CN101468890A - 立窑1350℃±100℃高温煅烧10-15%铬渣35-40%粉煤灰20-30%碱渣水泥建材骨料技术 - Google Patents
立窑1350℃±100℃高温煅烧10-15%铬渣35-40%粉煤灰20-30%碱渣水泥建材骨料技术 Download PDFInfo
- Publication number
- CN101468890A CN101468890A CNA2007100606399A CN200710060639A CN101468890A CN 101468890 A CN101468890 A CN 101468890A CN A2007100606399 A CNA2007100606399 A CN A2007100606399A CN 200710060639 A CN200710060639 A CN 200710060639A CN 101468890 A CN101468890 A CN 101468890A
- Authority
- CN
- China
- Prior art keywords
- chromium
- chromium slag
- slag
- alkaline residue
- shaft kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于铬渣的治理与综合利用技术,将10-15%铬渣35-40%粉煤灰20-30%碱渣与煤、粘土配比,均混,磨粉,成球,煅烧,利用立窑中高温1350℃±100℃环境及一氧化碳使铬渣中六价铬还原为三价铬,进而达到解毒和粉煤灰、碱渣的烧成料可做建材骨料,不产生二次污染,治理速度快,费用低,降低工程造价。
Description
技术领域
本发明属于危险固体废物铬渣与固体废物粉煤灰、建筑垃圾的治理与综合利用技术,特别涉及利用机立窑高温治理铬渣中六价铬及铬渣与粉煤灰、碱渣煅烧的技术,将铬渣、粉煤灰、碱渣与煤、粘土均混,磨粉,成球,煅烧,利用立窑中高温1350℃±100℃及一氧化碳环境使六价铬还原为三价铬,进而达到解毒的烧成料可做建材骨料,不产生二次污染,治理速度快,费用低,降低工程造价。
背景技术
由于传统铬盐工业所排放的大量铬渣缺少治理量大,费用低,无二次污染的治理方法,致使铬渣对环境造成严重污染,很大程度上制约了铬盐工业的发展甚至被迫停产。此外,燃煤行业产生大量粉煤灰,化工业产生大量碱渣污染环境,岌需合理处置。用立窑处置铬渣、粉煤灰、碱渣综合利用技术,国内外尚未有报道。本发明用立窑煅烧水泥熟料的1350℃±100℃温度和工艺条件,利用1350℃±100℃高温,还原物和酸性条件将铬渣中的六价铬还原为无毒的三价铬,并加入粉煤灰、碱渣实现资源化,工程化,特别是突破费用高,治理速度慢,实现社会效益,环境效益,经济效益明显,是本发明的任务。
发明内容
本发明是用立窑煅烧水泥熟料的1350℃±100℃高温及暗火操作产生的还原气氛使铬渣中六价铬还原为不造成二次污染的三价铬。本发明是将国内外普遍采用的高温还原解毒方法加以改进构成的利用立窑高温煅烧铬渣干法解毒铬渣的方法,形成一种铬渣、粉煤灰、碱渣煅烧成建材骨料的技术。
本发明赋予立窑具有1350℃±100℃高温、一氧化碳还原解毒的作用,将10-15%铬渣35-40%粉煤灰20-30%碱渣与煤、粘土均混,磨粉,成球,铬渣在立窑暗火操作下经过预热带、高温带,使铬渣中六价铬还原为三价铬,并固定在熔融体中,进入冷却带置烧成料出口处急速冷却或高压水急速水淬防止氧化,主要反应如下:在碱性条件下大于500℃时:
CrO3+3/2O2=2CrO3,在700~800℃,水淬产生氢气与一氧化碳:C+H2O=H2+CO杜绝铬渣中六价铬的扩散污染;利用立窑高温和一氧化碳还原作用将铬渣中六价铬与窑中1350℃±100℃高温和一氧化碳环境,还原为无毒的三价铬,并生成更稳定的络合物,铬渣得以解毒。同时,铬渣、粉煤灰、碱渣煅烧成建材骨料。本方法利用立窑高温大量治理铬渣、粉煤灰、碱渣,其工程实施的实质是形成一个结构简单的解毒和资源化的技术。一方面铬渣、粉煤灰、碱渣治理后不怕扬散,流失,渗透的永久物质,另一方面又创造条件充分利用烧成料的物理力学的性质,可做建材骨料,实现综合利用。
本发明所指1350℃±100℃高温还原干法解毒是指含立窑高温1350℃±100℃、一氧化碳还原机理,经过七小时左右煅烧有还原性物质环境中煅烧的烧结料在500℃出料时,急速冷却(水淬更好)对铬渣中已还原成的三价铬有防止氧化作用。
本发明利用水泥厂闲置机立窑专门煅烧铬渣干法解毒的方法是一种利用1350℃±100℃高温、一氧化碳条件;是采用国内外治理铬渣成熟的高温解毒技术经改进后的综合利用技术,是一个安全无二次污染,经济效益,社会效益,环境效益明显的综合利用铬渣、粉煤灰、碱渣的技术。
附图说明
附图是本方法的结构示意图
具体实施方式
下面结合附图对本方法作进一步的描述
实施例1
按图1的工程示意图,将铬渣、粉煤灰、碱渣粉碎后置于烘干机内烘干,然后经配料称与煤、粘土、碱渣分别进入生料粉磨,进均化仓,再经提升机、预加水、成球,入立窑高温烧成,在立窑经过预热带、高温带、冷却带,六小时左右时间(见图2)在高温1350℃±100℃,一氧化碳环境中烧成料,鉴别标准中有关六价铬的规定指数≦1.5mg/L成为建材骨料。
Claims (4)
1、一种将铬渣用于机立窑1350℃±100℃的高温,一氧化碳对铬渣中六价铬还原机理,形成铬渣解毒和粉煤灰、碱渣资源化技术;解毒后烧成料是:利用机立窑1350℃±100℃高温、一氧化碳还原条件下10-15%铬渣35-40%粉煤灰20-30%碱渣在机立窑暗火操作下经预热带进入高温带1350℃±100℃,使铬渣中六价铬还原为三价铬,进入冷却带后,置烧成料出口处在500℃±50℃急速冷却或高压水急速水淬防止氧化,进而生成稳定的铬渣烧成料,形成一个安全无二次污染经济、社会、环境效益明显的建材骨料技术。
2、权力要求“1”高温带温度1350℃±100℃下,高温煅烧在还原气氛下使六价铬还原为三价铬。
3、权力要求“1”和“2”机立窑中的预热带1350℃±100℃,高温带900℃,冷却带500℃±50℃;对铬渣中六价铬有强烈的还原、解毒和防止氧化作用。
4、权力要求“1-3”中铬渣、粉煤灰、碱渣、石灰石与煤、粘土的比例,应控制铬渣在10-15:35-40:20-30:15:10为宜。