CN101333860A - Anti-slip material coating on easily wettable and sliding floor and method of use thereof - Google Patents
Anti-slip material coating on easily wettable and sliding floor and method of use thereof Download PDFInfo
- Publication number
- CN101333860A CN101333860A CNA2007101124425A CN200710112442A CN101333860A CN 101333860 A CN101333860 A CN 101333860A CN A2007101124425 A CNA2007101124425 A CN A2007101124425A CN 200710112442 A CN200710112442 A CN 200710112442A CN 101333860 A CN101333860 A CN 101333860A
- Authority
- CN
- China
- Prior art keywords
- coating
- slip
- coated
- aggregate
- white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed is non-skid material used to be coated on the smooth floor which tends to be humid and skid; the non-skid material comprises a floor base coating and a non-skid coating; the floor base coating can be coated on the surface of the smooth floor and contains acryl resin of the acrylic ester cluster, inorganic aggregate and cement; the non-skid coating is coated on the surface of the floor base coating and comprises coating material and skid-preventing aggregate. Because the acryl resin of the acrylic ester cluster in the floor base coating has good adhering capability, strong contact force is formed even on the smooth floor without pores; the inorganic aggregate in the floor base coating and the skid-preventing aggregate in the non-skid coating are adopted to enable the surface of the floor to become uneven, so as to increase the friction coefficient; thereby, the non-skid function is realized.
Description
Technical field
The present invention relates to a kind of anti-slip material and using method thereof, particularly relate to a kind of anti-slip material and using method thereof that is coated on easily wettable and sliding floor.
Background technology
In society now, only pipe is popular all knows very well unexpected importance of preventing and treating, yet the injured accident that slips on the ground still keeps pouring in, wherein more there are many people to die from the contingency of slipping, and slip the most serious on wet and slippery ceramic tile ground, bathroom with the lower child of the ability of resisting, old man and pregnant woman.Hence one can see that, the importance that floor is anti-skidding.
At present general on the market for the place of wet and slippery easily floor, as place such as between corridor, stair, entry, lavatory, washbasin, kitchen, bath, around the swimming pool, the processing mode that its floor is anti-skidding, be the employing ship-and-galley tile, on floor, attach golden steel non-slip nosing, paste anti-skidding copper bar, or the slipmat of rubber material is set.Yet above-mentioned several non-skid feature still have not good place in the use, are described as follows:
One, adopts ship-and-galley tile: mainly be to allow the surface of floor tile form coarse shape, to increase friction factor, as glazing on-slip brick, anti-skidding quartz brick, chiltern glazed tile, the terrazzo brick etc. of waxing.Although integral aesthetic property is good and select variation, yet, when these floor tiles are attached with suds or grease, can become quite smooth, and lose anti-skidding effect.
Two, attach the diamond dust non-slip nosing: be stained with the high rigidity diamond dust of countless fine particles with surface glue, and attach on the smooth floor, to reach skidproof effect with the adhesive tape of viscosity extra-heavy.Usually, in use for some time, generally be less than 1 year, just begin to have the phenomenon of peeling off or being polished and produce, lose the function of on-slip gradually, therefore, need to attach again.Yet, before attaching again, must earlier previous non-slip nosing be struck off, unfortunately,, needing to cause the considerable time of cost on previous operations because the viscosity extra-heavy of its adhesive tape is removed and is not easy.The more important thing is that when this non-slip nosing runs into acid/akaline liquid, for example bathe the lavatory cleaning agent, its adhesive tape can lose viscosity, and make non-slip nosing produce the phenomenon that relief comes off.In addition, because this diamond dust non-slip nosing only has fixing color usually, and the design on original smooth floor of can't arranging in pairs or groups, and on this smooth floor, form the different color lumps that separates, therefore have lofty and inaesthetic situation usually and take place.
Three, paste anti-skidding copper bar: make the copper bar of concave-convex surface shape with copper metal, increase skin friction.Owing to be made with copper metal, if be mounted in the public place, in the local time of as stair, corridor, entry etc., then have the doubt that is stolen, if and be installed in general house, its cost is not only higher, and in the global design of shelter, seems comparatively undesirable again and is difficult to arrange in pairs or groups original decoration planning.
Four, the rubber antiskid pad is set: the slipmat of this type is normally intersected mutually with rubber strip and is repeatedly put institute's framework and form anti-skidding structure, owing to wherein exist many gaps, vacancy, shelter evil people and countenance evil practices easily and nourish bacterium, and suitable inconvenience in the cleaning, become and regularly to change, to guarantee its health, the real non-mode that can use for a long time.
In recent years, existing manufacturer is from the another kind of anti-slip technology of external introduction, be to the surface of smooth floor tile with corrosive liquid, after after a while, can allow the floor tile surface form countless small potholes, when floor humidity, ceramic tile pressurized, will produce the phenomenon of vacuum cup, increase the suction of pothole, reach anti-skidding effect whereby.
Yet; owing to exist dust, impurity in the air; or the grogs of sole can block these small potholes; little by little lose anti-skidding effect; therefore, the ship-and-galley tile of this type must use cleaning agent in use for some time; the dust, the impurity that are deposited in the pothole are removed, made and safeguard the quite inconvenience that becomes.Moreover,, except changing new product, be to have no chance to return back to original smooth state owing to be that floor tile is imposed destructive processing.
In addition, at present as general floor, as the place based on the plain ground of RC (typically referring to concrete floor) such as parking lot, warehouse, slope, market, mostly its non-skid feature is to adopt epoxy resin (Epoxy) and be added with inorganic aggregate (corundum, quartz sand), directly be coated on the concrete floor after the mixing, to form the zone of higher coefficient of friction, reach skidproof effect whereby.Yet; this mode but can't directly be coated on as on the smooth floor such as quartz brick, glazed tile; this is because the concrete floor surface can exist the pore that differs in size usually; epoxy resin can reach the effect that is adhering to of inhaling by infiltrating pore; and smooth floor is difficult to form powerful adhesiving effect with epoxy resin because of no pore, causes coming off easily.
Summary of the invention
The objective of the invention is for a kind of anti-slip material that is coated on easily wettable and sliding floor is provided, can be adhered on the smooth floor of no pore and form preferable adhesion, reach anti-skidding purpose.
Another object of the present invention is that a kind of using method that is coated on the anti-slip material of easily wettable and sliding floor is being provided, and can allow anti-slip material follow on the surface on smooth floor really, forms preferable skidproof effect.
For achieving the above object, the anti-slip material that is coated on easily wettable and sliding floor of the present invention comprises a base coating, and a nonskid coating.This base coating can be coated on the surface on this smooth floor, and contains acrylic ester acryl resin, inorganic aggregate, and cement, and this nonskid coating is to be coated on the surface of this base coating, and contains a coating material, and the on-slip aggregate.
The present invention is coated on the using method of the anti-slip material of easily wettable and sliding floor, comprise a base coating step in regular turn, an and anti-skidding coating step, this base coating step is to apply a base coating on this smooth floor, and this base coating contains acrylic ester acryl resin, inorganic aggregate, reaches compositions such as cement, this anti-skidding coating step is after this base coating drying, apply a nonskid coating more thereon, this nonskid coating contains a coating material, reaches compositions such as on-slip aggregate.
Beneficial functional of the present invention is: utilize the acrylic ester acryl resin in this base coating, has preferable adhesive capacity, just at last on the smooth floor of no pore, also can be formed with powerful adhesion, increase friction factor with inorganic aggregate in this base coating and the on-slip aggregate in this nonskid coating again, reach anti-skidding function whereby.
Description of drawings
Fig. 1 is a schematic diagram, illustrates that first preferred embodiment that the present invention is coated on the anti-slip material of easily wettable and sliding floor is the place that is applied to the lavatory.
Fig. 2 is a generalized section, illustrates that the on-slip aggregate in the nonskid coating of this first preferred embodiment is to be mixed with epoxy resin to apply again.
Fig. 3 is a generalized section, is illustrated in this first preferred embodiment, and the on-slip aggregate in this nonskid coating is in the mode of spraying, is attached on the epoxy resin.
Fig. 4 is a generalized section, and the 3rd preferred embodiment of the present invention is described.
Fig. 5 is a generalized section, and the 4th preferred embodiment of the present invention is described.
Fig. 6 is a flow chart, illustrates that the present invention is coated on first preferred embodiment of using method of the anti-slip material of easily wettable and sliding floor.
Fig. 7 is a flow chart, illustrates that the present invention is coated on second preferred embodiment of using method of the anti-slip material of easily wettable and sliding floor.
Fig. 8 is a flow chart, illustrates that the present invention is coated on the 3rd preferred embodiment of using method of the anti-slip material of easily wettable and sliding floor.
The specific embodiment
The present invention is described in detail below in conjunction with drawings and Examples.Before the present invention is described in detail, be noted that in the following description similarly assembly is to represent with identical numbering.
As shown in Figure 1, 2, for the present invention is coated on first preferred embodiment of the anti-slip material 2 of easily wettable and sliding floor, be suitable for spreading overlaying on the smooth floor 1 of bathing the lavatory, this anti-slip material 2 comprises a base coating 21, a nonskid coating 22, and a face coat 23.
This base coating 21 is directly to be coated on the surface on this smooth floor 1, and contains acrylic ester acryl resin (Acrylic Resin), inorganic aggregate, and cement (Cement), and can repeat the coating of twice above base coating 21.Acryl resin is to use acrylic ester, as methyl acrylate (Methylacrylate), ethyl acrylate (Ethylacrylate), butyl acrylate (Brtylacrylate), or 2-ethyl hexyl acrylate (Octylacrylate).And inorganic aggregate can short glass fiber (Short Glass Fiber) and quartz sand mix, central quartz sand is meant the silica (SiO that contains more than 90%
2) general name, also can corundum (mixed sand of aluminium ore and iron ore) replace, or the mixing of quartz sand and corundum.In this first preferred embodiment, the acrylic ester acryl resin be creamy white liquid, and inorganic aggregate and cement are powder, the inorganic aggregate, the percentage by weight that contain percentage by weight in this base coating 21 and be 2%-4% are the cement of 45%-75%, and all the other are the acrylic ester acryl resin.The acrylic ester acryl resin can acidproof/alkali, the erosion of grease or petroleum lubricant, and anti-weather variability is good.Quartz sand then is No. four quartz sands selecting for use industry to be commonly called as, its particle size of main standard, based on can be by the quartz sand that filter screen was filtered out of 100 meshes (mesh), certainly, also can use quartz sand No. five, based on the particle diameter of filter screen that can be by 60mesh, or No. six quartz sand particle diameter by the filter screen of 40mesh is main.And the length of employed short glass fiber is to cooperate quartz sand particle size No. four.
This nonskid coating 22 is to be coated on the surface of this base coating 21, and contains coating material, and the on-slip aggregate.This coating material can be aqueous epoxy resins, polyurethane resin (Polyurethane, PU), synthetic resin, macromolecule resin, acryl resin, transparent stone coating, or no-solvent type oiliness epoxy resin.And in this first preferred embodiment, this coating material is to be example with epoxy resin, on-slip aggregate in this nonskid coating 22 can account between percentage by weight 40%-60%, all the other are epoxy resin, when reality is used, can directly the on-slip aggregate be mixed use with epoxy resin with 1: 1 ratio, employed epoxy resin is the epoxy resin for water-based, can directly add water mixes and emulsification, tool exhibition fluidity is easy to brushing, and its coating film gloss degree is good, the water resistance excellence, and be good solid, but also can replace aqueous epoxy resins by no-solvent type oiliness epoxy resin.The on-slip aggregate is to select No. four quartz sand for use, mainly is as increasing surface roughness, but also can be to select No. five quartz sand, No. six quartz sand, corundum for use, or the mixing of above-mentioned material.In addition, what deserves to be mentioned is that this nonskid coating 22 is can repetitive coatings more than twice, so as to the thickness that increases this nonskid coating 22 and strengthen its wear resistence.
This face coat 23 is to be coated on this nonskid coating 22, can be the epoxy resin of water-based, but also can be the oiliness epoxy resin of no-solvent type.This face coat 23 can be protected this nonskid coating 22; prolong its useful life; and can be by its color and luster of allotment; cooperate context; to increase the attractive in appearance of integral body; but also can be by not adding any color and luster; and present transparence jointly with aforesaid this base coating 21, this nonskid coating 22; and be applicable to that being coated with of smooth floor 1 that need not be indicated especially in the general house is covered with; whereby; and can possess the tone and the globality on former smooth floor 1, reach anti-skidding effect under the situation attractive in appearance simultaneously having concurrently.
The present invention shop is overlying on second preferred embodiment of the anti-slip material 2 of easily wettable and sliding floor, is roughly identical with this first preferred embodiment, comprises a base coating 21, a nonskid coating 22 equally, and a face coat 23.Its different place is: in this second preferred embodiment, this base coating 21 is different with each composition proportion of composing with the material of this nonskid coating 22.
This base coating 21 comprises acrylic ester acryl resin, inorganic aggregate and cement, and the interpolation entry is mixed together.The mixture of this acrylic ester acryl resin, inorganic aggregate and cement, and the weight ratio of water is 5: 1: 1.And this inorganic aggregate is to be mixed as the white hollow minute particle and the sand shape white quartz of dispersing agent by pottery or the nature of glass, also can get the quartzy white quartz of aforesaid sand shape that replaces of the less powdery white of particle diameter, or both while dual-purposes also can, at this moment, this cement, this white hollow minute particle, and the weight ratio of this white quartz is 2: 1: 2 in regular turn.The particle size of this white hollow minute particle, obtained screening by the filter screen of 100～200mesh, quartzy its particle diameter of this sand shape white is that the filter screen screening by 80～200mesh obtains, and the quartzy particle diameter of this powdery white to be filter screen screening by 300～500mesh obtain.
This nonskid coating 22 is to be coated on the surface of this base coating 21, and comprises a coating material and on-slip aggregate, and in this second preferred embodiment, this coating material is to be example with transparent stone coating.This on-slip aggregate is by pottery or vitreous white hollow minute particle and sand shape white quartz, or mix by white hollow minute particle and bead sand, quartzy its particle diameter of sand shape in this on-slip aggregate white is that the filter screen screening by 30～50mesh obtains, and the particle diameter of this bead sand is that the filter screen screening by 30～50mesh obtains.When reality is used, can directly transparent stone coating, white quartz/bead sand be mixed use with white hollow minute particle with 100: 15: 1 ratio.
As shown in Figure 4, the present invention shop is overlying on the 3rd preferred embodiment of the anti-slip material 2 of easily wettable and sliding floor, be roughly identical with this first preferred embodiment, its different place is: in the 3rd preferred embodiment, 2 of this anti-slip materials comprise a base coating 21, and a nonskid coating 22, and do not have face coat 23 (see figure 2)s, except that the composition ratio of this nonskid coating 22 changed to some extent, the composition ratio of this base coating 21 all was identical with this first preferred embodiment.
On-slip aggregate in this nonskid coating 22 sand shape white that to be particle diameter obtained by the filter screen screening of 50～80mesh is quartzy, and this coating material can be aqueous epoxy resins, polyurethane resin, synthetic resin, macromolecule resin, acryl resin, or no-solvent type oiliness epoxy resin one of them, and the weight ratio of this coating material and this on-slip aggregate is 10: 3.
As shown in Figure 5; be overlying on the 4th preferred embodiment of the anti-slip material 2 of easily wettable and sliding floor for the present invention shop; be roughly identical with this first preferred embodiment; its different place is: in the 4th preferred embodiment; except original this base coating 21; this nonskid coating 22; outside this face coat 23; more comprise a protective coating 24 that is coated on this face coat 23; this face coat 23 can be possessed transparent aspect originally; also can add colorant to improve its conspicuousness; and more add its color and luster of tool and aesthetic feeling; and this protective coating 24 is a transparent stone coating, and can be as the protection of this face coat 23.
As shown in Figure 6, and cooperation Fig. 2, be coated on first preferred embodiment of using method of the anti-slip material 2 of easily wettable and sliding floor for the present invention, comprise a floor cleaning 3, a patch step 4, a base coating step 5, one anti-skidding coating step 6, a surface-coated step 7 in regular turn, and one removes patch step 8.
This floor cleaning 3 is scrubbed the available aqueous detergent of this smooth floor 1 desire construction place, with lip-deep spot, impurity cleaning totally, avoids influencing adhesiveness.
This patch step 4 is in this smooth floor 1 desire construction place, with the patch that easily tears off, as U.S. line paper masking tape, on this smooth floor 1, enclose put up one can be for the scope of construction, to avoid being coated to other place.
This base coating step 5 is to have enclosed to apply a base coating 21 in the boundary of works area of subsides on this smooth floor 1, this base coating 21 contains acrylic ester acryl resin, inorganic aggregate, reach compositions such as cement, and can repeat the coating of twice above base coating 21.In this first preferred embodiment, it is the cement of 45%-75% that this base coating 21 contains inorganic aggregate, the percentage by weight that percentage by weight is 2%-4%, and all the other are the acrylic ester acryl resin.In actual use, modulate aforementioned proportion for convenience, be that the inorganic aggregate of getting percentage by weight 5% earlier becomes the powder agent with the cement mixing of percentage by weight 95%, again with acrylic ester acryl resin and above-mentioned powder agent with 1: 1-1: 3 ratio mixes together.Inorganic aggregate is that the quartz sand or the corundum of short glass fiber and No. four mixes, and can certainly be the quartz sand of No. five or No. six.At this, what deserves to be mentioned is, in this first preferred embodiment, this base coating 21 also can adopt the composition with above-mentioned different proportion to mix, as get the mixture that weight ratio is 5: 1: 1 acrylic ester acryl resin, this inorganic aggregate and cement, and interpolation water is mixed.At this moment, the composition of this inorganic aggregate is to be mixed by pottery or vitreous white hollow minute particle and sand shape white quartz, and also can getting powdery white, quartzy to replace aforesaid sand shape white quartzy, or both while dual-purposes also can.This cement, this white hollow minute particle, the weight ratio that reaches this white quartz is 2: 1: 2, all the other detailed explanations have been seen before and have been stated, no longer superfluous words.
This anti-skidding coating step 6 is after these base coating 21 dryings, for example through after eight hours, again with composition such as coating material and on-slip aggregate and fully mixed, be coated on again on this base coating 21, to form a nonskid coating 22, and in this anti-skidding coating step 6, also can repeat the coating of twice above nonskid coating 22, and this coating material can be aqueous epoxy resins, polyurethane resin (Polyurethane, PU), synthetic resin, macromolecule resin, acryl resin, transparent stone coating, or no-solvent type oiliness epoxy resin.And in this first preferred embodiment, this coating material is to be example with an epoxy resin, this nonskid coating 22 contains the on-slip aggregate that percentage by weight is 40%-60% approximately, and all the other are epoxy resin, the general normal mixed proportion with 1: 1 of above-mentioned material is used, and the epoxy resin of selecting for use is the epoxy resin for water-based, but also can be no-solvent type oiliness epoxy resin.The on-slip aggregate can be selected No. four, No. five, No. six quartz sand, corundum for use, or above-mentioned material one of them, certainly, also can be that the material more than two kinds is mixed.And, except be with epoxy resin with the on-slip aggregate mixes, also can earlier epoxy resin be coated on this base coating 21, again the on-slip aggregate is sprayed on epoxy resin, make comparatively neighbouring surface of on-slip aggregate, the visible shown aspect of Fig. 3.
In addition, what deserves to be mentioned is, the coating material of this nonskid coating also can be taken transparent stone coating to replace aforesaid epoxy resin, also collocation contains adularescent hollow minute particle and the quartzy on-slip aggregate of sand shape white simultaneously, or collocation contains the on-slip aggregate of adularescent hollow minute particle and bead sand, and the weight ratio of this transparent stone coating, white quartz/bead sand and white hollow minute particle is 100: 15: 1.This surface-coated step 7 is on dry this nonskid coating 22 that finishes, and as through behind the twenty four hours, applies a face coat 23, and this face coat 23 is aqueous epoxy resins, but also can be no-solvent type oiliness epoxy resin.And when reality is implemented, because this aqueous epoxy resins or the oiliness epoxy resin of this no-solvent type are colourless and generally are transparence, therefore, can influence under the situation of the color and luster of suffered regions coated in desire not and use, to keep the global design of original environment, particularly can use on the smooth floor 1 in not needing the residence, house that is additionally indicated, floor, bath lavatory as family, can not present the lofty not reasonable situation of different color blocks, and destroy global design and aesthetic property in the residence.Certainly, implement and desire when coated smooth floor 1 is indicated in reality, also can in aqueous epoxy resins, add pigment (, then being the adding color) if use the oiliness epoxy resin of no-solvent type, and make this face coat 23 can present color and luster, so as to improving its conspicuousness.
At last, this removal patch step 8 is torn off this smooth floor 1 with the patch that this patch step 4 is attached, and finishes the construction of this anti-slip material 2.
As shown in Figure 7, and cooperation Fig. 4, be coated on second preferred embodiment of using method of the anti-slip material 2 of easily wettable and sliding floor for the present invention, it roughly is identical with this first preferred embodiment, and different places is: in this using method of this second preferred embodiment, be to exempt this surface-coated step 7, and comprise this floor cleaning 3, this patch step 4, this base coating step 5, this anti-skidding coating step 6 in regular turn, and this removes patch step 8.Except that the composition ratio of this nonskid coating 22 changed to some extent, the composition ratio of this base coating 21 all was identical with first preferred embodiment of this using method.And in second preferred embodiment, on-slip aggregate in this nonskid coating 22 sand shape white that to be particle diameter obtained by the filter screen screening of 50～80mesh is quartzy, this coating material can be aqueous epoxy resins, polyurethane resin, synthetic resin, macromolecule resin, acryl resin, or no-solvent type oiliness epoxy resin one of them, and the weight ratio of this coating material and this on-slip aggregate is 10: 3.
As shown in Figure 8; and cooperation Fig. 5; be coated on the 3rd preferred embodiment of using method of the anti-slip material 2 of easily wettable and sliding floor for the present invention; it roughly is identical with this first preferred embodiment; and different places is: in this using method of the 3rd preferred embodiment, be at this anti-skidding coating step 6 and this surface-coated step 7 increase by one topping coating step 9.This topping coating step 9 is on this face coat 23 that drying finishes after a while, applies a protective coating 24, and this protective coating 24 is transparent stone coatings, and can further protect this face coat 23.As shown in the above description, this anti-slip material 2 has following advantage really on reality is used:
One, can really and be firmly stuck on the smooth floor:, this anti-slip material 2 can closely be combined with this smooth floor 1 adhere to and difficult drop-off owing to contain acrylic ester acryl resin composition in this base coating 21.
Two, in wet and slippery environment, still has skidproof effect: because anti-skidding effect can still be possessed in the top layer of this anti-slip material 2 in wet and slippery environment such as suds or grease.Cooperate the inorganic aggregate be impregnated in this base coating 21 and the on-slip aggregate in this nonskid coating 22 again, when people trample on this anti-slip material 2, can make these anti-slip material 2 surfaces present a little concavo-convex, can under wet and slippery environment, reach the anti-skidding effect of on-slip really.
Three, safeguard easily and acid and alkali-resistance: when this anti-slip material 2 in use for some time, when existing situation of decreasing mill produces, can be at direct this anti-slip material 2 of coating in the zone of decreasing mill, the anti-slip material 2 that had before applied need not be struck off, could apply again, therefore the time that can save previous operations.Simultaneously, because the surface of this anti-slip material 2 has preferable resistance to acids and bases, therefore can use in the environment that has Acidity of Aikalinity liquid.
Four, cost is lower and collocation property is good: owing to be not to use metal material as anti-slip material, therefore, the installing cost is lower, and the indoor global design in house of arranging in pairs or groups, and can continue and carefree the anti-skidding environment that people's safety is provided.
Five, can not shelter evil people and countenance evil practices, have comparatively health: because this anti-slip material 2 is to form with the closely knit storehouse of laminated form, therefore, do not have the rubber antiskid pad and have the problem that can shelter evil people and countenance evil practices in the space, health comparatively in the use.
Six, need not destroy floor surface: this anti-slip material 2 is to follow on this smooth floor 1 in the mode that adds adhesion, do not destroy its surface, when causing the wet and slippery factor of floor to disappear, the mode of can strong detergent or striking off with specialist tools, this anti-slip material 2 is removed, to return to original shiny surface.
Seven, can possess the flooring look globality: if not because this anti-slip material 2 coloring material for mixing in addition outward, then integral body is generally to be transparence, therefore, need not indicate especially when the occasion that is used for general indoor house, just can adopt the transparent anti-slip material 2 that does not add colorant to be applied, therefore doublely possess this indoor smooth floor 1 color and design originally, be unlikely the variation that produces the difference color lump, and can not influence overall appearance and decoration.In sum, the present invention is coated on the anti-slip material and the using method thereof of easily wettable and sliding floor, utilize the acrylic ester acryl in this base coating 21, can form powerful adhesion and difficult drop-off with this smooth floor 1, and utilize as coating materials such as epoxy resin or transparent stone coatings in conjunction with the on-slip aggregate, and make that this anti-slip material 2 can be on wet and slippery floor, still possess preferable skidproof effect, and can not cover the color of floor surface originally because of the tool transparency in the use, can not shelter evil people and countenance evil practices and health comparatively, simultaneously, also floor need not be destroyed, therefore purpose of the present invention can be reached really.
Claims (24)
1. anti-slip material that is coated on easily wettable and sliding floor is characterized in that:
Described anti-slip material comprises a lip-deep base coating that can be coated on described smooth floor, an and lip-deep nonskid coating that is coated on described base coating, described base coating contains acrylic ester acryl resin, inorganic aggregate and cement, and described nonskid coating contains a coating material and on-slip aggregate.
2. according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 1, it is characterized in that:
Inorganic aggregate in the described base coating contains short glass fiber, and following one of them material: quartz sand, corundum, and the mixing of above-mentioned material, the particle diameter of the quartz sand in the described inorganic aggregate is to be selected from following one of them mesh number filtration to obtain: 40 meshes, 60 meshes, and 100 meshes.
3. according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 2, it is characterized in that:
Coating material in the described nonskid coating is to be selected from following one of them material: aqueous epoxy resins, polyurethane resin, synthetic resin, macromolecule resin, acryl resin, transparent stone coating, and no-solvent type oiliness epoxy resin.
4. according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 2, it is characterized in that:
On-slip aggregate in the described nonskid coating is that particle diameter is filtered the white quartz that obtains by 50～80 mesh numbers, described coating material is to be selected from following one of them material: aqueous epoxy resins, polyurethane resin, synthetic resin, macromolecule resin, acryl resin, and no-solvent type oiliness epoxy resin, and the weight ratio of described coating material and described on-slip aggregate is 10: 3.
5. according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 3, it is characterized in that:
Described anti-slip material also comprises a face coat that is coated on the described nonskid coating; an and protective coating that is coated on the described face coat; described face coat is to be selected from following one of them material: aqueous epoxy resins, transparent stone coating; and no-solvent type oiliness epoxy resin, described protective coating is a transparent stone coating.
6. according to 3 described anti-slip materials that are coated on easily wettable and sliding floor of claim the, it is characterized in that:
Inorganic aggregate in the described base coating contains particle diameter and is filtered the white hollow minute particle that obtains by 100～200 mesh numbers, and following one of them material: it is quartzy by the white that the filtration of 80～200 mesh numbers obtains that particle diameter filters the white quartz, the particle diameter that obtain by 300～500 mesh numbers, and the mixing of above-mentioned material, the material of described white hollow minute particle is the group that is selected from following formation: pottery, glass and combination thereof, and the quartzy weight ratio with described white hollow minute particle of white is 1: 2.
7. according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 4, it is characterized in that:
Inorganic aggregate in the described base coating contains particle diameter and is filtered the white hollow minute particle that obtains by 100～200 mesh numbers, and following one of them material: it is quartzy by the white that the filtration of 80～200 mesh numbers obtains that particle diameter filters the white quartz, the particle diameter that obtain by 300～500 mesh numbers, and the mixing of above-mentioned material, the material of described white hollow minute particle is the group that is selected from following formation: pottery, glass, and combination, and the quartzy weight ratio with described white hollow minute particle of white is 1: 2.
8. according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 1, it is characterized in that:
On-slip aggregate in the described nonskid coating contains following one of them material: quartz sand, corundum, and the mixing of above-mentioned material.
9. according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 5, it is characterized in that:
On-slip aggregate in the described nonskid coating contains following one of them material: quartz sand, corundum, and the mixing of above-mentioned material.
10. according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 1, it is characterized in that:
On-slip aggregate in the described nonskid coating contains the adularescent hollow minute particle, and following one of them material: particle diameter filters the bead sand that the white that obtains is quartzy, particle diameter is obtained by the filtration of 30～50 mesh numbers by 30～50 mesh numbers, and the mixing of above-mentioned material, the material of described white hollow minute particle is the group that is selected from following formation: pottery, glass, and combination.
11., it is characterized in that according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 5:
On-slip aggregate in the described nonskid coating contains the adularescent hollow minute particle, and following one of them material: particle diameter filters the bead sand that the white that obtains is quartzy, particle diameter is obtained by the filtration of 30～50 mesh numbers by 30～50 mesh numbers, and the mixing of above-mentioned material, the material of described white hollow minute particle is the group that is selected from following formation: pottery, glass, and combination.
12., it is characterized in that according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 1:
Described base coating contains the inorganic aggregate of percentage by weight 2%-4%, the cement of percentage by weight 45%-75%, all the other are the acrylic ester acryl resin, the on-slip aggregate that contains percentage by weight 40%-60% in the described nonskid coating, all the other are described coating material.
13., it is characterized in that according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 1:
Also be added with water in the described base coating, and the mixture of acrylic ester acryl resin, described inorganic aggregate and cement, and the weight ratio of water is 5: 1: 1.
14., it is characterized in that according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 1:
Coating material in the described nonskid coating is a transparent stone coating, and described on-slip aggregate contains the adularescent hollow minute particle and white is quartzy, and the weight ratio of described transparent stone coating, white quartz and white hollow minute particle is 100: 15: 1.
15., it is characterized in that according to the described anti-slip material that is coated on easily wettable and sliding floor of claim 1:
Coating material in the described nonskid coating is a transparent stone coating, and described on-slip aggregate contains adularescent hollow minute particle and bead sand, and the weight ratio of described transparent stone coating, bead sand and white hollow minute particle is 100: 15: 1.
16. a using method that is coated on the anti-slip material of easily wettable and sliding floor is characterized in that:
Described using method comprises a base coating step and an anti-skidding coating step in regular turn, described base coating step is to apply a base coating on described smooth floor, described base coating contains acrylic ester acryl resin, inorganic aggregate, and cement, described anti-skidding coating step is after described base coating drying, apply a nonskid coating more thereon, described nonskid coating contains a coating material, and the on-slip aggregate.
17., it is characterized in that according to the described using method that is coated on the anti-slip material of easily wettable and sliding floor of claim 16:
Described using method also comprises a surface-coated step behind described anti-skidding coating step, described surface-coated step is to apply a face coat on the dry described nonskid coating that finishes, described face coat is to be selected from following one of them material: aqueous epoxy resins, transparent stone coating, and no-solvent type oiliness epoxy resin.
18., it is characterized in that according to the described using method that is coated on the anti-slip material of easily wettable and sliding floor of claim 17:
Described using method also comprises a floor cleaning before described base coating step; one patch step between between described floor cleaning and base coating step; one protective coating coating step after described surface-coated step; an and removal patch step that is positioned at behind the described protective coating coating step; described floor cleaning is that desire construction place with described smooth floor is cleaned up; described patch step is to sentence the patch that easily tears off in the desire construction on described smooth floor to enclose the scope that can supply described base coating to construct of putting up; described protective coating coating step is to apply a protective coating on the dry face coat that finishes; and the material of described protective coating is transparent stone coating, and described removal patch step is torn off described smooth floor with the patch that described patch step is attached.
19., it is characterized in that according to the described using method that is coated on the anti-slip material of easily wettable and sliding floor of claim 16:
In described anti-skidding coating step, be that on-slip aggregate and coating material evenly are mixed into described nonskid coating to scale, again described nonskid coating is coated on the described dry described base coating that finishes, containing percentage by weight in the described nonskid coating is the on-slip aggregate of 40%-60%, all the other are described coating material, and described coating material is to be selected from following one of them material: aqueous epoxy resins, polyurethane resin, synthetic resin, macromolecule resin, acryl resin, transparent stone coating, and no-solvent type oiliness epoxy resin.
20., it is characterized in that according to the described using method that is coated on the anti-slip material of easily wettable and sliding floor of claim 16:
In described anti-skidding coating step, be earlier described coating material to be coated on the described base coating, again the on-slip aggregate is sprayed on described coating material, containing percentage by weight in the described nonskid coating is the on-slip aggregate of 40%-60%, all the other are described coating material, and described coating material is to be selected from following one of them material: aqueous epoxy resins, polyurethane resin, synthetic resin, macromolecule resin, acryl resin, transparent stone coating, and no-solvent type oiliness epoxy resin.
21., it is characterized in that according to the described using method that is coated on the anti-slip material of easily wettable and sliding floor of claim 16:
In described base coating step, it is the cement of 45%-75% that described base coating contains inorganic aggregate, the percentage by weight that percentage by weight is 2%-4%, and all the other are the acrylic ester acryl resin.
22., it is characterized in that according to the described using method that is coated on the anti-slip material of easily wettable and sliding floor of claim 16:
In described base coating step, also be added with water in the described base coating, and the mixture of acrylic ester acryl resin, described inorganic aggregate and cement, and the weight ratio of water is 5: 1: 1.
23., it is characterized in that according to the described using method that is coated on the anti-slip material of easily wettable and sliding floor of claim 16:
In described anti-skidding coating step, the coating material of described nonskid coating is a transparent stone coating, and described on-slip aggregate contains the adularescent hollow minute particle and white is quartzy, and the weight ratio of described transparent stone coating, white quartz and white hollow minute particle is 100: 15: 1.
24., it is characterized in that according to the described using method that is coated on the anti-slip material of easily wettable and sliding floor of claim 16:
In described anti-skidding coating step, the coating material of described nonskid coating is a transparent stone coating, and described on-slip aggregate contains adularescent hollow minute particle and bead sand, and the weight ratio of described transparent stone coating, bead sand and white hollow minute particle is 100: 15: 1.