CN101343508A - Preparation method for wood-construction water-based fire-proof paint - Google Patents

Preparation method for wood-construction water-based fire-proof paint Download PDF

Info

Publication number
CN101343508A
CN101343508A CNA2007100580736A CN200710058073A CN101343508A CN 101343508 A CN101343508 A CN 101343508A CN A2007100580736 A CNA2007100580736 A CN A2007100580736A CN 200710058073 A CN200710058073 A CN 200710058073A CN 101343508 A CN101343508 A CN 101343508A
Authority
CN
China
Prior art keywords
parts
preparation
based fire
wood
mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CNA2007100580736A
Other languages
Chinese (zh)
Inventor
张云波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhonghong Tianjin Industry Co Ltd
Original Assignee
Zhonghong Tianjin Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhonghong Tianjin Industry Co Ltd filed Critical Zhonghong Tianjin Industry Co Ltd
Priority to CNA2007100580736A priority Critical patent/CN101343508A/en
Publication of CN101343508A publication Critical patent/CN101343508A/en
Withdrawn legal-status Critical Current

Abstract

The invention relates to a preparation method of timber structure water-based fire retardant coating, which adopts that carboxyethyl cellulose is made into 1 percent water solution, 20 parts of ammonium polyphosphate, 9 parts of melamine, 6 parts of pentaerythrite, 5 parts of chlorinated paraffin, 5 parts of titanium dioxide, 4 parts of talcum powder, 0.6 part of ethyl cellulose water solution and tap water are mixed, the mixture is dispersed and stirred for 20 to 60 minutes through a high-speed dispersion machine, the dispersed sizing material is filled into a grinding miller to grind, and the grinded sizing material and 30 parts of silicone-acrylate emulsion are mixed, stirred, filtrated and checked. The preparation method of the timber structure water-based fire retardant coating has the advantages that the normal growth of the tree is not affected through painting the coating on the wood trunk during the growing period, and the coating also has the fireproof function.

Description

Preparation method for wood-construction water-based fire-proof paint
Technical field
The present invention relates to a kind of preparation method for wood-construction water-based fire-proof paint.
Background technology
In the prior art, the chemical ingredients that contains in the timber structure frie retardant coating just is brushed on the trunk of growing period trees, influences the normal growth of trees.
Summary of the invention
The objective of the invention is to overcome above-mentioned deficiency, a kind of preparation method for wood-construction water-based fire-proof paint is provided, on the trunk of the woods that it just is brushed at growing period, do not influence the normal growth of trees, also had fiery function.
Technical scheme of the present invention is: a kind of preparation method for wood-construction water-based fire-proof paint, it is characterized in that: carboxyethyl cellulose is made 1% aqueous solution, 20 parts of polyphosphoric acid amine, 9 parts of trimeric cyanamides, 6 parts of tetramethylolmethanes, 5 parts of chlorinated paraffins, 5 parts of titanium dioxides, 4 parts of talcum powder, 0.6 part of the ethyl cellulose aqueous solution and tap water is mixed, disperse to stir 20-60 minute with high speed dispersor, slurry after disperseing got in the shredder grind, ground slurry and vinyl acetate emulsion are mixed for 30 parts, stir, filter check.
Beneficial effect of the present invention: on the trunk of the woods that just are brushed at growing period, do not influence the normal growth of trees, also had fiery function.
Embodiment
Embodiment: a kind of preparation method for wood-construction water-based fire-proof paint, carboxyethyl cellulose is made 1% aqueous solution, 20 parts of polyphosphoric acid amine, 9 parts of trimeric cyanamides, 6 parts of tetramethylolmethanes, 5 parts of chlorinated paraffins, 5 parts of titanium dioxides, 4 parts of talcum powder, 0.6 part of the ethyl cellulose aqueous solution and tap water is mixed, disperse to stir 20-60 minute with high speed dispersor, slurry after disperseing got in the shredder grind, ground slurry and vinyl acetate emulsion are mixed stirring for 30 parts, filter check.

Claims (1)

1, a kind of preparation method for wood-construction water-based fire-proof paint, it is characterized in that: carboxyethyl cellulose is made 1% aqueous solution, 20 parts of polyphosphoric acid amine, 9 parts of trimeric cyanamides, 6 parts of tetramethylolmethanes, 5 parts of chlorinated paraffins, 5 parts of titanium dioxides, 4 parts of talcum powder, 0.6 part of the ethyl cellulose aqueous solution and tap water is mixed, disperse to stir 20-60 minute with high speed dispersor, slurry after disperseing got in the shredder grind, ground slurry and vinyl acetate emulsion are mixed stirring for 30 parts, filter check.
CNA2007100580736A 2007-07-12 2007-07-12 Preparation method for wood-construction water-based fire-proof paint Withdrawn CN101343508A (en)