CN101574640B - Mineral micro powder lasting aldehyde and odor removing bag - Google Patents
Mineral micro powder lasting aldehyde and odor removing bag Download PDFInfo
- Publication number
- CN101574640B CN101574640B CN2008100964675A CN200810096467A CN101574640B CN 101574640 B CN101574640 B CN 101574640B CN 2008100964675 A CN2008100964675 A CN 2008100964675A CN 200810096467 A CN200810096467 A CN 200810096467A CN 101574640 B CN101574640 B CN 101574640B
- Authority
- CN
- China
- Prior art keywords
- micro powder
- mineral micro
- lasting
- aldehyde
- removal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a lasting aldehyde and odor removing bag with mineral micro powder which is a solid control product for removing air odor pollutions, i.e. formaldehyde, benzene, TVOC, and thelike which are generated due to decoration. The lasting aldehyde and odor removing bag with the mineral micro powder is formed in such a way that aldehyde and odor removing mineral micro powder is ma nufactured into swelling hollow beads (strips), and then the swelling hollow beads (strips) are respectively packaged into porous fibre bags. The swelling hollow beads (strips) are prepared from the follow four groups of components: 60-98 percent of mineral micro powder combined by one or several of meerschaum with the particle diameter of 500-2000 meshes, fluorspar, sodium bentonite, kaoline, diatomite, activated clay, tourmaline powder, white mica power, titanium pigment, expansion graphite, corundum, and the like, 1-40 percent of aldehyde and odor removing matters, 0.01-5 percent of bondingagent, and the balance of 5-15 percent of water. The lasting aldehyde and odor removing bag with the mineral micro powder can be conveniently and neatly placed at air pollution sources, thereby achie ving the purpose of lasting aldehyde and odor removal.
Description
Technical field:
Mineral micro powder lasting aldehydes removal, taste removal bag relate to the Pollution Control product of the solid of peculiar smell such as formaldehyde that a kind of removing produces because of decorations, benzene, TVOC.
Background technology:
Administer in the industry at indoor environmental pollution at present, use following several method usually: 1. use the method for activated carbon (carbon fiber) absorption, but because the ability of its absorbing formaldehyde is very limited, and easy saturated inefficacy.2. with the method for ozone or negative oxygen ion, the effect of improvement is ofer short duration, and ozone is excessive to be harmful to health again.3. cure the symptoms, not the disease with the method for air purifier, consumed power not only, more the renew cartridge cost is high again, and can't resolve lasting problem up to standard.4. the present ubiquity of method of " photocatalyst " improvement the unfavorable problem of actual regulation effect.5. most of at present aldehydes removal, taste removal products of still using liquid type.But exist one up to standard at that time, not up to standard later, the unabiding problem of regulation effect; It is not too convenient also to exist a fluid product construction, and volatility is big, influences the problem of health of people.So, expect a kind of flexible, the cheap and high adsorption capacity easy to use and don't little aldehydes removal, the taste removal product of volatility of saturated solid easily.Can combine with the liquid type product, reach the lasting purpose of regulation effect.This product is exactly to invent for this reason.
Summary of the invention:
Mineral micro powder lasting aldehydes removal, taste removal bag be a kind of be used for removing because of the solid of air smell pollutions such as formaldehyde that decorations produce, benzene, TVOC administer product.It is low that it has a cost, absorption affinity is strong, it is saturated to be difficult for, effect lasting, use more convenient flexibly, the characteristics of energy-conserving and environment-protective.
The objective of the invention is to realize by following technical solution:
It is that the mineral micro powder of aldehydes removal, taste removal is made expanded hollow bead (bar), and then is respectively charged into porous fibre bag packing and forms.Hollow bead (bar) has following four components to make:
1, is key component with the mineral micro powder at first, accounts for the 60-98% of total amount, and refine to 500-2000 order particle diameter.Mineral micro powder can be the one or more combination in sepiolite, fluorite, sodium bentonite, kaolin, diatomite, activated clay, tourmaline powder, white mica powder, titanium dioxide, expanded graphite, the corundum etc.
The component of 2, aldehydes removal, taste removal; Account for the 1-40% of total amount.Specifically be meant the one or more combination in the alkane ketone, amino acid hydrazides, amine, ammonium class of solid.
3, the component 0.01-5% of adhesive.Specifically be meant soluble starch, cellulose etc.
4, moisture 5-15%.Specifically be meant deionized water.
Material (2) and adhesive (3) with above-mentioned aldehydes removal, taste removal are dissolved in the deionized water (4), mix with mineral micro powder (the 1) dipping of refinement then, make expanded hollow bead (bar) with special equipment again.Making moisture through vacuum drying below 80 ℃ is 5-15%, can obtain the expanded hollow dried particles (bar) of mineral micro powder.When producing, can make one or more hollow beads (bar) according to the difference of aldehydes removal, taste removal material.With dried hollow bead (bar), be respectively charged into porous fibre bag inner packing and can obtain this invention product again.
The specific embodiment:
1, embodiment 1:
Take by weighing 1000 purpose sepiolites, 300 grams, sodium bentonite 300 grams, tourmaline powder 200 grams, 2-imidazolidinone 190 grams, cellulose 3 grams, deionized water 200-800 gram.It is standby earlier cellulose to be dissolved in deionized water, again the 2-imidazolidinone is dissolved in deionized water, mixes with the mineral micro powder dipping then, makes expanded hollow bead (bar) with special equipment again.Through vacuum drying below 80 ℃ (moisture is about about 7%), make dry hollow bead (bar).Be respectively charged into the sample 1 that porous fibre bag inner packing can obtain the invention product then.
2, embodiment 2:
Take by weighing 1000 purpose fluorites, 300 grams, diatomite 300 grams, white mica powder 200 grams, lysine 185 grams, soluble starch 5 grams, deionized water 200-800 gram.It is standby earlier soluble starch to be dissolved in deionized water, again lysine is dissolved in deionized water, mixes with the mineral micro powder dipping then, makes expanded hollow bead (bar) with special equipment again.Through vacuum drying below 80 ℃ (moisture is about about 10%), make dry hollow bead (bar).Be respectively charged into the sample 2 that porous fibre bag inner packing can obtain the invention product then.
3, embodiment 3:
Take by weighing 1000 purpose sepiolites, 200 grams, fluorite 150 grams, sodium bentonite 200 grams, diatomite 160 grams, corundum 150 grams, adipic dihydrazide 60 grams, urea 70 grams, cellulose 2 grams, deionized water 200-500 gram.It is standby earlier cellulose to be dissolved in deionized water, again adipic dihydrazide, urea are dissolved in deionized water, mix with the mineral micro powder dipping then, make expanded hollow bead (bar) with special equipment again, through vacuum drying below 80 ℃ (moisture is about about 8%), make dry hollow bead (bar).Be respectively charged into the sample 3 that porous fibre bag inner packing can obtain the invention product then.
Result of implementation
(the single face area is 25cm with the test plate (panel) of area from the thick medium-density plate intercepting of same 18mm for we
2, the two sides area amounts to 50cm
2) some, randomly draw five test specimens, and be numbered 1,2,3,4,5 as the formaldehyde source of release.Put into respectively then 1., 2., 3., 4., 5., put into the sample 1 heavy 50g that embodiment 1 obtains in the environment storehouse in 2. again with the simulated environment storehouse of the synthermal 40L with humidity of volume; The sample 2 heavy 50g that embodiment 2 obtains are put in the environment storehouse in 3.; The sample 3 heavy 50g that embodiment 3 obtains are put in the environment storehouse in 4.; The heavy 50g of certain famous brand name activated carbon meter is put in the environment storehouse in 5.; The test comparison result is as follows:
Concentration value in the following table is (mg/m
3).
The 40L case number (CN) | Test piece number | Test for the first time | Test for the second time | Test for the third time | The concentration value average | Adsorption rate | Remarks |
① | Test plate (panel) 1 | 0.31 | 0.39 | 0.47 | 0.39 | Blank | |
② | Test plate (panel) 2 | 0.10 | 0.09 | 0.08 | 0.09 | 77% | Sample 1,50g |
③ | Test plate (panel) 3 | 0.12 | 0.11 | 0.10 | 0.11 | 72% | Sample 2,50g |
④ | Test plate (panel) 4 | 0.13 | 0.14 | 0.15 | 0.14 | 64% | Sample 3,50g |
⑤ | Test plate (panel) 5 | 0.26 | 0..32 | 0.42 | 0.33 | 15% | Carbon, 50g |
Annotate: 1, adsorption rate=adsorbance ÷ total amount;
2, adsorbance=original content value-absorption back net concentration value
3, for the first time the survey time is behind the joint sealing the 3rd day, test in the tenth day for the second time, test in the 30 day is for the third time.
Claims (2)
1. a mineral micro powder lasting aldehydes removal, taste removal bag, the mineral micro powder of aldehydes removal, taste removal is made expanded hollow bead or strip, being respectively charged into porous fibre bag inner packing again forms, 1., the mineral micro powder of 500-2000 order particle diameter it is characterized in that: aldehydes removal wherein, the mineral micro powder of taste removal have following four components:, one or more the combination that it is selected from sepiolite, fluorite, sodium bentonite, kaolin, diatomite, activated clay, tourmaline powder, white mica powder, titanium dioxide, expanded graphite, the corundum accounts for the 60-98% of total amount; 2., the material of aldehydes removal, taste removal, account for the 1-40% of total amount; 3., adhesive, account for the 0.01-5% of total amount; 4., all the other are deionized water, account for the 5-15% of total amount; Four kinds of constituent content sums are 100%; Aldehydes removal wherein, taste removal material are meant the one or more combination in the alkane ketone, amino acid, hydrazides, amine, ammonium class of solid.
2. mineral micro powder lasting aldehydes removal according to claim 1, taste removal bag is characterized in that: described adhesive is soluble starch or cellulose.