CN101324118B - Magnetic putty powder and construction method of magnetic wall surface - Google Patents
Magnetic putty powder and construction method of magnetic wall surface Download PDFInfo
- Publication number
- CN101324118B CN101324118B CN2008101407999A CN200810140799A CN101324118B CN 101324118 B CN101324118 B CN 101324118B CN 2008101407999 A CN2008101407999 A CN 2008101407999A CN 200810140799 A CN200810140799 A CN 200810140799A CN 101324118 B CN101324118 B CN 101324118B
- Authority
- CN
- China
- Prior art keywords
- magnetic
- putty
- wall surface
- powder
- putty powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a construction method for magnetic putty powders and magnetic wall surfaces. According to the part by weight, the magnetic putty powder consists of 5-60 parts of putty powders or adhesive and 95-40 parts of magnetic iron mine powders or iron powders which are uniformly mixed with each other; when the magnetic putty powder of the invention is used for plastering the wall surface, according to the design requirement, a trough with a certain length, width and depth is remained on the new wall surface which is not decorated or no the original wall surface; the magnetic putty powder added with water is uniformly mixed to prepare the magnetic putty; subsequently, the magnetic putty is filled in the trough and plastered flatly; after the magnetic wall surface is dried, required coatings are brushed on the magnetic wall surface. When the magnetic putty of the invention is used for plastering the wall surface, the wall surface has magnetism, facilitates the hanging of drawings, paints and decorations, and is convenient and beautiful.
Description
One, technical field:
The present invention relates to a kind of material of construction putty powder, particularly relate to a kind of constructional method that is suitable for the magnetic putty powder and the magnetic wall surface thereof of inner wall render and interior decoration.
Two, background technology:
Along with progress of science and technology, people more and more pay attention to the layout and the style of room, office, meeting room, and the brushing of indoor wall is played very basic effect in whole decoration link.Especially the promotion and application of coating and paint make the color of metope and texture more and more colourful colorful.But when these finishing material of brushing, must be through certain processing, this class is used for the material of interface processing such as wall, top, becomes usually " interfacial agents ", is commonly called as " putty ".Adopt general in the market putty powder to whitewash interior metope, on the metope after whitewashing when article such as wall chart paper, picture or ornament, people need fix with materials such as nail, paste, adhesive tapes usually, or tumble in iron sheet on wall, and are fixing with magnet absorption.Preceding several fixing meanss can produce certain destruction and not attractive in appearance to the metope that whitewashes, and office or meeting room need frequent replacing drawing usually simultaneously, adopt aforesaid method comparatively constant; Though the latter has satisfied the needs of frequent replacing drawing, iron sheet is set in protrudes on the metope outside the metope, can cause drawing unsettled, neither attractive in appearancely since so also be not easy on drawing, write or other relating operation.
Three, summary of the invention:
The problem that exists when the objective of the invention is to overcome at present article such as on metope wall chart paper, picture provides the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof.
In order to address the above problem, the technical solution used in the present invention is:
The invention provides a kind of magnetic putty powder, comprise putty powder and magnetite powder, is unit with the weight part, and described magnetic putty powder is to be mixed for 75～40 parts by 25～60 parts of putty powder and magnetite powder to be prepared from.
According to above-mentioned magnetic putty powder, described putty powder is any putty powder of selling on the market, and the granularity of described magnetite powder is-20 orders.
A kind of magnetic putty powder comprises putty powder and iron filings powder, is unit with the weight part, and described magnetic putty powder is to be mixed for 75～40 parts by 25～60 parts of putty powder and iron filings powder to be prepared from.
According to above-mentioned magnetic putty powder, described putty powder is any putty powder of selling on the market, and the granularity of iron filings powder is-20 orders.
A kind of constructional method of magnetic wall surface, according to design requirements, on former metope, mark the groove of certain-length, width and the degree of depth, groove depth is 2～4 millimeters, magnetic putty powder is added entry, make magnetic putty after stirring, then that the magnetic putty full-filling is also floating in groove, after treating the magnetic wall surface airing, brush coating in the above with former metope solid colour.
A kind of constructional method of magnetic wall surface, when on the new metope of not fitting up, whitewashing general putty, according to design requirements, reserve the groove of certain-length, width and a degree of depth, groove depth is 2～4 millimeters, and magnetic putty powder is added entry, make magnetic putty after stirring, then with the magnetic putty full-filling in groove and floating, treat the magnetic wall surface airing after, the required coating of brushing on the metope of brushing general putty and magnetic putty.
According to the constructional method of above-mentioned magnetic wall surface, the amount that described magnetic putty powder adds entry is 8～12% of a magnetic putty powder total amount.
Positive beneficial effect of the present invention:
1, adopt product magnetic putty powder of the present invention not only can play the effect of general putty powder plastering wall, have promptly that water resistance is strong, a scrubbing resistance, bonding strength height, after scraping wall and receiving light, very smooth exquisiteness; And the metope after whitewashing has magnetic.
2, adopt the metope after product magnetic putty powder of the present invention whitewashes to have magnetic, therefore, on having the metope of magnetic, not be used on the wall during article such as wall chart paper, picture and nail, be coated with paste, adhesive tape, also not be used in and inlay iron sheet on the wall, directly get final product with magnet absorption is fixing, not only convenient but also attractive in appearance like this, be convenient on the drawing of being hung, write, ruler operation etc.
Four, embodiment:
Following examples only in order to further specify the present invention, do not limit content of the present invention.
Embodiment one: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof
With the weight part is unit, gets putty powder 20kg and magnetite powder 80kg, and the two is mixed, and makes product magnetic putty powder of the present invention.
The constructional method of magnetic wall surface: according to design requirements, on former metope, mark the groove of certain-length, width and the degree of depth, groove depth is 2～4 millimeters, the magnetic putty powder of making is added entry, the add-on of water is generally 8～12% of magnetic putty powder gross weight, makes magnetic putty after stirring, and is then that the magnetic putty full-filling is also floating in groove, after treating the magnetic wall surface airing, brush coating in the above with former metope solid colour.
Embodiment two: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment one, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 25kg and magnetite powder 75kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment one.
Embodiment three: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment one, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 32kg and magnetite powder 68kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment one.
Embodiment four: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment one, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 38kg and magnetite powder 62kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment one.
Embodiment five: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment one, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 43kg and magnetite powder 57kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment one.
Embodiment six: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment one, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 50kg and magnetite powder 50kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment one.
Embodiment seven: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof
With the weight part is unit, gets putty powder 55kg and magnetite powder 45kg, and the two is mixed, and makes product magnetic putty powder of the present invention.
The constructional method of magnetic wall surface: when on the new metope of not fitting up, brushing general putty, according to design requirements, reserve the groove of certain-length, width and a degree of depth, groove depth is 2～4 millimeters, the magnetic putty powder of making is added entry, make magnetic putty after stirring, the add-on of water is generally 8～12% of magnetic putty powder gross weight, then that the magnetic putty full-filling is also floating in groove, treat magnetic wall surface and whitewash with general putty powder after the metope airing after, brush required coating in the above.
Embodiment eight: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment seven, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 60kg and magnetite powder 40kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment seven.
Embodiment nine: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment seven, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 16kg and magnetite powder 84kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment seven.
Embodiment ten: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment seven, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 12kg and magnetite powder 88kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment seven.
Embodiment 11: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment seven, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 5kg and magnetite powder 95kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment seven.
Embodiment 12: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment seven, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 28kg and magnetite powder 72kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment seven.
Embodiment 13: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment seven, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 35kg and magnetite powder 65kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment seven.
Embodiment 14: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and basic identical with embodiment seven, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 47kg and magnetite powder 53kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment seven.
Embodiment 15: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof
With the weight part is unit, gets putty powder 60kg and iron filings powder 40kg, and the two is mixed, and makes product magnetic putty powder of the present invention.
The constructional method of magnetic wall surface: according to design requirements, on former metope, mark the groove of certain-length, width and the degree of depth, groove depth is 2～4 millimeters, the magnetic putty powder of making is added entry, the add-on of water is 8～12% of a magnetic putty powder gross weight, makes magnetic putty after stirring, and is then that the magnetic putty full-filling is also floating in groove, after treating the magnetic wall surface airing, brush coating in the above with former metope solid colour.
Embodiment 16: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment pentadecyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 52kg and iron filings powder 48kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 15.
Embodiment 17: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment pentadecyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 56kg and iron filings powder 44kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 15.
Embodiment 18: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment pentadecyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 40kg and iron filings powder 60kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 15.
Embodiment 19: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment pentadecyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 45kg and iron filings powder 55kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 15.
Embodiment 20: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment pentadecyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 48kg and iron filings powder 52kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 15.
Embodiment 21: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment pentadecyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 32kg and iron filings powder 68kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 15.
Embodiment 22: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof
With the weight part is unit, gets binding agent 36kg and iron filings powder 64kg, and the two is mixed, and makes product magnetic putty powder of the present invention.
The constructional method of magnetic wall surface: when on the new metope of not fitting up, brushing general putty, according to design requirements, reserve the groove of certain-length, width and a degree of depth, groove depth is 2～4 millimeters, and the magnetic putty powder of making is added entry, makes magnetic putty after stirring, the add-on of water is 8～12% of a magnetic putty powder gross weight, then with the magnetic putty full-filling in groove and floating, treat magnetic wall surface and the metope airing that whitewashes with general putty powder after, on its metope, brush required coating.
Embodiment 23: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment docosyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 25kg and iron filings powder 75kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 22.
Embodiment 24: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment docosyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 28kg and iron filings powder 72kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 22.
Embodiment 25: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment docosyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 20kg and iron filings powder 80kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 22.
Embodiment 26: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment docosyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 12kg and iron filings powder 88kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 22.
Embodiment 27: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment docosyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets putty powder 16kg and iron filings powder 84kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 22.
Embodiment 28: the constructional method of a kind of magnetic putty powder and magnetic wall surface thereof, and originally identical with the embodiment docosyl, something in common is no longer narrated, and difference is:
With the weight part is unit, gets binding agent 5kg and iron filings powder 95kg, and the two is mixed, and makes magnetic putty powder.
The constructional method of magnetic wall surface is with embodiment 22.
Claims (5)
1. a magnetic putty powder comprises putty powder and magnetite powder, it is characterized in that: be unit with the weight part, described magnetic putty powder is to be mixed for 75～40 parts by 25～60 parts of putty powder and magnetite powder to be prepared from.
2. magnetic putty powder according to claim 1 is characterized in that: described putty powder is any putty powder of selling on the market, and the granularity of described magnetite powder is-20 orders.
3. the constructional method of a magnetic wall surface, according to design requirements, on former metope, mark the groove of certain-length, width and the degree of depth, groove depth is 2～4 millimeters, it is characterized in that: the described magnetic putty powder of claim 1 is added entry, make magnetic putty after stirring, then that the magnetic putty full-filling is also floating in groove, after treating the magnetic wall surface airing, brush coating in the above with former metope solid colour.
4. the constructional method of a magnetic wall surface, when on the new metope of not fitting up, whitewashing general putty, according to design requirements, reserve the groove of certain-length, width and a degree of depth, groove depth is 2～4 millimeters, it is characterized in that: the described magnetic putty powder of claim 1 is added entry, make magnetic putty after stirring, then with the magnetic putty full-filling in groove and floating, treat the magnetic wall surface airing after, the required coating of brushing on the metope of brushing general putty and magnetic putty.
5. according to the constructional method of each described magnetic wall surface of claim 3～4, it is characterized in that: the amount that described magnetic putty powder adds entry is 8～12% of a magnetic putty powder total amount.