CN101423616A - 彩色彩虹水晶树脂及制备工艺 - Google Patents
彩色彩虹水晶树脂及制备工艺 Download PDFInfo
- Publication number
- CN101423616A CN101423616A CNA200710144545XA CN200710144545A CN101423616A CN 101423616 A CN101423616 A CN 101423616A CN A200710144545X A CNA200710144545X A CN A200710144545XA CN 200710144545 A CN200710144545 A CN 200710144545A CN 101423616 A CN101423616 A CN 101423616A
- Authority
- CN
- China
- Prior art keywords
- weight
- unsaturated polyester
- crystal resin
- parts
- polyester resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
彩色彩虹水晶树脂及制备工艺，目前的不饱和聚酯树脂所用的着色剂——色糊，只是对不饱和聚酯树脂进行着色，色泽混浊的同时，并没有水晶般的透明感。彩色彩虹水晶树脂，其组成包括：不饱和聚酯树脂基料、水彩颜料、水粉颜料、染料、水性有机色浆，所述的不饱和聚酯树脂基料的重量份数为100，所述的水彩颜料的重量份数为0.1～0.5，所述的水粉颜料的重量份数为0.1～0.5，所述的染料的重量份数为0.1～0.5，所述的水性有机色浆的重量份数为0.1～0.3。本发明用于工业法加工生产彩色彩虹水晶树脂。
Description
技术领域：
本发明涉及一种彩色彩虹水晶树脂及制备工艺。
背景技术：
目前的不饱和聚酯树脂所用的着色剂——色糊，只是对不饱和聚酯树脂进行着色，色泽混浊的同时，并没有水晶般的透明感。
发明内容：
本发明的目的是提供一种彩色彩虹水晶树脂及制备工艺，产品色泽鲜艳、晶莹剔透。
上述的目的通过以下的技术方案实现：
彩色彩虹水晶树脂，其组成包括：不饱和聚酯树脂基料、水彩颜料、水粉颜料、染料、水性有机色浆，所述的不饱和聚酯树脂基料的重量份数为100，所述的水彩颜料的重量份数为0.1～0.5，所述的水粉颜料的重量份数为0.1～0.5，所述的染料的重量份数为0.1～0.5，所述的水性有机色浆的重量份数为0.1～0.3。
所述的彩色彩虹水晶树脂，含有特殊钻石珑光泽效果颜料的重量份数为0.5。
所述的彩色彩虹水晶树脂的制备工艺是：按上述重量份数比在不饱和聚酯树脂基料中，添加水彩颜料、水粉颜料、染料、水性有机色浆、特殊钻石珑光泽效果颜料，搅拌均匀，静止12～24小时后，过滤，即得到彩色彩虹水晶树脂。
所述的彩色彩虹水晶树脂，所述的水性有机色浆为永固紫或酞菁蓝。
这个技术方案有以下有益效果：
1.本发明产品由不饱和聚酯树脂基料、水彩颜料、水粉颜料、染料、水性有机色浆、特殊钻石珑光泽效果颜料制成，色泽鲜艳、明亮如镜、晶莹剔透，发出犹如水晶钻石般的光泽。
2.本发明所用的材料廉价并且容易获得，工艺简单易行，有利于大型工业化生产。
本发明的具体实施方式：
实施例1：
一种彩色彩虹水晶树脂，其组成包括：不饱和聚酯树脂基料、水彩颜料、水粉颜料、染料、水性有机色浆，所述的不饱和聚酯树脂基料的重量份数为100，所述的水彩颜料的重量份数为0.1～0.5，所述的水粉颜料的重量份数为0.1～0.5，所述的染料的重量份数为0.1～0.5，所述的水性有机色浆的重量份数为0.1～0.3。
实施例2：
一种彩色彩虹水晶树脂，其组成包括：不饱和聚酯树脂基料、水彩颜料、水粉颜料、染料、水性有机色浆，所述的不饱和聚酯树脂基料的重量份数为100，所述的水彩颜料的重量份数为0.1～0.5，所述的水粉颜料的重量份数为0.1～0.5，所述的染料的重量份数为0.1～0.5，所述的水性有机色浆的重量份数为0.1～0.3。
所述的彩色彩虹水晶树脂，含有特殊钻石珑光泽效果颜料的重量份数为0.5。
所述的彩色彩虹水晶树脂的制备工艺是：按上述重量份数比在不饱和聚酯树脂基料中，添加水彩颜料、水粉颜料、染料、水性有机色浆、特殊钻石珑光泽效果颜料，搅拌均匀，静止12～24小时后，过滤，即得到彩色彩虹水晶树脂。
所述的彩色彩虹水晶树脂及制备工艺，所述的水性有机色浆为永固紫或酞菁蓝。
实施例3：
在100g不饱和聚酯树脂基料中，添加水彩颜料0.1g、水粉颜料0.5g、染料0.1g、永固紫0.1g，搅拌均匀，静止12小时后，过滤，即得到彩色彩虹水晶树脂。
实施例4：
在100g不饱和聚酯树脂基料中，添加水彩颜料0.5g、水粉颜料0.1g、染料0.5g、永固紫0.1g、特殊钻石珑光泽效果颜料0.5g，搅拌均匀，静止24小时后，过滤，即得到彩色彩虹水晶树脂。
实施例5：
在100g不饱和聚酯树脂基料中，添加水彩颜料0.4g、水粉颜料0.5g、染料0.3g、酞菁蓝0.1g、特殊钻石珑光泽效果颜料0.5g，搅拌均匀，静止18小时后，过滤，即得到彩色彩虹水晶树脂。
实施例6：
在100g不饱和聚酯树脂基料中，添加水彩颜料0.3g、水粉颜料0.5g、染料0.4g、酞菁蓝0.1g，搅拌均匀，静止20小时后，过滤，即得到彩色彩虹水晶树脂。
Claims (5)
1.一种彩色彩虹水晶树脂，其组成包括：不饱和聚酯树脂基料、水彩颜料、水粉颜料、染料、水性有机色浆，其特征是：所述的不饱和聚酯树脂基料的重量份数为100，所述的水彩颜料的重量份数为0.1～0.5，所述的水粉颜料的重量份数为0.1～0.5，所述的染料的重量份数为0.1～0.5，所述的水性有机色浆的重量份数为0.1～0.3。
2.根据权利要求1所述的彩色彩虹水晶树脂，其特征是：含有特殊钻石珑光泽效果颜料的重量份数为0.5。
3.根据权利要求1或2所述的彩色彩虹水晶树脂的制备工艺是：按上述重量份数比在不饱和聚酯树脂基料中，添加水彩颜料、水粉颜料、染料、水性有机色浆、特殊钻石珑光泽效果颜料，搅拌均匀，静止12～24小时后，过滤，即得到彩色彩虹水晶树脂。
4.根据权利要求1或2所述的彩色彩虹水晶树脂，其特征是：所述的水性有机色浆为永固紫或酞菁蓝。
5.根据权利要求3所述的彩色彩虹水晶树脂的制备工艺，其特征是：所述的水性有机色浆为永固紫或酞菁蓝。