The heat treating method of mounting frame for air conditioner motor
Technical field:
The present invention relates to air conditioner motor, particularly relate to a kind of heat treating method of mounting frame for air conditioner motor.
Technical background: existing mounting frame for air conditioner motor material adopts the method for 65Mn Conventional Heat Treatment, and hardness reaches HRC22-26, and with 2 grades of tests of U.S. ASTM4169 truck vibrations standard, support ruptured after 2 hours, and work-ing life is short, has hidden danger.
Summary of the invention:
Purpose of the present invention is exactly the heat treating method that a kind of mounting frame for air conditioner motor will be provided, and it can overcome the existing defective of method that existing mounting frame for air conditioner motor material adopts the 65Mn Conventional Heat Treatment well.The object of the present invention is achieved like this, and a kind of heat treating method of mounting frame for air conditioner motor is to adopt the mounting bracket of 65Mn material to carry out vacuum heat treatment, and its vacuum oven process of thermal treatment is as follows: mounting bracket is cleaned with gasoline; Drying treatment, holding temperature are controlled at 105 ± 5 ℃, and soaking time is controlled at 12 ± 3min; Preheating in vacuum oven, rate of heating are controlled at 60-70 ℃/10-12min, and holding temperature is controlled at 710 ± 5 ℃, and soaking time is controlled at 20 ± 3min; Quench, at 15-20 ℃/6-8min, holding temperature is controlled at 840 ± 2 ℃ in vacuum oven internal heating speed control, and soaking time is controlled at 35 ± 2min, goes into quenching oil when charging into high pure nitrogen to 0.056MPa and stirs 12min; Clean cooling with aqueous rust preventive; Tempering in tempering stove, holding temperature are controlled at 420 ± 5 ℃, and soaking time is controlled at 190 ± 10min, oil dripping 3-5min, and air cooling is to room temperature; Clean with gasoline after the tempering.Hardness of the present invention reaches HRC37-48, and with 2 grades of tests of U.S. ASTM4169 truck vibrations standard, support ruptured after 6 hours, and long service life has been eliminated hidden danger.
Embodiment:
A kind of heat treating method of mounting frame for air conditioner motor is to adopt the mounting bracket of 65Mn material to carry out vacuum heat treatment, and its vacuum oven thermal treatment process is as follows: mounting bracket is cleaned with gasoline; Drying treatment, holding temperature are controlled at 105 ± 5 ℃, and soaking time is controlled at 12 ± 3min; Preheating in vacuum oven, rate of heating are controlled at 60-70 ℃/10-12min, and holding temperature is controlled at 7105 ℃, and soaking time is controlled at 20 ± 3min; Quench, at 15-20 ℃/6-8min, holding temperature is controlled at 840 ± 2 ℃ in vacuum oven internal heating speed control, and soaking time is controlled at 35 ± 2min, goes into quenching oil when charging into high pure nitrogen to 0.056MPa and stirs 12min; Clean cooling with aqueous rust preventive; Tempering in tempering stove, holding temperature are controlled at 420 ± 5 ℃, and soaking time is controlled at 190 ± 10min, oil dripping 3-5min, and air cooling is to room temperature; Clean with gasoline after the tempering.During concrete enforcement, carry out vacuum heat treatment with the mounting bracket of 65Mn material, with mounting bracket in cleaning barrels with the gasoline cleaning, reach no greasy dirt, no foul; Carry out drying treatment with the mode that mounts again in dry bucket, holding temperature is 107 ℃, and soaking time is 14min; With batch preheating in vacuum oven of 3000 mounting brackets, rate of heating is 65 ℃/11min, and holding temperature is 712 ℃, and soaking time is 21min; Quenching, is 18 ℃/7min in vacuum oven internal heating speed, and holding temperature is 840 ℃, and soaking time is 36min, goes into quenching oil when charging into high pure nitrogen to 0.056MPa and stirs 12min, reaches hardness HRC40-50; Mounting bracket is put into cleaning barrels clean cooling with aqueous rust preventive; Tempering in tempering stove, holding temperature are 420 ℃, and soaking time is 195min, and oil dripping 4min, air cooling reach hardness HRC37-48 to room temperature, microstructure 1-3 level, outward appearance: flawless, no black, non-oxidation look etc.; Clean in cleaning barrels with gasoline after the tempering, reach no greasy dirt, foul.