CN101429662A - 一种用于低硬度低碱度水体系的碳素钢复合缓蚀剂 - Google Patents
一种用于低硬度低碱度水体系的碳素钢复合缓蚀剂 Download PDFInfo
- Publication number
- CN101429662A CN101429662A CNA2008102367823A CN200810236782A CN101429662A CN 101429662 A CN101429662 A CN 101429662A CN A2008102367823 A CNA2008102367823 A CN A2008102367823A CN 200810236782 A CN200810236782 A CN 200810236782A CN 101429662 A CN101429662 A CN 101429662A
- Authority
- CN
- China
- Prior art keywords
- carbon steel
- corrosion inhibitor
- steel composite
- low
- composite corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用于低硬度低碱度水体系的碳素钢复合缓蚀剂,按重量百分比计,由16%~29%多羟基羧酸盐、6%~28%钨酸盐、2%~10%聚羧酸、3%~5%羧酸共聚物、1.5%~2.5%锌盐、39%~55%水组成。用于低硬度低碱度水系统的碳素钢防腐蚀,碳素钢腐蚀速度小于GB 50050-2007规定值(0.125mm/a)。本发明碳素钢复合缓蚀剂制备简单、不含磷,对环境无污染、有利于环境保护。
Description
技术领域
本发明涉及一种用于低硬度低碱度水体系的碳素钢复合缓蚀剂。本发明属于化学和水处理领域。
背景技术
低硬度低碱度水对碳素钢的腐蚀性很强,所以低硬度低碱度水系统的碳素钢腐蚀问题是工业用水系统中比较难解决的问题。为了减轻碳素钢腐蚀,一般采取添加缓蚀剂、阴极保护、涂敷防腐漆等防腐措施,以添加缓蚀剂最常用。目前运用最广的磷系缓蚀剂因为磷含量较大,排放水体后容易引起富营养化,造成环境污染。所以研制一种不含磷的环保型碳素钢缓蚀剂是非常必要的。
由于低硬度低碱度水具有很强的腐蚀性,目前还没有一种缓蚀剂单体能满足这类水质条件下的防腐要求。研究结果表明,采用多种缓蚀剂单体混合,利用单体之间存在的协同作用,制成一种复合缓蚀剂,不仅可以降低缓蚀剂的用量、提高缓蚀效果,而且可以降低成本。近十几年来,出现了环境友好且缓蚀性能良好的葡萄糖酸钠、聚环氧琥珀酸、聚天冬氨酸、钨酸盐等一些缓蚀剂单体,这为开发环保型复合碳素钢缓蚀剂奠定了基础。
发明内容
本发明的目的是提供一种用于低硬度低碱度水体系的环保型碳素钢复合缓蚀剂,该复合缓蚀剂制备简单、防腐蚀能力强、对环境无污染。
本发明提供的技术方案是:一种用于低硬度低碱度水体系的碳素钢复合缓蚀剂,按重量百分比计,由16%~29%多羟基羧酸盐、6%~28%钨酸盐、2%~10%聚羧酸、3%~5%羧酸共聚物、1.5%~2.5%锌盐、39%~55%水组成。
上述多羟基羧酸盐为葡萄糖酸钠。
上述钨酸盐为钨酸钾或钨酸钠或二水钨酸钠。
上述聚羧酸为聚天冬氨酸或聚环氧琥珀酸。
上述羧酸共聚物为马来酸-丙烯酸共聚物(MA/AA)。
上述锌盐为无水硫酸锌或七水硫酸锌。
本发明碳素钢复合缓蚀剂制备方法是:将缓蚀剂的各组分和水混合均匀,此混合液即为产品。
本发明的有益效果是:本发明碳素钢复合缓蚀剂制备简单、用于低硬度低碱度水系统的碳素钢防腐蚀,碳素钢腐蚀速度小于GB50050-2007规定值0.125mm/a;复合缓蚀剂不含磷,有利于环境保护。
用于低硬度低碱度水体系的碳素钢复合缓蚀剂的使用剂量为200mg/L~300mg/L。
具体实施方式
实施例1
用于低硬度低碱度水体系的碳素钢复合缓蚀剂,以复合药剂重量为100%计,包括:由16%葡萄糖酸钠、28%钨酸钠、10%聚天冬氨酸、4%羧酸共聚物、2%锌盐、40%水组成。其制备方法是:将缓蚀剂的各组分和水混合均匀即为产品。当使用复合缓蚀剂的剂量为220mg/L时,碳素钢腐蚀速度等于0.0090mm/a。
实施例2
用于低硬度低碱度水体系的碳素钢复合缓蚀剂,以复合药剂重量为100%计,包括:由27%葡萄糖酸钠、15%钨酸钾、2.5%聚环氧琥珀酸、3.5%羧酸共聚物、2%锌盐、50%水组成。其制备方法是:将缓蚀剂的各组分和水混合均匀即为产品。当使用复合缓蚀剂的剂量为270mg/L时,碳素钢腐蚀速度等于0.0040mm/a。
实施例3
用于低硬度低碱度水体系的碳素钢复合缓蚀剂,以复合药剂重量为100%计,包括:由23%葡萄糖酸钠、22%二水钨酸钠、6%聚天冬氨酸、4%羧酸共聚物、2%锌盐、43%水组成。其制备方法是:将缓蚀剂的各组分和水混合均匀即为产品。当使用复合缓蚀剂的剂量为240mg/L时,碳素钢腐蚀速度等于0.0061mm/a。
实施例4
用于低硬度低碱度水体系的碳素钢复合缓蚀剂,以复合药剂重量为100%计,包括:由29%葡萄糖酸钠、6%钨酸钾、5%聚天冬氨酸、3.5%羧酸共聚物、1.5%锌盐、55%水组成。其制备方法是:将缓蚀剂的各组分和水混合均匀即为产品。当使用复合缓蚀剂的剂量为300mg/L时,碳素钢腐蚀速度等于0.0101mm/a。
上述所用羧酸共聚物为马来酸-丙烯酸共聚物(MA/AA)。
Claims (6)
1.一种用于低硬度低碱度水体系的碳素钢复合缓蚀剂,按重量百分比计,由16%~29%多羟基羧酸盐、6%~28%钨酸盐、2%~10%聚羧酸、3%~5%羧酸共聚物、1.5%~2.5%锌盐、39%~55%水组成。
2.根据权利要求1所述的碳素钢复合缓蚀剂,其特征是:多羟基羧酸盐为葡萄糖酸钠。
3.根据权利要求1或2所述的碳素钢复合缓蚀剂,其特征是:钨酸盐为钨酸钾或钨酸钠或二水钨酸钠。
4.根据权利要求1或2所述的碳素钢复合缓蚀剂,其特征是:聚羧酸为聚天冬氨酸或聚环氧琥珀酸。
5.根据权利要求1或2所述的碳素钢复合缓蚀剂,其特征是:羧酸共聚物为马来酸-丙烯酸共聚物。
6.根据权利要求1或2所述的碳素钢复合缓蚀剂,其特征是:锌盐为无水硫酸锌或七水硫酸锌。