CN101585212A - A kind of preparation method of TZ-PSBSR thermal weld rubber plastic blend waterproof roll - Google Patents
A kind of preparation method of TZ-PSBSR thermal weld rubber plastic blend waterproof roll Download PDFInfo
- Publication number
- CN101585212A CN101585212A CNA200910020365XA CN200910020365A CN101585212A CN 101585212 A CN101585212 A CN 101585212A CN A200910020365X A CNA200910020365X A CN A200910020365XA CN 200910020365 A CN200910020365 A CN 200910020365A CN 101585212 A CN101585212 A CN 101585212A
- Authority
- CN
- China
- Prior art keywords
- rubber
- banburying
- waterproof roll
- plastic blend
- mills
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of TZ-PSBSR thermal weld rubber plastic blend waterproof roll, form by POE (7380), butadiene-styrene rubber (1502), SBS (1401), precipitated calcium carbonate, carbon black N330, modifier TP-10, DOP, sulphur, anti-aging agent RD, TMTD, antioxidant 4010, pressing formula rate adds all raw material in the banburying, the banburying time is 9min, the banburying temperature is 130-150 ℃, make it mixing evenly, blowing; Fall in 560 mills glue, be cooled to≤90 ℃ after following bar, through the rubber strainer impurity screening, in 450 mills, carry out thin-pass, mixing, mixingly descend bar after evenly.Extruder for shaping, the coiled material after the moulding vulcanizes under 160 ℃, 0.3MPa condition through 20 meters long continuous vulcanization jar, batches packing at last; Solve the bonding problem of rubber plastic blend waterproof roll, make it form whole watertight composition.
Description
Technical field
The present invention relates to a kind of architectural waterproof material, be specifically related to a kind of preparation method of TZ-PSBSR thermal weld rubber plastic blend waterproof roll.
Background technology
Present traditional haloflex rubber plastic blend waterproof roll, the adhesive that adopt bonding bonding with adhesive tape more, and such adhering method exists the coiled material overlap bonding not firm, is prone to cracking phenomena, influence the overall waterproof effect of coiled material, can not form whole watertight composition.And adhesive and adhesive tape can not with the same life-span of body coiled material.
Summary of the invention
The objective of the invention is to be, a kind of preparation method of TZ-PSBSR thermal weld rubber plastic blend waterproof roll is provided.
The technical solution used in the present invention is: a kind of preparation method of TZ-PSBSR thermal weld rubber plastic blend waterproof roll, be by POE (7380); butadiene-styrene rubber (1502); SBS (1401); precipitated calcium carbonate; carbon black N330; modifier TP-10; DOP; sulphur; anti-aging agent RD; TMTD; antioxidant 4010 is formed; POE (7380); butadiene-styrene rubber (1502); SBS (1401); precipitated calcium carbonate; carbon black N330; modifier TP-10; DOP; sulphur; anti-aging agent RD; TMTD; the weight ratio of antioxidant 4010 is 100: 100: 100: 320: 65: 2: 15: 3: 5: 5: 2.5; press formula rate all raw material is added in the banburying; the banburying time is 9min; the banburying temperature is 130-150 ℃; make it mixing evenly, blowing.Fall in 560 mills glue, be cooled to≤90 ℃ after following bar, through the rubber strainer impurity screening, in 450 mills, carry out thin-pass, mixing, mixingly descend bar after evenly.Extruder for shaping, the coiled material after the moulding vulcanizes under 160 ℃, 0.3MPa condition through 20 meters long continuous vulcanization jar, batches packing at last.
The invention has the beneficial effects as follows: solve the bonding problem of rubber plastic blend waterproof roll, make it form whole watertight composition.
Description of drawings
Fig. 1 is technological process of production figure of the present invention
The specific embodiment
A kind of preparation method of TZ-PSBSR thermal weld rubber plastic blend waterproof roll, be by POE (7380); butadiene-styrene rubber (1502); SBS (1401); precipitated calcium carbonate; carbon black N330; modifier TP-10; DOP; sulphur; anti-aging agent RD; TMTD; antioxidant 4010 is formed; POE (7380); butadiene-styrene rubber (1502); SBS (1401); precipitated calcium carbonate; carbon black N330; modifier TP-10; DOP; sulphur; anti-aging agent RD; TMTD; the weight ratio of antioxidant 4010 is 100: 100: 100: 320: 65: 2: 15: 3: 5: 5: 2.5; press formula rate all raw material is added in the banburying; the banburying time is 9min; the banburying temperature is 130-150 ℃; make it mixing evenly, blowing.Fall in 560 mills glue, be cooled to≤90 ℃ after following bar, through the rubber strainer impurity screening, in 450 mills, carry out thin-pass, mixing, mixingly descend bar after evenly.Extruder for shaping, the coiled material after the moulding vulcanizes under 160 ℃, 0.3MPa condition through 20 meters long continuous vulcanization jar, batches packing at last.
This invention is adjusted by prescription, introduces the thermoplastic elastomer composition in prescription, and rubber plastic blend sulfuration coiled material is carried out modification, makes its high weldability that had both had thermoplastic elastomer, thermoplastification melting property.The characteristic that has blended rubber simultaneously, we just can at high temperature weld it like this, and the coiled material after the welding forms an integral body, have solved the bonding problem of rubber plastic blend waterproof roll, improved adhesive strength, made watertight composition form the watertight composition of an integral body.
Get EPDM rubber waterproof rolling material special bonding glue, EPDM rubber waterproof rolling material special glue adhesive tape, the rubber plastic blend waterproof roll is carried out adhesive test, heat-obtaining welding rubber plastic blend waterproof roll is done the thermal weld test.
Result's contrast:
| Test item | Bonded adhesives is bonding | Adhesive tape is bonding | Thermal weld rubber plastic blend waterproof roll | Sulfuration rubber plastic blend waterproof roll |
| Adhesive strength N/mm | 1.47 | 1.75 | Web break | |
| Hot strength MPa | 7.6 | 6.0 | ||
| Fracture elongation % | 568 | 400 | ||
| Impermeability 0.3MPa, 30min | Waterproof | Waterproof | ||
| Low temperature flexibility-30 ℃ | Flawless | Flawless |
Claims (1)
1, a kind of preparation method of TZ-PSBSR thermal weld rubber plastic blend waterproof roll, be by POE (7380); butadiene-styrene rubber (1502); SBS (1401); precipitated calcium carbonate; carbon black N330; modifier TP-10; DOP; sulphur; anti-aging agent RD; TMTD; antioxidant 4010 is formed; POE (7380) wherein; butadiene-styrene rubber (1502); SBS (1401); precipitated calcium carbonate; carbon black N330; modifier TP-10; DOP; sulphur; anti-aging agent RD; TMTD; the weight ratio of antioxidant 4010 is 100: 100: 100: 320: 65: 2: 15: 3: 5: 5: 2.5; it is characterized in that all raw material being added in the banburying; the banburying time is 9min; the banburying temperature is 130-150 ℃; make it mixing evenly, blowing by formula rate; Fall in 560 mills glue, be cooled to≤90 ℃ after following bar, through the rubber strainer impurity screening, in 450 mills, carry out thin-pass, mixing, mixingly descend bar after evenly.Extruder for shaping, the coiled material after the moulding vulcanizes under 160 ℃, 0.3MPa condition through 20 meters long continuous vulcanization jar, batches packing at last.