CN101450409A - Connection method of main body and batting panel of golf rod head - Google Patents
Connection method of main body and batting panel of golf rod head Download PDFInfo
- Publication number
- CN101450409A CN101450409A CNA2007101875903A CN200710187590A CN101450409A CN 101450409 A CN101450409 A CN 101450409A CN A2007101875903 A CNA2007101875903 A CN A2007101875903A CN 200710187590 A CN200710187590 A CN 200710187590A CN 101450409 A CN101450409 A CN 101450409A
- Authority
- CN
- China
- Prior art keywords
- batting panel
- club head
- glof club
- welding bead
- joint method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a method for jointing the body of a brassie head and a ball hitting panel. The method uses a filling gap welding process without smelting welding pieces for carrying out jointing operation. The method comprises: a step of providing the body, a step of providing the ball hitting panel, a step of coating a welding material into a welding channel groove, a step of embedding the ball hitting panel into the body and a step of carrying out the jointing operation of the body and the ball hitting panel. When operated, the method can achieve better jointing strength and simultaneously hold the finished precision before jointing.
Description
Technical field
The present invention relates to a kind of joint method of glof club head, particularly relate to and a kind ofly can increase bond strength, and keep the body of glof club head of the existing machining accuracy before engaging and the joint method of batting panel.
Background technology
Known golf clubs head structure mostly by be embedded cooperate or different welding manner in conjunction with a batting panel, but above-mentioned combination has many shortcomings, for example be embedded cooperation and cause the batting panel distortion easily, the rod head noumenon of welding xenogenesis material and batting panel can produce the compatible not enough problem of welding, and if use the known solder technology higher than the fusing point of weldment, its original machining accuracy before joint can can't be kept, and it is smooth and bright and clean that the body of this glof club head and the composition surface of batting panel are difficult for keeping, have again, the tissue property of body and batting panel is susceptible to also, and then cause stress concentrate and deflection big, can't keep the structure machining accuracy before engaging, have again, the body of this glof club head and the composition surface of batting panel can not keep well bright and clean, so must be in subsequent technique machining and shaping, finish the shaping of glof club head.
Defective for the batting panel combined structure that overcomes above-mentioned known glof club head, known technology development the technology of directly utilizing the gluing combination of high-intensity resin at normal temperatures, but, owing to be subject to the upper limit of the gluing bond strength of high-intensity resin, though rod head noumenon and batting panel use gluing combination can quicken technology and make, but when rod head noumenon is combined with batting panel, has the stress of enough bond strengths for the supporting batting.
Therefore, the rod head noumenon of known glof club head and batting panel, the not good defective of bond strength is arranged, can't effectively bear batting stress, known joining technique has many bonding and molding defectives simultaneously, so how to redesign a kind of joint method of glof club head, can increase bond strength and keep the preceding existing machining accuracy of joint, become practitioner's research and development purpose.
Summary of the invention
Main purpose of the present invention is, overcome the defective that the joint construction of the body of existing glof club head and batting panel exists, and provide a kind of body of new glof club head and the joint method of batting panel, technical problem to be solved is to make its rod head noumenon that solves known glof club head and batting panel use known joining technique to be combined with the problems such as defective of many bonding and moldings, also overcome simultaneously known joining technique, the defective that machines precision before can't keeping engaging, thus be suitable for practicality more.
The object of the invention to solve the technical problems realizes by the following technical solutions.The body of a kind of glof club head that proposes according to the present invention and the joint method of batting panel, the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, and it comprises the following step: a body is provided, and this body one side forms a welding bead groove; One batting panel is provided; Apply a scolder in this welding bead groove; Carry out this batting panel and insert this body operation; And the bonding operation of carrying out this body and this batting panel, make this solder fusing in this welding bead groove by this welding bead groove that heats this batting panel and this body, and make this body and this batting panel bonding and molding.
The object of the invention to solve the technical problems also can be applied to the following technical measures to achieve further.
The body of aforesaid glof club head and the joint method of batting panel, the wherein said scolder that applies is in welding bead groove step and carry out batting panel and insert the body operating procedure and can oppositely carry out in regular turn.
The body of aforesaid glof club head and the joint method of batting panel, wherein said welding bead groove comprise one with the stepped guide groove of this welding bead groove, in order to this scolder of drainage.
The body of aforesaid glof club head and the joint method of batting panel, this scolder of the nonfused filling weld seam of wherein said utilization weldment technology is a brazing metal.
The body of aforesaid glof club head and the joint method of batting panel, the mode of this body of wherein said heat and this batting panel are arc welding torch heating, LASER HEATING, flatiron heating, heat-treatment furnace heating, gas flame heating, immerse heating, high frequency heating or infrared ray heating.
The body of aforesaid glof club head and the joint method of batting panel, this welding bead groove of wherein said body also comprise one and support only structure.
The body of aforesaid glof club head and the joint method of batting panel, wherein said is a continuous ringwall to ending structure.
The body of aforesaid glof club head and the joint method of batting panel, wherein said is a discontinuous pad that is equidistantly or does not equidistantly arrange to ending structure.
The object of the invention to solve the technical problems also realizes by the following technical solutions.The body of a kind of glof club head that proposes according to the present invention and the joint method of batting panel, the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, and it comprises the following step: a body is provided, and this body one side forms a welding bead groove; One batting panel is provided; Carry out this batting panel and insert the body operation; Carry out this welding bead warm-up operation; Heating a bonding wire makes this bonding wire fusing insert the welding bead groove; And the bonding operation of carrying out this body and this batting panel, by the welding bead that heats this body and batting panel in advance and heat this scolder, this scolder is flowed in this welding bead groove slit because of capillarity, realize the bonding and molding of body and this batting panel.
The object of the invention to solve the technical problems also can be applied to the following technical measures to achieve further.
The body of aforesaid glof club head and the joint method of batting panel, wherein said welding bead groove comprise one with the stepped guide groove of this welding bead groove, in order to this scolder of drainage.
The body of aforesaid glof club head and the joint method of batting panel, this scolder of the nonfused filling weld seam of wherein said utilization weldment technology is a brazing metal.
The body of aforesaid glof club head and the joint method of batting panel, the mode of this body of wherein said preheating and this batting panel are arc welding torch heating, LASER HEATING, heat-treatment furnace heating, gas flame heating, high frequency heating or infrared ray heating.
The body of aforesaid glof club head and the joint method of batting panel, this welding bead groove of wherein said body also comprise one and support only structure.
The body of aforesaid glof club head and the joint method of batting panel, wherein said is a continuous ringwall to ending structure.
The body of aforesaid glof club head and the joint method of batting panel, wherein said is a discontinuous pad that is equidistantly or does not equidistantly arrange to ending structure.
The present invention compared with prior art has tangible advantage and beneficial effect.As known from the above, in order to achieve the above object, the invention provides a kind of body of glof club head and the joint method of batting panel, the nonfused filling weld seam of utilization weldment technology is carried out bonding operation, this joint method comprises provides a body step, one batting panel step is provided, apply a scolder in welding bead groove step, carry out batting panel and insert the body operating procedure, carry out the bonding operation step of body and batting panel, one body step is provided earlier, and the one side forms a welding bead groove, then, one batting panel step is provided, apply a scolder again in welding bead groove step, then, carry out batting panel and insert the body operation, at last, carry out the bonding operation of body and batting panel, solder fusing is filled in the gap of batting panel and welding bead groove, make body and batting panel bonding and molding by the welding bead groove that heats batting panel and body.
Via as can be known above-mentioned, the invention discloses a kind of body of glof club head and the joint method of batting panel, the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, this joint method comprises provides a body step, one batting panel step is provided, apply a scolder in welding bead groove step, carry out the bonding operation step that batting panel is inserted the body operating procedure and carried out body and batting panel, during the invention process utilization, can reach preferable bond strength, machine precision before also keeping simultaneously engaging.
By technique scheme, the body of a kind of glof club head of the present invention and the joint method of batting panel have following advantage at least:
1. the present invention is a kind of body of glof club head and the joint method of batting panel, this body and this batting panel are two weldments, the nonfused filling weld seam of utilization weldment technology is carried out structural engagement, enforcement utilization by the joint method of the body of this glof club head and batting panel, can make the unaffected and stress of the tissue property of body and batting panel and be out of shape little, so can keep the structure machining accuracy before engaging, have, it is well bright and clean that the body of this glof club head and the composition surface of batting panel can keep again.
2. the present invention is a kind of body of glof club head and the joint method of batting panel, this body and this batting panel are two weldments, the nonfused filling weld seam of utilization weldment technology is carried out structural engagement, enforcement utilization by the joint method of the body of this glof club head and batting panel, can the body and the batting panel of heterogeneity and different size be engaged, and can boost productivity the whole heating of weldment.
Above-mentioned explanation only is the general introduction of technical solution of the present invention, for can clearer understanding technological means of the present invention, and can be implemented according to the content of specification, and for above-mentioned and other purposes, feature and advantage of the present invention can be become apparent, below especially exemplified by preferred embodiment, and conjunction with figs., be described in detail as follows.
Description of drawings
Figure 1A is the first example flow chart of a preferred embodiment of the joint method of the body of glof club head of the present invention and batting panel.
Figure 1B is the second example flow chart of a preferred embodiment of the joint method of the body of glof club head of the present invention and batting panel.
Fig. 2 A is the body of glof club head of the present invention and a preferred embodiment first example generalized section of batting panel.
Fig. 2 B is a preferred embodiment first example generalized section of the body coated with solder of glof club head of the present invention.
The a preferred embodiment first example generalized section that Fig. 2 C finishes for the joint of the body of glof club head of the present invention and batting panel.
Fig. 3 A is the body of glof club head of the present invention and a preferred embodiment second example generalized section of batting panel.
Fig. 3 B places a preferred embodiment second example generalized section of body for the batting panel of glof club head of the present invention.
The a preferred embodiment second example schematic diagram that Fig. 3 C finishes for the joint of the body of glof club head of the present invention and batting panel.
Fig. 4 is another preferred embodiment flow chart of the joint method of the body of glof club head of the present invention and batting panel.
Fig. 5 A is a shaping aspect generalized section of another preferred embodiment of the body of glof club head of the present invention and batting panel.
Fig. 5 B places a shaping aspect generalized section of another preferred embodiment of body for the batting panel of glof club head of the present invention.
Fig. 5 C is the shaping aspect generalized section that the body of glof club head of the present invention carries out another preferred embodiment of welding bead preheating.
Fig. 5 D is a shaping aspect generalized section of another preferred embodiment of the joint of the body of glof club head of the present invention and batting panel.
Another shaping aspect generalized section of the preferred embodiment that Fig. 5 E finishes for the joint of the body of glof club head of the present invention and batting panel.
Fig. 6 ends structural representation for one of the welding bead groove of glof club head of the present invention supports.
Fig. 7 ends structural representation for another of the welding bead groove of glof club head of the present invention supports.
1: glof club head 10: body
11: welding bead groove 111: ringwall
112: pad 20: batting panel
30: scolder 40,40 ': welding gun
The specific embodiment
Reach technological means and the effect that predetermined goal of the invention is taked for further setting forth the present invention, below in conjunction with accompanying drawing and preferred embodiment, the body of the glof club head that foundation the present invention is proposed and its specific embodiment of joint method, structure, feature and the effect thereof of batting panel, describe in detail as after.
At first, please refer to Figure 1A, the present invention is a kind of body of glof club head and the joint method of batting panel, this body and this batting panel are two weldments, and the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, the nonfused filling weld seam of weldment technology is made filling weld seam technology for the weldment fusing point is higher than scolder herein, and the joint method S1 of the body of this glof club head and batting panel comprises provides a body (step S10), one batting panel (step S20) is provided, apply a scolder in welding bead groove (step S30), carry out the bonding operation (step S50) that batting panel is inserted body operation (step S40) and carried out body and batting panel.
The present invention is the body of glof club head and the joint method of batting panel, this body and this batting panel are two weldments, and the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, the nonfused filling weld seam of weldment technology is made filling weld seam technology for the weldment fusing point is higher than scolder herein, please refer to Figure 1A and Fig. 2 A, one body (step S10) is provided earlier, the body 10 of this glof club head 1 is provided, these body 10 1 sides form a welding bead groove 11, then, one batting panel (step S20) is provided, the batting panel 20 of this glof club head 1 is provided, then, please refer to Fig. 2 B, apply a scolder in welding bead groove (step S30), apply the welding bead groove 11 of a scolder 30 in above-mentioned body 10, have again, please refer to Figure 1A and Fig. 2 C, carry out batting panel and insert body operation (step S40), batting panel 20 is inserted in the welding bead groove 11 of body 10, at last, carry out the bonding operation (step S50) of body and batting panel, the welding bead groove 11 by a welding gun 40 heating batting panels 20 and body 10 melts in welding bead groove 11 scolder 30, make body 10 and batting panel 20 bonding and moldings, and then finish the making of glof club head 1.
Have again, please refer to Figure 1B, the present invention is a kind of body of glof club head and the joint method of batting panel, this body and this batting panel are two weldments, and the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, the nonfused filling weld seam of weldment technology is made filling weld seam technology for the weldment fusing point is higher than scolder herein, and the joint method S1 ' of the body of this glof club head and batting panel comprises provides a body (step S10), one batting panel (step S20) is provided, carry out batting panel and insert body operation (step S30 '), apply a scolder in welding bead groove (step S40 ') and carry out the bonding operation (step S50) of body and batting panel.
The present invention is the body of glof club head and the joint method of batting panel, this body and this batting panel are two weldments, and the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, the nonfused filling weld seam of weldment technology is made filling weld seam technology for the weldment fusing point is higher than scolder herein, another example of joint method S1 of the body of this glof club head and batting panel, please refer to Figure 1B and Fig. 3 A, one body (step S10) is provided earlier, the body 10 of this glof club head 1 is provided, these body 10 1 sides form a welding bead groove 11, then, please refer to Figure 1B, Fig. 3 B and Fig. 3 C, one batting panel (step S20) is provided, the batting panel 20 of this glof club head 1 is provided, then, carry out batting panel and insert body operation (step S30 '), batting panel 20 is placed in the body 10, in particular, batting panel 20 is placed in the welding bead groove 11 of body 10, then, apply a scolder in welding bead groove (step S40 '), apply a scolder 30 in above-mentioned body 10, at last, carry out the bonding operation (step S50) of body and batting panel, heat the welding bead groove 11 of batting panels 20 and body 10 again by a welding gun 40, scolder 30 is melted in the gap of batting panel and welding bead groove 11, so as to making body 10 and batting panel 20 bonding and moldings, and then finish the making of glof club head 1.
Please refer to Fig. 4, the body of glof club head of the present invention and the joint method of batting panel, the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, the nonfused filling weld seam of weldment technology is made filling weld seam technology for the weldment fusing point is higher than scolder herein, the joint method S1 of the body of this glof club head and batting panel " comprises, a body (step S10 ") is provided, one batting panel (step S20 "); carry out batting panel and insert body operation (step S30 ") is provided, carry out welding bead warm-up operation (step S40 "); heat a bonding wire and make bonding wire fusing insert welding bead groove (step S50 ") and carry out the bonding operation (step S60 ") of body and batting panel.
The present invention is the body of glof club head and the joint method of batting panel, the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, the nonfused filling weld seam of weldment technology is made filling weld seam technology for the weldment fusing point is higher than scolder herein, please refer to Fig. 4 and Fig. 5 A, one body (step S10 "); a batting panel (step S20 ") is provided is provided, the another form joint method of the body 10 of this glof club head 1 and batting panel 20, comprise a body 10 and a batting panel 20 equally, these body 10 1 sides form a welding bead groove 11, please refer to Fig. 4 and Fig. 5 B, carry out batting panel and insert body operation (step S30 "); above-mentioned batting panel 20 is placed in the body 10; please refer to Fig. 4 and Fig. 5 C; carry out welding bead warm-up operation (step S40 "), with the welding bead groove 11 of body 10 by a welding gun 40 ' carry out warm-up operation, refer again to Fig. 4 and Fig. 5 D, heat a bonding wire make bonding wire fusing insert the welding bead groove (step S50 "); with a scolder 30 with in the gap of sending bonding wire 50 modes and through heating after, flowing into batting panel and welding bead groove 11; at last; please refer to Fig. 4 and Fig. 5 E; carry out bonding operation (the step S60 ") of body and batting panel, by the welding bead groove 11 of heater body 10 in advance, scolder 30 is melted in welding bead groove 11, make body 10 and batting panel 20 bonding and moldings, finish the making of glof club head 1.
The present invention is the body of glof club head and the connected structure of batting panel, this body and this batting panel are two weldments, and the nonfused filling weld seam of its utilization weldment technology is carried out structural engagement, the nonfused filling weld seam of weldment technology is made filling weld seam technology for the weldment fusing point is higher than scolder herein, above-mentioned welding bead groove 11 can further comprise a guide groove (not shown) stepped with welding bead groove 11, and this guide groove is used for the drainage scolder.
The present invention is the body of glof club head and the connected structure of batting panel, this body and this batting panel are two weldments, and the nonfused filling weld seam of its utilization weldment technology is carried out structural engagement, the nonfused filling weld seam of weldment technology is made filling weld seam technology for the weldment fusing point is higher than scolder herein, the welding bead groove 11 of above-mentioned body 10 further comprises one again and supports only structure, be used for ending for fixing the supporting of batting panel, please refer to Fig. 6, this only supports, and structure is a continuous ringwall 111, perhaps, please refer to Fig. 7, this is a discontinuous pad 112 that is equidistantly or does not equidistantly arrange to ending structure.
At last, the present invention is a kind of body of glof club head and the connected structure of batting panel, this body and this batting panel are two weldments, and the nonfused filling weld seam of its utilization weldment technology is carried out structural engagement, the nonfused filling weld seam of weldment technology is made filling weld seam technology for the weldment fusing point is higher than scolder herein, the scolder of the nonfused filling weld seam of above-mentioned utilization weldment technology is a brazing metal, and the joint method of the body of this glof club head and batting panel, the mode of its preheating body 10 and batting panel 20, above-mentioned for the arc welding torch heating, also can be LASER HEATING, the flatiron heating, the heat-treatment furnace heating, the gas flame heating, immerse heating, high frequency heating or infrared ray heating.
The above, it only is preferred embodiment of the present invention, be not that the present invention is done any pro forma restriction, though the present invention discloses as above with preferred embodiment, yet be not in order to limit the present invention, any those skilled in the art, in not breaking away from the technical solution of the present invention scope, when the technology contents that can utilize above-mentioned announcement is made a little change or is modified to the equivalent embodiment of equivalent variations, in every case be not break away from the technical solution of the present invention content, according to technical spirit of the present invention to any simple modification that above embodiment did, equivalent variations and modification all still belong in the scope of technical solution of the present invention.
Claims (15)
1, the joint method of a kind of body of glof club head and batting panel, the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, it is characterized in that it comprises the following step:
One body is provided, and this body one side forms a welding bead groove;
One batting panel is provided;
Apply a scolder in this welding bead groove;
Carry out the operation that this batting panel is inserted this body; And
Carry out the bonding operation of this body and this batting panel, make this solder fusing in this welding bead groove by this welding bead groove that heats this batting panel and this body, and make this body and this batting panel bonding and molding.
2, the joint method of the body of glof club head according to claim 1 and batting panel is characterized in that the wherein said scolder that applies is in welding bead groove step and carry out batting panel and insert the body operating procedure and can oppositely carry out in regular turn.
3, the joint method of the body of glof club head according to claim 1 and batting panel, it is characterized in that wherein said welding bead groove comprise one with the stepped guide groove of this welding bead groove, in order to this scolder of drainage.
4, the joint method of the body of glof club head according to claim 1 and batting panel is characterized in that this scolder of the nonfused filling weld seam of wherein said utilization weldment technology is a brazing metal.
5, the joint method of the body of glof club head according to claim 1 and batting panel, the mode that it is characterized in that this body of wherein said heat and this batting panel are arc welding torch heating, LASER HEATING, flatiron heating, heat-treatment furnace heating, gas flame heating, immerse heating, high frequency heating or infrared ray heating.
6, the joint method of the body of glof club head according to claim 1 and batting panel is characterized in that this welding bead groove of wherein said body also comprises one to ending structure.
7, the joint method of the body of glof club head according to claim 6 and batting panel is characterized in that wherein said is a continuous ringwall to ending structure.
8, the joint method of the body of glof club head according to claim 6 and batting panel is characterized in that wherein said is a discontinuous pad that is equidistantly or does not equidistantly arrange to ending structure.
9, the joint method of a kind of body of glof club head and batting panel, the nonfused filling weld seam of its utilization weldment technology is carried out bonding operation, it is characterized in that it comprises the following step:
One body is provided, and this body one side forms a welding bead groove;
One batting panel is provided;
Carry out the operation that this batting panel is inserted body;
Carry out this welding bead warm-up operation;
Heating a bonding wire makes this bonding wire fusing insert the welding bead groove; And
Carry out the bonding operation of this body and this batting panel, by the welding bead that heats this body and batting panel in advance and heat this scolder, this scolder is flowed in this welding bead groove slit because of capillarity, realize the bonding and molding of body and this batting panel.
10, the joint method of the body of glof club head according to claim 9 and batting panel, it is characterized in that wherein said welding bead groove comprise one with the stepped guide groove of this welding bead groove, in order to this scolder of drainage.
11, the joint method of the body of glof club head according to claim 9 and batting panel is characterized in that this scolder of the nonfused filling weld seam of wherein said utilization weldment technology is a brazing metal.
12, the joint method of the body of glof club head according to claim 9 and batting panel, the mode that it is characterized in that this body of wherein said preheating and this batting panel are arc welding torch heating, LASER HEATING, heat-treatment furnace heating, gas flame heating, high frequency heating or infrared ray heating.
13, the joint method of the body of glof club head according to claim 9 and batting panel is characterized in that this welding bead groove of wherein said body also comprises one to ending structure.
14, the joint method of the body of glof club head according to claim 13 and batting panel is characterized in that wherein said is a continuous ringwall to ending structure.
15, the joint method of the body of glof club head according to claim 13 and batting panel is characterized in that wherein said is a discontinuous pad that is equidistantly or does not equidistantly arrange to ending structure.