CN101531838A - 水性隔热粉末涂料 - Google Patents

水性隔热粉末涂料 Download PDF

Info

Publication number
CN101531838A
CN101531838A CN200910061572A CN200910061572A CN101531838A CN 101531838 A CN101531838 A CN 101531838A CN 200910061572 A CN200910061572 A CN 200910061572A CN 200910061572 A CN200910061572 A CN 200910061572A CN 101531838 A CN101531838 A CN 101531838A
Authority
CN
China
Prior art keywords
water
coating
heat insulation
powder
borne
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910061572A
Other languages
English (en)
Inventor
李家权
黄澄华
李训生
金广泉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUBEI ZHONGHE BOCE NEW MATERIAL INST
Original Assignee
HUBEI ZHONGHE BOCE NEW MATERIAL INST
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUBEI ZHONGHE BOCE NEW MATERIAL INST filed Critical HUBEI ZHONGHE BOCE NEW MATERIAL INST
Priority to CN200910061572A priority Critical patent/CN101531838A/zh
Publication of CN101531838A publication Critical patent/CN101531838A/zh
Pending legal-status Critical Current

Abstract

一种水性隔热粉末涂料，采用纳米级复合钛酸酯粉作隔热材料，采用复合硅酸三钙和铁铝酸四钙作纳米级复合钛酸酯的载体材料，采用聚丙烯单体－聚乙烯醇混合物(1∶1)作复合剂。其优点是：有优异的隔热、保温效果，隔热效果在10－18℃；使用极其方便，加自来水调至所需粘度即可刷涂或喷涂；无任何有害重金属，无溶剂，安全、环保；对建筑墙体的水泥有增强、增耐候性效果；与水泥有相同的耐水性、耐候性，对雨水有防渗能力；可用作建筑物堵漏剂使用；可涂刷在水泥、钢板、玻璃等多种材料表面，用在钢板上时对钢板有防锈效果。

Description

水性隔热粉末涂料
技术领域
本发明涉及涂料技术领域，具体的说是一种水性隔热粉末涂料。
背景技术
目前建筑节能成为当前节能工作的重中之重，各地先后研发出各种内外墙隔热涂料，中央发改委也于2007年11月1日实施了相关标准，按其标准其隔热性能、耐老化性能均不及国外同类产品，且国内各地同类产品无论是油性外墙涂料还是水性外墙涂料，其耐候性多不超过3-5年，所用的隔热材料无非是普通的水蛭石、海泡石之类，也有用玻璃微珠的，可又不能解决其带来的“镜框效应”，同时由于普通隔热涂料的涂刷厚度受到限制，因此在阳光数小时的照射下，其隔热效果大打折扣。
发明内容
本发明的目的是研制一种价格低廉、使用寿命长、隔热效果好的水性隔热粉末涂料。
本发明水性隔热粉末涂料采用纳米级复合钛酸酯粉作隔热材料，采用复合硅酸三钙和铁铝酸四钙作纳米级复合钛酸酯的载体材料，采用聚丙烯单体-聚乙烯醇混合物(1:1)作复合剂。
本发明水性隔热粉末涂料，其水性隔热粉末组份质量百分比为：
纳米级复合钛酸酯隔热粉         5～20％
复合硅-铝酸盐                  30～65％
聚丙烯单体-聚乙烯醇            10～30％
钛白粉                 2～25％
轻质碳酸钙             2～5％
纳米级复合钛酸酯隔热粉，为钛酸酯和二氧化钛以2:1的比例混合而成。
将上述组份经混合机充分搅拌，得到水性隔热粉末。
将水性隔热粉末与水按1:0.5-0.8的重量比混合，调至合适的粘度，即得到水性隔热涂料。
本发明水性隔热粉末涂料的优点是：有优异的隔热、保温效果，隔热效果在10-18℃；使用极其方便，加自来水调至所需粘度即可刷涂或喷涂；无任何有害重金属，无溶剂，安全、环保；对建筑墙体的水泥有增强、增耐候性效果；与水泥有相同的耐水性、耐候性，对雨水有防渗能力；可用作建筑物堵漏剂使用；可涂刷在水泥、钢板、玻璃等多种材料表面，用在钢板上时对钢板有防锈效果。
具体实施方式
实施例一
一种水性隔热粉末涂料，其水性隔热粉末组份质量(kg)如下：
纳米级复合钛酸酯隔热粉         20kg
复合硅-铝酸盐                  30kg
聚丙烯单体-聚乙烯醇            30kg
钛白粉                         18kg
轻质碳酸钙                     2kg
将上述组份经混合机充分搅拌，得到水性隔热粉末。
将上述100kg水性隔热粉末与50kg水混合，调至合适的粘度，即得到水性隔热涂料。
将水性隔热涂料刷涂在20×20×1cm水泥板上，涂膜厚度100цm，在红外灯照射下一小时，水泥板上面与背面温差达25℃。
实施例二
一种水性隔热粉末涂料，其水性隔热粉末组份质量百分比为：
纳米级复合钛酸酯隔热粉                   5kg
复合硅-铝酸盐                            65kg
聚丙烯单体-聚乙烯醇                      10kg
钛白粉                                   15kg
轻质碳酸钙                               5kg
将上述组份经混合机充分搅拌，得到水性隔热粉末。
将上述100kg水性隔热粉末与80kg水混合，调至合适的粘度，即得到水性隔热涂料。
将水性隔热涂料刷涂在聚丙烯塑料板上测试其隔热效果为25℃。
实施例三
一种水性隔热粉末涂料，其水性隔热粉末组份质量百分比为：
纳米级复合钛酸酯隔热粉              14kg
复合硅-铝酸盐                       48kg
聚丙烯单体-聚乙烯醇                 20kg
钛白粉                              14kg
轻质碳酸钙                     4kg
将上述组份经混合机充分搅拌，得到水性隔热粉末。
将上述100kg水性隔热粉末与65kg水混合，调至合适的粘度，即得到水性隔热涂料。
将水性隔热涂料涂刷在水泥水池内侧，720小时无渗水现象。

Claims (3)

1、一种水性隔热粉末涂料，其特征在于：其水性隔热粉末组份质量百分比为：
纳米级复合钛酸酯隔热粉              5～20％
复合硅-铝酸盐                       30～65％
聚丙烯单体-聚乙烯醇                 10～30％
钛白粉                              2～25％
轻质碳酸钙                          2～5％
将上述组份经混合机充分搅拌，得到水性隔热粉末；
将水性隔热粉末与水按1:0.5-0.8的重量比混合，调至合适的粘度，即得到水性隔热涂料。
2、根据权利要求1所述的水性隔热粉末涂料，其特征在于：采用纳米级复合钛酸酯粉作隔热材料，采用复合硅酸三钙和铁铝酸四钙作纳米级复合钛酸酯的载体材料，采用聚丙烯单体-聚乙烯醇混合物(1:1)作复合剂。
3、根据权利要求1所述的水性隔热粉末涂料，其特征在于：纳米级复合钛酸酯隔热粉，为钛酸酯和二氧化钛以2:1的比例混合而成。
CN200910061572A 2009-04-14 2009-04-14 水性隔热粉末涂料 Pending CN101531838A (zh)