CN101481585A - Tourmaline gloss oil and preparation thereof - Google Patents
Tourmaline gloss oil and preparation thereof Download PDFInfo
- Publication number
- CN101481585A CN101481585A CNA2009100736743A CN200910073674A CN101481585A CN 101481585 A CN101481585 A CN 101481585A CN A2009100736743 A CNA2009100736743 A CN A2009100736743A CN 200910073674 A CN200910073674 A CN 200910073674A CN 101481585 A CN101481585 A CN 101481585A
- Authority
- CN
- China
- Prior art keywords
- tourmaline
- oil
- gloss oil
- photochemical
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a tourmaline photochemical oil and a preparation method thereof, and is characterized in that the tourmaline photochemical oil further contains tourmaline, titanium dioxide, silicon oxide and aluminum oxide; the preparation method of the tourmaline photochemical oil is characterized in that the tourmaline, titanium dioxide, silicon oxide and aluminum oxide are firstly respectively crushed in stepwise manner and are ball-milled till 0.1 micron to 0.5 microns of superfine powder; the powder of each component according to proportions by weight are then added to photochemical oil after being uniformly mixed so that the tourmaline photochemical oil is obtained after intensive and uniform stirring. The tourmaline photochemical oil takes full advantage of piezoelectric effect and pyroelectric effect specific for tourmaline, thereby emitting far infrared rays, releasing negative ions, and having the functions of bacteriostasis, rot resistance, moisture protection, odor elimination, and the like; the tourmaline photochemical oil has the advantages of eliminating hazardous substances of furniture and room such as formaldehyde and toluene, improving indoor air quality, and the like. The tourmaline photochemical oil can be widely applied to printed matters, packaging products, oil painting decoration, and spray painting at the surface of indoor wall and at the surface of indoor wallpaper.
Description
Technical field
The invention belongs to a kind of functional fine chemical product, be specifically related to tourmaline gloss oil composite functional material that is used for body surface spray treatment such as oil painting, furniture surface, wallpaper surface, surface of wall and preparation method thereof.
Background technology
Many characteristics such as at present, gloss oil is good, colour-fast because of its glossiness, and nondiscoloration is fast dry, and moistureproofness is good, it is widely used in the spray treatment of printed matter, packaged product, decorative painting, furniture surface, wallpaper surface, surface of wall.Along with present rapid growth of economy, people's environmental consciousness also strengthens gradually, payes attention to self health, and required commodity not only require gloss oil that good decoration effect is arranged, also urgent to its environmental protection, health care function simultaneously requirement.
Summary of the invention
The objective of the invention is at non-functional gloss oil on the existing market, a kind of distinctive piezoelectric effect of tourmalinite and thermoelectric effect utilized is provided, emitting far-infrared and discharge negative ion, and effects such as antibacterial, mildew-resistant, protection against the tide, elimination peculiar smell, also can remove objectionable impuritiess such as formaldehyde in furniture, the room air, toluene simultaneously, improve tourmaline gloss oil of IAQ (indoor air quality) and preparation method thereof.
Technical scheme of the present invention is:
Tourmaline gloss oil comprises gloss oil, is characterized in that this tourmaline gloss oil also contains tourmalinite, titanium dioxide, silicon oxide and aluminum oxide; This tourmaline gloss oil each component weight percentage is:
Gloss oil 93~96.8wt%;
Tourmalinite 0.1~5wt%;
Titanium dioxide 0.05~2wt%;
Silicon oxide 0.05~2wt%;
Aluminum oxide 0.05~2wt%.
The preparation method of tourmaline gloss oil is characterized in that earlier tourmalinite, titanium dioxide, silicon oxide, aluminum oxide being pulverized the superfine powder of ball milling to 0.1 μ m~0.5 μ m respectively step by step; After getting each component powder uniform mixing then by weight, add again in the gloss oil, after full and uniform stirring, both got tourmaline gloss oil.
Because the asymmetry of tourmalinite crystal C axle makes it can spontaneously excite electric charge under pressure, temperature variation, emitting far-infrared, as to discharge negative ion and generation 0.06mA bioelectric current.The peculiar smell that obnoxious flavour, bacterium and human body produce etc. are all positively charged, negative ion can neutralize airborne oxyradical and corrupt peculiar smell (oxidizing gas), and neutralization or coat obnoxious flavour particles such as the formaldehyde have positive charge, hydrogen sulfide, dimethylamine, ammonia, sedimentation behind no electric charge does not work the mischief to HUMAN HEALTH.Bacterium is subjected to electric field action and the little galvanic action of the formed 0.06m A of electric field in electric field, be killed or suppress its division and proliferation.Bacterium is positively charged mostly, a large amount of H of quilt in air or water
3O
2 -Coat or by H
3O
2 -Neutralize, lose the condition of hyperplasia and breeding, far infrared radiation also can be played the antibacterial bacteriostatic effect.
The strong oxidation capacity of titanium dioxide can promote the potent decomposition of organic pollutant, and oxygen and water molecules around making are excited into the OH that has oxidizing power
-Reach negative ion, and organic pollutant is resolved into free of contamination CO
2And H
2O also has functions such as antibiotic, sterilization, deodorizing, antifouling, hydrophilic, antiultraviolet simultaneously.
Silicon oxide character is very stable, and water insoluble also not with the water reaction, superfine powder can play excellent waterproof effect and wearability.Aluminum oxide can increase the viscosity of gloss oil, stops the formation of large particle crystal body, the bonding force of reinforcement and dirt settling, and the while can be strengthened hardness, physical strength, weathering resistance ability, creep resistance and the heat-shock resistance of spray-coated film again.
A kind of tourmaline gloss oil provided by the invention and preparation method thereof.Make full use of distinctive piezoelectric effect of tourmalinite and thermoelectric effect, emitting far-infrared and discharge negative ion, effects such as antibacterial, mildew-resistant, protection against the tide, elimination peculiar smell have objectionable impuritiess such as removing furniture, the formaldehyde in indoor, toluene, improve advantages such as IAQ (indoor air quality).Can be widely used in the spraying on printed matter, packaged product, decorative painting, indoor wall surface and indoor wall paper surface.
Embodiment
The present invention will be further described below in conjunction with embodiment.
Embodiment 1: a kind of tourmaline gloss oil of the present invention, raw material are got each component by weight and are:
The 96.8wt% gloss oil
The 2wt% tourmalinite
0.5wt% titanium dioxide
The 0.3wt% silicon oxide
The 0.4wt% aluminum oxide
Tourmalinite, titanium dioxide, silicon oxide, aluminum oxide are pulverized respectively step by step, the superfine powder of ball milling to 0.1 μ m~0.5 μ m, get each component powder uniform mixing by weight after, add again in the gloss oil, after full and uniform stirring, both tourmaline gloss oil.This tourmaline gloss oil must seal the shading cryopreservation, is mainly used in the spraying of oil painting, calligraphy and painting, furniture surface.
Embodiment 2: a kind of tourmaline gloss oil of the present invention, raw material are got each component by weight and are:
The 93wt% gloss oil
The 5wt% tourmalinite
1wt% titanium dioxide
The 0.5wt% silicon oxide
The 0.5wt% aluminum oxide
Tourmalinite, titanium dioxide, silicon oxide, aluminum oxide are pulverized respectively step by step, the superfine powder of ball milling to 2 μ m~5 μ m, get each component powder uniform mixing by weight after, add again in the gloss oil, after full and uniform stirring, both tourmaline gloss oil.This tourmaline gloss oil must seal the shading cryopreservation, is mainly used in the spraying on wall surface, wallpaper surface.
Claims (2)
1, a kind of tourmaline gloss oil comprises gloss oil, it is characterized in that this tourmaline gloss oil also contains tourmalinite, titanium dioxide, silicon oxide and aluminum oxide; This tourmaline gloss oil each component weight percentage is:
Gloss oil 93~96.8wt%;
Tourmalinite 0.1~5wt%;
Titanium dioxide 0.05~2wt%;
Silicon oxide 0.05~2wt%;
Aluminum oxide 0.05~2wt%.
2, according to the preparation method of the described tourmaline gloss oil of claim 1, it is characterized in that: earlier tourmalinite, titanium dioxide, silicon oxide, aluminum oxide are pulverized the superfine powder of ball milling to 0.1 μ m~0.5 μ m respectively step by step; After getting each component powder uniform mixing then by weight, add again in the gloss oil,, both got tourmaline gloss oil through full and uniform stirring.