CN101565531A - High-strength rigid polyvinyl chloride finned tube - Google Patents

High-strength rigid polyvinyl chloride finned tube Download PDF

Info

Publication number
CN101565531A
CN101565531A CNA2008100366366A CN200810036636A CN101565531A CN 101565531 A CN101565531 A CN 101565531A CN A2008100366366 A CNA2008100366366 A CN A2008100366366A CN 200810036636 A CN200810036636 A CN 200810036636A CN 101565531 A CN101565531 A CN 101565531A
Authority
CN
China
Prior art keywords
polyvinyl chloride
lubricant
stablizer
composition
finned tube
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100366366A
Other languages
Chinese (zh)
Inventor
崔杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI TIANYUAN GROUP SHENGDE PLASTICS CO Ltd
Original Assignee
SHANGHAI TIANYUAN GROUP SHENGDE PLASTICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI TIANYUAN GROUP SHENGDE PLASTICS CO Ltd filed Critical SHANGHAI TIANYUAN GROUP SHENGDE PLASTICS CO Ltd
Priority to CNA2008100366366A priority Critical patent/CN101565531A/en
Publication of CN101565531A publication Critical patent/CN101565531A/en
Pending legal-status Critical Current

Abstract

The invention relates to a high-strength rigid polyvinyl chloride finned tube which comprises the following components by weight part: polyvinyl chloride resin: 100 of major ingredient, polyacrylate copolymer: 4-6 of plasticiser, composite lead heat stabilizer: 4-8 of stabilizer, stearic acid: 0.1-0.6 of lubricant, calcium stearate: 0.1-0.5 of stabilizer and lubricant, filling agent: 25-50 of filling materials, and calcium carbonate: 25-50 of filling materials.

Description

High-strength rigid polyvinyl chloride finned tube
Technical field:
The present invention relates to rigid polyvinyl chloride finned tube, refer to a kind of high-strength rigid polyvinyl chloride finned tube especially.
Background technology:
Polychloroethylene pipes is a kind of kind of tube types that is most widely used in the existing market, and, easy construction simple, with low cost because of its processing obtains very high share of market.
China to last century the nineties begin to introduce advanced foreign technology and produce the bigbore ground draining polyvinyl chloride finned tube that buries, its cost performance with excellence has progressively replaced traditional cement pipe, steel pipes etc. are obtained good effect.
But along with the strictness of construction requirement and the requirement of some large-scale public works promote, original polyvinyl chloride finned tube anti-pressure ability can't satisfy construction requirement gradually.
Summary of the invention:
Technical problem to be solved by this invention just is to overcome deficiency of the prior art, a kind of high-strength polyvinyl chloride riffled tube is provided, the ring stiffness of this product can reach more than ten grades, surpasses eight grades of the highest rigidity of existing market, for the scope of having expanded is used in the extension of this tubing.
The invention provides a kind of high-strength polyvinyl chloride riffled tube, with listed as parts by weight, composition is:
Polyvinyl chloride (PVC) RESINS 100 major ingredients
Acrylate copolymer 4-6 softening agent
Lead salt composite thermal stabilizer 4-8 stablizer
Stearic acid 0.1-0.6 lubricant
Calcium stearate 0.1-0.5 stablizer, lubricant
Weighting agent 25-50 stopping composition
Lime carbonate 25-50 stopping composition.
Production method of the present invention adopts operational path commonly used, with the logical overheated machine of polyvinyl chloride resin and auxiliary agent mediate, cold machine stirs, plastify extrude, moulding, cutting, enlarging get final product.
The invention has the beneficial effects as follows:
By absorption, digestion, constantly test to advanced person's prescription, adjusted the type of functional agent, added novel weighting agent, material stiffness is got a promotion.Mould is transformed, made moulding product have higher compressive property.
Embodiment:
Tubing is pressed the ring stiffness grade separation, sees Table 1:
Table 1 nominal ring stiffness grade (unit: thousand Ns/square metre)
Figure A20081003663600051
The physical and mechanical property of tubing should meet the regulation of table 2.
Press the regulation of GB/T 9647-2003.Compression speed is determined ring stiffness by the external diameter of tubing.
Table 2 tubing physical and mechanical property index.
Figure A20081003663600052
Figure A20081003663600061
The test impact property:
Regulation by GB/T 14152-2001 is tested.The tup radius-of-curvature of dropping hammer is 50.0mm ± 0.5mm, and shock height is 2000mm ± 10mm, and test temperature is (0 ± 1) ℃, and other test parameter sees Table 5.
Table 3 shock resistance test parameter
Specified size DN/ID Every sample is answered the setting-out number The quality of dropping hammer, kg
150 8 1.0
225 14 2.5
300 20 3.2
400 20 3.2
500 20 3.2
600 20 3.2
800 20 3.2
1000 20 3.2
Observe the sample after impacting, any position is crack-free all, and the stress whitening that produces because of impacting is arranged.

Claims (4)

1. high-strength polyvinyl chloride riffled tube, with listed as parts by weight, composition is:
Polyvinyl chloride (PVC) RESINS 100 major ingredients,
Acrylate copolymer 4-6 softening agent,
Lead salt composite thermal stabilizer 4-8 stablizer,
Stearic acid 0.1-0.6 lubricant,
Calcium stearate 0.1-0.5 stablizer, lubricant,
Weighting agent 25-50 stopping composition,
Lime carbonate 25-50 stopping composition.
2, high-strength polyvinyl chloride riffled tube according to claim 1 is characterized in that, with listed as parts by weight, composition is:
Lead salt composite thermal stabilizer 4-6 stablizer,
Stearic acid 0.1-0.4 lubricant,
Calcium stearate 0.1-0.4 stablizer, lubricant,
All the other components unchanged.
3, high-strength polyvinyl chloride riffled tube according to claim 1 is characterized in that, with listed as parts by weight, composition is:
Lead salt composite thermal stabilizer 4-6 stablizer,
Stearic acid 0.3-0.4 lubricant,
Calcium stearate 0.2-0.4 stablizer, lubricant,
All the other components unchanged.
4, high-strength polyvinyl chloride riffled tube according to claim 1 is characterized in that, with listed as parts by weight, composition is:
Lead salt composite thermal stabilizer 5-8 stablizer,
Stearic acid 0.3-0.6 lubricant,
Calcium stearate 0.2-0.5 stablizer, lubricant,
Lime carbonate 25 stopping composition,
All the other components unchanged.
CNA2008100366366A 2008-04-25 2008-04-25 High-strength rigid polyvinyl chloride finned tube Pending CN101565531A (en)