CN101451032A - Ink composition for ink jet recording and ink jet recording method - Google Patents
Ink composition for ink jet recording and ink jet recording method Download PDFInfo
- Publication number
- CN101451032A CN101451032A CN 200710032338 CN200710032338A CN101451032A CN 101451032 A CN101451032 A CN 101451032A CN 200710032338 CN200710032338 CN 200710032338 CN 200710032338 A CN200710032338 A CN 200710032338A CN 101451032 A CN101451032 A CN 101451032A
- Authority
- CN
- China
- Prior art keywords
- solvent
- ink composite
- ink
- weight
- jet recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a printing ink composition for ink jet recording. The printing ink composition comprises the following components by weight percentage: 0.1 to 8.0 percent of dye and 60.0 to 98.0 percent of organic solvent. The printing ink composition can be applied to a water type ink jet printing device for printing on hydrophobic mediums such as glass, ceramics, metal and plastics.
Description
Technical field
The present invention relates to a kind of ink-jet recording device with ink composite and use the ink jet recording method of this ink composite, particularly can be at solvent-based ink composition of using on the water type ink-jet recording device and the ink jet recording method that on water type ink-jet recording device, prints with solvent-based ink composition.
Background technology
Ink-jet recording device can be divided into water type ink-jet recording device and solvent-borne type ink-jet recording device according to the type difference of employed ink composite.Wherein, water type ink-jet recording device uses with the water color ink of water as main solvent, and it is inner not corrosion-resistant with the contacted parts of printing ink.The solvent-borne type ink-jet recording device uses with the solvent type ink of organic solvent as main solvent, and it is inner all corrosion-resistant with the contacted parts of printing ink.
At present, use reaches its maturity and water type ink-jet recording device generally, but because of water in the employed water color ink has accounted for sizable ratio, therefore can only be used to be printed onto hydrophilic recording medium, on the hydrophobic recording medium such as glass, metal, pottery, plastics that is difficult to be printed onto water-fast surface, the printed image water tolerance that adds water color ink formation is also relatively poor, and this causes the application of water type ink-jet recording device to be subjected to limitation.
Though existing solvent type ink has excellent water tolerance; can be printed onto on the recording mediums such as glass, metal, pottery and plastics; but it can only be used for the solvent-borne type ink-jet printer usually, can occur shortcomings such as disconnected China ink, obstruction printhead, shutdown back start at intermittence fluency difference because of its physical and chemical parameter that can not adjust to the water type ink-jet printer that suits when being used for water type ink-jet printer.In addition, solvent-based inks also can cause corrosion to the parts that contact with printing ink in the not corrosion resistant water type printer usually.
Summary of the invention
The inkjet printing methods that order of the present invention is to provide the good solvent-based ink composition that can be used for water type inkjet-printing device of a kind of water resistance and uses this ink composite.
For realizing one of purpose of the present invention, one of technical scheme that the utility model provides is: composition for ink jet recording, contain: the water-insoluble dyestuff of 0.1～8.0 weight %; And 60.0～98.0 weight % organic solvent.
By in above-mentioned ink composite, improving the usage quantity of organic solvent, can make whole ink system transfer the hydrophobic system to by hydrophilic system, therefore can improve the water tolerance of ink composite, and then can use it on hydrophobic mediums such as glass, pottery, metal, plastics, to print.
Scheme is that the hydrogen bond value scope of organic solvent is between 12.0-19.0 preferably.The organic solvent corrodibility of hydrogen bond value in this scope is little, can make ink composite have less corrodibility, to be applicable to water type ink discharge device.
Better scheme is that organic solvent is selected from one or more the mixture in alcohol derivate, ether derivant or the ketone derivatives, to improve the wettability of ink composite, ink composite is obtained and the akin physico-chemical parameter of water type printing ink.
Better scheme is that dyestuff is selected from a kind of in solvent black 46, solvent black 29, solvent black 27, solvent black 28, solvent blue 5, solvent blue 4, solvent blue 70, solvent red 122, solvent red 119, solvent red 218, solvent red 124, solvent red 125, solvent red 49, solvent yellow 82, solvent yellow 19, the solvent yellow 79 or several mixing.Therefore above-mentioned dyestuff has excellent water tolerance, weather resisteant and have good solubility in organic solvent, can make ink composite have better water-fast, sun-proof performance and good fluency.
Again one preferably scheme be the tackiness agent that ink composite further comprises 1.0～20.0 weight %.Tackiness agent can guarantee that printing ink has the ability of certain sticking power and anti-physics or chemical action.
Better scheme is that tackiness agent is a spirit-soluble resin, because of itself and alcohol, pure ethers, ketone solvent etc. have good intermiscibility, can improve the tack of ink composite to hydrophobic medium.
Not bad scheme is that the viscosity of ink composite is 1～10Mpas, and the viscosity of this viscosity and corresponding common water-base ink is close, therefore can guarantee that ink composite has good fluency and stability when being used for water type inkjet-printing device.
Not bad scheme is that ink composite is further introduced deionized water, with the surface tension of controlling described ink composite between 29～38mN/m, so that the fluency of ink composite is better.
For realizing another object of the present invention, another technical scheme provided by the invention is: ink jet recording method, use aforementioned any ink composite to print on water type ink-jet recording device.
Embodiment
In ink composite of the present invention, can use various dyestuffs in the prior art as tinting material, preferred non-water-soluble dyestuff, preferably by the receptible cyan of aqueous ink, magenta, yellow or black solvent type dye, as solvent black 46, solvent black 29, solvent black 27, solvent black 28, solvent blue 5, solvent blue 4, solvent blue 70, solvent red 122, solvent red 119, solvent red 218, solvent red 124, solvent red 125, solvent red 49, solvent yellow 82, solvent yellow 19, solvent yellow 79 etc.
These dyestuffs can use separately, can also be with being used in combination more than 2 kinds or 2 kinds in them.
In ink composite of the present invention, the content of dyestuff can suitably be selected according to purposes or printing characteristic, and with respect to the gross weight of ink composite, the content of dyestuff can be 0.1～8.0 weight %.
In ink composite of the present invention, the hydrogen bond value of organic solvent can be controlled between 12.0～19.0, and preferably 12.8～18.8.Organic solvent can be selected any in alcohol derivate, ether derivant or the ketone derivatives, or several mixtures with arbitrary mixed in them.
As alcohol derivate can be ethanol, n-propyl alcohol, Virahol, propyl carbinol, isopropylcarbinol, isooctyl alcohol, ethylene glycol, Diethylene Glycol etc., wherein is preferably the primary alcohol of carbon 2～carbon 8.
As ether derivant can be n-butyl ether, ethyl isobutyl ether, ethylene glycol ethyl ether, propylene-glycol ethyl ether, butyl glycol ether, propylene glycol butyl ether, diethylene glycol ether, Diethylene Glycol butyl ether, triglycol ether, triglycol butyl ether etc., wherein is preferably glycol ethers.
As ketone derivatives can be acetone, butanone, pimelinketone, different Fu Er ketone etc.
Ink composite of the present invention can also further comprise tackiness agent except containing tinting material and organic solvent.Tackiness agent can guarantee that printing ink has certain sticking power, and the ability of anti-physics or chemical action.Tackiness agent can select to have with organic solvents such as alcohol, pure ethers, ketone solvents the spirit-soluble resin of good intermiscibility, to improve the tack of ink composite to hydrophobic mediums such as glass, metal, pottery and plastics.Spirit-soluble resin tackiness agent itself is water insoluble in addition, therefore can make ink composite have favorable waterproof property.Spirit-soluble resin can be that rosin remodeling Synolac, thermoplasticity phenol, aldehyde resin, polyketone resin, alcohol contain intermingle with any in the acid amides, also can be wherein several with arbitrary proportion blended mixture.Selecting preferably is that aldehyde resin or alcohol contain intermingle with acid amides, perhaps the mixture of the two.The content of tackiness agent can suitably be selected according to purposes or printing characteristic, and with respect to the gross weight of ink composite, its content can be 0.1～20.0 weight %, and is preferred 0.5%-15%, and preferably 1%-10%
The present invention passes through the selection of solvent, colorant and tackiness agent and the control of content, the viscosity of ink composite is adjusted to close, can be guaranteed that ink composite has good fluency and stability when being used for water type inkjet-printing device with the viscosity of corresponding common water-base ink.The viscosity of ink composite of the present invention is controlled between 1～10Mpas, preferably between 1.2～8Mpas, is preferably between 2～6Mpas.(LVDV～II+) tester records the viscosity of ink composite of the present invention by Brookfield Digital Viscometer.
Ink composite of the present invention can further comprise deionized water.Deionized water has good surface tension.The surface tension of ink composite of the present invention can be controlled between 29～38mN/m, between preferred 30～35mN/m.Deionized water low price in addition can reduce the cost of ink composite.The content of deionized water can suitably be selected according to the purposes and the printing characteristic of ink composite, and with respect to the gross weight of ink composite, the content of deionized water can be 0～20.0 weight %, and is preferred 1%-15%, and preferably 2%-10%.。
Ink composite of the present invention is except that containing colorant, organic solvent, tackiness agent, deionized water, can also further contain other additive that in common ink composite, contains, as contain oxidation inhibitor, sanitas, ultraviolet absorbers, PH conditioning agent etc., to improve the performance of ink composite at aspects such as storage stability, printing stability and image keeping qualities.
One of method of using ink composite printing of the present invention is that water type inkjet-printing device prints.Not only can keep the print performance consistent under this kind situation with water-base ink; as: constantly China ink, do not block printhead, intermittently to shut down back start fluency good; can reach simultaneously water type type printer is printed have good optical density on hydrophobic mediums such as glass, pottery, metal, plastics, the purpose of the image of wear resistance, sticking power and color; widen the Application Areas of water type inkjet-printing device, and remedied the deficiency that solvent-based ink composition in the past can not be used for water type ink-jet printer.
Embodiment 1
Modulate the ink composite that following gradation composition constitutes:
Solvent black 29:(Suzhou three prestige provide) weight 5.0%;
Propyl carbinol: weight 50.0%;
Propylene glycol butyl ether: weight 37.0%;
Butanone: weight 4.0%;
Deionized water: weight 2.2%;
Alcohol contains intermingle with acid amides: (commercially available) weight 1.8%.
Preparation method: with the propylene glycol butyl ether of 37.0 weight %, 30.0 the propyl carbinol of weight %, 2.2 the deionized water of weight %, 4.0 the butanone of weight % mixes in reactor, A～62 alcohol that add 1.8 weight % then in reactor contain intermingle with acid amides stirring at low speed to solution and clarify, and the propyl carbinol that adds solvent black 29, the 20.0 weight % of 5.0 weight % successively mixes in reactor.Airtight stirring 3 hours was left standstill 1 hour, 0.5 μ m filter element filtering, pack ink composite 1.
Embodiment 2
Solvent yellow 82:(Suzhou three prestige provide) weight 5.4%;
Virahol: isooctyl alcohol (1:1) weight 50.0%;
Propylene glycol butyl ether: weight 30.0%;
Butanone: weight 4.0%;
Deionized water: weight 8.8%;
Aldehyde resin: (commercially available) weight 1.8%;
Preparation method: with the propylene glycol butyl ether of 30.0 weight %, 30.0 the Virahol of weight %: isooctyl alcohol (1:1), 4.0 the butanone of weight %, 8.8 the deionized water of weight % mixes in reactor, KR～A81 aldehyde resin stirring at low speed to the solution that adds weight 1.8% in reactor is clarified then, and add the Virahol of solvent yellow 82, the 20.0 weight % of 5.4 weight % successively: isooctyl alcohol (1:1) mixes in reactor.Airtight stirring 3 hours was left standstill 1 hour, 0.5 μ m filter element filtering, pack ink composite 2
Embodiment 3
Solvent yellow 82:(Suzhou three prestige provide) weight 5.4%;
Virahol: weight 40.0%;
Propylene glycol butyl ether: weight 50.0%;
Deionized water: weight 2.6%;
Aldehyde resin: (commercially available) weight 2.0%;
Preparation method: with the propylene glycol butyl ether of 50.0 weight %, the deionized water of 2.6 weight %, 2.0 the KR of weight %～A81 aldehyde resin mixes in reactor, stirring at low speed to solution is clarified, and the Virahol that adds solvent yellow 82, the 40.0 weight % of 5.4 weight % successively mixes in reactor.Airtight stirring 3 hours was left standstill 1 hour, 0.5 μ m filter element filtering, pack ink composite 2
Comparative Examples 1
Modulation is used for the ink composite 3 of water type ink-jet printer:
The water stain (mixed black Ciba provides) weight 2.7%
Ethylene glycol: weight 2.0%
Glycerine: weight 15.0%
Ethylene glycol monobutyl ether: weight 3%
Surfynol 465 (tensio-active agent): weight 1%
PROXEL GXL (sanitas): weight 0.1%
Deionized water weight 76.2%
Comparative Examples 2
Modulation is used for the ink composite 4 of solvent-borne type inkjet-printing device
Yellow H4G 01 30 (Clariant provides) weight 8%;
Ethylene glycol monobutyl ether: weight 12.0%;
Butylacetate: weight 51.0%;
Pimelinketone: weight 18.0%;
Vinyl chloride-vinyl acetate resin: weight 4.0%;
Propyl carbinol: weight 15.0%.
The contrast experiment
On EPSON R230 water type ink-jet printer, use ink composite 1～4 on the original-pack printing paper of EPSON, ABS plastic plate, metal sheet, to carry out following printing test respectively:
Test event 1: print stability test: 100% goes out the China ink amount prints 3 print cartridges continuously.
Test event 2: wearability test: after the model drying, rub back and forth on the surface 20 times, see the cut on surface with 500 gram counterweights.
Test event 3: water-repellancy: after the model drying, half immerses in the water with model, and whether it fades to soak taking-up observation in 24 hours.
Test event 4: to the corrodibility of printer component: soak pipeline, printhead, pump accessory etc. with ink, observe its corrodibility.
Test event 5: to the performance test of ink sun-proof: ultraviolet lamp box, X～RITE colour density instrument, measure the colour density of hard copy before and after ultra violet lamp 4.5 hours.
Test result sees Table 1 to table 3.
Test result as can be seen from table 1 to table 3, than traditional aqueous ink composition, ink composite of the present invention is used for water type ink-jet printer, not only can obtain and the same printing stability of water color ink combination, but also have good wear resistance, water-repellancy, realized the purpose that water type inkjet-printing device prints on hydrophobic mediums such as plastics, metal sheet.Than traditional solvent borne ink, ink composite of the present invention is used for can not stopping up printhead on the water type inkjet-printing device, and can the interior and contacted parts of printing ink of corrosive water type inkjet-printing device.
Table 1:EPSON printing paper
| Assessment item | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative Examples 1 | Comparative Examples 2 |
| Print stability | Good | Good | Good | Good | Stop up shower nozzle |
| Wear resistance | Good | Good | Good | Good | Good |
| Water-repellancy | Good | Good | Good | Difference | Good |
| The corrodibility of component | Do not corrode | Do not corrode | Do not corrode | Do not corrode | Corrosion |
| Light permanency | Good | Good | Good | Difference | Good |
Table 2:ABS plastics
| Assessment item | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative Examples 1 | Comparative Examples 2 |
| Print stability | Good | Good | Good | Good | Stop up shower nozzle |
| Wear resistance | Good | Good | Good | Difference | Good |
| Water-repellancy | Good | Good | Good | Difference | Good |
| The corrodibility of component | Do not corrode | Do not corrode | Do not corrode | Do not corrode | Corrosion |
| Light permanency | Good | Good | Good | Difference | Good |
Table 3: metal sheet
| Assessment item | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative Examples 1 | Comparative Examples 2 |
| Print stability | Good | Good | Good | Good | Stop up shower nozzle |
| Wear resistance | Good | Good | Good | Difference | Good |
| Water-repellancy | Good | Good | Good | Difference | Good |
| The corrodibility of component | Do not corrode | Do not corrode | Do not corrode | Do not corrode | Corrosion |
| Light permanency | Good | Good | Good | Difference | Good |
Claims (10)
1, composition for ink jet recording is characterized in that, contains:
0.1 the water-insoluble dyestuff of～8.0 weight %; And
60.0～98.0 weight % organic solvents.
2, according to the described ink composite of claim 1, it is characterized in that:
The hydrogen bond value scope of described organic solvent is between 12.0～19.0.
3, according to the described ink composite of claim 2, its thing is levied and is:
Described organic solvent is selected from one or more the mixture in alcohol derivate, ether derivant or the ketone derivatives.
4, according to the described ink composite of claim 3, it is characterized in that:
Described dyestuff is selected from a kind of in solvent black 46, solvent black 29, solvent black 27, solvent black 28, solvent blue 5, solvent blue 4, solvent blue 70, solvent red 122, solvent red 119, solvent red 218, solvent red 124, solvent red 125, solvent red 49, solvent yellow 82, solvent yellow 19, the solvent yellow 79 or several mixing.
5, according to the described ink composite of claim 3, it is characterized in that: described ink composite further comprises the tackiness agent of 1.0～20.0 weight %.
6, according to the described ink composite of claim 5, it is characterized in that: described tackiness agent is a spirit-soluble resin.
7, according to each described ink composite of claim 1 to 6, it is characterized in that: the viscosity of described ink composite under 25 ℃ ± 2 ℃ is 1～10Mpas.
8, according to the described ink composite of claim 7, it is characterized in that:
Described ink composite further comprises deionized water.
9, described according to Claim 8 ink composite, it is characterized in that: the surface tension of described ink composite is between 29～38mN/m.
10, ink jet recording method is characterized in that: use each described ink composite of claim 1 to 9 to print on water type ink-jet recording device.