CN101560061A - Method for preparing patterned polymer brush - Google Patents
Method for preparing patterned polymer brush Download PDFInfo
- Publication number
- CN101560061A CN101560061A CNA2009100521493A CN200910052149A CN101560061A CN 101560061 A CN101560061 A CN 101560061A CN A2009100521493 A CNA2009100521493 A CN A2009100521493A CN 200910052149 A CN200910052149 A CN 200910052149A CN 101560061 A CN101560061 A CN 101560061A
- Authority
- CN
- China
- Prior art keywords
- substrate
- polymer brush
- initiator
- patterned polymer
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method for preparing a patterned polymer brush, which belongs to the technical field of micro nano material preparation. The micron patterned polymer brush is obtained by fixing a thioxanthone photoinitiator containing coinitiator amine on the surface of a base material by covalent bond self-assembly technology, performing patterned photobleaching on the initiator through mask photoetching and performing photo-initiation monomer polymerization. The method is simple and effective, is suitable for large-scale preparation of various patterned polymer brushes, can prepare functional patterned polymer brushes and develops direction for potential application of the polymer brush.
Description
Technical field
The present invention relates to a kind of preparation method of patterned polymer brush.Belong to technical field of micro nano material preparation.
Background technology
The surface micronano patternization can realize artificially controlled to material surface character and structure becoming the previous ten minutes active research of order focus.The patternization of especially surperficial high molecular polymer has a wide range of applications in fields such as microelectronic industry, chemistry and bioanalysis, microfluid, photonic crystal and biochips.Polymkeric substance pattern method commonly used is vacuum ultraviolet (VUV) photetching technology (" the submicron order patterning on polymethyl methacrylate film surface ", " material Leader: a research piece of writing " the 23rd the 4th phase of volume of in April, 2009 (descending)).This technology has higher requirement to light transmission, the photosensitivity of polymkeric substance, and the hardness of polymkeric substance has very big influence to the stability of surface micro-structure, has limited the use of this method.And polymer brush surface stability height has obtained broad research, so researchdevelopment is simple effectively, extensively the polymer brush preparation method of suitable micro-nano patternization has great importance.
Summary of the invention
The objective of the invention is at the deficiencies in the prior art, provide a kind of simple effectively, preparation method that can the various patterned polymer brush of mass preparation.
For realizing this purpose, the present invention is fixed on substrate material surface by the thioxanthone photo initiator that the covalent linkage self-assembling technique will contain coinitiator amine, initiator is carried out the photobleaching of patternization by the mask photoetching.Trigger monomer polymerization then obtains the polymer brush of micron order pattern.
The detailed process that the present invention prepares patterned polymer brush is as follows:
1) substrate is carried out surface treatment.Substrate is placed on boil in the mixing solutions of the vitriol oil and hydrogen peroxide and handles 1-2h, the mass ratio of the vitriol oil and hydrogen peroxide is 7: 3 in the mixing solutions, then substrate is placed the ultrasonic 10-30min of acetone, use deionized water rinsing, oven dry at last, remove the organism and the impurity of substrate surface.
2) epoxy silane coupling agent self-assembly.The concentration that the substrate of cleaning oven dry is immersed 3-R-GLYCIDOL propoxy-Trimethoxy silane is to leave standstill 2h-24h in the toluene solution of 1-10mM, then with the substrate ultrasonic cleaning in toluene and acetone successively of taking out, dry, obtain the substrate of epoxy silane coupling agent self-assembly.
3) light trigger grafting.With the substrate immersion photoinitiator concentration of epoxy silane coupling agent self-assembly is in the chloroformic solution of 2-10mM, and 40 ℃ of heating of lucifuge 2-12h takes out back ultrasonic cleaning in chloroform, and oven dry obtains surperficial initiator grafted substrate; Described light trigger is the thioxanthone photo initiator that contains coinitiator amine.
4) mask photobleaching.Mask is covered surperficial initiator grafted substrate surface, place illumination 30-60 second under the ultraviolet lamp, obtain the substrate behind the surperficial initiator photobleaching.
5) polymer brush of light-initiated preparation patternization.It is the solution of 0.5-5M that substrate behind the surperficial initiator photobleaching is immersed monomer concentration, ultraviolet lighting after the logical nitrogen 30min deoxygenation, light application time 30min-5h; With substrate ultrasonic cleaning in toluene, chloroform, acetone or straight alcohol, dry after the reaction, obtain the polymer brush of micron order patternization.
Light trigger described in the present invention is DAB-16-TX, DAB-4-TX, DAB-64-TX or HPTX.
Described monomer is the monomer that can carry out light initiation polymerization, as methyl methacrylate (MMA), and N-isopropylacrylamide (NIPAM), glycidyl methacrylate (GMA) or the like.
It is simple to operate that the present invention prepares the method for patterned polymer brush, and the initiator grafting density is big, the fast efficient height of velocity of initiation.The pattern of the used mask of the present invention is varied, and is widely used in carrying out the monomer of light initiation polymerization.By causing functional monomer, can prepare graphical polymer brush to environment such as temperature, pH value sensitivity.And further polymer brush is carried out modification, and some biomolecules such as polysaccharide, polypeptide, protein are incorporated in the patterned polymer brush, can obtain having different bioactive surfaces in the micron order zone.These researchs lay the first stone for the micro-nano transmitter of preparation, biochip.
Description of drawings
Fig. 1 is the schema of the inventive method.
The PMMA patterned polymer brush figure that Fig. 2 obtains for example of the present invention.
The PNIPAM patterned polymer brush figure that Fig. 3 obtains for example of the present invention.
Embodiment
Below in conjunction with drawings and Examples technical scheme of the present invention is further described.Following examples are to further specify of the present invention, rather than limit the scope of the invention.
Fig. 1 is the schema of the inventive method.As shown in Figure 1, at first substrate (silicon chip or quartz plate) is cleaned and obtain the silicon hydroxyl surface, immerse then in the toluene solution of 3-R-GLYCIDOL propoxy-Trimethoxy silane.The silane coupling agent that contains methoxyl group reacts with the substrate surface hydroxyl, and self-assembly is in substrate surface.The silane coupling agent of flush away substrate surface absorption, initiator solution is immersed in the oven dry back, obtains initiator grafting individual layer behind 40 ℃ of heating of lucifuge 2-12h.The initiator of ultrasonic flush away individual layer surface adsorption, oven dry.Mask is covered initiator grafted substrate surface, place illumination 30-60 second under the ultraviolet lamp.Immerse monomer solution medium ultraviolet illumination 30min-5h then, obtain the polymer brush of patternization.
Embodiment 1
1, the processing of substrate
Handle 1h with being placed at the bottom of the silicon wafer-based to boil in the mixing solutions of the vitriol oil and hydrogen peroxide, the mass ratio of the vitriol oil and hydrogen peroxide is 7: 3 in the mixing solutions, then substrate is placed the ultrasonic 30min of acetone, use deionized water rinsing, oven dry at last, remove the organism and the impurity of substrate surface.
2, epoxy silane coupling agent self-assembly
Leave standstill 12h with cleaning in the toluene solution that the substrate immersion 3-R-GLYCIDOL propoxy-Trimethoxy silane concentration of drying is 5mM.With the substrate ultrasonic cleaning in toluene and acetone successively of taking out, dry then, obtain the silicon chip of epoxy silane coupling agent self-assembly.
3, initiator DAB-16-TX grafting
With the substrate immersion light trigger DAB-16-TX concentration of epoxy silane coupling agent self-assembly is in the chloroformic solution of 2mM, and 40 ℃ of heating of lucifuge 12h takes out back ultrasonic cleaning in chloroform, and oven dry obtains surperficial initiator grafted silicon chip.
4, mask photobleaching
Mask is covered surperficial initiator grafted substrate surface, placed under the ultraviolet lamp illumination 30 seconds.Obtain the substrate behind the surperficial initiator photobleaching.
5, light-initiated preparation patterned polymer brush
Substrate behind the surperficial initiator photobleaching is immersed the toluene solution of the MMA of monomer concentration 1M, ultraviolet lighting 1h after the logical nitrogen 30min deoxygenation, with substrate ultrasonic cleaning in toluene, chloroform, acetone or straight alcohol, dry after the reaction, obtain the PMMA polymer brush of patternization.
Figure 2 shows that the PMMA polymer brush of the patternization of 50 times of magnifications.
Embodiment 2
1, the processing of substrate
Handle 1.5h with being placed at the bottom of the silicon wafer-based to boil in the mixing solutions of the vitriol oil and hydrogen peroxide, the mass ratio of the vitriol oil and hydrogen peroxide is 7: 3 in the mixing solutions, then substrate is placed the ultrasonic 20min of acetone, use deionized water rinsing, oven dry at last, remove the organism and the impurity of substrate surface.
2, epoxy silane coupling agent self-assembly
Leave standstill 12h with cleaning in the toluene solution that the silicon chip immersion 3-R-GLYCIDOL propoxy-Trimethoxy silane concentration of drying is 5mM.With the silicon chip ultrasonic cleaning in toluene and acetone successively of taking out, dry then, obtain the substrate of epoxy silane coupling agent self-assembly.
3, initiator DAB-16-TX grafting
With the substrate immersion light trigger DAB-16-TX concentration of epoxy silane coupling agent self-assembly is in the chloroformic solution of 5mM, and 40 ℃ of heating of lucifuge 12h takes out back ultrasonic cleaning in chloroform, and oven dry obtains surperficial initiator grafted substrate;
4, mask photobleaching
Mask is covered initiator grafted silicon chip surface, placed under the ultraviolet lamp illumination 45 seconds.
5, light-initiated preparation patterned polymer brush
With the NIPAM solution of the immersion of the silicon chip behind surperficial initiator photobleaching monomer concentration 1M, solvent is methyl alcohol and 1: 1 mixing solutions of water volume ratio.Ultraviolet lighting 2h after the logical nitrogen 30min deoxygenation with substrate ultrasonic cleaning in toluene, chloroform, acetone or straight alcohol, is dried after the reaction, obtains the PNIPAM polymer brush of patternization.Fig. 3 A is the pattern PNIPAM polymer brush of 1250 times of magnifications.Fig. 3 B is the AFM figure of PNIPAM patterned polymer brush, because rolling up after the polymer chain oven dry, there is projection on the surface.
Embodiment 3
1, the processing of substrate
Handle 2h with being placed at the bottom of the silicon wafer-based to boil in the mixing solutions of the vitriol oil and hydrogen peroxide, the mass ratio of the vitriol oil and hydrogen peroxide is 7: 3 in the mixing solutions, then substrate is placed the ultrasonic 10min of acetone, use deionized water rinsing, oven dry at last, remove the organism and the impurity of substrate surface.
2, epoxy silane coupling agent self-assembly
Leave standstill 12h with cleaning in the toluene solution that the silicon chip immersion 3-R-GLYCIDOL propoxy-Trimethoxy silane concentration of drying is 10mM.With the silicon chip ultrasonic cleaning in toluene and acetone successively of taking out, dry then, obtain the substrate of epoxy silane coupling agent self-assembly.
3, initiator DAB-16-TX grafting
With the substrate immersion light trigger DAB-16-TX concentration of epoxy silane coupling agent self-assembly is in the chloroformic solution of 10mM, and 40 ℃ of heating of lucifuge 12h takes out back ultrasonic cleaning in chloroform, and oven dry obtains surperficial initiator grafted substrate;
4, mask photobleaching
Mask is covered initiator grafted silicon chip surface, placed under the ultraviolet lamp illumination 60 seconds.
5, light-initiated preparation patterned polymer brush
Silicon chip behind the surperficial initiator photobleaching is immersed glycidyl methacrylate (GMA) monomer solution of monomer concentration 1M.Ultraviolet lighting 2h after the logical nitrogen 30min deoxygenation with substrate ultrasonic cleaning in toluene, chloroform, acetone or straight alcohol, is dried after the reaction, obtains the PGMA polymer brush of patternization.
Claims (3)
1, a kind of preparation method of patterned polymer brush is characterized in that comprising the steps:
1) substrate is placed on boil in the mixing solutions of the vitriol oil and hydrogen peroxide and handles 1-2h, the mass ratio of the vitriol oil and hydrogen peroxide is 7: 3 in the mixing solutions, then substrate is placed the ultrasonic 10-30min of acetone, use deionized water rinsing, oven dry at last, remove the organism and the impurity of substrate surface;
2) substrate that will clean oven dry immerses in the toluene solution that the concentration of 3-R-GLYCIDOL propoxy-Trimethoxy silane is 1-10mM and leaves standstill 2h-24h, then with the substrate ultrasonic cleaning in toluene and acetone successively of taking out, dry, obtain the substrate of epoxy silane coupling agent self-assembly;
3) the substrate immersion photoinitiator concentration with the epoxy silane coupling agent self-assembly is in the chloroformic solution of 2-10mM, and 40 ℃ of heating of lucifuge 2-12h takes out back ultrasonic cleaning in chloroform, and oven dry obtains surperficial initiator grafted substrate; Described light trigger is the thioxanthone photo initiator that contains coinitiator amine;
4) mask is covered surperficial initiator grafted substrate surface, place illumination 30-60 second under the ultraviolet lamp, obtain the substrate behind the surperficial initiator photobleaching;
5) substrate behind the surperficial initiator photobleaching being immersed monomer concentration is the solution of 0.5-5M, ultraviolet lighting after the logical nitrogen 30min deoxygenation, light application time 30min-5h; With substrate ultrasonic cleaning in toluene, chloroform, acetone or straight alcohol, dry after the reaction, obtain the polymer brush of micron order patternization.
2, according to the preparation method of the patterned polymer brush of claim 1, it is characterized in that described light trigger is DAB-16-TX, DAB-4-TX, DAB-64-TX or HPTX.
3,, it is characterized in that described monomer is for carrying out the monomer of light initiation polymerization according to the preparation method of the patterned polymer brush of claim 1.