CN101525839B - Waterproof agent used for waterproof oil wax cloth - Google Patents
Waterproof agent used for waterproof oil wax cloth Download PDFInfo
- Publication number
- CN101525839B CN101525839B CN2009100970257A CN200910097025A CN101525839B CN 101525839 B CN101525839 B CN 101525839B CN 2009100970257 A CN2009100970257 A CN 2009100970257A CN 200910097025 A CN200910097025 A CN 200910097025A CN 101525839 B CN101525839 B CN 101525839B
- Authority
- CN
- China
- Prior art keywords
- waterproof
- waterproof agent
- oil wax
- agent used
- wax cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a waterproof agent used for waterproof oil wax cloth. The waterproof agent consists of the following components by weight: 9%-14% of paraffin, 3%-5% of stearic acid, 0.2%-0.4% of sodium hydroxide, 0.5%-3.5% of aluminium sulphate, 12%-20% of polyvinyl alcohol, 4%-7% of chrome green, 6%-13% of chrome oxide green and 40%-60% of stone dust. The oil wax cloth produced by using the waterproof agent has wide application range and can be used in the environment with the temperature ranging from minus 40 DEG C to plus 80 DEG C, is not crisp in cold climate, and does not soften in high temperature climate, feels always the same and is kept in the stable state; and the production of the waterproof agent is environment-friendly, nontoxic and harmless. Therefore, the product has good economic and social benefits.
Description
Technical field
The present invention relates to cloth waterproofing agent technical field, be specifically related to a kind of waterproof agent used for waterproof oil wax cloth.
Background technology
Present developing rapidly along with oily cerecloth industry, market is more and more higher for the quality requirement of oily cerecloth, because the use of oily cerecloth generally is used for outdoor in the majority, therefore the water resistance to oily cerecloth has more strict requirement, thereby for the waterproofing agent that is used to produce the dubbin cerecloth special requirement is arranged also.But the waterproofing agent waterproof effect that is used for oily cerecloth at present is undesirable, thereby and smell is heavier in production and the use that environment is polluted.The oily cerecloth scope of application that exists waterproofing agent to produce simultaneously is narrow, and cold climate is easily crisp hard, and hot weather is easily softening, its feel instability, so the economic benefit of product and social benefit are undesirable.
Summary of the invention
The technical problem to be solved in the present invention is the above-mentioned deficiency at prior art, and a kind of good water-proof effect is provided, the waterproof agent used for waterproof oil wax cloth of environmentally safe.
In order to solve the problems of the technologies described above, the technical scheme that the present invention takes is: a kind of waterproof agent used for waterproof oil wax cloth, form by following components in weight percentage: paraffin 9%～14%, stearic acid 3%～5%, NaOH 0.2%～0.4%, aluminum sulfate 0.5%～3.5%, polyvinyl alcohol 12%～20%, art green 4%～7%, chrome oxide green 6%～13%, stone flour 40%～60%.
As preferably, a kind of waterproof agent used for waterproof oil wax cloth of the present invention, form by following components in weight percentage: paraffin 10%～12.5%, stearic acid 3.2%～4%, NaOH 0.24%～0.3%, aluminum sulfate 1.0%～2%, polyvinyl alcohol 15%～17%, art green 5%～6%, chrome oxide green 9%～11%, stone flour 48%～55%.
Advantage of the present invention and beneficial effect:
1. waterproofing agent of the present invention is strengthened management in the production process because of no hypertoxic harmful substance in the prescription, does not leak material in accomplishing to produce, and surplus material is continued to employ and do not discharged, and therefore more environmental protection in production and use is nontoxic, harmless; The existence of " NaOH, aluminum sulfate " the two kinds of agent material in the prescription simultaneously can reduce smell and pollute.
2. hang water with the oily cerecloth of waterproofing agent production of the present invention by the normal temperature routine and do not leak, the existence because of " NaOH, aluminum sulfate " the two kinds of agent material in the prescription has improved waterproof effect.
3. the oily cerecloth scope of application of producing with waterproofing agent of the present invention is wide, and cold climate is not crisp hard, and hot weather is not softening, and its feel remains stable state, so product has good economic benefit and social benefit.
The specific embodiment
Below by embodiment the present invention is described further, but the present invention not only is confined to following examples.
Embodiment
Experimental procedure is as follows: the paraffin that will fuse earlier in boiling the still bucket is 80～100 ℃ of fusions, all components agent material is put in the mediation bucket and is in harmonious proportion evenly in will filling a prescription then, grind through grinder then, detect feel and do not have particle, normally (color is by the color decision of the art green in the prescription for color soon, detection method is for judging sample cloth and the cloth contrast of dying system with waterproofing agent, to be color normal when color and sample cloth solid colour), concentration is normal, and (concentration changes with variation of temperature, in the time of 60～80 ℃, test its flow velocity with funnel, its used time is about 3 times of identical water gaging, it is normal to be concentration), be qualified waterproofing agent, the constant temperature deposit is stand-by under 60～80 ℃ of temperature.
Each component prescription of embodiments of the invention sees Table 1:
Each component prescription of table 1 embodiment
Be that grey cloths such as 4 * 3,4 * 4,2 * 2,6 * 6 terylene, polyester cotton blending, regenerated fiber are produced the dubbin cerecloth through blade coating---oven dry---coiling of prior art with above-mentioned waterproofing agent for preparing and cloth then, then the cloth specimen performance is tested, content measurement by " test of national textile garment product quality supervision and inspection " center ", test data is as shown in table 2:
The oily cerecloth cloth specimen performance that table 2 is produced with waterproofing agent of the present invention
(annotate: " water permeability resistance (cm.H in the above-mentioned table 2
2O) " tester is " a FZ/T 01004-1991 coated fabric water permeability resistance energy tester ")
Can be got by above-mentioned test result, product of the present invention is compared with existing product, with the oily cerecloth that production of the present invention goes out, and its water permeability resistance of good water-proof effect (cm.H
2O) can be high (with the water permeability resistance of existing product than improving about 10% approximately); Ultimate strength ideal, cold climate are not crisp hard, and hot weather is not softening, and its feel remains stable state, so product has good economic benefit and social benefit.
Claims (2)
1. waterproof agent used for waterproof oil wax cloth, it is characterized in that: form: paraffin 9%～14% by following components in weight percentage, stearic acid 3%～5%, NaOH 0.2%～0.4%, aluminum sulfate 0.5%～3.5%, polyvinyl alcohol 12%～20%, art green 4%～7%, chrome oxide green 6%～13%, stone flour 40%～60%.
2. waterproof agent used for waterproof oil wax cloth according to claim 1, it is characterized in that: form: paraffin 10%～12.5% by following components in weight percentage, stearic acid 3.2%～4%, NaOH 0.24%～0.3%, aluminum sulfate 1.0%～2%, polyvinyl alcohol 15%～17%, art green 5%～6%, chrome oxide green 9%～11%, stone flour 48%～55%.