CN101338055A - Acrylic resin for manufacturing medical infusion bottle - Google Patents
Acrylic resin for manufacturing medical infusion bottle Download PDFInfo
- Publication number
- CN101338055A CN101338055A CNA2007100433703A CN200710043370A CN101338055A CN 101338055 A CN101338055 A CN 101338055A CN A2007100433703 A CNA2007100433703 A CN A2007100433703A CN 200710043370 A CN200710043370 A CN 200710043370A CN 101338055 A CN101338055 A CN 101338055A
- Authority
- CN
- China
- Prior art keywords
- acid
- acrylic resin
- antioxidant
- butyl
- resin binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Polypropylene resin used for manufacturing medical transfusion bottles is composition, and the components comprise resin binders, acid neutralizers and antioxidants; wherein, the resin binder are random copolymer of propylene and ethylene, the ethylene content of the resin binders is 0.5 percent to 4 wt percent, the melting temperature is 140 DEG C to 165 DEG C, and the melt flow rate is 1.0g to 4.0g/10min. The mixture radio of the components by the weight ratio is as follows: the ratio of the resin binder and the acid neutralizer is equal to 100 : 0.1 to 0.06; the ratio of the resin binder and the antioxidant is equal to 100 : 0.02 to 0.30. The antioxidants are one or the mixture of hindered phenolic antioxidants and phosphate antioxidants; the acid neutralizers are the mixture of calcium stearate and hydrogenated talcum powders, the ratio of the calcium stearate and the hydrogenated talcum powders by the weight ratio is equal to 1: 0.8 to 1.3. The invention has the advantage that the adding amount of the acid neutralizer is reduced on the premise that the same acid neutralization effect is obtained.
Description
Technical field
The present invention relates to a kind of acrylic resin, particularly be exclusively used in the acrylic resin of making medical infusion bottle.
Background technology
Early stage plastics medical infusion container adopts vinylchlorid to make, but because of vinyl chloride monomer, softening agent etc. is easily separated out, substantially, replaced by materials such as polypropylene, polyethylene in recent years, as Chinese patent 99814444,98807300,01813402,01111112 etc. introduce.At present, the most normal use is propylene and ethylene atactic copolymer, and with regard to performances such as thermotolerance, intensity, toughness and transparency, propylene is compared with other material with ethylene atactic copolymer has remarkable advantages.
The catalyzer that is used to prepare propylene and ethylene atactic copolymer generally all contains the Cl ion, and the Cl ion can can't be present in the copolymer product with avoiding.The Cl ionic exists can form sour environment, and this will impel polymer degradation, thereby influence the quality of its goods infusion bottle.Usually adopting the method for adding acid neutralizing agent in propylene and ethylene atactic copolymer to prevent the generation of degrading in the prior art, is that 200410017402.9 Chinese patent application is introduced as application number.But for propylene and ethylene atactic copolymer, acid neutralizing agent also belongs to a kind of impurity in essence, and the physicals of copolymer artcle will be subjected to the increase of its add-on more or less and descend.Therefore, if can obtain same sour neutralization, the add-on that reduces acid neutralizing agent has positive effect beyond doubt.
Summary of the invention
The invention provides a kind of acrylic resin that is used to make medical infusion bottle, the technical problem that it will solve is that requirement obtains to reduce the add-on of acid neutralizing agent under the prerequisite of same sour neutralization.
Below be the technical scheme that the present invention solves the problems of the technologies described above:
A kind of acrylic resin that is used to make medical infusion bottle, this acrylic resin is a composition, component comprises resin binder, acid neutralizing agent and oxidation inhibitor, wherein resin binder is propylene and ethylene atactic copolymer, its ethylene content is 0.5~4wt%, melt temperature is 140~165 ℃, and melt flow rate (MFR) is 1.0~4.0g/10min.
In weight ratio, the ratio of each component is:
Resin binder: acid neutralizing agent=100: 0.01~0.06;
Resin binder: oxidation inhibitor=100: 0.02~0.30.
Above-mentioned oxidation inhibitor is a kind of in Hinered phenols antioxidant or the phosphite ester kind antioxidant or both mixtures; Acid neutralizing agent is calcium stearate and the talcous mixture of hydrogenation, in weight ratio, and calcium stearate: hydrogenation talcum powder=1: 0.8~1.3.
Above-mentioned oxidation inhibitor is preferably the mixture of Hinered phenols antioxidant and phosphite ester kind antioxidant, and the weight ratio of Hinered phenols antioxidant and phosphite ester kind antioxidant is 1: 0.2~8.
Above-mentioned Hinered phenols antioxidant preferably takes from 1,3,5-trimethylammonium-2,4,6-three (3,5-di-t-butyl-4 hydroxybenzyl) a kind of in benzene, two-[3,3-two-(3-tert-butyl-hydroxy phenyl)-butyric acid] glycol ester or four [β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester; Phosphite ester kind antioxidant is preferably taken from three (2, the 4-di-tert-butyl-phenyl) phosphorous acid esters or two (2, the 4-di-tert-butyl-phenyl) pentaerythritol esters of diphosphorous acid.
Key of the present invention is that the contriver found through experiments to the selection of acid neutralizing agent and the combination of prescription thereof, with this acid neutralizing agent that is used in combination, can reduce the add-on of acid neutralizing agent under the prerequisite that obtains same sour neutralization.Therefore, the present invention compared with prior art has tangible advantage.
Below will the invention will be further described by specific embodiment.
Embodiment
[embodiment 1]
Resin binder is propylene and ethylene atactic copolymer:
Ethylene content 0.2wt%, 140~165 ℃ of melt temperatures, melt flow rate (MFR) 1.5g/10min;
Oxidation inhibitor is 1,3,5-trimethylammonium-2,4,6-three (3,5-di-t-butyl-4 hydroxybenzyl) benzene;
In weight ratio, the proportioning of acid neutralizing agent is:
Calcium stearate: hydrogenation talcum powder=1: 0.8
Proportioning between each component sees Table 1.
[embodiment 2]
The proportioning of acid neutralizing agent is:
Calcium stearate: hydrogenation talcum powder=1: 1.0.
All the other are with embodiment 1.
[embodiment 3]
The proportioning of acid neutralizing agent is:
Calcium stearate: hydrogenation talcum powder=1: 1.3.
All the other are with embodiment 1.
[embodiment 4]
The proportioning of acid neutralizing agent is:
Calcium stearate: hydrogenation talcum powder=1: 0.9.
All the other are with embodiment 1.
[embodiment 5]
Resin binder is propylene and ethylene atactic copolymer:
Ethylene content 0.5wt%, 140~165 ℃ of melt temperatures, melt flow rate (MFR) 1.2g/10min;
Oxidation inhibitor is three (2, the 4-di-tert-butyl-phenyl) phosphorous acid ester;
The proportioning of acid neutralizing agent is:
Calcium stearate: hydrogenation talcum powder=1: 1.
All the other are with embodiment 1.
[embodiment 6]
Resin binder is propylene and ethylene atactic copolymer:
Ethylene content 2.9wt%, 140~165 ℃ of melt temperatures, melt flow rate (MFR) 2.0g/10min;
Oxidation inhibitor is two-[3,3-two-(3-tert-butyl-hydroxy phenyl)-butyric acid] glycol esters;
The proportioning of acid neutralizing agent is:
Calcium stearate: hydrogenation talcum powder=1: 1.
All the other are with embodiment 1.
The various embodiments described above acrylic resin is measured the melt flow rate (MFR) no change after 30 days, it is 2 listed that all the other physical indexs see Table.
Table 1.
Resin binder: acid neutralizing agent (weight ratio) | Resin binder: oxidation inhibitor (weight ratio) | |
Embodiment 1 | 100∶0.01 | 100∶0.30 |
Embodiment 2 | 100∶0.05 | 100∶0.15 |
Embodiment 3 | 100∶0.04 | 100∶0.25 |
Embodiment 4 | 100∶0.06 | 100∶0.10 |
Embodiment 5 | 100∶0.02 | 100∶0.09 |
Embodiment 6 | 100∶0.03 | 100∶0.02 |
Table 2.
Tensile strength (MPa) | Modulus in flexure (GPa) | Socle girder notched Izod impact strength (J/M) | |
Embodiment 1 | 31.5 | 1.35 | 345 |
Embodiment 2 | 31.2 | 1.30 | 320 |
Embodiment 3 | 30.3 | 1.21 | 397 |
Embodiment 4 | 32.2 | 1.33 | 387 |
Embodiment 5 | 30.4 | 1.25 | 356 |
Embodiment 6 | 29.5 | 1.20 | 498 |
Get the acrylic resin of the foregoing description 4, adopt injection stretch blow moulding to make the medical transfusion container, container wall thickness is 0.9mm, and recording turbidity is 6.8%.
Claims (4)
1, a kind of acrylic resin that is used to make medical infusion bottle, this acrylic resin is a composition, component comprises resin binder, acid neutralizing agent and oxidation inhibitor, wherein resin binder is propylene and ethylene atactic copolymer, its ethylene content is 0.5~4wt%, melt temperature is 140~165 ℃, and melt flow rate (MFR) is 1.0~4.0g/10min
In weight ratio, the ratio of each component is:
Resin binder: acid neutralizing agent=100: 0.01~0.06;
Resin binder: oxidation inhibitor=100: 0.02~0.30,
It is characterized in that above-mentioned oxidation inhibitor is a kind of in Hinered phenols antioxidant or the phosphite ester kind antioxidant or both mixtures; Acid neutralizing agent is calcium stearate and the talcous mixture of hydrogenation, in weight ratio, and calcium stearate: hydrogenation talcum powder=1: 0.8~1.3.
2, acrylic resin according to claim 1 is characterized in that described oxidation inhibitor is the mixture of Hinered phenols antioxidant and phosphite ester kind antioxidant, and the weight ratio of Hinered phenols antioxidant and phosphite ester kind antioxidant is 1: 0.2~8.
3, acrylic resin according to claim 1 and 2, it is characterized in that described Hinered phenols antioxidant takes from 1,3,5-trimethylammonium-2,4,6-three (3,5-di-t-butyl-4 hydroxybenzyl) benzene, two-[3,3-two-(3-tert-butyl-hydroxy phenyl)-butyric acid] a kind of in glycol ester or four [β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester.
4, acrylic resin according to claim 1 and 2 is characterized in that described phosphite ester kind antioxidant takes from two (2, the 4-di-tert-butyl-phenyl) pentaerythritol esters of three (2, the 4-di-tert-butyl-phenyl) phosphorous acid esters or diphosphorous acid.