CN101555570A - High-chromium-nickel quinary alloy casting and production process thereof - Google Patents
High-chromium-nickel quinary alloy casting and production process thereof Download PDFInfo
- Publication number
- CN101555570A CN101555570A CNA2009103022092A CN200910302209A CN101555570A CN 101555570 A CN101555570 A CN 101555570A CN A2009103022092 A CNA2009103022092 A CN A2009103022092A CN 200910302209 A CN200910302209 A CN 200910302209A CN 101555570 A CN101555570 A CN 101555570A
- Authority
- CN
- China
- Prior art keywords
- chromium
- nickel
- percent
- time
- heat treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a high-chromium-nickel quinary alloy casting and a production process thereof. The weight percentage content of each component of the casting is as follows: 3.00-3.40 percent of carbon, 9.50-10.50 percent of chromium, 0.5-1.00 percent of Mn, 1.40-1.80 percent of silicon, 0.50-0.55 percent of Mo, 5.00-5.50 percent of nickel, 0.10-0.13 percent of vanadium, 0.10-0.15 percent of rare earth, no more than 0.04 percent P, no more than 0.004 percent S, and the balance of iron and impurities. The invention is divided into twice heat treatment; for the first heat treatment, the temperature is 400-950 DEG C, the time is 40 hours; and for the second heat treatment, the temperature is 200-350 DEG C, and the time is 9 hours. By adopting the technical proposal, the invention leads the components of metal elements to be stable, improves the wear resistance of the product, can also eliminate internal stress and improve the stability of product performance.
Description
Technical field
The present invention relates to a kind of alloy-steel casting and production technique thereof, especially a kind of high-chromium-nickel quinary alloy casting and production technique thereof.
Background technology
Alloy-steel casting is widely used in China, is mainly used in fields such as mineral products, machinery, building materials, belongs to the rapid wear wearing piece.The alloy-steel casting that for example is used for the vertical mill liner plate is because the industrial and mineral environment is abominable, very high to the wear resisting property requirement of material.Existing alloy-steel casting is owing to adding metallic element component and each set of dispense than irrational reason, for example chromium, the nickel component concentration is on the low side, can not effectively improve the hardness of alloy-steel casting, has influenced the wear resisting property of foundry goods.In addition, existing alloy-steel casting is owing to only carry out a thermal treatment in process of production, temperature is about 900 ℃, can't effectively eliminate the internal stress that produces in the production process, cause foundry goods in long-time use, can crack or crack performance, the unstable properties of foundry goods also can have influence on work-ing life of foundry goods.
Summary of the invention
The technical problem to be solved in the present invention provides a kind of high-chromium-nickel quinary alloy casting and production technique thereof that can improve wear resisting property.
Technical problem to be solved by this invention is achieved by the following technical solution: the weight percentage of each component of high-chromium-nickel quinary alloy casting is: carbon 3.00-3.40, chromium 9.50-10.50, manganese 0.5-1.00, silicon 1.40-1.80, molybdenum 0.50-0.55, nickel 5.00-5.50, vanadium 0.10-0.13, rare earth 0.10-0.15, phosphorus≤0.04, sulphur≤0.004, all the other are iron and impurity.
The production technique of high-chromium-nickel quinary alloy casting of the present invention, the weight percentage of each component of foundry goods is: carbon 3.00-3.40, chromium 9.50-10.50, manganese 0.5-1.00, silicon 1.40-1.80, molybdenum 0.50-0.55, nickel 5.00-5.50, vanadium 0.10-0.13, rare earth 0.10-0.15, phosphorus≤0.04, sulphur≤0.004, all the other are iron and impurity, and technological process may further comprise the steps:
(1) mould: with the signatory drawing design check and correction of client's contract;
(2) mulling: quartz sand and water glass are mixed rolling 3-8 minute in the trolley type sand mill, the weight percent of quartz sand and water glass is 92-94: 6-8;
(3) moulding: mold flask, rising head, core are examined the back and are operated by working specification;
(4) smelt: prepare A3-45 steel scrap, the 16-22 pig iron and each metallic element by the electric furnace worker and throw in, each metallic element component strictness is measured in proportion;
(5) cast: the cast of driving system control bull ladle, sandbox insulation 36-48 hour;
(6) sand removal: manual handling;
(7) soldering: cutting is mended in hot weld;
(8) ball blast: treating product any surface finish;
(9) thermal treatment: divide second heat treatment in full fiber electronic number car controlling stove, thermal treatment temp is 400-950 ℃ for the first time, and the time is 40 hours, and the tempering heat treatment temperature is 200-350 ℃ for the second time, and the time is 9 hours.
The technique scheme that the present invention adopts, the sandbox soaking time is long during owing to cast, and the metallic element structural constituent is stable; High-load chromium, nickel element have also improved the hardness of product, thereby improve the wear resisting property of product; Adopt second heat treatment technology also can eliminate internal stress, reduce crackle, crack performance, the stability of enhancing product performance.
Embodiment
Embodiment 1:
High-chromium-nickel quinary alloy casting of the present invention, the weight percentage of its each component is: carbon 3.00, chromium 9.50, manganese 0.5, silicon 1.40, molybdenum 0.50, nickel 5.00, vanadium 0.10, rare earth 0.10, phosphorus 0.01, sulphur 0.001, all the other are iron and impurity.
The production technique of high-chromium-nickel quinary alloy casting of the present invention includes the following step:
(1) mould: with the signatory drawing design check and correction of client's contract;
(2) mulling: quartz sand and water glass are mixed rolling 3 minutes in the trolley type sand mill, the weight percent of quartz sand and water glass is 92: 8;
(3) moulding: mold flask, rising head, core are examined the back and are operated by working specification;
(4) smelt: prepare A3 steel scrap, No. 16 pig iron and each metallic element by the electric furnace worker and throw in, each metallic element component is strict measures in embodiment 1 ratio;
(5) cast: the cast of driving system control bull ladle, sandbox insulation 36 hours;
(6) sand removal: manual handling;
(7) soldering: cutting is mended in hot weld;
(8) ball blast: treating product any surface finish;
(9) thermal treatment: divide second heat treatment in full fiber electronic number car controlling stove, thermal treatment temp is 400 ℃ for the first time, and the time is 40 hours, and the tempering heat treatment temperature is 200 ℃ for the second time, and the time is 9 hours.
Embodiment 2:
High-chromium-nickel quinary alloy casting of the present invention, the weight percentage of its each component is: carbon 3.20, chromium 10.00, manganese 0.80, silicon 1.60, molybdenum 0.52, nickel 5.20, vanadium 0.11, rare earth 0.12, phosphorus 0.02, sulphur 0.002, all the other are iron and impurity.
The production technique of high-chromium-nickel quinary alloy casting of the present invention includes the following step:
(1) mould: with the signatory drawing design check and correction of client's contract;
(2) mulling: quartz sand and water glass are mixed rolling 5 minutes in the trolley type sand mill, the weight percent of quartz sand and water glass is 93: 7;
(3) moulding: mold flask, rising head, core are examined the back and are operated by working specification;
(4) smelt: prepare A40 steel scrap, No. 20 pig iron and each metallic element by the electric furnace worker and throw in, each metallic element component is strict measures in embodiment 2 ratios;
(5) cast: the cast of driving system control bull ladle, sandbox insulation 42 hours;
(6) sand removal: manual handling;
(7) soldering: cutting is mended in hot weld;
(8) ball blast: treating product any surface finish;
(9) thermal treatment: divide second heat treatment in full fiber electronic number car controlling stove, thermal treatment temp is 700 ℃ for the first time, and the time is 40 hours, and the tempering heat treatment temperature is 300 ℃ for the second time, and the time is 9 hours.
Embodiment 3:
High-chromium-nickel quinary alloy casting of the present invention, the weight percentage of its each component is: carbon 3.40, chromium 10.50, manganese 1.00, silicon 1.80, molybdenum 0.55, nickel 5.50, vanadium 0.13, rare earth 0.15, phosphorus 0.04, sulphur 0.004, all the other are iron and impurity.
The production technique of high-chromium-nickel quinary alloy casting of the present invention includes the following step:
(1) mould: with the signatory drawing design check and correction of client's contract;
(2) mulling: quartz sand and water glass are mixed rolling 8 minutes in the trolley type sand mill, the weight percent of quartz sand and water glass is 94: 6;
(3) moulding: mold flask, rising head, core are examined the back and are operated by working specification;
(4) smelt: prepare A45 steel scrap, No. 22 pig iron and each metallic element by the electric furnace worker and throw in, each metallic element component is strict measures in embodiment 3 ratios;
(5) cast: the cast of driving system control bull ladle, sandbox insulation 48 hours;
(6) sand removal: manual handling;
(7) soldering: cutting is mended in hot weld;
(8) ball blast: treating product any surface finish;
(9) thermal treatment: divide second heat treatment in full fiber electronic number car controlling stove, thermal treatment temp is 950 ℃ for the first time, and the time is 40 hours, and the tempering heat treatment temperature is 350 ℃ for the second time, and the time is 9 hours.
Component and production technique that the present invention adopts make the tensile strength of high-chromium-nickel quinary alloy casting be not less than 650MPa, and impelling strength is not less than 3J/cm2, and elongation is not more than 8%, and surface hardness can reach 60-62HRC.
Claims (2)
1. high-chromium-nickel quinary alloy casting, the weight percentage that it is characterized in that each component is: carbon 3.00-3.40, chromium 9.50-10.50, manganese 0.5-1.00, silicon 1.40-1.80, molybdenum 0.50-0.55, nickel 5.00-5.50, vanadium 0.10-0.13, rare earth 0.10-0.15, phosphorus≤0.04, sulphur≤0.004, all the other are iron and impurity.
2. the production technique of a high-chromium-nickel quinary alloy casting, the weight percentage of each component of foundry goods is: carbon 3.00-3.40, chromium 9.50-10.50, manganese 0.5-1.00, silicon 1.40-1.80, molybdenum 0.50-0.55, nickel 5.00-5.50, vanadium 0.10-0.13, rare earth 0.10-0.15, phosphorus≤0.04, sulphur≤0.004, all the other are iron and impurity, it is characterized in that may further comprise the steps:
(1) mould: with the signatory drawing design check and correction of client's contract;
(2) mulling: quartz sand and water glass are mixed rolling 3-8 minute in the trolley type sand mill, the weight percent of quartz sand and water glass is 92-94: 6-8;
(3) moulding: mold flask, rising head, core are examined the back and are operated by working specification;
(4) smelt: prepare A3-45 steel scrap, the 16-22 pig iron and each metallic element by the electric furnace worker and throw in, each metallic element component strictness is measured in proportion;
(5) cast: the cast of driving system control bull ladle, sandbox insulation 36-48 hour;
(6) sand removal: manual handling;
(7) soldering: cutting is mended in hot weld;
(8) ball blast: treating product any surface finish;
(9) thermal treatment: divide second heat treatment in full fiber electronic number car controlling stove, thermal treatment temp is 400-950 ℃ for the first time, and the time is 40 hours, and the tempering heat treatment temperature is 200-350 ℃ for the second time, and the time is 9 hours.