CN101579972A - Metallic transfer printing film - Google Patents
Metallic transfer printing film Download PDFInfo
- Publication number
- CN101579972A CN101579972A CNA2008100995226A CN200810099522A CN101579972A CN 101579972 A CN101579972 A CN 101579972A CN A2008100995226 A CNA2008100995226 A CN A2008100995226A CN 200810099522 A CN200810099522 A CN 200810099522A CN 101579972 A CN101579972 A CN 101579972A
- Authority
- CN
- China
- Prior art keywords
- layer
- transfer printing
- printing film
- metallic transfer
- protective layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a metallic transfer printing film which is provided with a first side and a second side and sequentially comprises an anti-after tack layer, a PET layer, a release layer, a protection layer, a resin layer, a metal layer and a glue layer from the first side to the second side, wherein the protection layer can be made of thermoplastic polyurethane (TPU), polythene (PE) or thermoplastic polyester elastomer (TPEE). Therefore, the metallic transfer printing film not only has convenient use but also has no toxicity.
Description
Technical field
The present invention is relevant with multilayer film, is meant a kind of metallic transfer printing film especially, and it is easy to use and do not contain the toxicity material.
Background technology
As shown in Figure 1, the visible aluminium transfer film 1 in market is in a PET film 2 surfaces coating in regular turn one release layer 3, a resin bed 4, an aluminium lamination 5 and a glue-line 6 at present, transfer film 1 can utilize thermal transfer mode that release layer 3, resin bed 4, aluminium lamination 5 are needed on leather or other flexible substrate surface together with glue-line 6, makes base material have metallic luster.
Because release layer 3, resin bed 4 and the only thick about 1000nm of aluminium lamination 5; easily come off because of scraped finish or dissolving; therefore, generally need aluminium lamination 5 surfaces after transfer printing to be coated with or to paste a protective layer (as PVC or PU film) again, to protect fragile aluminium lamination 5; therefore; needed for two road procedure beginnings can finish the transfer printing operation, comparatively inconvenience in the use, and PVC has toxicity; have the title of " malicious plastics ", suffered green group to appeal forbidding.
Summary of the invention
A purpose of the present invention is to provide a kind of metallic transfer printing film, and it is comparatively convenient on using, and does not contain toxicity.
For achieving the above object, metallic transfer printing film provided by the present invention has one first side and one second side, includes a pet layer, a protective layer and a metal level in regular turn by this first side to this second side.
Wherein, can establish a release layer between this pet layer and this protective layer, can establish a resin bed between this protective layer and this metal level, this first side can be established an anti-after tack layer and is overlying on this pet layer, and this second side can be established a glue-line and is overlying on this metal level; This protective layer can be made by thermoplastic polyurethane (TPU), polyethylene (PE) or thermoplastic polyester elastomer (TPEE).
Say further that again metallic transfer printing film provided by the invention has one first side and one second side, is included in regular turn by this first side to this second side:
One pet layer, a protective layer and a metal level.
Wherein, has a release layer between this pet layer and this protective layer.
Wherein, has a resin bed between this protective layer and this metal level.
Wherein, also including a glue-line is positioned at this second side and is overlying on this metal level.
Wherein, also including an anti-after tack layer is positioned at this first side and is overlying on this pet layer.
Wherein, this protective layer is made by thermoplastic polyurethane (TPU).
Wherein, this protective layer is made by polyethylene (PE).
Wherein, this protective layer is made by thermoplastic polyester elastomer (TPEE).
Thus, the use step of metallic transfer printing film provided by the present invention is simple, and not only convenience is splendid, and can avoid in the known technology adopting noxious material such as PVC, has the effect of environmental protection concurrently.
Description of drawings
Fig. 1 is the generalized section of known transfer film;
Fig. 2 is the generalized section of a preferred embodiment of the present invention;
Fig. 3 is the schematic diagram that applies of a preferred embodiment of the present invention;
Fig. 4 is the schematic diagram of a preferred embodiment of the present invention transfer printing finished product.
Primary clustering symbol description in the accompanying drawing:
1 aluminium transfer film
2 PET films
3 release layers
4 resin beds
5 aluminium laminations
6 glue-lines
10 metallic transfer printing films
11 first sides
12 second sides
14 anti-after tack layers
16 pet layers
18 release layers
20 protective layers
22 resin beds
24 metal levels
26 glue-lines
30 base materials
32 heated wheel
The specific embodiment
In order more to understand characteristics of the present invention place, act is described as follows with next preferred embodiment and conjunction with figs..
See also Fig. 2; the metallic transfer printing film 10 that a preferred embodiment of the present invention provided has one first side 11 and one second side 12, includes an anti-after tack layer 14, a pet layer 16, a release layer 18, a protective layer 20, a resin bed 22, a metal level 24 and a glue-line 26 in regular turn by this first side 11 to this second side 12.
Wherein, PET is the abbreviation of PET (Poly (ethylene terephthalate)), because this pet layer 16 has good toughness, as the base material of metallic transfer printing film 10, all the other each layers then cover thereon respectively in present embodiment.
This release layer 18 is made by acryl resin or fibre bundle resin, and it acts on and makes this protective layer 20 be easy to break away from this pet layer 16.
This protective layer 20 is by thermoplastic polyurethane (ThermoplasticPolyurethane in present embodiment; TPU) made; characteristic with anti-scratching wearproof; and can not suffer alcohol, acetone or go to steep the wet goods dissolution with solvents; except that above-mentioned TPU; also can adopt and be not limited to polyethylene (Polyethylene, PE), thermoplastic polyester elastomer (Thermoplastic polyester elastomer, TPEE) etc. make by material.
This anti-after tack layer 14 is to add silica flour in by U.S.'s resin of anti-ware the (Melamine Resin) to form in present embodiment, and main function is to avoid this protective layer 20 to be bonded together with this pet layer 16 in metallic transfer printing film 10 technologies; Wherein, the U.S. resin of anti-the ware can be substituted by melamine resin or other resin as the carrier of silica flour.
This resin bed 22 is made by amine resin, and it acts on this metal level 24 is combined with this protective layer 20.
This metal level 24 is an aluminium lamination in present embodiment, is covered in this resin bed 22 surfaces in the mode of evaporation, and wherein, aluminium also can be substituted by other metals like gold, silver or copper etc. according to need.
This glue-line 26 is that polyurethane resin (or claiming PU glue) is formed, and meets heat and has extremely strong stickiness.
When this metallic transfer printing film 10 is needed on leather or other base material 30; as shown in Figure 3; be that this metallic transfer printing film 10 is overlying on this base material 30; and contact with this base material 30 with this glue-line 26; then utilize 32 pairs of these metallic transfer printing films 10 of a heating plate or heated wheel to exert pressure; it is fusible and this metallic transfer printing film 10 and this base material 30 are combined that this glue-line 26 is heated; at last; this pet layer 16 is removed in the lump together with this anti-after tack layer 14; the function of this release layer 18 promptly removed operation and was easy to carry out making this moment; so; only surplus this glue-line 26; this metal level 24; this resin bed 22 and this protective layer 20 are covered on this base material 30 surfaces, and as shown in Figure 4, this metal level 24 makes these base material 30 surfaces have metallic luster; 20 of this protective layers can protect this metal level 24 not to be subjected to scraped finish or dissolving; thus, the use step of metallic transfer printing film 10 provided by the present invention is simple, and not only convenience is splendid; and can avoid adopting in the known technology noxious materials such as PVC, have the effect of environmental protection concurrently.
Based on spirit of the present invention, the structure of this metallic transfer printing film 10 can be changed design, for example: this glue-line 26 also can be established according to need and not, treat that metallic transfer printing film is covered in before the base material 30, in this base material 30 surfaces earlier coating one glue-lines also can, in addition, this anti-after tack layer, this release layer or this resin bed also can be established according to need and not, such as these easy full of beard and structural change, the claim scope that all should be the present patent application contains.
Claims (8)
1. a metallic transfer printing film has one first side and one second side, is included in regular turn by this first side to this second side:
One pet layer, a protective layer and a metal level.
2, metallic transfer printing film as claimed in claim 1 wherein, has a release layer between this pet layer and this protective layer.
3, metallic transfer printing film as claimed in claim 1 wherein, has a resin bed between this protective layer and this metal level.
4, metallic transfer printing film as claimed in claim 1 wherein, also includes a glue-line and is positioned at this second side and is overlying on this metal level.
5, metallic transfer printing film as claimed in claim 1 wherein, also includes an anti-after tack layer and is positioned at this first side and is overlying on this pet layer.
6, metallic transfer printing film as claimed in claim 1, wherein, this protective layer is made by thermoplastic polyurethane.
7, metallic transfer printing film as claimed in claim 1, wherein, this protective layer is made by polyethylene.
8, metallic transfer printing film as claimed in claim 1, wherein, this protective layer is made by thermoplastic polyester elastomer.