CN101417889A - 一种含硼不烧铝碳锆滑动水口砖 - Google Patents
一种含硼不烧铝碳锆滑动水口砖 Download PDFInfo
- Publication number
- CN101417889A CN101417889A CNA2008102309508A CN200810230950A CN101417889A CN 101417889 A CN101417889 A CN 101417889A CN A2008102309508 A CNA2008102309508 A CN A2008102309508A CN 200810230950 A CN200810230950 A CN 200810230950A CN 101417889 A CN101417889 A CN 101417889A
- Authority
- CN
- China
- Prior art keywords
- boron
- zirconium
- carbon
- kilograms
- containing unfired
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种含硼不烧铝碳锆滑动水口砖，涉及一种耐火材料，本发明的目的是提供一种抗热冲击和抗磨性能好使用寿命长的含硼不烧铝碳锆滑动水口砖。本发明的技术方案是，一种含硼不烧铝碳锆滑动水口砖，包含有铝、碳、锆和刚玉及结合剂，所述硼为不定性单质硼，硼∶刚玉∶铝∶碳∶锆∶硅的重量比为0.2－3∶60－80∶0.5－3∶0.2－6∶0.5－20∶1－3。所述结合剂为树脂。本发明用于冶金。
Description
技术领域：
本发明涉及一种耐火材料，特别是一种含硼不烧铝碳锆滑动水口砖。
背景技术：
炼钢滑动水口砖在炼钢过程中受到钢水的热冲击，而引起的裂纹和剥落以及钢水冲刷磨损作用，导致水口砖寿命缩短，成为困扰炼钢的难题。
发明内容：
本发明的目的是提供一种抗热冲击和抗磨性能好使用寿命长的含硼不烧铝碳锆滑动水口砖。本发明的技术方案是，一种含硼不烧铝碳锆滑动水口砖，包含有铝、碳、锆和刚玉及结合剂，其特征在于：所述硼为不定性单质硼，硼：刚玉：铝：碳：锆：硅的重量比为0.2-3：60-80：0.5-3：0.2-6：0.5-20：1-3。所述结合剂为树酯。本发明由于含有不定形单质硼不烧铝碳锆水口砖，因而与现有技术比较具有常温和高温强度高，抗钢水侵蚀、抗冲刷性，抗氧化及抗热震性能好的显著优点。
具体实施方式：
本发明有以下实施例：
实施例1：
1、将27千克小于等于400目的板状刚玉粉，0.5千克小于等于300目的金属铝粉，1.5千克小于等于500目的金属硅粉，3.3千克小于等于400目的碳黑和0.2千克小于等于500目灰色的硼，放在锥形混练机中混匀成混合粉。
2、分别取28千克1-3mm板状刚玉颗粒、5千克的小于0.5mm的板状刚玉颗粒、19.5千克的0.5-1mm锆莫来石颗粒、15千克的小于等于0.5mm锆刚玉颗粒进行搅拌混合。将混合好的颗粒倒入湿碾机中，先加入4千克树脂的2/3，即2666克树脂与混合好颗粒进行混碾均匀后，再加入上述的混合粉和剩下的1/3树脂进一步充分混合均匀成泥料。
3、将上述混合好的泥料由摩擦压力机上成型、干燥、套箍、磨制、涂布即成不烧铝碳锆质滑动水口砖。
其中干燥工艺要求：
| 温度范围(℃) | 要求干燥时间(h) |
| 常温～80 | 8～10 |
| 80～120 | 10～14 |
| 120～200 | 8～10 |
| 200±10 | ≥8 |
实施例2：
1、将23千克小于等于400目的板状刚玉粉，3千克小于等于300目的金属铝粉1千克小于等于500目的金属硅粉，2千克小于等于400目的碳黑和1千克小于500目灰色的硼，放在锥形混练机中混匀成混合粉。
2、分别取30千克1-3mm板状刚玉颗粒，13千克的0.5-1mm板状刚玉颗粒，9千克的小于0.5mm的板状刚玉颗粒、10千克的0.5-1mm锆莫来石颗粒、8千克的小于0.5mm锆刚玉颗粒进行搅拌混合。将混合好的颗粒倒入湿碾机中，先加入5千克树脂的2/3，即3333克树脂与混合好颗粒进行混碾均匀后，再加入上述的混合粉和剩下的1/3树脂进一步充分混合均匀成泥料。
3、将上述混合好的泥料由摩擦压力机上成型、干燥、套箍、磨制、涂布即成不烧铝碳锆质滑动水口砖。
其中干燥工艺要求：
| 温度范围(℃) | 要求干燥时间(h) |
| 常温～100 | 6～9 |
| 100～200 | 12～14 |
| 200～300 | 8～10 |
| 300 | ≥12 |
实施例3：
1、将20千克小于等于400目的板状刚玉粉，3千克小于等于300目的金属铝粉3千克小于等于500目的金属硅粉，6千克小于等于400目的碳黑和3千克小于500目筛的深灰色的无定形硼，放在锥形混练机中混匀成混合粉。
2、分别取25千克1-3mm板状刚玉颗粒，20千克的0.5-1mm板状刚玉颗粒，15千克的小于0.5mm的板状刚玉颗粒、5千克的小于0.5mm锆刚玉颗粒进行搅拌混合。将混合好的颗粒倒入湿碾机中，先加入6千克树脂的2/3，即4千克树脂与混合好颗粒进行混碾均匀后，再加入上述的混合粉和剩下的1/3树脂进一步充分混合均匀成泥料。
3、将上述混合好的泥料由摩擦压力机上成型、干燥、套箍、磨制、涂布即成不烧铝碳锆质滑动水口砖。
其中干燥工艺要求：
| 温度范围(℃) | 要求干燥时间(h) |
| 常温～100 | 8～12 |
| 100～250 | 10～14 |
| 250～350 | 8～10 |
| 350～450 | 15～18 |
| 450±10 | ≥10 |
比较例：
按铝碳锆烧成滑动水口砖常规生产配料和工艺烧成铝碳锆烧成滑动水口砖，按铝碳不烧滑动水口砖常规生产配料和工艺制成不烧铝碳滑动水口砖。
表1：实施例不烧滑动水口砖的特性
表2比较例烧成铝碳锆质、不烧铝碳质滑动水口砖的特性
Claims (2)
1、一种含硼不烧铝碳锆滑动水口砖，包含有铝、碳、锆和刚玉及结合剂，其特征在于：所述硼为不定性单质硼，硼：刚玉：铝：碳：锆：硅的重量比为0.2-3：60-80：0.5-3：0.2-6：0.5-20：1-3。
2、如权利要求1所述的一种含硼不烧铝碳锆滑动水口砖，其特征在于：所述结合剂为树酯。