，基板形成熔池处在XOY坐标系下纵坐标值为y，y＝0mm时粉末汇聚于基板；y＜0mm时为粉末负离焦；y＞0mm时为粉末正离焦；产生自愈合效应最强的粉末负离焦量为：y＝-1.5mm。所述激光金属成形包括单道激光金属成形或薄壁零件堆积成形。
本发明从粉末离焦的角度出发，进行了相应的成形工艺实验研究，得到了粉末负离焦情况下激光金属直接成形零件时的自愈合现象，并研究了在粉末负离焦的情况下成形零件的自愈合机制，成形过程中出现凸凹现象，凸起处粉末负离焦增大，下一层熔覆层厚度减小，凸起减小；而凹陷处粉末负离焦减小，下一层熔覆层厚度增大，凹陷被填平，而成形过程中始终存在自愈合效应，熔覆层表面凹凸不平能随着后续层的成形而得到消除，起到了稳定熔覆成形的目的。本发明能够在开环控制系统下，有效消除成形过程中出现的成形表面凹凸不平的现象，保证成行过程的稳定进行，有效控制成形零件高度。避免为获得稳定成形过程而引入的闭环控制，在保证成形精度的前提下，降低激光成形系统的成本，促进了激光金属直接制造的发展，具有非常重要的应用前景。
附图说明
图1是本发明方法的流程图。
图2是定义粉末正、负离焦的示意图。
图3是粉末离焦量与单层熔覆层厚度的关系曲线。
图4是激光金属直接成形自愈合机制的原理图。
图5是在粉末汇聚或正离焦情况下成形的单道多层薄壁零件照片(实施例1)。
图6是在粉末负离焦情况下成形的单道多层薄壁零件照片(实施例2)。
图7是在粉末负离焦1.5mm情况下成形的复杂薄壁零件照片(实施例3)。
具体实施方式
以下结合附图及实施例对本发明做进一步的详细说明。
图1是本发明成形实验方法的流程图，成形过程中基本工艺参数为：激光光斑直径为0.5mm，扫描速度为6mm/s，送粉量为8.8g/min，送气量为8L/min。金属成形的基材和熔覆粉末为316L、不锈钢或高温合金等材料。
如图2所示，不同粉末离焦定义如下：粉末汇聚点O距喷粉头出口为4mm，基板形成熔池处在XOY坐标系下纵坐标值为y，y＝0mm时粉末汇聚于基板，称其为粉末汇聚；y＜0mm时粉末到达基板时尚未汇聚，称其为粉末负离焦；y＞0mm时粉末尚未到达基板已经汇聚，称其为粉末正离焦；
(1)采用相同工艺参数，分别在不同粉末离焦量情况下进行激光单道金属成形实验，测量不同粉末离焦量情况下单道金属成形熔覆层厚度，得到粉末离焦量对熔覆层厚度影响规律如下：粉末汇聚(y＝0mm)时，熔覆层厚度最大；粉末负离焦(y＜0mm)时，单层熔覆层厚度随离负焦量增大(y减小)而减小；粉末正离焦时，单层熔覆层厚度随正离焦量增大(y增大)而减小(图3)。
(2)分析粉末离焦量对熔覆层厚度影响规律，得到在粉末负离焦情况下多层堆积存在自愈合机制。如图4所示，成形面出现凸凹时，凹陷处负离焦量减小(y2＞y)，下一层熔覆时熔覆层厚度会增大(h2＞h)，凹陷被填平；凸起处负离焦量增大(y1＜y)，下一层熔覆层厚度会减小(h1＜h)，凸起减小；自动愈合或消除成形过程中因工艺参数不稳定出现的凹凸现象，分析粉末离焦量对熔覆层厚度影响规律，得到相同工艺参数情况下，产生自愈合效应最强的粉末负离焦量为：y＝-1.5mm
若多层堆积出现凹凸现象，凹陷处粉末正离焦，下一层熔覆层厚度减小，凹陷越来越深；凸起处粉末负离焦，下一层熔覆层厚度减小，凸起得到控制，多层堆积后零件局部存在严重凹陷。在粉末正离焦时成形，若多层堆积出现凹凸现象，凹陷处粉末正离焦量增大，下一层熔覆层厚度减小，凹陷越来越深；凸起处粉末正离焦量减小，下一层熔覆层厚度增大，凸起更多，多层堆积后零件存在严重凹凸不平。
实施例1
采用粉末汇聚或正离焦工艺进行单道激光金属成形，堆积出零件成形表面凹凸不平，如图5所示。
实施例2
采用粉末负离焦工艺进行单道激光金属成形，与图5对比成形质量，堆积出的薄壁零件成形面很平整，如图6所示。
实施例3
采用粉末负离焦进行复杂零件激光金属直接成形；y＝-1.5mm，Z轴增量为0.08mm，堆积层数为100层，粉末负离焦时激光金属直接成形存在自愈合效应，能保证成行的稳定进行。
如图7所示，当粉末负离焦量为y＝-1.5mm，Z轴增量为0.08mm，堆积层数为530层，零件高度为42.6±0.03mm。实验得到薄壁零件，其成形表面相当平整。

Claims (3)

1、一种基于自愈合机制的激光金属直接成形实验方法，其特征在于，包括以下步骤：
(1)设定基本工艺参数为：激光光斑直径为0.5mm，扫描速度为6mm/s，送粉量为8.8g/min，载气量为8L/min；
(2)采用相同的基本工艺参数，分别在不同粉末离焦量情况下进行激光金属成形实验，测量不同粉末离焦量情况下激光金属成形熔覆层厚度，得到粉末离焦量对熔覆层厚度影响规律为：粉末汇聚时，熔覆层厚度最大；粉末负离焦时，熔覆层厚度h随负离焦量增大而减小；粉末正离焦时，熔覆层厚度h随正离焦量增大而减小；
(3)分析粉末离焦量对熔覆层厚度的影响规律，得到粉末在负离焦情况下，多层堆积存在自愈合效应，表现为成形面出现凸凹时，凹陷处负离焦量减小，下一层熔覆时熔覆层厚度会增大，凹陷被填平；凸起处负离焦量较大，下一层熔覆时，熔覆层厚度会减小，凸起处变平缓；
(4)根据步骤(3)粉末在负离焦情况下，多层堆积存在自愈合效应，选用粉末离焦量为负的工艺条件进行激光金属直接成形，从而实现自动愈合或消除成形过程中因工艺参数不稳定而出现的工件表面凹凸不平现象。
2、如权利要求1所述的基于自愈合机制的激光金属直接成形实验方法，其特征在于，所述粉末离焦量参数定义如下：粉末汇聚点O距喷粉头出口为4mm，基板形成熔池处在XOY坐标系下纵坐标值为y，y＝0mm时粉末汇聚于基板；y＜0mm时为粉末负离焦；y＞0mm时为粉末正离焦；产生自愈合效应最强的粉末负离焦量为：y＝-1.5mm。
3、如权利要求1所述的基于自愈合机制的激光金属直接成形实验方法，其特征在于，所述激光金属成形包括单道激光金属成形或薄壁零件堆积成形。
CN 200910022659 2009-05-22 2009-05-22 基于自愈合机制的激光金属直接成形实验方法 Expired - Fee Related CN101590571B (zh)