CN101323722B - Nanometer silver carbon based inner wall coating - Google Patents
Nanometer silver carbon based inner wall coating Download PDFInfo
- Publication number
- CN101323722B CN101323722B CN2008100510530A CN200810051053A CN101323722B CN 101323722 B CN101323722 B CN 101323722B CN 2008100510530 A CN2008100510530 A CN 2008100510530A CN 200810051053 A CN200810051053 A CN 200810051053A CN 101323722 B CN101323722 B CN 101323722B
- Authority
- CN
- China
- Prior art keywords
- powder
- nanometer silver
- wall coating
- diatomite
- order
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a nano-silver carbon silicon interior wall paint. Calcium powder and diatomite powder crushed into 300 meshes to 400 meshes of fine powder, perlite powder and active carbon powder crushed into 50 meshes to 70 meshes of fine powder are mixed and added with nano-silver and water to be blended into slurry state to form the paint. The paint of the invention utilizes the nano-silver broad-spectrum high-efficiency sterilization (virus killing) mechanism, and the coconut shell carbon and diatomite adsorption filtration energy-conservation principle to act on the surface of the wall, and is characterized by sterilization, mold resistance, adsorption, air purification, negative ion releasing, fireproofness, fire retardation, heat preservation, energy conservation, etc., and remedies and solves all the disadvantages of traditional wall materials. The paint of the invention can be used for the decoration and fitment of all interior walls as the wall materials.
Description
Technical field:
The present invention discloses a kind of nanometer silver carbon based inner wall coating, is used for the functional ornamentation of house inner wall, belongs to technical field of construction and decoration materials.
Background technology
In building decoration technology neck, the decoration coating that is used for interior wall has a lot, and the decorating wall surfacing extensively adopts traditional materials such as wallpaper, ceramic tile, Art Stone.The a lot of weak points of these material ubiquities: the free property content of chemical substances height that has, human body are irritated easily; Become mildewed easily after the humidity that has, mouldy, blackening, and insulation, flame retardant properties are bad; The ceramic tile that also has contains a large amount of radioactive substances, and HUMAN HEALTH is produced harm, and in a word, these interior wall coatings are not suitable for the daily life in people's modern times.
Summary of the invention:
The invention provides a kind of nanometer silver carbon based inner wall coating, overcome shortcomings such as the existing interior walls finishing material feature of environmental protection is poor, function singleness.
Nanometer silver carbon based inner wall coating of the present invention, make by following raw material:
Diatomite 5.5～40kg, gac 1.5～3kg, calcium powder 2.0～8.0kg, perlite 0.2～1.0kg, redispersible latex powder 0.03～0.05kg, nanometer silver 100～500ml, surplus are water.
Described interior wall coating, calcium powder are selected from one or more combinations in water-ground limestone, precipitated chalk, calcium hydroxide, the treated carbonates.
Described interior wall coating, gac comprise vegetable active carbon such as coconut husk, rice husk, bamboo.
The preparation technology of nanometer silver carbon based inner wall coating of the present invention, it is characterized in that: diatomite, calcium powder, redispersible latex powder are ground into 300～400 order fine powders, perlite, activity charcoal powder are broken into 50～70 order fine powders, above-mentioned fine powder is mixed the back add nanometer silver and water furnishing pulpous state.
During use, get coating of the present invention with special tool to direct blade coating of metope or spraying, seasoning, it is saturated that 3 ~ 7 days intensity can reach, and when possessing suitable intensity, can embody its function of nanometer silver carbon silicon wall material fully.
The present invention is to be the major function material with nanometer silver, coconut carbon and diatomite; By nanometer silver with in all fungal spore substance metabolic enzymes of metope-the SH combination, enzyme is lost activity, thus efficient kill fungi; Utilize superpower absorption, the purification function of cocoanut active charcoal, airborne organic chemicalss such as " formaldehyde, benzene,toluene,xylene, acetone, sulfide, mercury vapour " is thoroughly adsorbed.The absorption property of performance diatomite (Sio2), negative ion switching performance, adjusting psychometric performance and fire protection flame retarding, energy-efficient performance.Nanometer silver and cocos active carbon and diatomaceous the combination can efficiently improve 50～200 times of cocos active carbon and diatomaceous various functions.Naturally produce objectionable impurities in the absorbed air, the quality that purifies air, regulate atmospheric moisture, discharge negative ion and fire protection flame retarding (not producing obnoxious flavour during fire).And, the various functions such as malicious mist that produce because of fire of purification filtering.
Positively effect of the present invention is: utilize nanometer silver broad-spectrum high efficacy sterilization (poison) mechanism and coconut carbon and diatomite adsorption to filter energy-saving principle and act on surface of wall, have sterilization, prevent going mouldy, adsorb, purify air, discharging characteristics such as negative ion, fire protection flame retarding, heat preservation energy-saving.Remedy, solve all drawbacks of conventional wall material.Can be used for all inner wall decoration finishings and do body of wall wall material.
Embodiment:
By following examples the present invention is described for example further.And do not limit the present invention in any way.Do not deviate from that those skilled in the art realize easily any change or change all will fall into
Within the claim scope of the present invention.
Embodiment 1:
With 400 order diatomite rt 3040kg, 70 order cocoanut active charcoal 2.5kg, 400 order water-ground limestone 2kg, 400 order precipitated chalk 3.5kg, 400 order calcium hydroxide 2.5kg, 400 order redispersible latex powders, 400 order 0.03kg, 70 order perlite 0.2kg, nanometer silver 500ml, pure water 5kg, uniform mixing gets the present invention.
Embodiment 2:
Get diatomite ps5 (300 order) 25kg, rice hull active carbon (50 order) 3.0kg, heavy Calcium hydrogen carbonate (300 order) 2kg, calcium hydroxide (300 order) 2.5kg, treated carbonates (300 order) 1.0kg, redispersible latex powder (300 order) 0.05kg, perlite (40 order) 1.0kg, nanometer silver 100ml, pure water 8kg, uniform mixing gets the present invention.
Embodiment 3
Diatomite (350 order) 20g, bamboo gac (60 order) 1.5kg, water-ground limestone (350 order) 2kg, precipitated chalk (350 order) 2.5kg, redispersible latex powder (350 order) 0.04kg, treated carbonates (350 order) 3kg, perlite (40 order) 0.2kg, nanometer silver 500ml, pure water 7kg, uniform mixing gets the present invention.
Embodiment 4
Diatomite (400 order) 12kg, cocoanut active charcoal 3.0kg (70 order), water-ground limestone 2kg (400 order), precipitated chalk 3.5kg (400 order), redispersible latex powder (400 order) 0.03kg, perlite 0.2kg (40 order), nanometer silver 300ml, pure water 9kg, uniform mixing get the present invention.
Embodiment 5
Diatomite (300 order) 5.5kg, gac (50 order) 1.0kg, precipitated chalk (300 order) 2.5kg, redispersible latex powder (300 order) 0.03kg, perlite (50 order) 0.1kg, nanometer silver 100ml, pure water 9kg, uniform mixing gets the present invention.
Claims (4)
1. nanometer silver carbon based inner wall coating, it is characterized in that being made by following raw material: diatomite 5.5～40kg, gac 1.5～3kg, calcium powder 2.0～8.0kg, perlite 0.2～1.0kg, redispersible latex powder 0.03～0.05kg, nanometer silver 100～500ml, surplus are that water is with above-mentioned raw materials furnishing pulpous state.
2. the described interior wall coating of claim 1, it is characterized in that: calcium powder is selected from one or more combinations in water-ground limestone, precipitated chalk, calcium hydroxide, the treated carbonates.
3. the described interior wall coating of claim 1, it is characterized in that: gac is selected from any in coconut husk, rice husk, the bamboo vegetable active carbon.
4. the preparation technology of the described interior wall coating of claim 1, it is characterized in that: diatomite, calcium powder, redispersible latex powder are ground into 300～400 order fine powders, perlite, activity charcoal powder are broken into 50～70 order fine powders, above-mentioned fine powder is mixed the back add nanometer silver and water furnishing pulpous state.