Summary of the invention
In order to solve metal part surface in making the antiseptic process of galvanizing; the thickness that occurs increasing zinc-impregnating layer for the good threaded hole of preprocessing; cause difficult problem for the installation of metal parts; the invention provides the guard method of a kind of metal component screwed hole in the galvanizing rotproofing; the staff is taken this method; can make metal part surface in making the antiseptic process of galvanizing; do not increase the thickness of zinc-impregnating layer; when having avoided thread mill drilling because the increase of the thickness of zinc-impregnating layer; and the difficulty of accurately determining the thickness of galvanizing that occurs has solved the accurate installation question of galvanizing metal parts.
For achieving the above object, the technical solution used in the present invention is:
The guard method of a kind of metal component screwed hole in the galvanizing rotproofing, it mainly may further comprise the steps:
The first step, the preparation mastic is poured terra alba in the container into, according to volume ratio
Terra alba: water=3-4: 1
Pour water into, stir, churning time is 30 to 120 seconds, and container is rolled, and container is rocked with top rade according to being 30 degree with level again, melts fully mutually with water until terra alba, forms mastic;
Second step was packed into said mastic in the threaded hole to be protected of metal parts with iron plate, and the extruding of filling back is closely knit, smoothly wipes remaining mastic off with iron plate;
In the 3rd step, the metal parts of above-mentioned populated mastic is done the galvanizing rotproofing;
The 4th step, the mastic that is packed into metal parts is taken out, clean out threaded hole, finish the protection of metal component screwed hole in heat dip zinc treating.
Said metal component screwed hole in the technique scheme also can be cylinder shape threaded hole or circular cone bench-type threaded hole.
The said threaded hole of technique scheme only is applicable to logical threaded hole, is not suitable for blind threaded hole.
The principle of method of the present invention is:
Gypsum is resistant to elevated temperatures material, and its chemical structure is behind the chance water
C
aSO
4·2H
2O
C
aSO
4With acids such as hydrochloric acid, sulfuric acid chemical reaction not taking place, guarantees that mastic is intact in the acid cleaning process before galvanizing.Contain two crystal water molecules in the gypsum, just contain weight and account for 21% water greatly, Here it is so-called " fire extinguishing water ", and when high temperature, above-mentioned mastic can discharge the crystal water molecule in this structure of matter,
These water moleculess can be diffused in the air on metal component screwed hole surface rapidly; and then in metal component screwed hole surface formation one deck vapor membrane; said aqueous vapor film both can reduce the temperature on metal component screwed hole surface; can play again isolate oxygen effect; so these performances of gypsum can be born the high temperature of galvanizing and no change fully when the parts galvanizing that is used for metal; this material itself is pollution-free; not easy to crack in the use; this performance meets the requirement of the preceding protection of galvanizing threaded hole; and the mastic plasticity-of making is strong, makes things convenient for actually operating.
The present invention has more following effects and positively effect:
The invention provides the guard method of a kind of metal component screwed hole in the galvanizing rotproofing; the staff is taken this method; can make metal part surface in making the antiseptic process of galvanizing; do not increase the thickness of metal component screwed hole zinc-impregnating layer; avoided thread mill drilling can't install or other problems owing to the thickness that increases zinc-impregnating layer causes; can guarantee that metal parts soaks the quality of the screw thread of preprocessing behind the zinc, present method is simple, can raise labour efficiency greatly.
Specific implementation method:
The present invention will be further described in detail below in conjunction with embodiment:
Embodiment 1:
The guard method of a kind of metal component screwed hole in the galvanizing rotproofing, it mainly may further comprise the steps:
The first step, the preparation mastic is poured terra alba in the container into for three parts, according to volume ratio
Terra alba: water=3-4: 1
Pour a water into, stir, churning time is 100 seconds, and container is rolled, and rocks with top rade according to being 30 degree with level again, melts fully mutually with water until terra alba, forms mastic;
Second step was packed into said mastic in the cylinder shape threaded hole to be protected of metal parts with iron plate, and the extruding of filling back is closely knit, smoothly wipes remaining mastic off with iron plate;
In the 3rd step, the metal parts of above-mentioned populated mastic is done the galvanizing rotproofing;
The 4th step, the mastic that is packed into metal parts is taken out, clean out threaded hole, finish metal component screwed hole in the protection in heat dip zinc treating.