CN101298550B - Nanometer mildewproof sealing neutral silicone resin - Google Patents

Nanometer mildewproof sealing neutral silicone resin Download PDF

Info

Publication number
CN101298550B
CN101298550B CN2008101306930A CN200810130693A CN101298550B CN 101298550 B CN101298550 B CN 101298550B CN 2008101306930 A CN2008101306930 A CN 2008101306930A CN 200810130693 A CN200810130693 A CN 200810130693A CN 101298550 B CN101298550 B CN 101298550B
Authority
CN
China
Prior art keywords
portions
mildew
neutral silicone
nano
environment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2008101306930A
Other languages
Chinese (zh)
Other versions
CN101298550A (en
Inventor
陈炳耀
陈炳强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Sanhe Chemical Industry Technology Co Ltd
Original Assignee
Guangdong Sanhe Chemical Industry Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Sanhe Chemical Industry Technology Co Ltd filed Critical Guangdong Sanhe Chemical Industry Technology Co Ltd
Priority to CN2008101306930A priority Critical patent/CN101298550B/en
Publication of CN101298550A publication Critical patent/CN101298550A/en
Application granted granted Critical
Publication of CN101298550B publication Critical patent/CN101298550B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a nano-neutral mildew resistant silicone sealant, the formula of which is as follows by weight portion: 90-110 portions of hydroxyl-terminated polysiloxane, 1-20 portions of gas phase silica, 30-60 portions of active calcium carbonate, 2 to 5 portions of dye, 3-15 portions of methyl triethoxy silane, 0.4-2 portions of composite titanic compound, 1-6 portions of Gamma-chloropropyl triethoxy silane, 0.05-0.2 portion of anti-mildew agent, and 0.5-2.5 portions of anion additive. The invention has following advantages: 1. fresh odor by adopting the methyl triethoxy silane as a cross linker; 2. rapid vulcanizing speed by adopting environment protective composite titanic compound as a catalyst; 3. the adding of environment protective anti-mildew agent to improve the durable anti-mildew property of the sealant in humid environment such as a bathroom and a kitchen etc, being environment friendly without side effects to human body; 4. the adding of anion additive which can continuously release anion to improve the quality of indoor air.

Description

Nano mildew-proof neutral silicone sealer
Technical field
The present invention relates to a kind of architecture indoor finishing and use sealing material, specifically is nano mildew-proof neutral silicone sealer.
Technical background
In recent years, the decoration of residential building requires increasingly high, and warming installation is gradually improved, and the room airtight performance is constantly strengthened, and the steam accumulation phenomena that thereupon in bathroom, kitchen, produces is also comparatively general.Cause growing in a large number of wall and corner mould thus, having a strong impact on the improvement of people's health and living environment.Especially at plum rain season, indoor glass, wall surface even the globule that can condense more help the breeding of mould.
The architecture indoor finishing is of a great variety with sealing material in the market, and quality is uneven, and commonly single-component room temperature vulcanized Zylox is claimed silicone sealant again.Silicone sealant is divided into two kinds usually; A kind of is acid silicone sealant; Another kind is the neutral silicone sealer, and acid silicone sealant can discharge the acetic acid small molecules when vulcanizing, and irritating smell is strong; Part neutral silicone sealer can discharge ketoxime class organic cpds, and a kind of special odor is arranged.In addition, a lot of silicone sealants do not possess antimildew function yet, after use for some time easy " mouldy, blackening ".In silicone sealant, add mould inhibitor,, very be necessary, but traditional mould inhibitor itself has certain toxicity, during especially for the kitchen, be prone to HUMAN HEALTH is produced harm to prevent growing of mould.
The silicone sealant that the smell of Development of New Generation is little, environmentally friendly, mildew resistance is good is the inevitable requirement of social development.
Summary of the invention
The purpose of this invention is to provide nano mildew-proof neutral silicone sealer, common silicone sealant is improved, adopt Union carbide A-162 as linking agent, discharge ethanol during sulfuration, smell is pure and fresh; The compound titaniferous compound that adopts environment-friendly type is as catalyzer, and vulcanization rate is fast; Add the environment-friendly type mould inhibitor, improved the lasting fungicidal properties of sealer in wet environments such as bathroom, kitchen, environmentally friendly, to the human non-toxic spinoff; Add anionic additive, can continue to discharge negative ion, improved IAQ.
Nano mildew-proof neutral silicone sealer of the present invention is achieved in that prescription is by weight ratio:
90~110 parts of hydroxy-end capped ZGK 5
1~20 part of aerosil
30~60 parts of treated carbonatess
2~5 parts of pigment
3~15 parts of Union carbide A-162s
0.4~2 part of compound titaniferous compound
1~6 part of γ-chloropropyl triethoxysilane
0.05~0.2 part of mould inhibitor
0.5~2.5 part of anionic additive
Aforesaid hydroxy-end capped ZGK 5 is α, alpha, omega-dihydroxy polydimethyl siloxane;
Aforesaid aerosil heated 5 hours in 90~150 ℃ of baking ovens before using;
Aforesaid pigment is at least a in carbon black, white titanium pigment, iron oxide red, phthalocyanine blue, the phthalocyanine green, heating 5 hours in 90~150 ℃ of baking ovens before using;
Aforesaid compound titaniferous compound is the mixture of tetra isopropyl titanate and two (acetylacetone based) di-isopropyl titanic acid ester, and weight ratio is a tetra isopropyl titanate: two (acetylacetone based) di-isopropyl titanic acid ester=2: 0.5~2;
Aforesaid mould inhibitor is a nano-Ag particles;
Aforesaid anionic additive is a negative ion paint additive catalyst type.
The method of manufacture of nano mildew-proof neutral silicone sealer of the present invention:
Hydroxy-end capped ZGK 5, aerosil are added in the planetary mixer, vacuumize, vacuum tightness 0.09MPa stirred 30~120 minutes under rotating speed 25~60rpm; Add treated carbonates, pigment, be heated to 100 ℃, vacuumize, vacuum tightness 0.09MPa stirred 30~120 minutes under rotating speed 25~35rpm; Add Union carbide A-162, compound titaniferous compound, γ-chloropropyl triethoxysilane, mould inhibitor, anionic additive, at vacuum tightness 0.09MPa, rotating speed 25~60rpm reacted 45~120 minutes down, made nano mildew-proof neutral silicone sealer.
The present invention compared with prior art has following characteristics:
1. adopt Union carbide A-162 as linking agent, smell is pure and fresh;
2. the compound titaniferous compound that adopts environment-friendly type is as catalyzer, and vulcanization rate is fast;
3. add the environment-friendly type mould inhibitor, improved the lasting fungicidal properties of sealer in wet environments such as bathroom, kitchen, environmentally friendly, to the human non-toxic spinoff;
4. the interpolation anionic additive can continue to discharge negative ion, improves IAQ.
Embodiment
Embodiment 1
With α, 100 kilograms of alpha, omega-dihydroxy polydimethyl siloxanes, aerosil add in the planetary mixer for 12 kilograms, vacuumize; Vacuum tightness 0.09MPa, rotating speed 35rpm stirs after 60 minutes; Add 50 kilograms of treated carbonatess, 2 kilograms of carbon blacks, be heated to 100 ℃, vacuumize; Vacuum tightness 0.09MPa; Stirred 60 minutes, and added 14 kilograms of Union carbide A-162s, 4 kilograms of γ-chloropropyl triethoxysilanes, 0.5 kilogram of tetra isopropyl titanate, 0.3 kilogram of two (acetylacetone based) di-isopropyl titanic acid ester, 0.1 kilogram of nano-Ag particles, 1.2 kilograms on negative ion paint additive catalyst type again, at vacuum tightness 0.09MPa; Rotating speed 35rpm reacted 90 minutes down, made nano mildew-proof neutral silicone sealer.
Embodiment 2
With α, 110 kilograms of alpha, omega-dihydroxy polydimethyl siloxanes, aerosil add in the planetary mixer for 10 kilograms, vacuumize; Vacuum tightness 0.09MPa, rotating speed 35rpm stirs after 60 minutes; Add 60 kilograms of treated carbonatess, 4 kilograms of white titanium pigments, be heated to 100 ℃, vacuumize; Vacuum tightness 0.09MPa; Stirred 60 minutes, and added 13.5 kilograms of Union carbide A-162s, 5 kilograms of γ-chloropropyl triethoxysilanes, 0.6 kilogram of tetra isopropyl titanate, 0.4 kilogram of two (acetylacetone based) di-isopropyl titanic acid ester, 0.2 kilogram of nano-Ag particles, 1.5 kilograms on negative ion paint additive catalyst type again, at vacuum tightness 0.09MPa; Rotating speed 35rpm reacted 90 minutes down, made nano mildew-proof neutral silicone sealer.
Embodiment 3
With α, 90 kilograms of alpha, omega-dihydroxy polydimethyl siloxanes, aerosil add in the planetary mixer for 15 kilograms, vacuumize; Vacuum tightness 0.09MPa, rotating speed 35rpm stirs after 60 minutes; Add 30 kilograms of treated carbonatess, 5 kilograms of iron oxide reds, be heated to 100 ℃, vacuumize; Vacuum tightness 0.09MPa; Stirred 60 minutes, and added 11.5 kilograms of Union carbide A-162s, 3 kilograms of γ-chloropropyl triethoxysilanes, 0.8 kilogram of tetra isopropyl titanate, 0.3 kilogram of two (acetylacetone based) di-isopropyl titanic acid ester, 0.05 kilogram of nano-Ag particles, 2.0 kilograms on negative ion paint additive catalyst type again, at vacuum tightness 0.09MPa; Rotating speed 35rpm reacted 90 minutes down, made nano mildew-proof neutral silicone sealer.
Main raw material(s) title, technical indicator:
1. α, alpha, omega-dihydroxy polydimethyl siloxane
Outward appearance: the water white transparency thick liquid, do not have mechanical impurity
Viscosity (25 ℃, mPas): 2000~300000
2. aerosil
Specific surface area (m 2/ g): 150~200
Dioxide-containing silica is (based on firing product, %): >=99.8
Apparent density (g/L): 25~60
3. treated carbonates
Outward appearance: white fine and smooth lightweight powder
Calcium carbonate content (%): >=97
Moisture (%) :≤0.3
4. carbon black
Outward appearance: black superfine powder
Specific surface area (m 2/ g): 10~35
Screenings (63 μ m sieve apertures, %) :≤0.3
5. white titanium pigment
Outward appearance: white powder
Content of titanium dioxide (%): >=92
Screenings (63 μ m sieve apertures, %) :≤0.3
6. iron oxide red
Outward appearance: red powder
Iron level is (with Fe 2O 3Meter, %):>=95
Screenings (63 μ m sieve apertures, %) :≤0.3
7. phthalocyanine blue
Outward appearance: mazarine powder
Tinting strength is (with the standard ratio, %): 95~105
Screenings (63 μ m sieve apertures, %) :≤0.3
8. phthalocyanine green
Outward appearance: dark green powder
Tinting strength is (with the standard ratio, %): 95~105
Screenings (63 μ m sieve apertures, %) :≤0.3
9. Union carbide A-162
Outward appearance: colourless transparent liquid, do not have mechanical impurity
Chromatographic purity (%): >=98
10. tetra isopropyl titanate
Outward appearance: colourless or little yellow homogeneous transparent liquid
Density (25 ℃, g/cm 3): 0.96~1.00
Content of titanium dioxide (%):>27
Two 11. (acetylacetone based) di-isopropyl titanic acid ester
Outward appearance: light red transparent liquid
Density (25 ℃, g/cm 3): 0.98~1.02
Content of titanium dioxide (%): 16~17
12. nano-Ag particles
Particle diameter (nm):<25
13. negative ion paint additive catalyst type
Outward appearance: white powder
Specification (order): >=4000
14. γ-chloropropyl triethoxysilane
Chromatographic purity (%): >=98
Density (25 ℃, g/cm 3): 0.998~1.002.
By standard " JC/T 885-2001 mildewproof sealant for building " standard sampling inspection, its main performance index such as following table.
Preface Project Technical indicator Assay Conclusion
1 Outward appearance The uniform and smooth paste Meet Qualified
2 Fungicidal properties 1 grade Meet Qualified
3 Surface drying time, h ≤3 0.15 Qualified
4 Extrudability, s ≤10 6 Qualified
5 Sag, mm ≤3 0 Qualified
6 Elastic restoration ratio, % ≥60 80 Qualified
7 Tensile modulus, MPa >0.4 0.85 Qualified

Claims (3)

1. nano mildew-proof neutral silicone sealer is characterized in that prescription is by weight ratio:
Figure FSB00000784747100011
Described compound titaniferous compound is the mixture of tetra isopropyl titanate and two (acetylacetone based) di-isopropyl titanic acid ester, is by weight ratio: tetra isopropyl titanate: two (acetylacetone based) di-isopropyl titanic acid ester=2: 0.5~2.
2. nano mildew-proof neutral silicone sealer as claimed in claim 1 is characterized in that pigment is at least a in carbon black, white titanium pigment, iron oxide red, phthalocyanine blue, the phthalocyanine green.
3. nano mildew-proof neutral silicone sealer as claimed in claim 1 is characterized in that anionic additive is a negative ion paint additive catalyst type.
CN2008101306930A 2008-07-03 2008-07-03 Nanometer mildewproof sealing neutral silicone resin Active CN101298550B (en)